Ultrabond® 365Low Temperature Cure Acrylic Adhesive
Ultrabond® 365 is a two-component, (10:1 ratio), methylmethacrylate adhesive. It is a high strength, moistureinsensitive, non-sag paste adhesive system. Ultrabond 365Acrylic Adhesive is a low temperature cure product that isformulated for anchoring threaded rods, bolts, and fastenersinto concrete, grout filled block, hollow block, andunreinforced masonry as well as anchoring rebar dowels and
smooth dowels into pavement/concrete. Ultrabond 365 hasbeen tested in accordance with AC-58 for creep, seismic,freeze-thaw, in-service temperature and damp/wet-holeapplications.
GENERAL USES• Grouting dowel bars and tie bars for full-depth concretepavement repairs
• Anchoring/Fastening into solid-base materials: Stadiumseating, Pallet racking & Airport runway/taxi-way expansion
• Anchoring/Fastening into hollow-base materialswith screen)
ADVANTAGES & FEATURES• Moisture insensitive and can be used in damp holes• Non- sag adhesive
• Exceptional strength• Extended temperature range allows for setting of anchorsin extreme environments for both elevated and lowtemperature applications
Ultrabond® 1300Epoxy Anchoring Adhesive
Ultrabond® 1300 Epoxy Anchoring Gel is a two-component(1:1 ratio), 100% solids, high modulus, structural, epoxy gel.It is a solvent free, no odor, high strength, moistureinsensitive, non-sag epoxy system.
.GENERAL USES• Fastening in grout filled block and unreinforced masonry• Anchoring and bracing for short term tensile load wheredynamic, vibratory, wind or intermittent loads exist
• Doweling applications for rebar and tie bars for full depthconcrete pavement repairs
• Bulk dispensing flowability for efficient application
ADVANTAGES & FEATURES• High strength• Moisture insensitive• Non-sag epoxy system• Easy to use (1:1 ratio) system
Ultrabond® 2Epoxy Anchoring Adhesive
Ultrabond® 2 Epoxy Anchoring Gel is a two component(1:1 ratio), 100% solids, high modulus epoxy gel. It is asolvent free, high strength, moisture insensitive, non-sagepoxy system. Ultrabond® 2 Epoxy Anchoring Gel isformulated for anchoring threaded rod, bolts, rebar and
smooth dowels into concrete, grout filled block, andunreinforced masonry. Ultrabond® 2 has been tested inaccordance with AC58 and is acceptable for long term tensileloads. It may also be used for short term tensile loadanchors, which includes wind and seismic forces.
GENERAL USES• Seismic anchoring and bracing• Grouting dowel bars and tie bars for full-depth concretepavement repairs
ADVANTAGES & FEATURES• High strength epoxy system• Non-Sag formula• Easy to use (1:1 ratio) system
• Long working time• Moisture insensitive• Great for setting anchors in elevated temperatureenvironments
Ultrabond® 1Epoxy Anchoring Adhesive
Ultrabond® 1 Epoxy Anchoring Gel is a two component(1:1 ratio), high modulus, structural epoxy gel. It is a solventfree, no odor, high strength, moisture insensitive, non-sagepoxy system.
GENERAL USES• Anchoring threaded rod, bolts, rebar dowels and smooth dowelsinto concrete, grout filled block and unreinforced masonry
• Seismic anchoring and bracing• Grouting dowel bars and tie bars for full-depth concretepavement repairs
ADVANTAGES & FEATURES• Exceptional strength• Long working time (20 minutes at 75°F)• Easy to use & can be used with any standard caulking gun• Load time in as little as 4 hrs
ANCHORING & DOWELING
Color When Mixed Gray
Viscosity Non-Sag gel
Gel Time 14 minutes
Load Time (75°F) 4 hours
Temperature Range 35°F – 115°F
Quick Selection Guide
Color When Mixed Concrete Gray
Viscosity Non-Sag gel
Gel Time (60gm @ 75°F) 15 minutes
Load Time 10 hours
Temperature Range 40°F – 110°F
Quick Selection Guide
Color When Mixed Gray
Viscosity Non-Sag gel
Working Time (75°F) 6 min.
Load Time (75°F) 30-35 min.
Temperature Range 0°F – 100°F
Quick Selection Guide
Color When Mixed Gray
Viscosity Non-Sag gel
Gel Time (60gm @ 75°F) 14 min.
Load Time (75°F) 2 hrs.
Temperature Range 35°F – 110°F
Quick Selection Guide
22 - 24See rendering of building in this brochurefor applications.
For more product details including Technical Data, Catalog, MSDS and Instructions refer to our website at www.atc.ws
Rail AnchoringRunway DowelingD.O.T. Doweling
with
Deep Embedment Anchors
Ultrabond® 2300Epoxy Anchoring Adhesive
Ultrabond® 2300 is a two-component, 100% solids, highstrength epoxy bonding adhesive. It is a solvent free, highmodulus, moisture insensitive, non-sag epoxy system.Ultrabond 2300 is ideal for use in temperatures ranging from
60°F - 110°F. Acceptable uses for the Ultrabond 2300include rebar dowel and anchor installations where dynamic,vibratory or intermittent loads exist. Ultrabond 2300 can alsobe used for bonding fresh/plastic concrete to hardenedconcrete and other substrates or projects that require a non-sag epoxy with a long working time.
GENERAL USES• Bonding fresh concrete to hardened concrete• Bonding hardened concrete to hardened concrete• Anchoring threaded rod fasteners and rebar dowels• Mortar Repair Material (when mixed with dry silica sand)
ADVANTAGES & FEATURES• High Strength Epoxy Adhesive• Non-Sag Epoxy System• Easy to Use (1:1 ratio)• Moisture Insensitive Epoxy
Ultrabond® SpeedSet2Doweling Adhesive
Ultrabond® SpeedSet2 Doweling Adhesive is a two-component, (10:1 ratio), polyester blend adhesive. It is asolvent free, high modulus, high strength, non-sag adhesivesystem Ultrabond® SpeedSet2 can be applied attemperatures ranging from 25° F to 120° F.
GENERAL USES• Rebar dowel installations where dynamic, vibratory orintermittent loads exist
• Vertical, horizontal and screen applications• Use in concrete, hollow block, brick, clay and stone
ADVANTAGES & FEATURES• Exceptional strength• Moisture insensitive allowing usage in dampenvironments
• Minimum loading time of 1 hour at 78° F, which is greatfor applications that require minimum down times
Ultrabond® HS200Doweling Adhesive
Ultrabond® HS200 EpoxyAnchoring Gel is a two component(2:1 ratio), 100% solids, high modulus, structural epoxy gel.It is a solvent free, no odor, high strength, moistureinsensitive, non-sag epoxy system. HS-200 has been testedin accordance with ICC - AC58 and is acceptable for longterm sustained loads as well as short term loading.
GENERAL USES• Anchoring threaded rod and rebar doweling wheredynamic, vibratory or intermittent loads exist
• Seismic anchoring and bracing for long term sustainedloads in accordance to ICC AC-58
• Grouting dowel bars and tie bars for full-depth concretepavement repairs
ADVANTAGES & FEATURES• Tested for long term creep at elevated temperatures,static loads, seismic / wind loading.• Freeze-thaw conditions, damp holes• A solvent free system means low VOC content• High Strength
Ultrabond®RT66Rebar and Doweling Adhesive
Ultrabond® RT66 is a new 2-component Hybrid Ester-Blendformula designed for doweling applications in both cold andelevated temperatures, 25°F to 120°F. It is a high strength,high modulus and moisture insensitive adhesive forinstallations in damp environments.
GENERAL USES• Perfect for horizontal, vertical and screen applications• May be used in concrete, brick, stone, clay and hollow block• Rebar dowel installations where dynamic, vibratory orintermittent loads exist
ADVANTAGES & FEATURES• High strength, non-sag structural Hybrid Ester blend system• Minimum down time with a very fast cure time• Moisture insensitive for installations in damp holes• 100% solvent free system means low VOC content
Ultrabond® 4CCRebar and Doweling Adhesive
Ultrabond® 4CC is a high performance epoxy adhesive foranchoring and doweling applications in both cracked and un-cracked concrete. It’s TESTED IN ACCORDANCE TOICC-ESAC-308 and Meets 2009 IBC requirements. Refer toICC-ES ESR-3218 Evaluation Report.
GENERAL USES• Anchoring threaded rods, bolts and fasteners into grout filledmasonry, solid brick or either cracked or uncracked concrete
• Anchoring rebar dowels and smooth dowels intopavement/concrete
• Suitable for long term sustained loads and seismic bracing• Can be used dry, water-saturated or water-filled andsubmerged applications with no load reductions
• Airport runways and taxi-way expansions, stadium seating,pallet racking
• Concrete traffic barriers to concrete bridge decks
ADVANTAGES & FEATURES• Non-sag epoxy gel anchoring• High strength• Moisture insensitive
Color When Mixed Concrete Gray
Viscosity Non-Sag gel
Gel Time (75°F) 32 minutes
Load Time (75°F) 10 hours
Temperature Range 60°F – 110°F
Quick Selection Guide
Color When Mixed Concrete Gray
Viscosity Non-Sag gel
Gel Time (60g sample @ 75°F) 7 minutes
Load Time (75°F) 60 minutes
Temperature Range 25°F – 120°F
Quick Selection Guide
Color When Mixed Medium Gray
Viscosity Non-Sag gel
Gel Time (60g sample @ 75°F) 8 min.
Load Time (75°F) 1 hr.
Temperature Range 25°F – 120°F
Quick Selection Guide
Color Concrete Gray
Viscosity Non-Sag gel
Gel Time (60gm @ 75°F) 10 minutes
Load Time (75°F) 4 hours
Temperature Range 35° F – 110° F
Quick Selection Guide
Color Gray
Viscosity Non-Sag gel
Working Time (70°F) 15 minutes
Cure Time 24 hours
Temperature Range 70° F – 110° F
Quick Selection Guide
Used for the seismic retrofit of the Golden Gate Bridge.
For more product details including Technical Data, Catalog, MSDS and Instructions refer to our website at www.atc.ws
Miracle Bond®1350Multi-Purpose Repair Epoxy
Miracle Bond® 1350 is a two-component, high strength, highmodulus, moisture insensitive, non-sag, ceramic blend epoxysystem. It’s ideal for use as a bonding agent for almost anymaterial, including metal, concrete, brick, wood, stone, blockand other substrates.
GENERAL USES• Repairing holes and spalls in concrete• Repairing rotted wood• Bonding fresh concrete to hardened concrete• Bonding hardened concrete to hardened concrete• Capping paste sealer around ports and cracks for crackinjection process
• Non-sag patching material for cracks and small spalls• Bonds to a multitude of substrates
ADVANTAGES & FEATURES• Non-sag, high strength epoxy makes it great foroverhead and vertical repair
• Easy to use (1:1 ratio) system• 100% solvent free system means low VOC content• Moisture insensitive system-can be used ondamp surface
Color Concrete Gray
Viscosity Non-Sag Gel
Gel Time (75°F) 8 minutes
Cure Time 2 hours @ 75°F
Temperature Range 40° F – 100° F
Quick Selection Guide
Crackbond® JF311Polyurea Joint Filler
Crackbond® JF-311 is a 2-component, rapid curing,elastomeric, polyurea joint filler. It is designed for heavy dutytraffic and freezer applications.
GENERAL USES• Joint filler for control joints or new construction saw joints• Specifically formulated for industrial floor applicationsreceiving heavy-duty vehicle traffic.
ADVANTAGES & FEATURES• Self leveling• 100% solids• Flexible system that provides 10-15% movement ofinstalled joint width
• Can be used at temperatures between -40°F - 120°F• Rapid cure allows repaired joints to be opened to trafficwithin 90 minutes (at 72°F)
Crackbond® LR-321Low Viscosity Epoxy
Crackbond® LR-321 is formulated for use as an injectionresin for cracks in structural concrete, masonry & wood. It’salso perfect for an epoxy grout, healer/sealer or as a mortarwhen mixed with sand. It has the viscosity of light oil and lowsurface tension, allowing it to deeply penetrate fine cracks.It cures to a solid with no shrinkage, bonds to both surfacesof the crack, bonding the structure back to its originalmonolithic strength.
GENERAL USES• Pressure injection of fine to medium size cracks(3mm to ¼”)
• Primer for industrial coatings• Bonding agent for new to old concrete repair• Resin binder for epoxy mortar patching using additionof aggregate
• Sealer for interior slabs and exterior above-ground slabsfrom water, chlorides and mild chemical attack
• Gravity feed structural crack repair in horizontal concrete,masonry and wood in fine to medium size cracks
ADVANTAGES & FEATURES• High strength• Moisture insensitive system-can be used ondamp surfaces
• 100% solvent free system means zero VOC content• Low Viscosity epoxy system ideal for gravity feedcrack injection applications
BONDING & COATING
Color When Mixed Concrete Gray
Viscosity of Resin 525cps @ 77°F
Gel Time (72°) 3 minutes
Cure Time (72°) 90 minutes
Temperature Range -40°F – 120°F
Quick Selection Guide
Color When Mixed Amber
Viscosity When Mixed 350 – 450cps
Gel Time (ASTM 60g mass) 20 minutes
Initial Cure Time (30 mil thin film) 6 hrs. and 30 min.
Temperature Range 40°F – 100°F
Quick Selection Guide For LR-321
1 - 21See rendering of building in this brochurefor applications.
26 - 28See rendering of building in this brochurefor applications.
26 - 28See rendering of building in this brochurefor applications.
Healer/Sealers, Injection Repairs, Grouting & Patching
KEY USES• Crack injection• Concrete crack and spall repair• Bonding concrete to concrete• Patching Material• Primer for industrial coatings• Healer Sealer• Epoxy Grouting• Gravity fed structural crack repair• Mortar when mixed with sand• Capping paste sealer• Fix Cracks• Rotted Wood• Loose Railing• Broken Steps• Broken Concrete
Crack-KitCrack Injection and Concrete Repair Kit
Our new and improved patented T-Port System with observationwindows is everything you need to perform crack injection andconcrete repair to multiple applications.
KEY CRACK-KIT ADVANTAGES• Latex Storage Pod delivers constant injection pressure andindicates if more injection is required
• Flexible T-Port absorbs disturbances during installation helping toeliminate reattaching ports
• Leak free direct port /nozzle connection keeps epoxy resin inwhile allowing air and water to escape
• Observation windows allows installer to view and confirm the flowof resin within the injected crack
For more product details including Technical Data, Catalog, MSDS and Instructions refer to our website at www.atc.ws
Crackbond® LR-321GLow Viscosity Thixotropic Formula
This unique formula will flow as a liquid when being pumpedwith a dispensing tool but will cease flowing within (or out) ofthe crack when pumping stops. This characteristic makes itperfect for blind side crack repairs. Visit our website for all thecomplete technical data.
AlsoAvailable
Crackbond® SLV-302Super Low Viscosity Epoxy Resin
Crackbond® SLV-302 is formulated for use as an injectionresin for cracks in concrete/wood structures and as apenetrating healer/sealer/primer. It has the viscosity of a verylight oil, and low surface tension, allowing it to deeplypenetrate fine/hairline cracks. It cures to a solid with noshrinkage, bonds to both surfaces of the crack, bonding thestructure back to its original monolithic strength.
GENERAL USES• Pressure injection of hairline to fine cracks• Primer for industrial coatings• Gravity feed structural crack repair in horizontal concrete,masonry and wood in fine cracks
• Epoxy resin binder for epoxy mortar patching and overlayof interior surface using addition of aggregate
• Sealer for interior slabs and exterior above-ground slabs,decks, patios, driveways, parking garages and otherstructures from water, chlorides and mild chemical attack
• Shear fracture repairs on interior/exterior concrete slabs• Bonding agent for new to hardened or hardened tohardened concrete
ADVANTAGES & FEATURES• Crackbond SLV-302 is a moisture insensitive product andcan be used in damp environments
• Super low viscosity and low surface tension allows it todeeply penetrate hairline to fine cracks
• Cures to a solid with no shrinkage and bonds to allsurfaces of the crack bonding the structure back to itsoriginal monolithic strength
• 100% solids, solvent free system with zero VOC content.
Crackbond®CSRRapid Cure Polyurethane Crack/Spall Repair
Crackbond® CSR is a specially formulated very low viscositytwo-part hybrid polyurethane rapid cure concrete repairmaterial.
GENERAL USES• Repair spalls & cracks in high traffic areas• Repair floors prior to floor grinding/polishing• Rebuild spalled floor joints and concrete edges• Repair concrete on bridge & parking decks• Repair of interior and exterior hairline cracks
ADVANTAGES & FEATURES• Penetrating super low viscosity provides high bond strength• Reaches 4,900 psi in 1 hour• Use in temperatures down to 0°F• Cures in 20 minutes• Self-leveling
• Provides excellent results when polished• Add aggregate for use as mortar
Crackbond® FE-2315Flexible Pick-Proof Epoxy
Crackbond® FE-2315 is a pick-proof, two component(1:1 ratio), semi-flexible, epoxy adhesive. It is a solvent-free,no odor, moisture insensitive, non-sag epoxy adhesive.
GENERAL USES• Seals joints in facilities requiring pick-proof andtamper resistance
• Adhesive for marine applications• Hollow block joint repairs• Sealing joints in concrete to prevent water intrusion• Crack sealer/ filler• Capping gel for crack-injection
ADVANTAGES & FEATURES• Pick-proof, tamper resistance (windows, doors, etc.),Ideal for correctional facilities
• Great for bonding metal to metal
Color When Mixed Amber
Viscosity 190 cps
Gel Time (ASTM 60g mass at 75°F) 10 minutes
Initial Cure Time (30 mil thin film) 7 hours
Temperature Range 50°F – 100°F
Quick Selection Guide
Color When Mixed Black, then light gray
Viscosity 60cps mixed
Gel Time (75°F) 2.5 minutes
Cure Time 20 minutes
Temperature Range 0°F – 115°F
Quick Selection Guide
Color When Mixed Off-White
Viscosity Non-Sag gel
Gel Time (60g mass @ 75°F) 35 minutes
Full Cure Time (Pick-Proof) 72 hours
Temperature Range 40°F – 110°F
Quick Selection Guide
26 - 27See rendering of building in this brochurefor applications.
25See rendering of building in this brochurefor applications.
For more product details including Technical Data, Catalog, MSDS and Instructions refer to our website at www.atc.ws
Ultrabond 2100, Crackbond LR321 LPL,Ultrabond 2100 LPLEpoxy Bonding/Coating Adhesives -Extended tack free time
PRODUCT DESCRIPTIONThe three featured products in this section are all two component, solvent free,high strength, moisture insensitive self leveling epoxies. The main differencesbetween the products can be found in their color, mixing ratios, viscosity, cureand tack free times.
GENERAL USES• Bonding fresh concrete to hardened concrete• Bonding hardened concrete to hardened concrete• Mortar repair material (when mixed with dry silica sand)• Gravity feed crack repairs• Deep hole anchoring
Ultrabond 2100 Crackbond LR321 LPL Ultrabond 2100 LPL
Viscosity Mixed (cps) 3,600 525 4,000
Gel time (60 gm sample at 75°F) min. 37 50 90
Tack Free Time 30 mil thin film 3 hrs, 40 min 8-10 hrs 5 hrs, 15 min.
Tensile Strength psi 7 days-ASTM D638 7,210 8,000 3,511
Heat Deflection Temperature °F ASTM D648 135° 121° 122°
Compressive Strength-psi 7 days ASTM D695 10,100 10,800 9,146
Bond Strength-psi 14 day ASTM C882 1,690 3,300 2,600
Mixing Ratio 1:1 2:1 1:1
Color Gray Amber Gray
ASTM C881, Type I, II, IV & V, Grade 2, Class B & C X
ASTM C881, Type I, II, IV & V, Grade 1, Class B & C X
ASTM C881, Type I, II & V, Grade 2, Class C X
Quick Selection Guide
The Cracker®Non-Explosive Cracking Agent
The Cracker® is a non-explosive cracking agentthat can crack any hard rock or reinforced concrete.The Cracker is a universal product which may notonly be substituted for explosives, hydraulicwedges, rock-breakers, and concrete-crackers, butcan also be used in many places where othermethods are impractical. Produced in powder form,The Cracker need only be mixed with water andpoured into predrilled holes for dramatic results.
KEY USAGE FACTSYou’ll need to know the following to determine howmuch product you’ll need. What is the size andshape of the object to be demolished? What sizepieces are you looking to create? Is there a freeedge? Will the substrate be over or under 72°F? Isthe substrate reinforced? What is the substrate psi?For complete info, watch our Cracker video on ourwebsite and download the Cracker technicalmanual.
ADVANTAGES & FEATURES• SAFE - High safety factor when compared toother methods of demolition
• QUIET - Ideal for use in or near occupied buildings• NON-TOXIC - 100% biodegradable after activated• POWERFUL - Breaks concrete from 8 inches to10 feet thick
Hard-RokAnchoring Cement
HARD-ROK Anchoring cement is a high strength, fast setting,non-shrink, nonmetallic cementitious product used foranchoring and grouting applications. This hydraulic cement isquickly and easily mixed with water to either a pourable orputty-like consistency.
GENERAL USES• Anchoring Threaded Rods, Bolts and Rebar Dowels• Anchoring Railing, Signs, Posts and Parking Meters• Anchoring Machinery• Patching Holes and Cracks in Concrete
ADVANTAGES & FEATURES• High Strength• Fast cure anchoring cement: fast initial set of 15 minutes at75°F when mixed to fluid consistency
• Ideal for interior and exterior applications• Contains no metals to rust and cause unsightly stains• Compressive strength of 7,200 psi in 28 days insures a firmbed in grouting applications
• Mixed to a free flowing consistency: Flows like pancakebatter eliminating the labor required in Roding or vibratingto eliminate voids.
Hard-RokJet Patch
JET PATCH is a Portland Cement blend of specialtyaggregates and admixtures providing a rapid setting, highstrength, durable concrete repair for use on airport runways,taxiways, concrete floors, highway pavements, bridge decksand other applications requiring early resumption of traffic oruse. Jet Patch is formulated to meet the requirements ofASTM C928 Packaged, Dry, Rapid Hardening CementitiousMaterial for Concrete Repair.
GENERAL USES• Excellent for all types of concrete repair applications: bridgedecks, concrete pavements and joints, airport runways andtaxiways, industrial floors, loading docks, pre-stressed andprecast concrete
• Specifically designed for those applications requiring veryrapid strength gain
ADVANTAGES & FEATURES• For deeper spalls ( >3”) add pea gravel. See InstallationInstructions for details
• Thermal expansion & contraction similar to concrete,Freeze-thaw resistant
• For repairing depths between 1/2” to 3” use as packaged,mixed with water
• Flowable and Self Compacting• Sulfate resistant• High early strength with low permeability
SPECIALTY PRODUCTS
See rendering of building in thisbrochure for applications.
33
Hard-Rok Jet Patch used for runway repair.
This brochure is intended to be used as a quick reference guide only. Information is subject to change without notice.For more product details including Technical Data, Catalog, MSDS and Instructions refer to our website at www.atc.ws
Ultrabond® EGPHigh StrengthGrouting System
Ultrabond® EGP is a threecomponent, 100% solids, highperformance, high strength epoxygrouting system. It is a solvent-free,low-odor, moisture insensitive, pre-
packaged epoxy grout system. EGP is ideal for precisionseating of baseplates, and grouting under heavy-dutyequipment. It is ideal as an epoxy grout for concrete patchingand overlays. EGP can be mixed to three differentconsistencies:1) Trowelable2) Plastic /Flowable3) Pourable /Self-Leveling
GENERAL USES• High strength grouting – vibratory, high impact, heavyload conditions
• Patch and Spall repair• Patching / repairing warehouse, office and garage floors• Machine Base Grouting (heavy impact and vibratorymachinery, reciprocating engines, compressors and pumps)
• Grouting under crane rails
ADVANTAGES & FEATURES• Fast strength gain• Low exotherm• Oil and Chemical Resistant• Pre-proportioned kit• High strength epoxy grout• High effective bearing area• Corrosion and impact resistant
• High vibration resistance• Non-shrink• Moisture insensitive• Variable ratio fill system: ratio of special blend aggregateto total liquids
Color When Mixed Tan
Viscosity Thick Grout
Gel Time (60g mass @ 77°F) 35 – 60 minutes
Cure Time 24 hrs.
Temperature Range 40°F – 110°F
Quick Selection Guide
High Strength Grout, Cementitious Products, Concrete Demolition