Belgo BekaertWelding RodsE 6013

Belgo Bekaert E 6013 Welding Rods are produced

by Belgo Bekaert Arames S.A.

0800 31 0614www.belgobekaert.com.br

Produced by Belgo Bekaert employing the most advanced technology, the E 6013 is a rutile welding rod of superb operating characteristics and affordable cost. Its web is made of high-quality, low-carbon Belgo Bekaert wire, with very low content of phosphorus and sulfur which assures superior mechanical properties to the welding bead.Its coating, consisted of rutile, iron-manganese alloy, iron-silicon alloy, and potassium silicate,allows its use in alternating current and low amperage, providing optimum arc stability and rapidly releasing the slag from the bead.Metal transfer is easy, smooth, and uniform, producing beads of excellent quality and finefinishing. Ideal for general applications in all types of joints and positions, such as in metalstructures, and general construction; naval industry welding; thin plate welding; field welding;general equipment maintenance; and metal shop work.

Characteristics

Welding CurrentCurrent and Diameter

Mechanical Properties of the Metal

Deposited

Other Welding Data

Chemical Analysis of the Deposited Metal

Dimensions

Posição de Soldagem

High-quality and low-carbon Belgo Bekaert wires having very lowcontent of phosphorus (P) and sulfur (S), which assures superiormechanical properties to the welding bead.

Rutile, iron-manganese alloy, iron-silicon alloy, and potassiumsilicate allow its use in alternating current and low amperage.

Metal structures, general construction, naval industry welding, thin plate welding, field welding, general equipment maintenance,and metal shop work.

Flat Horizontal Horizontal

Web Coating

Applications

Vertical Upward Vertical Downward Upside Down

Diameter (mm) Current (A)

2,00 50 702,50 60 1003,25 80 1504,00 105 2055,00 155 3006,00 195 350

Diameter Length Box Weight(mm) (mm) (kg)

2,00 300 152,50 350 183,25 350 204,00 350 205,00 350 206,00 450 25

Tensile Strength (MPa) 420 minimum

Yield Strength (MPa) 340 minimum

Elongation (%) 22 - 24

Voltage: 18 a 27V CA> 50V CC + ou -

% C 0,07

% Mn 0,35

% Si 0,20

400350300250200150100

500

0 2,00 2,50 3,25 4,00 5,00 6,00