reference material 2008 - 2009 seishin.pdf · · 2009-03-103 3.20 cao 66.25 mgo 1.08 so 3 0.25 na...
TRANSCRIPT
Reference Material
2008 - 2009
Distribuiti da:
Simar Analytical S.r.l. Via Roma, 117 / 8
35020 Albignasego PADOVA
Tel. 049 862 53 86 Fax 049 862 53 80
Website: www.simarsrl.com E-Mail: [email protected]
Japan Cement Association ● 102L : Certificate of Fineness Analysis
(Ordinary Portland Cement)
● 211R : Certificate of Chemical Analysis Standard Reference Material
(Portland Cement) Constituent Percent by Weight (%)
Ignition loss (ig. loss) 1.86 Insoluble residue (insol.) 0.08
SiO 2 20.77 Al 2 O 3 5.67 Fe 2 O 3 2.65
CaO 64.37 MgO 1.16 SO 3 2.13
Na 2 O 0.22 K 2 O 0.44 TiO 2 0.31 P 2 O 5 0.10 MnO 0.07
Cl 0.009 ● 301Q : Certificate of Reference Material for Heat of Hydration (Moderate Heat Portland Cement)
Heat of solution of dry cement 2481 (J/g) 7 days 267 (J/g)
Heat of hydration 28 days 327 (J/g)
Analytical value (cm 2 /g) Certificate Value 3220
Standard Deviation 9
● 401G : Reference Material for Strength Test
(Ordinary Portland Cement) Compressive Strength (N/mm 2 )
3 days 7 days 28 days Certificate Value 28.1 45.8 64.8
Standard Deviation 0.33 0.85 0.81 ● 701A : Certificate of for Sieving Method (Ordinary Portland Cement)
45 m 32 m 20 m 16 m 10 m
Certificate Value 8.6 18.9 38.5 48.6 68.0 Standard Deviation 0.27 0.27 0.37 0.51 0.32
● JCA-RM-611 : Reference Material for X-ray Fluorescence Analysis
Constituents Reference values (mass%) SiO 2 21.84
Al 2 O 3 5.41 Fe 2 O 3 3.20
CaO 66.25 MgO 1.08 SO 3 0.25
Na 2 O 0.40 K 2 O 0.34 TiO 2 0.30 P 2 O 5 0.59 MnO 0.06 SrO 0.28
● JCA-RM-612 : Reference Material for X-ray Fluorescence Analysis
Constituents Reference values (mass%) SiO 2 20.12
Al 2 O 3 5.19 Fe 2 O 3 2.81
CaO 62.95 MgO 1.52 SO 3 4.51
Na 2 O 0.52 K 2 O 0.90 TiO 2 0.28 P 2 O 5 1.02 MnO 0.06 SrO 0.045
● JCA-RM-613 : Reference Material for X-ray Fluorescence Analysis
Constituents Reference values (mass%) SiO 2 19.51
Al 2 O 3 5.36 Fe 2 O 3 2.78
CaO 63.00 MgO 1.07 SO 3 6.07
Na 2 O 0.23 K 2 O 1.20 TiO 2 0.35 P 2 O 5 0.15 MnO 0.08 SrO 0.15
● JCA-CRM-1 : Certified Reference Material
(Ordinary Portland Cement) Constituents Certified Values (mass%)
SiO 2 20.99 ± 0.05 Al 2 O 3 5.26 ± 0.04 Fe 2 O 3 2.67 ± 0.02
CaO 65.21 ± 0.10 MgO 2.13 ± 0.03 SO 3 2.05 ± 0.09
Na 2 O 0.26 ± 0.02 K 2 O 0.56 ± 0.02 TiO 2 0.35 ± 0.01 P 2 O 5 0.28 ± 0.01 MnO 0.06 ± 0.01 SrO 0.05 ± 0.01
● JCA-CRM-2 : Certified Reference Material (Portland Blast furnace Slag Cement)
Constituents Certified Values (mass%) SiO 2 25.66 ± 0.07
Al 2 O 3 8.94 ± 0.04 Fe 2 O 3 2.08 ± 0.03
CaO 56.33 ± 0.10 MgO 3.05 ± 0.03
Na 2 O 0.24 ± 0.01 K 2 O 0.31 ± 0.02 TiO 2 0.50 ± 0.01 P 2 O 5 0.07 ± 0.01 MnO 0.15 ± 0.01 SrO 0.07 ± 0.01
● Standard sand for the strength test of cement
(JIS R 5201 – 1997) Particle size distribution of JIS Standard sand
Square mesh size (㎜) Cumulative sieve residue (%) 2 0
1.6 7 ± 5 1 33 ± 5
0.5 67 ± 5 0.16 87 ± 5 0.08 99 ± 1
Moisture content of JIS standard sand Less than 0.2% Reference : Chemical analysis (CAJS I-12-1981)
Chemical composition (%) Ig.loss SiO2 Al2O3 Fe2O3 CaO MgO Na2O K2O
0.0 98.4 0.41 0.36 0.16 0.00 0.01 0.01
● 601A : Cement Reference Materials for X-ray Fluorescence Analysis
NOTE : The reference values express mass % on the basis of ignited (975℃) sample whose masses reach constant by making successive 15 minutes ignitions at 975℃ followed each time by cooling and then weighing. The constant mass is reached when the difference between two successive weighings is less than 0.0005 g.
Constituent
Sample No.
SiO 2 Al 2 O 3 Fe 2 O 3 CaO MgO SO 3 Na 2 O K 2 O TiO 2 P 2 O 5 MnO SrO
XRF-1 22.23 5.35 3.05 64.14 1.75 2.33 0.29 0.40 0.33 0.06 0.15 0.037 XRF-2 21.31 5.29 2.93 65.17 1.77 1.91 0.38 0.50 0.31 0.11 0.21 0.045 XRF-3 20.67 4.57 2.43 66.32 1.53 3.18 0.30 0.45 0.28 0.13 0.08 0.049 XRF-4 20.71 4.73 2.80 66.17 1.37 2.64 0.24 0.54 0.26 0.40 0.05 0.036 XRF-5 20.52 5.07 2.99 65.99 0.94 3.02 0.32 0.46 0.25 0.10 0.28 0.027 XRF-6 20.71 5.02 2.70 66.23 1.81 2.61 0.26 0.23 0.24 0.05 0.19 0.035 XRF-7 22.76 4.26 4.11 64.27 1.03 2.42 0.17 0.35 0.25 0.06 0.06 0.030 XRF-8 23.23 3.82 4.02 64.15 1.52 1.93 0.10 0.54 0.27 0.19 0.21 0.038 XRF-9 23.82 3.40 4.18 64.75 0.78 1.94 0.24 0.39 0.16 0.06 0.11 0.024
XRF-10 22.99 6.29 2.39 61.67 2.71 - 0.17 0.62 0.52 0.13 0.14 0.043 XRF-11 24.43 7.37 2.26 59.15 2.63 - 0.26 0.51 0.55 0.23 0.16 0.046 XRF-12 26.34 8.95 1.82 54.90 3.33 - 0.23 0.44 0.73 0.17 0.18 0.051 XRF-13 26.62 9.22 2.02 55.36 2.98 - 0.30 0.41 0.41 0.06 0.61 0.037 XRF-14 25.74 8.70 2.03 55.15 3.98 - 0.26 0.31 0.66 0.04 0.28 0.051 XRF-15 29.29 10.70 1.32 49.28 5.12 - 0.25 0.42 0.64 0.06 0.48 0.071
REFERENCE MATERIALS OF THE CERAMIC SOCIETY OF JAPAN For calibration in chemical investigations of ceramics and glass the Ceramic Society Japan offers following reference materials.
The chemical compositions of those materials were determined by round robin tests.
Chemical Composition of the reference Materials of the Ceramic Society of Japan
Reference Material Chemical Composition (mass %)
Oxide Powder Material
SiO2 Al2O3 Fe2O3 TiO2 ZrO2
(HfO2)
CaO MgO Na2O K2O P2O5 MnO T.S Cr2O3 Ig. loss
Size
JCRM R301 Burned Bauxite 7.24 87.5 1.40 2.90 0.13 0.03 0.02 0.03 0.04 0.07 0.35 100g
JCRM R302 Burned Bauxite 3.45 90.6 1.76 3.17 0.30 0.02 0.03 0.02 0.02 0.05 0.22 100g
JCRM R303
JCRM R304
JCRM R041
Burned Bauxite
Sillimanite
Mullite
5.55
35.90
28.11
89.49
55.94
70.18
1.51
0.585
0.598
2.93
1.33
0.185
0.110
0.105
0.058
0.012
0.427
0.059
0.006
0.451
0.190
0.273
0.197
0.329
0.174
0.064
0.136
4.26
100g
100g
100g
JCRM R404
JCRM R405
JCRM R406
Quartz powder
Silica powder
Silica powder
>99.99
97.78
96.71
111.07
1.31
0.60.053
0.102
60.022
0.564
0.20.029
0.016
(<0.1)0.023
0.005
(1)0.060
0.030
(0.4)0.71
0.13
(0.00)
0.23
(<0.2)28
0.00
0.13
0.97
Italic type: mass ppm
100g
100g
100g
JCRM R501 Zircon Sand 32.6 0.39 0.06 0.16 66.5 0.11 100g
JCRM R502 Zircon Sand 32.8 5.87 0.10 0.24 60.3 0.26 100g
JCRM R651 Aluminous Shale 21.74 71.7 1.48 3.15 0.18 0.19 0.10 0.03 0.65 0.19 0.58 100g
JCRM R701 Feldspar 68.0 17.31 0.092 0.009 3.35 10.4 0.49 50g
JCRM R802 Pyrophllite 60.7 32.3 0.23 0.19 0.04 <0.01 0.09 0.07 0.05 6.0 50g
JCRM R901
JCRM R902
JCRM R903
Talc
Talc
Talc
59.77
60.77
55.76
0.924
0.115
2.447
1.224
0.091
0.564
0.019
0.004
0.075
0.438
0.342
0.998
31.22
31.97
31.84
0.054
0.006
0.029
0.004
0.003
0.007
0.195
0.046
0.051
0.004
( 0.002 )
( 0.003 )
6.14
6.64
8.23
50g
50g
50g
SO3
JCRM R031
JCRM R032
JCRM R033
Alumina Fine Powder
Alumina Fine Powder
Alumina Fine Powder
0.0009
0.015
0.095
0.000
0.015
0.0000
0.013
0.004
0.0001
0.034
0.020
0.0000
0.001
0.001
0.0019
0.343
0.064
0.0003
0.003
0.003
0.017 0.25
0.25
0.08
50g
50g
50g
Nonoxide Material T.Si T.N Al Fe Ca Mg W Ti Mn Co O C V Cr Ni Zr
JCRM R003
JCRM R004
JCRM R005
Silicon Nitride Powder
Silicon Nitride Powder
Silicon Nitride Powder
59.55
59.41
59.24
39.00
38.58
38.44
0.035
0.184
0.0042
0.028
0.130
0.0036
0.222
0.0026
0.0040
1.27
1.67
1.65
0.096
0.214
0.170
20g
20g
20g
T.C F.C F.Si F.SiO2
JCRM R021
JCRM R022
JCRM R023
Silicon Carbide Powder
Silicon Carbide Powder
Silicon Carbide Powder
68.8
68.1
69.3
29.9
30.4
29.6
0.039
0.058
0.003
0.018
0.051
0.015
0.007
0.025
0.003
0.0021
0.005
0.001
0.86
1.62
0.39
0.010
0.003
<0.001
<0.001
0.001
<0.001
0.15
0.01
0.01
1.08
0.98
0.86
0.57
0.31
0.20
0.002
<0.001
<0.001
0.004
0.006
0.001
0.0010
0.001
0.001
0.001
0.001
<0.001
50g
50g
50g
Glass SiO2 Al2O3 Fe2O3 TiO2 ZrO2 Na2O K2O B2O3 Cl
JCRM R102 Borosilicate Glass 80.5 2.27 0.033 0.011 0.032 4.00 0.029 12.7 0.057 50g
( ): Reference value
Reference Material Chemical Composition (mass %)
Oxide Powder Material
SiO2 Al2O3 Fe2O3 TiO2 MnO P2O5 CaO MgO Na2O K2O Nb2O5 HfO2 S Ig. loss
Size
JCRM R051
JCRM R052
JCRM R053
JCRM R054
Zirconia powder
Zirconia powder
Zirconia powder
Zirconia powder
(0.005)
0.019
0.036
0.300 0.136
0.0017
(0.0004)
0.030
0.132
(0.0005)
0.0012
0.127
0.136
0.0017
0.019
0.021
0.535
0.0004
0.0042
0.0020
0.208
0.015
0.021
0.028
0.0027
0.0013
(0.0007)
(0.0003)
0.054
0.427
1.96
1.81
1.67
1.60
0.71
0.25
0.65
0.15
50g
50g
50g
50g
JCRM R604
JCRM R605
JCRM R751
Gairome Clay
Caolin
Pottery Stone
47.88
49.77
79.32
35.37
35.64
14.15
1.357
0.283
0.340
0.865
0.068
0.010
0.006
0.003
0.020
0.105
0.009
0.216
0.004
0.033
0.251
0.004
0.049
0.083
0.032
0.121
0.468
(0.008)
(3.00)
(0.014)
(0.023)
(0.0010)
13.37
13.90
2.73
50g
50g
50g
JCRM R702
JCRM R703
JCRM R803
Albite
Potassiumfeldspar
Pyrophyllite
67.69
66.99
68.52
19.64
17.93
23.95
0.058
0.082
0.047
0.030
0.005
0.104
0.004
0.003
0.0014
0.139
0.008
0.018
0.546
0.095
0.033
0.103
0.040
0.017
11.31
3.32
0.165
0.137
11.02
2.32
0.02
0.23
0.36
4.40
50g
50g
50g
( ): Reference value
Certified Reference Material Series for X-ray Fluorescence Analysis of Refractories
JRRM 101-110 (Series No.1 for Fireclay Refractories)
Unit: mass% Constituent SiO2 Al2O3 Fe2O3 TiO2 MnO CaO MgO Na2O K2O JRRM 101 88.57 8.16 0.314 0.302 0.116 1.061 0.217 1.013 0.165
JRRM 102 80.47 13.79 3.978 0.454 0.015 0.049 0.673 0.303 0.145
JRRM 103 80.32 18.07 0.407 0.370 0.005 0.072 0.016 0.124 0.350
JRRM 104 67.35 22.52 3.244 2.943 0.017 0.259 0.070 0.300 3.048
JRRM 105a 69.17 25.35 0.768 2.249 0.119 0.407 0.222 0.651 0.817 JRRM 106 63.61 29.91 1.922 0.679 0.024 0.146 0.980 0.599 1.816
JRRM 107 55.32 37.08 2.202 1.155 0.019 0.710 0.492 0.218 2.573
JRRM 108 55.31 40.08 1.547 1.053 0.020 0.277 0.270 0.207 0.809
JRRM 109 54.23 41.24 0.892 1.961 0.011 0.146 0.126 0.307 0.793
JRRM 110 49.54 46.68 0.848 1.666 0.014 0.107 0.166 0.085 0.342
Note: The above values show the contents after igniting for one hour at 800±25℃.
Certified Reference Material Series for X-ray Fluorescence Analysis of Refractories
JRRM 121-135 (Series No.2 for Fireclay Refractories)
Unit: mass% Constituent SiO2 Al2O3 Fe2O3 TiO2 MnO CaO MgO Na2O K2O P2O5 Cr2O3 ZrO2 LOI* JRRM 121 86.30 6.073 0.407 0.056 0.023 1.967 0.126 3.207 0.234 0.324 0.018 1.119 0.057
JRRM 122 78.24 10.26 0.248 1.037 0.204 0.435 0.657 1.041 2.057 4.898 0.818 0.203 0.127
JRRM 123 79.16 13.31 4.134 0.459 0.012 0.135 1.328 0.296 0.109 0.807 0.014 0.008 0.037
JRRM 124 73.92 16.56 2.603 2.746 0.246 1.099 0.109 0.313 1.791 0.191 0.117 0.112 0.103
JRRM 125 79.27 18.71 0.504 0.309 0.008 0.130 0.084 0.072 0.691 0.046 0.010 0.023 0.077
JRRM 126 66.96 21.39 3.349 2.848 0.038 0.456 0.127 0.284 3.135 0.497 0.650 0.049 0.175
JRRM 127 68.59 23.08 0.926 2.194 0.174 0.182 0.153 1.756 0.542 1.785 0.273 0.046 0.072
JRRM 128 54.38 26.05 4.458 1.379 0.244 2.803 3.106 0.374 1.849 3.362 0.854 1.014 0.024
JRRM 129 62.26 30.10 1.460 0.966 0.018 0.157 2.232 0.234 1.927 0.201 0.107 0.112 0.117
JRRM 130 53.47 32.74 0.531 3.358 0.370 1.954 0.619 2.320 1.420 0.919 1.054 0.835 0.116
JRRM 131 52.71 36.63 2.208 1.162 0.032 0.785 1.023 0.768 2.619 1.611 0.070 0.264 0.174
JRRM 132 50.61 39.11 1.645 0.298 0.119 1.298 0.349 2.162 0.797 2.386 0.116 0.752 0.154
JRRM 133 50.10 39.02 3.693 1.932 0.017 0.109 2.034 0.335 0.914 0.344 1.277 0.573 0.089
JRRM 134 47.28 44.36 1.079 1.740 0.245 0.200 0.205 0.132 0.375 3.834 0.244 0.358 0.146
JRMM 135 37.26 48.92 3.057 0.076 0.049 2.360 1.245 2.879 2.776 0.487 0.427 0.203 0.183
Note: The above values show contents after drying for two hours at 110±5℃. (*) Indicated value
Certified Reference Material Series for X-ray Fluorescence Analysis of Refractories
JRRM 201-210 (Series No.1 for Silica Refractories) Unit: mass%
Constituent SiO2 Al2O3 Fe2O3 TiO2 MnO CaO MgO Na2O K2O JRRM 201 84.36 9.715 1.465 0.032 0.147 2.779 0.732 0.316 0.144
JRRM 202 85.72 7.595 3.972 0.567 0.004 0.817 0.020 1.014 0.025
JRRM 203 87.33 5.094 1.785 0.182 0.112 3.976 0.471 0.616 0.242
JRRM 204 89.64 4.497 2.081 0.150 0.107 1.792 0.313 0.315 0.907
JRRM 205 90.40 3.089 1.248 0.325 0.064 3.110 0.092 0.932 0.500
JRRM 206 92.88 1.772 3.205 0.018 0.018 1.205 0.072 0.180 0.507
JRRM 207 94.05 1.703 0.965 0.079 0.042 2.518 0.160 0.047 0.212
JRRM 208 94.43 0.463 0.064 0.005 0.001 4.197 0.056 0.634 0.022
JRRM 209 96.22 0.876 0.373 0.050 0.068 1.893 0.106 0.033 0.170
JRRM 210 97.69 0.163 0.833 0.005 0.002 0.301 0.788 0.021 0.007
Note: The above values show contents after igniting for one hour at 800±25℃.
Certified Reference Material Series for X-ray Fluorescence Analysis of Refractories
JRRM 301-310 (Series No.1 for High Alumina Refractories)
Unit: mass% Constituent SiO2 Al2O3 Fe2O3 TiO2 MnO CaO MgO Na2O K2O B2O3* JRRM 301 43.91 46.80 3.529 1.031 0.018 0.797 0.690 0.170 2.007 0.87 JRRM 302 37.70 53.93 4.490 0.597 0.200 0.871 0.697 0.565 0.667 ― JRRM 303 36.16 59.25 1.476 0.164 0.008 1.039 0.855 0.699 0.207 ― JRRM 304 27.55 63.06 3.469 4.340 0.059 0.183 0.376 0.276 0.388 ― JRRM 305 20.03 68.69 2.816 3.300 0.010 0.655 0.304 0.808 3.116 ― JRRM 306 17.35 74.19 1.956 2.685 0.019 0.626 0.100 0.994 1.758 ― JRRM 307 10.87 80.14 2.972 1.229 0.016 0.152 0.612 1.084 2.361 ― JRRM 308 10.25 86.59 0.412 1.795 0.112 0.099 0.053 0.263 0.108 ― JRRM 309 2.124 89.83 1.277 3.856 0.003 1.023 0.288 0.422 0.922 ― JRRM 310 0.412 94.71 0.024 2.064 0.045 0.038 0.979 0.081 1.326 ―
Note: The above values show contents after igniting for one hour at 800±25℃. (*) Indicated value
Certified Reference Material Series for X-ray Fluorescence Analysis of Refractories
JRRM 401-410 (Series No.1 for Magnesia Refractories)
Unit: mass% Indicated value Constituent
SiO2 Al2O3 Fe2O3 CaO MgO TiO2 MnO Na2O K2O Cr2O3 P2O5 B2O3
JRRM 401 6.424 8.106 3.890 0.208 81.24 0.017 0.011 0.006 0.003 0.004 0.035 0.016
JRRM 402 5.462 1.999 5.050 3.570 83.77 0.026 0.011 0.010 0.001 0.006 0.077 0.127
JRRM 403 8.144 4.060 1.553 0.615 85.48 0.003 0.014 0.004 0.001 0.010 0.044 0.031
JRRM 404 1.223 6.014 2.908 1.786 88.02 0.007 0.030 0.009 0.001 0.006 0.053 0.011
JRRM 405 3.479 1.372 1.346 1.690 91.95 0.054 0.074 0.009 0.015 0.014 0.120 0.011
JRRM 406 1.196 1.139 0.874 4.805 91.85 0.004 0.011 0.002 0.000 0.006 0.041 0.013
JRRM 407 2.432 0.100 2.145 0.675 94.55 0.003 0.014 0.004 0.001 0.080 0.044 0.023
JRRM 408 0.460 2.554 0.134 0.672 96.19 0.004 0.010 0.001 0.000 0.009 0.015 0.099
JRRM 409 0.534 0.202 0.490 0.744 98.03 0.003 0.015 0.002 0.001 0.019 0.023 0.033
JRRM 410 0.188 0.058 0.050 0.595 99.08 0.003 0.010 0.001 0.000 0.003 0.045 0.026
Note: The above values show the contents after burning for sixty minutes at 1050±25℃.
Certified Reference Material Series for X-ray Fluorescence Analysis of Refractories
JRRM 501-510 (Series No.1 for Chrome-Magnesia Refractories)
Unit: mass% Indicated value Constituent SiO2 Al2O3 Fe2O3 TiO2 MnO CaO MgO Cr2O3
LOI P2O5 V2O5 NiO ZnO JRRM 501 0.926 2.922 4.806 0.006 0.020 0.923 87.60 2.828 0.137 0.036 0.019 0.018 0.006
JRRM 502 3.118 11.98 1.021 0.013 0.018 0.201 76.28 7.498 0.065 0.026 0.024 0.026 0.004
JRRM 503 9.096 7.147 3.006 0.047 0.038 3.815 63.11 13.60 0.111 0.032 0.037 0.036 0.013
JRRM 504 2.189 17.56 4.112 0.013 0.011 2.608 54.85 18.35 0.124 0.034 0.016 0.015 0.011
JRRM 505 1.823 7.768 17.76 0.118 0.109 0.492 50.14 21.74 0.085 0.023 0.075 0.078 0.021
JRRM 506 2.165 14.69 7.490 0.134 0.072 0.460 46.65 28.19 0.070 0.018 0.086 0.094 0.010
JRRM 507 5.698 25.02 12.98 0.166 0.115 1.615 22.36 32.03 -0.111 0.010 0.130 0.202 0.037
JRRM 508 3.081 3.891 22.70 0.014 0.006 1.031 30.86 38.18 0.053 0.016 0.008 0.010 0.005
JRRM 509 1.964 20.28 10.15 1.203 0.082 2.867 20.45 42.57 0.137 0.013 0.118 0.044 0.037
JRRM 510 4.914 12.21 14.99 0.133 0.176 0.291 16.86 50.38 -0.255 0.016 0.111 0.193 0.041
JRRM 511 2.909 6.684 27.22 0.105 0.127 0.071 10.62 52.51 -0.483 0.004 0.054 0.108 0.052
JRMM 512 10.57 29.25 26.01 0.047 0.025 4.061 24.81 4.989 0.028 0.019 0.012 0.018 0.013
Note: The above values show contents after drying for two hours at 110±5℃.
Certified Reference Material Series for X-ray Fluorescence Analysis of Refractories
JRRM 601-610 (Series No.1 for Zircon-Zirconia Refractories)
Unit: mass% Constituent SiO2 Al2O3 Fe2O3 TiO2 CaO MgO Na2O K2O P2O5 Cr2O3 ZrO2 HfO2 LOI* JRRM 601 0.263 0.119 0.101 0.168 5.581 0.064 0.004 0.002 0.007 0.003 92.01 1.591 0.079
JRRM 602 0.334 0.078 1.618 0.164 0.220 5.290 0.766 0.004 1.338 0.015 88.25 1.522 0.252
JRRM 603 0.966 5.293 2.858 0.932 0.953 0.967 0.187 0.652 0.837 0.029 84.70 1.453 0.115
JRRM 604 3.045 6.917 0.429 0.134 0.094 0.017 1.087 1.937 1.992 3.062 79.26 1.356 0.235
JRRM 605 10.78 4.832 0.176 0.127 1.939 1.993 0.457 0.541 0.352 1.548 75.36 1.314 0.314
JRRM 606 22.03 0.532 0.933 0.117 0.021 0.320 2.028 0.014 0.019 0.008 72.35 1.265 0.328
JRRM 607 32.75 3.519 0.120 0.136 0.048 0.031 0.026 0.043 0.085 0.002 61.31 1.211 0.569
JRRM 608 34.62 0.707 0.092 0.102 0.521 3.125 0.031 0.019 0.117 0.497 58.84 1.217 0.069
JRRM 609 40.50 0.885 0.150 0.153 0.300 0.150 0.942 0.028 0.081 0.012 55.56 1.122 0.122
JRRM 610 45.66 0.451 0.308 0.099 3.075 0.547 0.043 0.010 0.113 0.009 48.70 0.986 0.074
Note: The above values show contents after drying for two hours at 110±5℃. (*) Indicated value
Certified Reference Material Series for X-ray Fluorescence Analysis of Refractories
JRRM 701-710 (Series No.1 for Alumina-Zirconia-Silica Refractories)
Unit: mass% Indicated value
Constituent SiO2 Al2O3 Fe2O3 TiO2 CaO MgO Na2O K2O Cr2O3 ZrO2 HfO2 LOI MnO P2O5
JRRM 701 28.44 10.09 2.007 4.961 2.073 0.476 1.846 0.024 1.010 48.06 0.850 0.098 0.007 0.027
JRRM 702 9.99 38.14 0.374 0.210 1.552 1.979 2.024 0.579 0.111 42.54 2.086 0.180 0.004 0.028
JRRM 703 14.64 46.34 0.059 0.072 0.037 0.011 0.535 0.002 0.006 37.35 0.727 0.096 0.000 0.035
JRRM 704 42.61 19.58 0.553 1.025 0.155 0.515 0.228 0.402 0.518 33.46 0.682 0.079 0.089 0.130
JRRM 705 1.999 64.14 0.141 2.021 0.191 0.460 0.300 0.018 2.019 27.96 0.484 0.166 0.004 0.017
JRRM 706 39.33 25.95 0.130 3.778 1.587 0.158 3.496 0.952 0.010 22.72 1.190 0.729 0.004 0.016
JRRM 707 21.17 55.78 1.814 0.289 1.086 0.844 0.199 0.155 0.180 18.16 0.376 0.011 0.003 0.055
JRRM 708 0.546 79.52 0.800 1.020 1.172 1.646 0.089 0.746 0.297 12.84 1.033 0.136 0.001 0.002
JRRM 709 34.38 50.35 0.476 0.091 0.524 1.208 1.038 0.216 2.916 8.322 0.184 0.202 0.002 0.009
JRRM 710 5.624 82.29 1.150 3.002 0.225 0.049 1.419 0.636 1.027 2.965 1.511 0.094 0.002 0.042
Note: The above values show contents after drying for two hours at 110±5℃
Certified Reference Material Series for X-ray Fluorescence Analysis of Refractories
JRRM 801-810 (Series No.1 for Alumina-Magnesia Refractories)
Unit: mass% Indicated value
Constituent SiO2 Al2O3 Fe2O3 TiO2 CaO MgO Na2O K2O P2O5 LOI MnO Cr2O3 ZrO2
JRRM 801 0.355 93.49 2.009 0.217 0.141 3.261 0.199 0.014 0.002 0.149 0.002 0.003 0.008
JRRM 802 3.329 84.25 1.035 1.484 2.003 6.312 0.159 0.462 0.957 0.063 0.003 0.002 0.002
JRRM 803 0.583 74.23 4.904 2.516 0.576 16.20 0.869 0.007 0.017 0.364 0.005 0.002 0.004
JRRM 804 5.178 64.66 4.020 0.132 4.767 20.84 0.089 0.044 0.111 0.012 0.020 0.010 0.002
JRRM 805 2.498 58.03 0.732 1.059 0.282 36.04 0.540 0.015 0.682 0.174 0.006 0.001 0.000
JRRM 806 0.514 48.85 0.165 0.004 0.979 49.43 0.049 0.001 0.048 0.212 0.026 0.006 0.001
JRRM 807 0.586 39.96 0.323 0.198 2.759 55.07 0.329 0.153 0.530 0.574 0.005 0.002 0.001
JRRM 808 0.799 28.68 0.565 0.714 0.994 67.01 0.409 0.692 0.229 0.844 0.017 0.001 0.001
JRRM 809 0.363 19.86 0.115 2.888 4.479 70.11 0.049 0.989 1.068 0.484 0.006 0.001 0.001
JRRM 810 4.211 10.08 3.118 1.916 0.180 78.96 0.759 0.167 0.513 0.222 0.016 0.004 0.004
Note: The above values show contents after igniting for 30 minutes at 1000±25℃.
Certified Reference Material for Carbon Analysis of refractories
JRRM 1001-1009 (Series No.1 for Calibration of Carbon Analyzer)
Unit: mass% Certified value Approximate value
C Total C Free SiC LOI Al Fe Ti Ca Mg Si Free O N
JRRM 1001 (SiC 100) 29.81 0.04 99.58 ― 0.008 0.044 0.0035 <0.001 <0.001 0.06 0.048 0.030
JRRM 1002 (C 5) 5.03 4.98 0.06 5.11 ― ― ― ― ― ― ― ―
JRRM 1003 (C 10) 10.06 10.01 ― 10.11 ― ― ― ― ― ― ― ―
JRRM 1004 (C 20) 20.04 19.92 ― 20.01 ― ― ― ― ― ― ― ―
JRRM 1005 (C 30) 29.93 29.81 ― 29.95 ― ― ― ― ― ― ― ―
JRRM 1006 (C 50) 49.99 49.97 ― 49.95 ― ― ― ― ― ― ― ―
JRRM 1007 (C 10-SiC 90) 36.75 10.01 89.29 ― ― ― ― ― ― ― ― ―
JRRM 1008 (C 5-SiC 30) 14.12 5.21 29.74 ― ― ― ― ― ― ― ― ―
JRRM 1009 (C 40-SiC 6) 39.43 37.67 6.18 ― ― ― ― ― ― ― ― ―
Note: The above values show contents after drying for two hours at 110±5℃ *) JRRM 1001 are available individually. (Others are available at set only from JRRM 1001 to JRRM 1009)
I. CRMs for Chemical Analysis
I-1. Pure iron series
Mass content in % C Si Mn P S Ni Cr Mo Cu Co Al As Sn B N Na
JSS No.
○ 001-6 High grade pure iron 1 0.00024 0.0001 (0.000003) (0.00005) 0.00015 (0.00002) (<0.00006) (<0.00002) 0.000036 0.000032 (<0.0001) (<0.0003) (0.00003) (<0.00002) 0.00021
003-5 High grade pure iron 3 0.00046 0.0049 0.0027 0.00043 (0.0002) 0.00004 (0.0001) 0.00007 0.00154 0.00022 0.0078 (0.0002) 0.00049 (0.00002) 0.00078
○ 009-3 Pure iron (III) oxide (0.02) (<0.004) (0.00006) (<0.0002) (0.0001) (0.00003) 0.00097 (<0.0001) (<0.0001) (0.0003) (<0.0001) (<0.0002) (<0.0001)
☆Continued
Mass content in % Mg Ca W V Ti Pb Zn Zr Se Te Sb Nb Bi K T.Fe Net weight
JSS No. (g)
○ 001-6 High grade pure iron 1 (<0.00006) (<0.0002) (0.00001) (<0.00003) (<0.00002) 0.000018 0.00019 (<0.00003) 100
003-5 High grade pure iron 3 (<0.00003) (<0.0003) 0.00004 (<0.00003) (<0.0001) (<0.00001) (<0.00005) (<0.00002) (<0.0001) (<0.00005) (<0.00002) (<0.00005) 150
○ 009-3 Pure iron (III) oxide (0.00003) (<0.0001) (<0.0001) (<0.0001) (<0.0001) (<0.0002) (<0.0001) (<0.0002) 69.84 50
C.W.: 0.16 Ig.Loss: (0.4)
I-2. Carbon steel series
Mass content in % C Si Mn P S Cu Al N Net weight
JSS No. (g)
023-8 13 Carbon steel 0.112 0.22 0.48 0.020 0.0067 0.010 (0.015) (0.0037) 150
030-7 20 Carbon steel 0.196 0.24 0.75 0.024 0.0076 0.024 0.023 0.0033 150
050-6 40 Carbon steel 0.38 0.19 0.50 0.013 0.0057 0.008 0.023 0.0029 150
057-7 52 Carbon steel 0.522 0.231 0.726 0.0159 0.0125 0.0096 0.0338 0.0043 150
061-7 63 Carbon steel 0.626 0.206 0.513 0.0240 0.0106 0.0086 (0.002) 0.0036 150
066-4 85 Carbon steel 0.845 0.227 0.788 0.0175 0.0052 0.0117 0.038 0.0047 150
I-3. Pig iron series
Mass content in % C Si Mn P S Ni Cr Mo Cu V Ti As N Net weight
JSS No. (g)
X 102-7 Pig iron for steel making
○ 110-12 Pig iron for casting 4.18 1.70 0.392 0.0902 0.0251 0.0117 0.0162 0.003 0.0100 0.0324 0.0022 0.0044 100
120-1 Castiron: 3 C 2.85 1.32 0.70 0.053 0.0095 0.12 0.28 (0.007) 0.29 0.007 0.006 0.0058 150
( ) Non-certified value
*(This value means the carbon content in the metal with removal of contaminated carbon on the surface of test portion) ※ In preparation
○ New/Renewal CRMs
X Sold out
Japanese Iron and Steel Certified Reference Materials
I-4. Low alloy steel series
Mass content in % C Si Mn P S Ni Cr Mo Cu V Al Net weight
JSS No. (g)
○ 150-16 Low alloy steel No.1 0.475 0.219 0.137 0.0346 0.0296 3.98 0.298 0.201 (<0.003) 0.0195 0.023 150
○ 151-16 Low alloy steel No.2 0.393 0.103 1.697 0.0297 0.0174 2.92 0.101 0.0540 0.0969 0.0503 0.0279 150
○ 152-16 Low alloy steel No.3 0.277 0.387 0.440 0.0174 0.0056 1.98 0.584 1.010 0.500 0.100 0.0212 150
X 153-14 Low alloy steel No.4
154-14 Low alloy steel No.5 0.102 0.589 1.224 0.0023 0.0046 0.505 2.03 0.394 0.201 0.301 150
155-15 Low alloy steel No.6 0.0360 0.490 0.178 0.00163 0.0045 0.173 3.09 0.718 0.385 0.396 150
I-5. Minor elements determination series B
Mass content in % C Si Mn Ni Cr Mo V Co Ti Al As Sn B Zr Sb
JSS No.
168-7 Minor element No.1 0.053 0.20 0.43 0.017 0.020 0.095 0.077 0.041 0.012 0.0065
169-7 Minor element No.2 0.047 0.21 0.42 0.046 0.108 0.068 0.012 0.040 0.0050 0.013
170-7 Minor element No.3 0.052 0.18 0.43 0.081 0.049 0.011 0.105 0.045 0.032 0.056
171-7 Minor element No.4 0.042 0.21 0.40 0.099 0.074 0.036 0.039 0.037 0.046 0.040
172-7 Minor element No.5 0.051 0.20 0.43 0.010 0.052 0.012 0.0010 0.009 0.0022
173-7 Minor element No.6 0.038 0.21 0.40 0.028 0.031 0.019 0.0041 0.005 0.0051
174-7 Minor element No.7 0.042 0.21 0.40 0.065 0.011 0.034 0.0076 0.014 0.0102
X 175-7 Minor element No.8
☆Continued
Mass content in % Nb Ca Net weight
JSS No. (g)
168-7 Minor element No.1 0.0006 150
169-7 Minor element No.2 0.0008 150
170-7 Minor element No.3 0.0019 150
171-7 Minor element No.4 0.0027 150
172-7 Minor element No.5 0.050 150 ( ) Non-certified value
X 173-7 Minor element No.6 ※ In preparation
174-7 Minor element No.7 0.020 150 ○ New/Renewal CRMs
X 175-7 Minor element No.8 X Sold out
I-6. One element determination series
Mass content in % C Si P S Al B N Net weight
JSS No. (g)
116-1 Pig iron for casting 4.09 0.0186 100
201-13 Steel for carbon 0.0440 150
202-1 Steel for carbon 1.386 150
208- 2 Steel for carbon 1.056 150
X 1201-2 Steel for low carbon
X 1202-2 Steel for low carbon
○ 1203-3 Steel for low carbon 0.0097 150
X 1204-3 Steel for low carbon
○ 1205-1 Steel for low carbon 0.00105 150
230-5 Steel for phosphorus 0.0113 150
X 232-4 Steel for phosphorus
233-1 Steel for phosphorus 0.0069 150
X 240-13 Steel for sulfur
241-11 Steel for sulfur 0.0194 150
242-11 Steel for sulfur 0.0320 150
243-5 Steel for sulfur 0.339 150
○ 244-9 Steel for sulfur 0.0020 150
245-4 Steel for sulfur 0.062 150
280-1 Steel for silicon 0.023 150
330-3 Steel for aluminium 0.0057 150
331-3 Steel for aluminium 0.032 150
332-3 Steel for aluminium 0.049 150
362-1 Steel for boron 0.0018 150
363-1 Steel for boron 0.0027 150
364-1 Steel for boron 0.0045 150
366-8 Steel for nitrogen 0.00075 150 ( ) Non-certified value
367-8 Steel for nitrogen 0.0034 150 ※ In preparation
370-1 Steel for nitrogen 0.417 150 ○ New/Renewal CRMs
371-1 Steel for nitrogen 0.202 150 X Sold out
I-7. High tensile structural steel series A
Mass content in % C Si Mn P S Ni Cr Mo Cu V Ti Al N Net weight
JSS No. (g)
501-6 SCM 430 0.318 0.246 0.738 0.0232 0.0129 0.063 1.039 0.218 0.1034 0.0210 0.0322 0.0058 150
502-6 SCM 440 0.43 0.25 0.70 0.018 0.0097 0.049 1.01 0.17 0.067 (0.004) 0.026 0.0049 100
I-8. High tensile structural steel series B
Mass content in % C Si Mn P S Ni Cr Mo Cu Al N Net weight
JSS No. (g)
507-5 SCM 435 0.36 0.20 0.76 0.015 (0.0079) 0.075 0.99 0.21 0.17 0.022 0.0102 150
I-9. Cace hardening steel series
Mass content in % C Si Mn P S Ni Cr Mo Cu V Al N Pb Net weight
JSS No. (g)
512-7 S9CK 0.073 0.18 0.45 0.0089 0.0097 0.015 0.059 (0.010) 0.008 (0.001) (0.017) 0.0034 150
513-7 SCr 415 0.173 0.29 0.84 0.016 0.021 0.024 1.14 (0.005) 0.011 0.006 0.034 0.0077 150
X 514-7 SCM 420
517-7 SNCM 616 0.200 0.250 0.826 0.0107 0.0084 3.04 1.75 0.516 0.0132 (0.003) (0.006) 0.0061 150
X 519-1 Lead free cutting steel
I-10. Tool steel series
Mass content in % C Si Mn P S Ni Cr Mo Cu W V N Net weight
JSS No. (g)
601-10 SKS 21 1.143 0.237 0.441 0.0194 (0.0042) 0.0580 0.462 0.106 0.120 0.876 0.110 0.0109 150
602-10 SKS-11 1.242 0.218 0.376 0.0091 0.0089 0.047 0.364 0.101 0.0305 3.62 0.217 0.0082 150
604-9 SKD-6 0.362 1.056 0.346 0.0185 0.0122 0.177 4.90 1.079 0.0630 0.0114 0.512 0.0174 150
605-10 SKT 4 0.574 0.111 0.870 0.0150 0.0126 1.500 0.876 0.368 0.162 0.0072 0.0136 150
I-11. High speed steel series
Mass content in % C Si Mn P S Ni Cr Mo Cu W V Co N Net weight
JSS No. (g)
X 607-8 SKH 3
X 609-9 SKH 55
610-9 SKH 57 1.24 0.30 0.32 0.018 0.0029 0.100 4.04 3.06 0.040 9.07 3.26 9.61 0.0354 150
611-10 SKH 51 0.874 0.332 0.305 0.0267 0.00064 0.116 4.09 4.89 0.0479 6.21 1.83 0.535 0.0252 150
( ) Non-certified value
※ In preparation
○ New/Renewal CRMs
X Sold out
I-12. Stainless steel series
Mass content in % C Si Mn P S Ni Cr Mo Cu Co Al N Nb Net weight
JSS No. (g)
650-14 SUS 430 0.041 0.41 0.48 0.025 (0.0013) 0.21 16.20 0.012 0.047 0.028 0.002 0.0340 150
651-14 SUS 304 0.046 0.67 1.19 0.027 0.0058 9.03 18.26 0.11 0.12 0.17 (0.002) (0.0426) 150
652-14 SUS 316 0.0358 0.624 1.177 0.0315 0.00135 10.60 16.88 2.06 0.177 0.143 0.0030 0.0191 150
653-14 SUS 309S 0.0564 0.621 1.575 0.0307 0.00094 13.74 22.36 0.146 0.201 0.193 0.005 0.039 150
X 654-10 SUS 310S
655-10 SUS 347 0.045 0.63 0.96 0.024 (0.0005) 9.75 17.53 0.033 0.045 (0.073) (0.003) 0.0072 0.49 150
I-13. Heat resisting steel series
Mass content in % C Si Mn P S Ni Cr Mo Cu Ti Al N Net weight
JSS No. (g)
670-3 SUH 409 0.008 0.55 0.53 0.0020 (0.0005) 0.21 11.23 0.020 0.044 0.26 (0.055) 0.0064 150
I-14. Heat resisting super alloy series
Mass content in % C Si Mn P S Ni Cr Cu Co Ti Al Fe Mg Net weight
JSS No. (g)
680-3 NCF 2 0.051 0.44 0.95 (0.0009) 0.0018 32.80 20.92 0.20 0.40 0.42 0.51 (43.2) 150
683-2 NCF 1 0.049 0.39 0.32 (0.0008) 0.0013 73.43 15.82 0.051 (0.011) 0.013 0.12 9.66 0.013 150
I-15. Ferroalloy series
Mass content in % C Si Mn P S Ni Cr Mo Cu V Co Al Sn Ta Nb Net weight
JSS No. (g)
X 701-5 High carbon ferro manganese
X 705-4 Silicon manganese
720-4 Ferrosilicon (0.045) 76.35 0.21 0.032 (0.003) 1.52 150
X 732-2 High carbon ferro chromium
X 745-3 Low carbon ferromolybdenum
750-2 Ferro vanadium 0.14 0.52 0.018 0.010 53.40 3.20 150
755-2 Ferro niobium 0.100 1.82 0.065 0.013 1.79 0.053 (0.37) 68.14 150
760-3 Ferro nickel 1.73 1.29 0.162 0.0222 0.0093 19.56 1.19 0.0219 0.504 150
( ) Non-certified value
※ In preparation
○ New/Renewal CRMs
X Sold out
I-16. Iron ore series
Mass content in % CW T.Fe FeO SiO2 Mn P S Cu TiO2 Al2O3 CaO MgO BaO As Ni Cr
JSS No. [Fe2+] [Si] [Ti] [Al] [Ca] [Mg]
801-6 Indian hematite 4.07 61.75 (1.0) 1.95 0.707 0.060 0.0093 (0.002) 0.051 1.09 (0.014) (0.032) 0.0033 (0.005)
803-6 Hermersley hematite 1.93 65.50 (0.27) 2.88 0.020 0.048 (0.011) (0.001) 0.059 1.22 (0.018) 0.020 (0.001) 0.010
[1.35] [0.035] [0.64] [(0.013)] [0.012]
804-2 Iscor hematite 0.37 66.93 (0.29) [1.17] 0.016 0.050 0.0132 [0.023] [0.51] [0.0490] [0.0099] 0.0019 0.0028 0.0244
805-1 MBR hematite 0.72 68.04 0.49 0.25 0.044 (0.003) (0.001) 0.029 1.02 0.028 0.033
[0.23] [0.018] [0.54] [0.020] [0.020]
814-1 Pure magnetite 0.53 65.70 3.88 0.025 0.036 0.845 0.036 0.060 0.47 0.78 1.43 0.007
[1.81] [0.036] [0.25] [0.56] [0.86]
820-3 Robe river limonite 7.93 56.81 0.069 0.0404 0.0141 0.001 0.0027 0.004
X 831-1 Taharoa iron sand
850-4 Marcona pellet (0.07) 65.67 (0.30) 4.12 0.019 0.013 0.006 0.008 0.056 0.40 0.41 0.79 (0.006) (0.003)
[1.93] [0.033] [0.21] [0.30] [0.48]
X 851-4 Sintered ore
852-2 Savage river pellet (0.04) 66.83 1.70 0.077 0.014 (0.002) 0.006 0.48 0.38 0.13 1.15 0.045 (0.004)
[0.79] [0.29] [0.20] [0.094] [0.69]
X 853-1 Algarrobo pellet
☆Continued
Mass content in % V Pb Zn Na2O K2O Net weight
JSS No. [Na] [K] (g)
801-6 Indian hematite (0.003)
803-6 Hermersley hematite (0.002) (0.002) (0.006) (0.005) 100
[(0.004)] [(0.004)]
804-2 Iscor hematite 0.0031 100
805-1 MBR hematite (0.005) (0.002) (0.004) (0.006) 100
[(0.003)] [(0.005)]
814-1 Pure magnetite 0.045 0.032 0.117 0.103 100
[0.087] [0.085]
820-3 Robe river limonite 0.0039 0.001 0.0082 70
X 831-1 Taharoa iron sand
850-4 Marcona pellet 0.025 (0.007) 0.129 0.075 100
[0.095] [0.062]
X 851-4 Sintered ore
852-2 Savage river pellet 0.46 (0.005) 0.030 0.007 100
[0.022] [0.006]
X 853-1 Algarrobo pellet
I-17. Ore series
Mass content in % Mn O (Active) Cr2O3 CW T.Fe SiO2 P S Al2O3 CaO MgO BaO Net weight
JSS No. (g)
X 861-1 Manganese ore
870-2 Chromium ore 48.14 14.04 3.96 (0.002) 0.018 11.62 15.54 100
( ) Non-certified value
I-18. Fluorspar series [ ] Metallic form
Mass content in % CaF2 SiO2 CaCO3 P S As Net weight ※ In preparation
JSS No. (g) ○ New/Renewal CRMs
X 883-1 The people's republic of China X Sold out
I-19. Blast Furnace slag series
Mass content in % SiO2 Al2O3 CaO MgO TiO2 MnO T.Fe P S Na K Ni Cr Cl Net weight
JSS No. (g)
905-1 Blast furnace slag 34.2 14.2 42.1 6.8 0.56 0.22 0.17 0.008 0.558 0.143 0.308 70
II. CRMs for Instrumental Analysis
II-1. Carbon steel series
Mass content in % C Si Mn P S Ni Cr Cu Size
JSS No.
410-2 10 Carbon steel 0.099 0.116 0.43 0.029 0.030 0.011 0.011 0.102
411-2 15 Carbon steel 0.138 0.117 0.43 0.029 0.030 0.011 0.010 0.101 35mm φx 30mm
412-2 20 Carbon steel 0.196 0.117 0.43 0.029 0.030 0.011 0.011 0.101
413-2 40 Carbon steel 0.39 0.25 0.56 0.019 0.019 0.011 0.011 0.102
414-2 60 Carbon steel 0.61 0.25 0.55 0.019 0.019 0.011 0.013 0.102
415-2 80 Carbon steel 0.75 0.25 0.55 0.019 0.019 0.011 0.013 0.101
II-2. Low alloy steel series
Mass content in % C Si Mn P S Ni Cr Mo Cu V Size
JSS No.
X 150-13 Low alloy stee 1
X 151-13 Low alloy stee 2
X 152-13 Low alloy stee 3
X 153-13 Low alloy stee 4
X 154-13 Low alloy stee 5
X 155-13 Low alloy stee 6
II-3. Case hardening steel series
Mass content in % C Si Mn P S Ni Cr Mo Cu V Al Size
JSS No.
X 512-6 S9CK
X 513-6 SCr415
X 514-6 SCM420
X 515-6 SNC415
X 516-6 SNCM24
X 517-6 SNCM616
( ) Non-certified value
※ In preparation
○ New/Renewal CRMs
X Sold out
II-4. Tool steel series
Mass content in % C Si Mn P S Ni Cr Mo Cu W V Size ( ) Non-certified value
JSS No. ※ In preparation
620-1 SKS 3 0.95 0.24 0.96 0.0082 0.0095 0.038 0.90 0.051 0.022 0.66 (0.009) ○ New/Renewal CRMs
621-1 SKS 2 1.05 0.22 0.69 0.015 0.0065 0.109 0.75 0.107 0.092 1.13 0.064 35mm φx 30mm X Sold out
622-1 SKS 11 1.22 0.31 0.45 0.017 0.0069 0.16 0.36 0.16 0.037 3.44 0.16
623-1 SKD 4 0.30 0.28 0.54 0.013 0.0161 0.20 2.56 0.27 0.014 5.55 0.39
624-1 SKD 6 0.38 0.89 0.30 0.018 (0.012) 0.044 4.92 1.19 0.21 0.103 0.42
625-1 SKT 4 0.57 0.101 0.88 0.016 0.0165 1.51 0.87 0.36 0.16 (0.004) (0.007)
II-5. High speed steel series
Mass content in % C Si Mn P S Ni Cr Mo Cu W V Co N Size
JSS No.
606-8 SKH 2 0.76 0.28 0.31 0.016 0.0008 0.065 4.00 0.58 0.027 17.16 0.83 0.12 0.0290
607-8 SKH 3 0.78 0.30 0.35 0.026 0.0031 0.052 3.97 0.54 0.025 17.48 0.84 4.59 0.0270 35mm φx 30mm
608-8 SKH 4A 0.80 0.36 0.33 0.025 0.0028 0.044 3.99 0.41 0.017 17.03 0.99 9.09 0.0320
609-8 SKH 55 0.89 0.32 0.31 0.027 0.0007 0.12 3.98 4.85 0.053 6.10 1.87 4.63 0.0465
610-8 SKH 57 1.23 0.28 0.31 0.026 0.0015 0.18 3.96 3.09 0.066 8.94 3.25 9.60 0.0348
611-8 SKH 9 0.86 0.37 0.30 0.025 0.0013 0.13 3.97 4.88 0.046 6.27 1.88 0.40 0.0548
II-6. Stainless steel series
Mass content in % C Si Mn P S Ni Cr Mo Cu Co Nb Size
JSS No.
650-13 SUS 430 0.053 0.30 0.48 0.024 (0.0048) 0.18 16.70 0.013 0.020 0.017
651-13 SUS 304 0.018 0.42 1.81 0.026 0.0027 10.20 18.42 0.24 0.16 0.13 35mm φx 30mm
652-13 SUS 316 0.044 0.42 1.73 0.031 0.0027 11.38 16.56 2.13 0.20 0.18
653-13 SUS 309S 0.044 0.40 1.80 0.033 0.0006 13.96 22.43 0.20 0.16 0.20
654-13 SUS 310S 0.046 0.40 1.69 0.026 0.0006 19.42 24.79 0.23 0.15 0.15
655-13 SUS 347 0.036 0.62 1.81 0.028 0.0043 9.52 17.34 0.22 0.20 0.17 0.55
II-7. High Grade Pure Iron Disc Size: 32mm φx 25mm
Mass content in μg/g C Si Mn P S Ni Cr Mo Cu Co Al Sn W B N As
JSS No.
1000-1 Pure iron 4.6* 49 27 4.3 2* 0.4 (1) 0.7 15.4 2.2 78 4.9 0.4 (0.2) 7.8 (<2)
☆Continued
Mass content in % Bi Ca Cd Ce La Mg Nb Pb Sb Se Ta Te Ti V Zn Zr
JSS No.
1000-1 Pure iron (<0.1) (<3) (<0.1) (<0.1) (<0.1) (<0.3) (<0.5) (<0.1) (<0.2) (<1) (<0.1) (<0.5) (<1) (<0.3) (<0.5) (<0.2)
*) This value means the carbon content in the metal with removal of contaminated carbon on the surface of test portion
III. Setting-up sample for determination of gaseous elements in steel
Mass content in (μg/g) O N H Size
JSS No. (Uncertified) (Uncertified)
GS-1d 35.4 (200) 1.6
X GS-2d
X GS-3c (5mm dia. x 230mm x 8pcs: apprx. 280g)
○ GS-5e (144) 31.2
X GS-6b
○ GS-12a 4.8 (6mm dia. x 230mm x 8pcs: approx. 410g)
IV. Steel sample of isolation and determination of nonmetallic inclusion
IV-1. Carbide isolation series
Mass content in % Ti Fe Cr Mn Mo Size
JSS No.
221-1b M3C 1.91 0.384 0.138 0.022 18 φx 50mm
222-1a (Cr, Fe)23C6 (0.20) 0.74 18 φx 70mm
222-1b (Cr, Fe)23C6 (0.20) 0.73 18 φx 70mm
IV-2. Sulfide isolation series
Mass content in % S Size
JSS No.
260-1 MnS 0.0046 18 φx 60mm
261-1 MnS 0.023 18 φx 60mm
262-1 TiS 0.049 18 φx 55mm ( ) Non-certified value
263-1 Zr3S4 0.050 18 φx 55mm ※ In preparation
264-1 CaS 0.0016 18 φx 60mm ○ New/Renewal CRMs
265-1 CeS, MnS 0.018 18 φx 60mm X Sold out
October 25, 2007
STANDARD MATERIALS FOR GAS ANALYSIS
(SEISHIN ORIGINAL)
NITROGEN/OXYGEN IN STEEL PINS
Product No. N (ppm) O (ppm) Form Unit Size Price (JPY)
SS-2 10 - 20 100 - 120 1.0g pin (φ5mm×6.5mm) 100 pcs 23,000
SS-3 55 - 70 165 - 185 1.0g pin (φ5mm×6.5mm) 100 pcs 23,000
SS-4 135 - 145 10 - 15 1.0g pin (φ5mm×6.5mm) 100 pcs 23,000
Certificate of analysis for these items are not attached. Value is labeled on each bottle.
HYDROGEN IN STEEL
Product No. H (ppm) Form Unit Size Price (JPY)
SS-5 6.5 8 10g rod (φ4mm×100mm) 10 pcs 25,000
OXYGEN IN STEEL
Product No. O (ppm) Form Unit Size Price (JPY)
SMO-12 Approximate 1,000ppm 1.0g pin 100 pcs In prep
NOTE: Values listed are nominal and depend on the lot.
Sample № C Si Mn P S Cu Sol. Al Insol. Al Ni Cr Mo V Ti
ST01-d 0.0024 0.006 0.01 0.001 0.001 0.01 0.002 <0.001 0.01 0.01 0.001 0.001 0.001
ST02-d 0.100 0.60 0.15 ─ 0.0032 0.07 ─ ─ 0.05 4.02 0.50 0.40 0.022
ST03-d 0.149 0.40 0.75 ─ 0.006 0.69 0.014 <0.001 0.10 3.22 0.40 0.027 0.10
ST04-d 0.21 0.060 2.00 0.008 0.016 0.11 0.090 0.001 0.50 2.51 0.30 ─ 0.30
ST05-d 0.26 0.25 1.60 0.013 0.0017 0.40 0.041 <0.001 1.05 2.02 0.092 0.30 0.014
ST06-d 0.34 0.34 1.29 0.048 0.0013 0.49 0.023 <0.001 1.55 1.49 0.20 0.058 0.054
ST07-d 0.50 0.30 1.02 0.038 0.026 0.20 0.031 <0.001 2.02 1.02 0.60 0.11 0.20
ST08-d 0.64 0.15 0.51 0.028 0.020 0.30 0.058 <0.001 2.53 0.53 1.02 0.16 0.16
ST09-d 0.80 0.20 0.31 0.018 0.0029 0.17 0.049 <0.001 3.26 0.12 0.82 0.20 ─
ST10-d 0.99 0.11 0.10 0.003 0.009 0.05 0.071 <0.001 4.06 0.05 0.059 0.49 ─
Sample № Co As Sn Ca Nb B Pb Sb Zr W Ce Ta ─
ST01-d 0.002 0.001 0.001 0.0001 0.001 0.0001 <0.001 <0.001 <0.001 <0.01 0.001 <0.001
ST02-d 0.012 ─ 0.064 ─ 0.10 ─ ─ 0.005 ─ ─ 0.044 0.11
ST03-d 0.15 0.009 0.043 ─ 0.072 ─ ─ 0.010 ─ ─ 0.024 0.057
ST04-d 0.052 ─ 0.021 ─ 0.020 ─ ─ 0.050 ─ ─ 0.010 0.023
ST05-d 0.10 0.022 0.011 0.0004 0.051 ─ ─ 0.074 ─ ─ 0.004 0.006
ST06-d 0.20 0.063 ─ 0.0010 0.016 ─ 0.006 0.096 0.004 ─ ─ 0.003
ST07-d ─ 0.043 ─ 0.0020 0.010 0.0024 0.016 ─ 0.009 0.05 ─ 0.19
ST08-d ─ ─ ─ 0.0030 ─ 0.0036 0.003 ─ 0.048 0.11 ─ ─
ST09-d ─ ─ ─ 0.0036 ─ 0.0048 0.010 ─ 0.069 0.20 ─ ─
ST10-d ─ ─ ─ 0.0039 ─ 0.0061 0.086 ─ 0.090 0.16 ─ ─
mass %
Item No. KTC-1 Low alloy steel standard
10 pieces/set, Form: 35 dia x 20 mmt
Sample No. C Si Mn P S Cu Sol. Al Insol. Al Ni Cr
A-g 1.00 0.06 0.01 0.001 0.001 0.10 0.077 0.001 4.04 -
B-g 0.01 0.58 0.54 0.045 - 0.70 - - 0.52 3.98
C-g 0.11 - 1.96 - 0.028 - 0.016 0.001 - 0.49
Sample No. Mo V Ti Co As Sn Ca Nb B W
A-g - 0.03 0.30 - - - - 0.11 - 0.21
B-g 0.20 - 0.03 0.01 0.043 0.086 0.0033 - 0.0093 -
C-g 0.98 0.48 - 0.20 - - - - - -
mass %
Item No. KTC-2 Low alloy steel standard (for standardization)3 pieces/set, Form: 35 dia x 20 mmt
Sample No. C Si Mn P S Cu Sol. Al Insol. Al Ni
ST21-c 0.13 0.18 0.40 0.003 0.026 - - - 4.03
ST22-c 0.036 0.39 0.57 0.028 0.005 - 0.092 0.003 19.85
ST23-c 0.11 0.82 1.60 0.005 0.021 0.048 0.045 0.003 9.99
ST24-c 0.084 0.58 0.78 0.004 0.015 0.029 0.021 0.002 13.93
ST25-d 0.027 1.43 1.42 0.010 0.021 0.011 0.001 0.001 8.05
ST26-c 0.044 1.01 1.19 0.021 0.008 - 0.004 0.002 17.62
ST27-c 0.057 1.19 1.00 0.019 0.011 - 0.016 0.002 15.74
ST28-c 0.016 0.12 0.23 0.034 0.003 - - - 29.62
Sample No. Cr Mo Ti Co As Nb Pb Ta
ST21-c 27.02 - 0.003 0.003 - - - -
ST22-c 25.00 - - - 0.001 - - -
ST23-c 22.17 1.01 - - 0.104 <0.01 0.005 -
ST24-c 20.20 1.50 - - 0.056 - 0.013 -
ST25-d 18.32 2.49 - 0.050 0.012 - 0.044 -
ST26-c 16.18 0.49 0.075 0.21 - 0.29 - 0.40
ST27-c 13.39 0.008 0.24 0.014 - 1.53 - 0.24
ST28-c 10.34 - 0.49 - - 0.72 - 0.060
mass %
Item No. KTC-3 Stainless steel standard (austenite)8 pieces/set, Form: 35 dia x 20 mmt
Sample No. C Si Mn P S Cu Sol. Al Insol. Al Ni
D-c 0.093 0.50 1.01 0.007 0.027 0.019 0.046 0.004 4.06
E-c 0.055 1.57 1.45 0.010 0.008 0.060 0.030 0.002 14.74
F-d 0.016 0.42 0.20 0.037 0.004 0.014 0.023 <0.001 29.86
Sample No. Cr Mo Ti Co As Nb Pb Ta
D-c 27.12 0.051 0.045 0.026 0.14 0.10 0.014 0.007
E-c 15.71 2.40 0.15 0.21 0.077 0.41 0.14 0.22
F-d 4.62 0.97 0.58 0.068 0.002 1.32 0.001 0.070
mass %
Item No. KTC-4 Stainless steel standard (austenite for standardization)3 pieces/set, Form: 35 dia x 20 mmt
Sample No. C Si Mn P S Cu Sol. Al Insol. Al Ni
ST31-b 0.068 1.24 0.51 0.023 0.005 0.19 0.10 0.003 3.91
ST32-b 0.040 0.52 1.16 0.030 0.007 0.01 0.013 0.004 2.56
ST33-b 0.044 0.32 0.30 0.008 0.022 0.10 0.031 0.004 1.03
ST34-b 0.084 0.78 0.99 0.025 0.004 0.04 0.045 0.006 0.48
ST35-b 0.22 0.58 1.35 0.002 0.029 <0.01 0.057 0.007 0.05
ST36-b 0.15 0.14 0.43 0.014 0.009 <0.01 0.001 0.008 0.11
ST37-b 0.11 0.99 0.74 0.007 0.019 <0.01 0.001 0.002 0.20
ST38-b 0.30 0.40 0.19 0.010 0.013 <0.01 0.001 0.002 0.01
Sample No. Cr Mo Co Ti As Nb
ST31-b 11.23 0.71 0.19 0.31 0.10 0.90
ST32-b 12.71 1.01 0.014 0.051 0.008 0.082
ST33-b 15.12 1.19 0.10 0.007 0.001 0.30
ST34-b 16.99 0.48 0.051 0.098 0.009 0.083
ST35-b 24.14 0.029 0.005 0.005 <0.001 0.007
ST36-b 22.31 0.043 0.003 0.005 <0.001 0.001
ST37-b 19.51 0.20 0.002 0.003 <0.001 <0.001
ST38-b 25.52 0.004 0.002 0.003 <0.001 <0.001
mass %
8 pieces/set, Form: 35 dia x 20 mmtItem No. KTC-5 Stainless steel standard (ferrite)
Sample No. C Si Mn P S Cu Sol. Al Insol. Al Ni
G-b 0.031 1.26 1.37 0.029 0.005 0.19 0.086 0.005 3.87
H-b 0.088 0.50 0.47 0.009 0.010 0.04 0.031 0.005 0.57
I-b 0.26 0.22 0.19 0.004 0.028 <0.01 0.001 0.004 0.02
Sample No. Cr Mo Co Ti As Nb
G-b 11.85 1.14 0.19 0.30 0.075 0.98
H-b 17.95 0.49 0.054 0.094 0.011 0.094
I-b 24.47 0.048 0.006 0.013 0.002 0.007
mass %
Item No. KTC-6 Stainless steel standard (ferrite for standardization)3 pieces/set, Form: 35 dia x 20 mmt
Sample No. C Si Mn P S Cu Ni Cr Mo
B-1 2.4 3.0 0.05 0.005 0.10 0.05 1.0 1.0 0.05
B-2 2.6 2.8 0.2 0.025 0.09 0.2 0.8 0.8 0.2
B-3 3.0 2.2 0.4 0.05 0.06 0.4 0.6 0.6 0.4
B-4 3.3 1.8 0.6 0.07 0.04 0.6 0.4 0.4 0.6
B-5 3.7 1.4 0.8 0.09 0.02 0.8 0.2 0.2 0.8
B-6 4.0 1.0 1.0 0.12 0.003 1.0 0.05 0.05 1.0
mass %
Sample No. Mg C Si Mn P S
M-1 0.05 3.4 2.5 0.1 0.015 0.002
M-2 0.04 3.4 2.5 0.1 0.015 0.002
M-3 0.03 3.4 2.5 0.1 0.015 0.002
M-4 0.02 3.4 2.5 0.1 0.015 0.002
M-5 0.01 3.4 2.5 0.1 0.015 0.002
mass %
Item No. KTC-10 Ductile cast iron (Mg for calibration curve) 5 pieces/set, Form: 34 dia x 5 mmt
Item No. 9 Alloy cast iron (for calibration curve) 6 pieces/set, Form: 34 dia x 5 mmt
Sample No. C Si Mn P S Ni Cr Mo Cu V Ti
D-1a 3.20 3.31 0.13 0.028 0.005 - - 0.11 0.19 0.10 -
D-2a 3.47 2.99 0.50 0.016 0.001 0.41 - 0.22 0.04 0.20 0.010
D-3a 3.60 2.22 0.42 0.033 0.017 0.31 - 0.45 - - 0.24
D-4a 3.19 2.71 0.71 0.020 0.006 0.34 0.21 0.021 - 0.25 -
D-5a 3.78 2.47 0.24 0.044 0.014 - 0.02 0.32 - - 0.18
D-6a 3.93 1.64 0.37 0.071 0.033 0.10 0.31 - 0.31 0.15 0.047
D-7a 3.99 2.02 0.29 0.060 0.021 0.21 - 0.062 0.11 0.055 0.12
D-8a 2.98 2.87 0.20 0.050 0.037 0.01 0.29 0.008 0.52 0.009 -
D-9a 3.20 2.48 0.84 0.004 0.014 - 0.11 0.004 0.01 0.37 -
D-10a 2.79 2.40 0.02 0.008 0.011 - 0.40 - 0.40 0.003 -
Sample No. Al Sn B Pb Sb Ca Bi Zn Ce Mg
D-1a 0.087 - 0.028 0.001 0.062 - - 0.009 0.035 0.046
D-2a 0.074 0.004 0.055 - 0.094 - - 0.002 0.011 0.053
D-3a 0.012 0.014 0.010 - 0.024 - - 0.018 - 0.022
D-4a 0.053 0.44 0.12 0.004 0.009 0.0018 - - 0.008 0.048
D-5a 0.013 - 0.001 0.007 0.16 0.0005 0.001 0.029 - 0.020
D-6a 0.007 0.054 - 0.016 - 0.0005 0.005 - - 0.015
D-7a 0.014 - - 0.009 - - 0.011 0.051 - 0.013
D-8a 0.11 0.30 - 0.009 0.21 - 0.005 - 0.064 0.021
D-9a 0.10 0.20 - 0.037 - 0.0030 - - 0.092 0.007
D-10a 0.029 0.089 0.087 0.026 - 0.0035 0.003 - - 0.003
mass %
Item No. KTC-11 Ductile cast iron (for calibration curve)10 pieces/set, Form: 34 dia x 5 mmt
Sample No. C Si Mn P S Ni Cr Mo Cu V Ti
C-1a 4.00 0.50 0.80 0.005 0.032 - 0.10 0.30 0.50 - -
C-2a 3.85 0.80 0.65 0.012 0.021 - 0.20 0.20 0.40 - -
C-3a 3.70 1.20 0.05 0.020 0.08 - 0.30 0.10 0.30 - -
C-4a 3.55 1.60 0.50 0.30 0.06 0.01 0.40 0.40 0.20 0.04 -
C-5a 3.40 2.00 0.40 0.10 0.04 0.50 0.25 0.05 0.10 0.15 -
C-6a 3.30 2.20 0.35 0.075 0.025 0.40 0.35 0.003 0.01 0.05 0.01
C-7a 3.20 2.40 0.30 0.050 0.016 0.30 0.02 - - 0.10 0.10
C-8a 3.10 2.60 0.25 0.030 0.012 0.20 - - - 0.20 0.05
C-9a 2.95 2.80 0.20 0.50 0.008 0.10 - - - 0.30 0.15
C-10a 2.70 3.00 0.10 0.70 0.005 0.01 - - 0.50 0.01 0.20
Sample No. Al Sn B Pb Sb Ca Bi Zn Ce Mg
C-1a 0.005 - 0.10 - 0.15 - - 0.005 - -
C-2a 0.012 - 0.07 - 0.10 - 0.020 0.002 - -
C-3a 0.020 - 0.05 - 0.05 - 0.012 0.010 - -
C-4a 0.030 - 0.03 - 0.01 - 0.006 0.020 - -
C-5a - - 0.01 0.010 0.005 - 0.003 0.030 0.005 -
C-6a - 0.4 0.005 0.005 - 0.001 0.001 - 0.020 -
C-7a 0.040 0.3 - 0.003 - 0.0010 - - 0.10 -
C-8a 0.050 0.2 - 0.02 - 0.0015 - - 0.075 -
C-9a 0.060 0.1 - 0.03 - 0.0020 - - 0.010 -
D-10a 0.080 0.05 - 0.015 - 0.0040 - - 0.040 -
mass %
Item No. 12 Plain cast iren (for calibration curve)
10 pieces/set, 34 dia x 5 mmt
Sample No. C Si Mn P S Ni Cr Mo Cu V
FCD-A 3.5 2.5 0.1 <0.02 <0.01 - - - - -
FCD-B 2.1 3.0 0.05 0.7 0.06 0.01 0.5 0.3 0.55 <0.01
FCD-C 0.2 0.5 0.8 <0.01 <0.01 0.5 0.01 <0.01 0.01 0.3
Sample No. Ti Al Sn B Pb Sb Ca Bi Zn Mg
FCD-A <0.01 - - - - - - - - 0.055
FCD-B - <0.01 0.3 0.1 0.01 0.2 <0.001 <0.01 <0.01 -
FCD-C 0.3 0.1 <0.01 <0.01 0.05 0.01 0.003 0.02 0.06 -
mass %
Sample No. C Si Mn P S Ni Cr Mo Cu Mg
FCD-D 3.4 2.5 0.1 0.015 - - - - - 0.05
FCD-E 2.4 3.0 0.05 0.005 0.10 1.0 1.0 0.05 0.05 <0.01
FCD-F 4.0 1.0 1.0 0.12 0.005 0.05 0.05 1.0 1.0 -
mass %
10 pieces/set (A: 4 pieces, B: 4 pieces, C: 2 pieces) Form: 34 dia x 5 mmt, C: 35 dia x 20mmt
10 pieces/set (D: 2 pieces, E: 4 pieces, F: 4 pieces) Form: 34 dia x 5 mmt
Item No. KTC-13 Cast iron (for standardization)
Item No. KTC-14 Alloy cast iron (for standardization)
Sample No. Sol. N Insol. N C Si Mn P S Al Cr
N-1 0.0012 0.0001 0.015 0.10 0.10 0.002 0.003 0.050 0.21
N-2 0.0048 0.0002 0.014 0.10 0.10 0.002 0.003 0.048 0.29
N-3 0.0076 0.0003 0.012 0.10 0.10 0.002 0.003 0.048 0.19
N-4 0.0110 0.0002 0.012 0.10 0.10 0.003 0.004 0.048 0.20
N-5 0.0194 0.0008 0.012 0.10 0.11 0.003 0.004 0.050 0.41
mass %
Sample No. N C Si Mn P S Cu Ni Cr Mo
A-20 0.033 0.05 0.03 0.01 0.002 0.002 0.01 0.01 3.80 0.01
B-20 0.0015 0.01 0.01 0.01 0.001 0.002 0.01 0.01 0.01 0.01
mass %
Item No. KTC-15 Nitrogen for calibration curve
Item No. KTC-16 Nitrogen for standardization 4 pieces/set (A-20: 2 pieces, B-20: 2 pieces, Form: 35 dia x 20 mmt
5 pieces/set, Form: 35 dia x 20 mmt