title of presentation - inemithor.inemi.org/.../presentations/.../imc_williams.pdf · •...
TRANSCRIPT
![Page 1: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/1.jpg)
No Interfacial
IMC
Maureen Williams, NISTECTC, Reno, NV
May 29, 2007
![Page 2: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/2.jpg)
1
NIST NIST SnSn Whisker TeamWhisker Team
Metallurgy Division Gaithersburg, Maryland
William J. Boettinger
Kil-Won Moon
Gery Stafford
Maureen Williams
![Page 3: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/3.jpg)
2
Motivation for this experimentMotivation for this experimentMeasured Deflection Curves for 3 Alloys (16 µm) 2005 work
-160
-120
-80
-40
0
40
-40
-32
-24
-16
-8
0
8
1000 104 105 106
Can
tilev
er D
efle
ctio
n (µm
) Initial Film Stress (M
Pa)
time (s)
Sn
Sn-Pb
Sn-Cu
![Page 4: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/4.jpg)
3
How to separate the IMC effect from the deposit?How to separate the IMC effect from the deposit?
• To eliminate interfacial IMC electrodeposit Sn on a non-reactive substrate.– Sn on Tungsten (W)
Phase diagram constructed by U. Kattner, NIST, 2005
- based on Binary Phase Diagram, Massalski
![Page 5: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/5.jpg)
4
GoalGoal
• Electrodeposit Sn, SnCu, and SnPb on W, a substrate that does not form an interfacial intermetallic.
• Determine if IMC is needed for hillock & whisker growth.
• Measure– whisker growth
– Stress as a function of time
![Page 6: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/6.jpg)
5
OvOverview of erview of ApproachApproach
• Part One – experiments done in 2006 - Williams M.E., et al., JEM (36) 3, pp.214-219 (2007)
– 1 mm thick pure tungsten (W) substrates– Vapor deposited 0.2 µm (5-9’s) Sn with e-beam– Electroplated 15 µm Sn (made with 18 Mohm cm water)
• Part Two – experiments done in 2007– 150 µm phosphor bronze (Cu) cantilever substrate– Vapor deposited 0.02 µm (4-9’s) W with e-beam on both sides– Vapor deposited 0.2 µm (5-9’s) Sn with e-beam– Electroplated 15 µm Sn (made with 18 Mohm cm water)
![Page 7: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/7.jpg)
6
ResultsResults
Surface eruptions form without interfacial intermetallic (IMC) between Sn and substrate.
Both Cu & W substrates:
•Similar compressive stress values for Sn
•Sn deposits have similar hillock formation.•SnCu deposits have similar whisker formation.•SnPb deposits are clean (some plating bumps).
![Page 8: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/8.jpg)
7
ResultsResults
Avg. Stress 15 minutes after electroplatingmeasured by cantilever beam deflection (2007)
Pure Sn Sn-3 wt% Cu Sn-2 wt% Pb
W - 28.2 MPa - 57.6 MPa No data
Cu -31.2 MPa No data No data
![Page 9: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/9.jpg)
8
Surface Defects on Pure Surface Defects on Pure SnSn Deposits Deposits
W substrate (2006)
10 µm
100 µm
500 µm
141 days oldebeam W on Cu substrate (2007) Cu substrate (2006)
256 days old
500 µm
100 µm
10 µm
26 days old
SEM photos of deposit surface
![Page 10: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/10.jpg)
9
Surface Defects on Surface Defects on SnSn-- 3 wt% Cu Deposits3 wt% Cu Deposits
20 µm
100 µm
500 µm
Cu substrate176 days old
ebeam W on Cu substrate (2007)21 days old
500 µm
100 µm
10 µm
W substrate (2006)
10 µm
500 µm
100 µm
133 days old
SEM photos of deposit surface
![Page 11: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/11.jpg)
10
Experimental OutlineExperimental Outline
• Sample – preparation
– FIB cross sections of the deposit - substrate interface
• Stress Measurement– Deflection of cantilever as a function of time
• Sn and SnCu on W• Sn on Cu and W
![Page 12: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/12.jpg)
11
For Sn electroplating, need to overcome oxide barrier on W substrate surfacePreparation of a Preparation of a NNonon--reactive reactive Cantilever BeamCantilever Beam
Electron beam vapor deposition – Plasma etched the surface of diamond polished Cu cantilever beams in high vacuum (10-8 torr)
– vapor deposited 0.02 um of Tungsten (W) in high vacuum (10-6 torr) to both sides of cantilever beam
– vapor deposited 0.2 um of Tin (Sn) in high vacuum (10-6 torr) to one side of cantilever beam
–Performed ASTM adherence test
Surface of e-beam deposited Sn (0.2 um) on
e-beam deposited W layer (0.02 um)
10 um5 um
Surface of e-beam deposited W layer (0.02 um)
on Cu substrate
![Page 13: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/13.jpg)
12
Cantilever BeamsCantilever Beams
• Sample Mounting– Mask is cut and placed on substrate– Sample is attached to cathode
• Plating Conditions **(same as 2005 experiments)– 1 liter of electrolyte (made with 18 Mohm cm water)
• 100 rpm rotating cathode• 5-9s pure Sn anode• current density of 60 mA/cm2
** Boettinger W.J., et al., Acta Materialia 53, 5033 (2005)
![Page 14: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/14.jpg)
13
Pure Pure SnSn Deposit / Substrate InterfaceDeposit / Substrate Interface
Top FIB photo courtesy of
A. Deal, Lehigh Univ.
Bottom FIB photo courtesyof
G. Galyon & M. Palmer, IBM
3.0 µmSn / Cu interfaceCu substrate
Sn deposit
Cu6Sn5
Sn / W interface
W substrate
Sn deposit
1.0 µm
Sn on W substrateCu6Sn5
Sn on Cu substrate
![Page 15: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/15.jpg)
14
SnSn--3 wt% Cu Deposit / Substrate Interface3 wt% Cu Deposit / Substrate Interface
Top FIB photo courtesy of
A. Deal, Lehigh Univ.
2 µmSn-Cu / W interface
Cu6Sn5
W substrate
Sn-Cu deposit
Bottom FIB photo courtesy of
G. Galyon & M. Palmer, IBM
1.5 µm
Sn-Cu deposit
Cu substrateSn-Cu / Cu interface
Cu6Sn5
SnCu on W substrate
SnCu on Cu substrate
![Page 16: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/16.jpg)
15
-70
-60
-50
-40
-30
-20
-10
0
0 5 10 15 20 25
Sn-Cu
Sn
Time (days)
Stress Calculated from Stress Calculated from Cantilever Beam DeflectionCantilever Beam Deflection
Stoney’s single layer equation is valid - No interfacial IMC
Stre
ss (M
Pa)
![Page 17: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/17.jpg)
16
Comparison of 16 um thick Comparison of 16 um thick SnSn deposit on deposit on TungstenTungsten (W) and (W) and phosphor bronzephosphor bronze (Cu) substrates(Cu) substrates
100
-80
-60
-40
-20
0
0 5 10 15 20 25 30
Sn on P-Bronze
Sn on W
Time (days)
Bea
m D
efle
ctio
n (u
m)
-
Without IMC Sn deflectionrelaxes to constant value
With IMC reaction Sndeflection moves in
positive direction
![Page 18: Title of Presentation - iNEMIthor.inemi.org/.../Presentations/.../IMC_Williams.pdf · • Interfacial IMC is not required to initiate whisker growth. 18 Email contacts: Jim McElroy](https://reader030.vdocuments.us/reader030/viewer/2022011900/5ede4465ad6a402d666996dd/html5/thumbnails/18.jpg)
17
SummarSummaryy• Successfully plated Sn on a non-reactive cantilever beam• Measured residual stress in deposits without interfacial IMC
formation– Sn-Cu deposit shows higher initial stress than pure Sn– Sn has hillocks, and Sn-Cu has filament whiskers– deposits maintain compressive stress initially and after
relaxation• Comparison of Sn deposits on Cu and W cantilever beams
– with IMC, Sn deflection moves in positive direction– without IMC, Sn deflection relaxes to constant compressive
value• Interfacial IMC is not required to initiate whisker growth