task 4 hts material characterization & dipole insert conceptual design
DESCRIPTION
Task 4 HTS material characterization & dipole insert conceptual design. Mélanie Bruchon, Maria Durante, Thibault Lécrevisse, Jean-Marc Gheller, Olivier Louchart, Jean-Michel Rey CEA/IRFU/SACM. HTS characterization. Superpower AMSC. HTS characterization. Superpower (with insulation). - PowerPoint PPT PresentationTRANSCRIPT
![Page 1: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/1.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 1
Task 4HTS material
characterization &dipole insert conceptual
designMélanie Bruchon, Maria Durante, Thibault
Lécrevisse, Jean-Marc Gheller, Olivier Louchart, Jean-Michel Rey
CEA/IRFU/SACM
![Page 2: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/2.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 2
HTS characterization
Superpower
AMSC
![Page 3: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/3.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 3
HTS characterizationSuperpower (with insulation)
![Page 4: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/4.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 4
HTS characterizationSuperpower (without insulation)
![Page 5: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/5.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 5
HTS characterizationAMSC
![Page 6: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/6.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 6
HTS characterizationWhat next ?
Cooling influence: what happens if we remove insulation?
Quench propagation: next study using compact solenoids. MPZ and MQE determination versus temperature.
![Page 7: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/7.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 7
Dipole design
20 mm beam tube
3 double pancakes
2 flat one
1 with bent end, each pancake symetrical / mid plane (only one tooling needed)
External winding diameter: 98 mm
Bloc 2
Bloc 1
Bloc 3
X
Y
![Page 8: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/8.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 8
Dipole designInner bore diameter: 20 mm
254 A/mm² needed to reach 6T
Peak field 6,1T
Fx = 47,8 kdaNFy = 78,5 kdaN
No Nb3Sn contribution
Bloc 2
Bloc 1
Bloc 3
X
Y
![Page 9: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/9.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 9
Dipole designConductor extrapolation
Using Superpower SCS 4050 @ 20 T and 10 K extrapolation: 520 A for a 4 mm wide.
Assuming 2 12 mm wide ribbons and 60% efficiency on one of them the critical current may be 2496 A.
Assuming 12 mm wide conductor of 0,4 mm thickness corresponding to 0,2 mm conductor + 0,1 mm tin + 0,1 mm kapton insulation the critical current density is 520 A/mm².
Bloc 2
Bloc 1
Bloc 3
X
Y
![Page 10: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/10.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 10
Dipole designConductor length needed
With a straight length of 500 mmBlock 1: 69 mBlock 2: 105 mBlock 3: 142 mOnly block 3 needs « flare dance » end.
Or 1260 m of 12 mm wide ribbons needed (or 202 k$)
Bloc 2
Bloc 1
Bloc 3
X
Y
We may be able to discuss this number!
![Page 11: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/11.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 11
Dipole design
Junctions
Main conductor: SC face to face
Mid point and end connections: SC back to back
Bloc 2
Bloc 1
Bloc 3
X
Y
![Page 12: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/12.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 12
Thank you for your attention
12
![Page 13: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/13.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 13
![Page 14: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/14.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 14
![Page 15: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/15.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 15
Which HTS will fit?
Bi2212
YBCO
Bloc 4
Bloc 2
Bloc 1
Bloc 3
X
![Page 16: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/16.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 16
Bi 2212
Assume we can make a Rutherford cable using a round wire with 25% SC material
Ic @ 4.2K & 20T = 82A
Winding with 20% insulation
No cabling degradation
Good head treatment
Je = 130 A/mm²
We may expect B = 2.72T
Bloc 4
Bloc 2
Bloc 1
Bloc 3
X
![Page 17: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/17.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 17
YBCO
Using AMSC 344 Cu (made for magnets)4.55 x 0.22 = 1 mm²Ic @ 4.2K & 10T = 325AIc @ 4.2K & 15T = 245AExtrapolation : Ic @ 4.2K & 20T = 165AWinding with 20% insulationNo winding degradation
Je = 130 A/mm²We may expect B = 2.72T
Bloc 4
Bloc 2
Bloc 1
Bloc 3
X
Measured values
17
![Page 18: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/18.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 18
YBCO
Using AMSC 344 S (with stainless steel, not made for magnets)
1.41 mm²Ic @ 4.2K & 15T = 580AExtrapolation : Ic @ 4.2K & 20T = 500AWinding with 20% insulationNo winding degradation
Je = 285 A/mm²We may expect B = 5.96T
Bloc 4
Bloc 2
Bloc 1
Bloc 3
X
Measured value
18
![Page 19: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/19.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 19
YBCOUsing Super Power SCS 4050i
(with kapton insulation)
19
Unit Ribbon Insulated
Width mm 4 4.2
Thickness mm 0.1 0.3
Cross section mm² 0.4
SC cross section mm² 0.004
Cu Cross section mm² 0.016
SC / Non SC ratio % 1%
19
![Page 20: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/20.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010
YBCO ribbon characterization
16 mars 2010 20
Results (with 0.1 µV/cm criterion) :
Je = 275 A/mm² @ 20K & 13T
We may reach what we need !
(287 A/mm² @ 4.2K & 18T)
Worrying concern: this tape blew up after 8 critical current measurement under 15T at 4.2K and 30K
20
![Page 21: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/21.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010
YBCO ribbon characterization
Test “as purchased”
16 mars 2010 21
Test after “damaging quench”
21
![Page 22: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/22.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010
YBCO ribbon characterization•Some measurements problems :
To much heat power generated in the sample-current leads junctions : Uneasy to regulate the température.
The problem is corrected but we haven’t done the tests again yet.
•It’s very difficult to limit the heat generation next to the sample when high current (> 500A) flows through the sample over long period of time (> 20s).
A new measurement setup is needed for high current under low field
16 mars 2010 2222
![Page 23: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/23.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 23
A rough mechanical approach - Forces Blo
c 4
Bloc 2
Bloc 1
Bloc 3
X
1040 tonnes
50 tonnes
![Page 24: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/24.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 24
A rough mechanical approach - Stresses
Bloc 4
Bloc 2
Bloc 1
Bloc 3
X
Stress 270 MPa20 mm
Mid plane Stress 17 MPa
Interbloc Stress 9 MPa
![Page 25: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/25.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 25
Bloc 4
Bloc 2
Bloc 1
Bloc 3
X
StructureWhy should we keep the insert in a
circular bore?
25
![Page 26: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/26.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 26
Winding
Bloc 4
Bloc 2
Bloc 1
Bloc 3
X
How to use ribons for the mid plane pancake ?
Can we assemble ribbons to increase Ic ?
Can we mix Bi2212 and YBCO in the same insert ?
26
![Page 27: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/27.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010
Winding
27
Winding developments can be inspired from the INNOVAC project (Danish Technical Institute/Danfysik/ Siemens)
From an IOP presentation by Nikolaj Zangenberg, Danish Technological Institute
![Page 28: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/28.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 28
ProtectionBloc 4
Bloc 2
Bloc 1
Bloc 3
X
Can we allow HTS to quench ?HTS material degradation often observed after
quench
Where could we have copper ?The need of high current density does not
leave place for stabilizer
28
![Page 29: Task 4 HTS material characterization & dipole insert conceptual design](https://reader035.vdocuments.us/reader035/viewer/2022062806/56814f95550346895dbd5298/html5/thumbnails/29.jpg)
CEA DSM Irfu
i r f u
yalcas
i r f u
yalcas
- J-M Rey - EUCARD Meeting - UNIGE 08/06/2010 29
It may be wise to add a contribution of the HTS fringe field on the Nb3Sn
winding.
A sub task with T3 and T4 people for the interface definition is strongly
needed !
29