Chapter 3:Chapter 3:XX--ray Diffraction and Crystal Structure ray Diffraction and Crystal Structure
Determination Determination
LECTURE #06
Learning ObjectivesLearning Objectives
• To describe crystals in terms of the stacking of planes.
• How to use a dot product to solve for the angles between planes and directionsbetween planes and directions
• Describe a way to determine the crystal structure of a material using X-rays.
• Pages 83-87.Relevant Reading for this Lecture...
1
Recap of Miller IndicesRecap of Miller Indices
1) Last time we showed how to use vectors and Miller indices to define planes and directions in crystals.
2) Let’s start with a worked example of (2) and then move into today’s lecture.
2
2
z
In class example #2: SOLUTION
In a cubic unit cell, draw correctly a vector with indices [146].
Select your origin. Put it
wherever you want to.
This step is the opposite of clearing fractions!
Oy
[1 4 6]
. 6
These fractions denote
how far to step in the
4
6
1 6
6 6
indices
Div by
16
4 26 3
66 1
x
, , or directions
(away from the origin).
x y z
NOTE: It would be “wise” to select the origin so that you can complete the desired steps within the cell that you are using!
2
3
z
In class example #3:
In a cubic unit cell, draw correctly a vector with indices [542].
: [5 4 2]
. 55
5
4
5
2
5:
indices
Div by
O
y
5 5
1
52
5
4
5:step
145
25
x
NOTE: It would be “wise” to select the origin so that you can complete the desired steps within the cell that you are using!
5
4
3
MILLER INDICES FOR A SINGLE MILLER INDICES FOR A SINGLE PLANEPLANE
z
What is the plane bounded by the dash lines?
z
x y zIntercept 1 3/4 1/2
Reciprocal 1/1 4/3 2/1Clear 3 4 6
x
yINDICES 3 4 6
(346)
4
5
• When materials deform, they normally prefer to deform via shear in the closest packed directions on the closest
Remember this?Remember this? σ
directions on the closest packed planes!
The tensile axis is in a different direction than the shear direction.
[Direction]
σ
We’ll address this in more detail when we discuss mechanical properties!
(plane)
video6
[Plane normal]
2
4
Sometimes it is necessary to determine the angle between a couple of directions or g p
planes.
Sometimes it may be necessary to
Use the cosine law
determine whether a direction lies on a particular plane.
Use the dot product
7
Vector dot products“a dot b” = sum of each
vector index with its counterpart vector
1 2 3( , , )a a aa
E l Fi d h d d f d b if (1 2 3) d b (4 5 6)
1 2 3( , , )b b bba · b = a1 x b1 + a2 x b2 + a3 x b3
Example: Find the dot product of a and b if a = (1,2,3) and b = (4,5,6)
(4,5,6(1 ), 2,3) 1 4 10 12 3 84 325 6 a b· ·
8
5
Finding the angle between 2 vectorsa•b also equals the magnitude of atimes the magnitude of b times the cosine of the angle between vectors.
1 2 3( , , )a a aa
Vector Magnitudes1 2 3( , , )b b bb
1 21 2 33 cosa b baba ab ba
2 2 2 2 2 232 1 21 3 b ba a a b ba
·
Re-arrange and solve for cos θ. This yields the familiar cosine law:
1 2 3
2 2 2
1 2
1 2 32 2 2
1 2 3
3cosa a ab
b b ba
b b
a a
aa
bb
9
Finding the angle between 2 vectorsFinding the angle between 2 vectors
1 2 3( , , )a a aa
Example: Find the angle between a and b if a = (1,2,3) and b = (4,5,6)
1 2 3( , , )b b bb
2
1
2 22 22 4 5 6
32cos 0.9746
14 77
cos (0
1
.9746) 12
2 3
1 2
. 3
3
9
4 5 6
aa
bb
·
10
6
Angle between planes: Dot Product
We can define planes using vectors perpendicular to them!
Normal vectors have the same indices as the planes!
D D
cosD D D D
D u a v b w c
D u a v b w c
·
2 2 2 2 2 2cos
( ) ( ) ( )
D D u u v v w wD D u v w u v w
Equations work with Miller indices!11
How to tell if a direction lies on a planeHow to tell if a direction lies on a plane
If the dot product of the vector and plane = 0,
then the vector lies on the plane
cos 0D P D P u h v k w l
[ ]
D ua vb wc
uvw
( )
P ha kb lc
hkl
·
12
[ ]uvw
( )hkl
[ ]hkl
7
Which members of the <111> family of directions lie within the (110) plane?
In Class Example
13
Which members of the <111> family of directions lie within the (110) plane?
In Class Example: SOLUTION
The [110] direction is perpendicular (i.e., normal) to the (110) plane.
The directions that lie on this plane will give a zero dot product with [110].
Now substitute in the members of the <111> family and see which give a zero dot product. The <111> family is:
Substitute each direction in for [hkl] as shown below:
[110] [ ] 1 1 0hkl h k l
[111] , [111] , [111] , [111] , [111] , [111] , [111] , [111]
·
Substitute each direction in for [hkl] as shown below:
SOLUTION: [111],[111],[111], and [111]
[110] [111] 1 1 1 1 0 1 2
[110] [111] 1 1 1 1 0 1 0
...etc
This one is on the (110) plane.
Look for all instances where the dot product = zero.
·
·
14
8
Atomic packing and the unit cellAtomic packing and the unit cell
• We can visualize crystals structures as stacked planes of atoms.
A ABB
(a) Non-close-packed layer A. (b) Stack next layer on B sites. (c) The BCC unit cell
BB
(a) A square grid of spheres. (b) A second layer, B, nesting in the first, A; repeating this sequence gives ABABAB…
Packing resulting in (c) the BCC crystal structure.
Yields ABABAB… stacking. BCC packing.
15
2
Now that we understand planes – how do crystal structures compare?
Close Packed Stacking Sequence in FCC
16
9
BBC
BBCC
• ABCABC... Stacking Sequence• 2D Projection
What is the Close Packed Stacking Sequence in FCC?What is the Close Packed Stacking Sequence in FCC?
A sites
B B
BB B
C sites
C C
CA
B
B sitesB sites B B
BB BC C
CAA
C C
C
A• FCC Unit Cell B
C
5
17
• ABAB... Stacking Sequence
• 3D Projection • 2D Projection
Hexagonal CloseHexagonal Close--Packed Structure (HCP)Packed Structure (HCP)
• 3D Projection • 2D Projection
c
A sites
B sites
A sites A: Bottom layer
B: Middle layer
A: Top layer
• Coordination # = 12
• APF = 0.74
Adapted from Fig. 3.3(a),Callister 7e.
6 atoms/unit cell
ex: Cd, Mg, Ti, Zn
• c/a = 1.633
a
2
18
10
A comparison of the stacking sequence of close packed A comparison of the stacking sequence of close packed planes in HCP & FCC crystalsplanes in HCP & FCC crystals
FCC
Atoms in this plane lie directly above the bottom plane
Atoms in the C plane do
HCP
pnot lie directly above either A or B planes
Top View Side View
Atoms in this plane
lie directly above this plane
19
A comparison of HCP and FCC stacking sequence of A comparison of HCP and FCC stacking sequence of close packed planesclose packed planes
FCCHCP
This is similar to Figs. 3.30 – 3.32 on pages 78 and 79 of your book.
20
11
A comparison of the stacking sequence of close packed A comparison of the stacking sequence of close packed planes in HCP & FCCplanes in HCP & FCC
FCC This is the face of the FCC unit cell
HCP unit cell
HCP
Just another visual to help you out21
How Can We Determine Crystal Structures?How Can We Determine Crystal Structures?
• Measure the inter-planar spacing.• The inter-planar spacing in a particular direction is
the distance between equivalent planes of atoms.the d stance between equ valent planes of atoms.– Function of lattice parameter– Function of crystal symmetry
y
(100)(110)
z
(i.e., how atoms are arranged)
a
x
(210)
Assuming no intercept on z-axis
d210
22
12
How do we Measure this Spacing?How do we Measure this Spacing?XX--Ray DiffractionRay Diffraction
• Diffraction gratings must have spacing comparable to the wavelength () of diffracted radiation (X-rays).
• In crystals: diffraction gratings are planes of atoms. Spacing is the distance between parallel planes of atoms.
• We can only resolve a spacing that is bigger than .(This is why we use X-rays… they are approximately the same size as planar spacings)
23
Bragg’s Law:Bragg’s Law:
Bragg’s Law:
2 sinn d gg
Where:
• is half the angle between the diffracted beam and the original beam direction
• is the wavelength of X-ray
•d is the interplanar spacing 24
13
2 sinn d
Bragg’s Law:Bragg’s Law:
0
2 2 2 2sinhkl
add
n h k l
Interplanar spacing:
d
2 sinn d Lattice parameter
25d
Miller IndicesOrder of reflection(integer)
25
XX--Ray Diffraction PatternRay Diffraction Pattern
(110)
z
c
z
y
c
z
y
c
(110)
(200)
(211)
Inte
nsity
(re
lativ
e)
x
ya b
c
x
ya b
x
ya b
Adapted from Fig. 3.40, Callisterand Rethwisch 4e. P. 86
Diffraction angle 2
Diffraction pattern for polycrystalline -iron (BCC)
3
26
14
Why do different crystals diffract Why do different crystals diffract different planes?different planes?
It’s based on atomic arrangement.
Thus, there are rules that define which planes diffract.
Some reflections aren’t observed. WHY?
Atomic arrangement prevents it.27
Why is the Why is the {100} {100} not an allowed reflection in BCC?not an allowed reflection in BCC?
d
Diffraction from (001) planes.Diffracted X-rays are in phase(i.e., they line up perfectly).
001d002d
Diffraction from (002) planes.X-rays diffracted from (002)are shifted 180° out of phase
(i.e., they do not line up perfectly).
λ λ
Sums to zero.
Sums to twice as
large
Related to equations 3.16 and 3.16 on page 84.28
15
What would be the (hkl) indices for the three lowest diffraction-angle peaks for BCC metal?
In Class Example
29
First, satisfy reflection criteria for BCC (i.e., h + k + l = even number).
Second, combine d-spacing equation with Bragg’s Law:
What would be the (hkl) indices for the three lowest diffraction-angle peaks for BCC metal?
In Class Example: SOLUTION
d
Re-arrange so that we can determine θ; you will get:
Now we plug in hkl values such that the reflection rule is satisfied. NOTE: smallest θcorresponds to smallest combination of hkl values.
0
2 2 2 2sinhkl
add
n h k l
2 2 2sin2 o
h k la
corresponds to smallest combination of hkl values.
2 2 2
100 1110 2111 3200 4210 5211 6
Indices h k l h k l BCCodd no
odd no
odd no
even YES
even YES
even YES
A great variation on this question would be: What are the reflection angles
30
16
• We can use the dot product as a means to identify angles between planes and directions (this will be important when we get to mechanical behavior!)
• Crystal structure can be determined by measuring inter-planar
SummarySummary
spacing.
• We use X-ray Diffraction to measure this spacing.
• Inter-planar spacing can be calculated using:
• Bragg’s Law:
0
2 2 2 2sinhkl
add
n h k l
2 id • Bragg s Law:
• Depending on crystal types, certain {hkl} planes will diffraction and can be used to identify the crystal structure. We have a set of selection rules to help us identify them. (You do not need to memorize these rules – they would be given to you on an exam, if a question was asked.)
2 sinn d
31