VITA® Suprinity®Glass-ceramic manufactured by VITA Zahnfabrik H. Rauter GmbH & Co. KG

Zirconia-reinforced, high-strength glass-ceramic material for reliable full-contour restorations

EFFICIENCY Easy processing thanks to material blanks properties providing edge stability, good polishing characteristics and high firing stability

STRENGTHHigh strength thanks to a zirconia-reinforced glass-ceramic matrix

ESTHETICSVITA® Suprinity® is a highly esthetic material with integratedtranslucency, opalescence and fluorescence

In-house milling

C/M series

2

Available shades ► VITA® Suprinity® blocks (for in-house milling) are available in two levels of translucency: HT

(High Translucent) and T (Translucent). Both translucencies are available in 8 shades: 0M1, A1, A2, A3, A3.5, B2, C2 and D2.

TOOTH-BASED

Inlay Onlay Veneer Partial crown Coping

n/a n/a

Full-contour crown

Telescopic crown

Bridge/barframework

Full-contour bridge

Vestibular veneering

ABUTMENT-BASED (AVAILABLE WITHIN THE CARES® X-STREAM™ SOLUTION)

n/a n/a

Coping on Ti-Base

Full-contour crown on Ti-Base

Coping on CAD/CAM abutment

Full-contour crown on CAD/CAM abutment

Available indications ► For final restorations ► For single tooth only

Recommended indicationPossible indicationNot possible indication (n/a)

VITA SUPRINITY C14 BLOCKS (EACH ARTICLE CONTAINS 5 BLOCKS)

Shade Art. for translucency T Art. for translucency HT

0M1 EN1S03024445 EN1S04024445

A1 EN1S03364445 EN1S04364445

A2 EN1S03374445 EN1S04374445

A3 EN1S03384445 EN1S04384445

A3.5 EN1S03394445 EN1S04394445

B2 EN1S03424445 EN1S04424445

C2 EN1S03464445 EN1S04464445

D2 EN1S03494445 EN1S04494445

3

WorkflowSTEPS OPTIONS

Nesting Position the restoration in the block

Milling Recommendation: Straumann® C / M series

Crystallization Recommendation: VITA® SMART.FIRE® for CARES®

Finishing PolishingRecommendation: VITA® SUPRINITY® PC Polishing Sets technical or clinicalStaining & glazingRecommendation: VITA® AKZENT® Plus LayeringRecommendation: Layering: VITA® VM 11 veneering ceramic

Cementing Adhesive Self-adhesiveConventional

Physical propertiesPROPERTIES VALUE

CTE [10-⁶ K] approx. 12.3

3-point flexural strength [MPa] approx. 420

Elastic modulus [GPa] approx. 70

Hardness according to Vickers (HV) [MPa] approx. 7000

Chemical solubility [μg/cm²] approx. 40

Chemical compositionELEMENTS WEIGHT

ZrO₂ (zirconia) 8 – 12 %

SiO₂ (silicon dioxide) 56 – 64 %

Li2O (lithium oxide) 15 – 21 %

La2O3 (lanthanum oxide) 0.1 %

Pigments < 10

Various > 10

3

Wall thickness

OnlayInlay

Veneer Partial crown Full-contour crown

≥ 1.5 mm

≥ 1 mm

≥ 1.0 mm≥ 1.0 mm ≥ 1.0 mm

≥ 0.7 mm

≥ 1.0 mm ≥ 1.0 mm ≥ 1.0 mm ≥ 1.0 mm

MINIMAL RESTORATION DESIGN

Preparation guidelines ► The preparation shall not have angles or sharp edges ► The shoulder preparation shall be with rounded inner edges and/or chamfer ► The preparation shall have retentive surfaces for conventional cementation

International Headquarters Institut Straumann AG Peter Merian-Weg 12 CH-4002 Basel, Switzerland Phone +41 (0)61 965 11 11 Fax +41 (0)61 965 11 01 www.straumann.com

Suprinity®, Akzent® and SMART.FIRE® are registered trademarks of VITA Zahnfabrik H. Rauter GmbH & Co. KG, Germany.

© Institut Straumann AG, 2019. All rights reserved.Straumann® and/or other trademarks and logos from Straumann® mentioned herein are the trademarks or registered trademarks of Straumann Holding AG and/or its affiliates.

490.

398/

en/A

/00

01/1

9