Biodegradable Food Packages
Valentis Solution
Novel materials combining NCC and additional nanoparticles (NPs)
Incorporated as films in polymer products – easy integration into manufacturing processes
• Self-assembly • Strong • Transparent • Thin
• Gas barrier • Spectral control • Texture control • Anti bacterial • Super Hydrophobic
surface
Valentis Advanced Materials
Valentis
Know-how + IP
2
Patent in NP
Valentis Core Technology
A B C
A- Transparent NCC film B- Electron microscopy picture of highly ordered NCC multi layer film C- Electron microscopy picture of composite NCC + NPs film, with NPs spread
homogeneously between NCC layers
CNC: An Excellent Carrier for Nano-particles
Valentis Core Technology
Improve polymer qualities while maintaining/reducing costs:
• Lighter
• Stronger
• Provides spectrum control while still transparent
• Higher recyclability (CNC is biodegradable)
• Can be tailored for the customer needs
• Super hydrophobic surface
Research & Development – Reducing Oxygen Transfer Rate (OTR)
OTR – tested according to ASTM D3985 at 25°C 0%RH
1 2
Similar OTR results for laminated and coated films
1
1 PE+PET 2 PE + BOPP
1
Research & Development - Spectral Control
Adjustable UV barrier
6
Adjustable IR barrier
Research & Development – Improving Mechanical Properties
CNC coating improves PE, BOPP and PLA elastic modulus
Elastic Modulus
(MPa) Coat thickness film thickness Sample
176.6±2.8 - 67 µm PE Control
(uncoated PE)
385.6±48.8 1 µm 68 µm PE + ValCoat
2070±287 - 24 µm PLA Control
(uncoated PLA)
3331±570 < 1 µm 24 µm PLA + ValCoat
1898±99.7 - 18µm BOPP Control
(uncoated PE)
2313±301.6 < 1 µm 18µm BOPP + ValCoat
118% increase of coated PE films
61% increase of coated PLA films
22% increase of coated BOPP films
Valentis Delivers Results – First Generation Food Package
8
BOPP/PET base layer coated with CNC
Valentis 1st generation product Industry Required spec. Parameters
Less than 0.8 Less than 1.5 OTR (cc/m2 day)
1.8 Less than 2 WVTR (gr/m2 day)
up to 95% More than 80% UV absorbance
3.2-7.5 More than 3.5 Lamination strength (N/inch)
Direct printing
Valentis Delivers Results – Scale Up
1 2 1
Scale up has been done on a semi-industrial machinery
Results where better than expectations.
Coated films showed:
• Excellent OTR levels
• High lamination strength
• Excellent Migration tests (see next page)
Semi industrial roll-to-roll coating machine
Valentis Delivers Results – Scale Up (OTR)
Valentis Delivers Results – Migration Tests
1 2 1
Patent
Coatings combining NCC (Nano Crystal Cellulose) and Nano Particles (NP) with special abilities
Stable organic light emitting coating
Licensed from the Hebrew University
In National Phase in the following territories:
US
EU
China
Israel
Future additional patents:
New applications
Improvement of properties
Improved raw materials
New and improved production methodologies
Additional Applications
Construction materials
Biodegradable pipes
Green house films
Screens enforcement
LED lights coatings
Additional surfaces
Valentis Team
Dr. Tomer Cohen, CTO - Extensive experience in the field of biotech and was involved in the development of several novel therapeutic technologies. Established a consulting firm providing a technological due diligence services prior to investment called Tamuz BioScience.
14
Prof. Oded Shoseyov, HUJI, Inventor – Extensive experience in cellulose field, protein engineering; scientific founder of Futuragene Ltd; SP Nano Ltd.; Collplant Ltd. and other successful companies
Prof. Yossi Paltiel, HUJI, Inventor – Associate Professor, applied physics; previously researcher, Soreq Nuclear Research Center; head of Electro Optical Division, Compass EOS
Zvika Weiss, CEO – an experienced executive with wide background in management and innovation, including Capital Nature, Yissum, Technomatix, IDB, and more
Thank You
15
For Additional information please contact: Zvika Weiss – CEO [email protected] +972-54-9449442