02/11/14 CHAPTER 2 FOUNDARY PROCESSES 1 CHAPTER 2 FOUNDRY PROCESSES 2.1 INTRODUCTION ME 333 PRODUCTION PROCESSES II Foundry processes consist of making molds, preparing and melting the metal into the molds, cleaning the castings, and reclaiming the sand for reuse. Founding, or casting, is the process of forming objects by putting liquid or viscous material into a prepared mold or form. Generally solidification takes place by cooling (metallic materials) but cooling may not be necessary (some plastics). A casting (döküm) is an object formed by allowing the material to solidify. So, the casting is the product of the foundry. It may vary from a fraction of a gram to several tons. All metals and alloys can be cast. A foundry (dökümhane) is a collection of the necessary material and equipment to produce a casting.

Upload: erdi-karacal

Post on 15-Jul-2015

104 views

Category:

Engineering


3 download

TRANSCRIPT

Page 1: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

1

CHAPTER 2FOUNDRY PROCESSES

2.1 INTRODUCTION

ME 333 PRODUCTION PROCESSES II

Foundry processes consist of making molds, preparing and melting the metal into the molds, cleaning the castings, and reclaiming the sand for reuse.

Founding, or casting, is the process of forming objects by putting liquid or viscous material into a prepared mold or form. Generally solidification takes place by cooling (metallic materials) but cooling may not be necessary (some plastics).

A casting (döküm) is an object formed by allowing the material to solidify. So, the casting is the product of the foundry. It may vary from a fraction of a gram to several tons. All metals and alloys can be cast.

A foundry (dökümhane) is a collection of the necessary material and equipment to produce a casting.

Page 2: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

2

ME 333 PRODUCTION PROCESSES II

Selection of castings of various materials, shapes, and sizes

Page 3: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

3

ME 333 PRODUCTION PROCESSES II

Casting technology involves the next steps:

Casting nomenclatureThe figure in the right shows the nomenclature of mold and castings in sand casting.

Page 4: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

4

ME 333 PRODUCTION PROCESSES II

The pouring cup, downsprue, runners, etc., are known as the mold gating system, which serves to deliver the molten metal to all sections of the mold cavity.

Gating system in sand casting

Page 5: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

5

ME 333 PRODUCTION PROCESSES II

To understand the foundry process, it is necessary to know how a mold is made and what factors are important to produce a good casting.

The elements necessary for the production of sound casting will be considered throughout this chapter.

These include:

1. Mold2. Pattern3. Core4. Molding Procedure5. Sand6. Properties of Cast liquid7. Behavior of Cast Material

Page 6: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

6

A mold (kalıp) is the container that has the cavity of the shape to be cast. It may be made of metal, plaster, ceramics, or other refractory substances. Good castings can not be produced without good molds

There are two types of molds:

1. Permanent mold: A mold used more than once. They are generally produced from metallic materials such as; heat resisting (Ni-Cr) steels.

2. Expendable mold: A mold used only once and then destroyed to separate the component. They are generally produced from sand. (for casting of ferrous materials we have to use this type of mold, because melting points of ferrous materials are very high).

ME 333 PRODUCTION PROCESSES II

2.2 MOLDS

Page 7: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

7

There are plenty types of expendable molds, but we will deal with sand molds only;

a) Green Sand Molds: The most common type consisting of forming the mold from damp molding sand (silica, clay and moisture)

b) Skin-dried Molds: It is done in two ways; (1) The sand around the pattern to a depth of about 1/2 in(10 mm). is mixed with a binder so that when it is dried it will leave a hard surface on the mold. (2) Entire mold is made from green sand, but a spray or wash, which hardens when heat is applied, is used.

c) Dry Sand Molds: These molds are made entirely from fairly coarse molding sand mixed with binders (linseed oil: bezir yağı or gelatinised starch: nişasta). They baked before being used. A dry sand mold holds its shape when poured and is free from gas troubles due to moisture.

ME 333 PRODUCTION PROCESSES II

Page 8: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

8

A mold should have the following characteristics:

i) The mold must be strong enough to hold the weight of the metal,ii) The mold must resist the erosive action of the rapidly flowing

metal during pouring,iii) The mold must generate minimum amount of gas when filled with

molten metal.iv) The mold must be constructed in such a way that any gasses

formed can pass through the body of the mold itself (permeability).v) The mold must be refractory enough to withstand the high

temperature of the metal.vi) The mold must collapse easily after the casting solidifies.

ME 333 PRODUCTION PROCESSES II

Page 9: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

9

2.3 . PATTERNS

A pattern (model) is a form used to prepare and produce a mold cavity. It is generally made from wood but it can be produced from materials like aluminium alloys (low in density). (Disadvantage of wood is humidity absorption.)

The designer of a casting must look forward to the pattern to assure economical production. The design should be as simple as possible to make the pattern easy to draw from the sand and avoid more cores than necessary.

The pattern may be permanent, so that it may be reused repeatedly. Alternatively, the pattern may be expendable (disposable), made up of a material that is melted out before or burnt up during casting.

Pattern has some dimensional variations from that of the real component (i.e. casting). These variations from the real component are called Pattern Allowances.

ME 333 PRODUCTION PROCESSES II

Page 10: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

10

Patterns in sand casting are used to form the mold cavity. One major requirement is that patterns (and therefore the mold cavity) must be oversized:

(i) to account for shrinkage in cooling and solidification, and(ii) to provide enough metal for the subsequence machining operation(s).

ME 333 PRODUCTION PROCESSES II

Types of patterns used in sand casting:(a) solid pattern, (b) split pattern, (c) match-plate pattern, and (d) cope-and-drag pattern

Page 11: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

11

ME 333 PRODUCTION PROCESSES II

Solid pattern for a pinion gear Split pattern showing the two sections together and separated. Light-colored portions are core prints.

Page 12: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

12

1. Shrinkage Allowance: Shrinkage takes place in a volumetric way, but it is given linearly. Each dimension is measured with a shrinkage rule, which automatically gives shrinkage allowance. It is expressed as in/ft. When metal patterns are to be cast from an original master pattern, double shrinkage must be given.

ME 333 PRODUCTION PROCESSES II

2.3.1 Pattern Allowances

Fig. 2.1. Pattern Allowances for a Cast Connecting Rod.

Page 13: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

13

ME 333 PRODUCTION PROCESSES II

Typical shrinkage allowances:

Cast Iron Steel Al Brass Bronze

In/ft 1/8 1/4 5/32 3/36 1/8-1/4

% 1.04 2.08 1.30 2.0 1.04-2.08

Page 14: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

14

ME 333 PRODUCTION PROCESSES II

2. Draft: It is the taper placed on the sides of the pattern on the parting line. This allows the pattern to be removed from the mold without damaging the sand surface. Draft is added to the dimensions on the parting line

Exterior dimensions: 1/8 - 1/4 (in/ft), 1.04 %- 2.08 %Interior dimensions: As large as 3/4 (in/ft), 6.25 %

3. Machining Allowance: It is given on the working areas of the part where further machining will be performed. In value, it is equal to shrinkage allowance.

4. Shake: Negative allowance is given by making the pattern slightly smaller to compensate for the rapping of the mold.

Page 15: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

15

2.4 CORES

A core (maça) is a body of material, usually sand, used to produce a cavity in or on a casting. A core must have sufficient strength to support itself and should not fracture when liquid metal is approaching to it.

Cores may be classified as Green-Sand and Dry-Sand Cores. Green-sand cores are formed by the pattern and made from the same sand as rest of the mold. Dry-sand cores are made separately to be inserted after the pattern is drawn but before the mold is closed. They are usually made of clean river sand (40 parts) which is mixed with a binder (1 part) and then baked to give the desired shape. The box in which cores are formed to proper shape is called a CORE BOX. Generally, perforated pipe or wire frames are added to give sufficient strength.

ME 333 PRODUCTION PROCESSES II

Page 16: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

16

ME 333 PRODUCTION PROCESSES II

Most commonly used binder is Linseed oil. The oil forms a film around the sand grain and hardens when baked at 180-2200C for 2 hours. Other binders are wheat flour, dextrin, starch and several types of thermosetting plastics.

Fig. 2.2. Types of Cores.

Page 17: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

17

Cores serve to produce internal surfaces in castings In some cases, they have to be supported by chaplets for more stable positioning:

(a) Core held in place in the mold cavity by chaplets,(b) chaplet design,(c) casting with internal cavity

Page 18: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

18

Cores are made of foundry sand with addition of some resin for strength by means of core boxes:

Core box, two core halves ready for baking, and the complete core made by gluing the two halves together

Page 19: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

19

Pattern making

Mold makingPreparation of sand

If necessary core making

Raw material

Melting Pouring

Solidification and cooling

Removal of sand mold

Cleaning & Inspection

Finished casting

Production sequence in sand casting

Page 20: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

20

2.5 MOLDING PROCEDURE

Procedure for making green sand molds;

ME 333 PRODUCTION PROCESSES II

A. Pattern on molding board ready to ram up drag

Page 21: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

21

B. Drag rolled over and pattern assembled ready to ram cope

ME 333 PRODUCTION PROCESSES II

Page 22: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

22

C. Mold complete with dry sand core in place

ME 333 PRODUCTION PROCESSES II

Page 23: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

23

2.6 SAND

Silica sand (SiO2) is well suited for molding purposes because it can withstand a high temperature without decomposition. This sand is low in cost, has longer life, and is available in a wide range of grain sizes and shapes.

Pure silica sand is not suitable in itself for molding, since it lacks binding qualities. The binding qualities can be obtained by adding 8-15 % clay (kil).

ME 333 PRODUCTION PROCESSES II

Silica (SiO2) + Binders ⇒ Green Sand MoldMoisture 5-10% (used in castings of Cast IronClay 8-15% and Non-ferrous Alloys)

Silica (SiO2) + Binders ⇒ Dry Sand MoldLinseed Oil (used in castings of Steels)

(40 part) (1 part)

Dry it first and then bake at 180-2200C for 2 hours

Page 24: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

24

ME 333 PRODUCTION PROCESSES II

Synthetic molding sands are composed of washed, sharp grained silica to which 3-5 % clay is added. Less gas is generated with synthetic sands, since less than 5 % moisture is necessary to develop adequate strength.

The size of the sand grains will depend on the type of work to be molded. For small and intricate castings fine sand is desirable so that all details of the mold are brought out sharply. Sharp, irregular-shaped grains are usually preferred because they interlock and add strength to the mold.

Page 25: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

25

ME 333 PRODUCTION PROCESSES II

Foundry sandsThe typical foundry sand is a mixture of fresh and recycled sand, which contains 90% silica (SiO2), 3% water, and 7% clay.The grain size and grain shape are very important as they define the surface quality of casting and the major mold parameters such as strength and permeability:

Bigger grain size results in a worse surface finish

Irregular grain shapes produce stronger mold

Larger grain size ensures better permeability

Page 26: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

26

2.7 SAND QUALITY TEST

Periodic tests are necessary to determine the essential qualities of foundry sand. Various tests are designed to determine the following properties of molding sand.

a) Hardness Test (Mold Hardness): A spring loaded (2.3 N) steel ball 5.08 mm in diameter is pressed into the surface of the mold and depth of penetration is recorded as hardness. Medium hardness is about 75.

ME 333 PRODUCTION PROCESSES II

vibrator

612

270

b) Fineness Test: It is used to obtain percentage distribution of grain sizes in the sand. Sand is cleaned and dried to remove clay. It is placed on graded sieves, which are located on a shaker. Standard sieve sizes (mesh) are 6,12,20,30,40,50,70,100,200 and 270. Shaking time is 15 minutes.

Page 27: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

27

c) Moisture Content: Measure the weight of the given sand sample. Dry it around 1000C and then weigh it again. Calculate the percentage.

d) Clay Content: A sample of sand is dried and then weighed. Then clay is removed by washing the sand with caustic soda which has absorbed the clay. Sand is dried and weighed again. The percentage gives the clay content.

e) Strength Test: Most common compressive test. A universal strength tester loads a 50 mm long 50 mm diameter specimen by means of dead weight pendulum with a uniform loading rate.

f) Permeability: It is measured by the quantity of air that passes through a given sample of sand in a prescribed time under standard pressures.

g) Refractoriness Test: High temperature withstanding ability of sand is measured.

piston

Page 28: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

28

2.8 PROPERTIES OF CAST LIQUID

The properties of the castings depend on foundry skin as well as other material properties. Under similar foundry conditions, the properties will be affected by:

a) Viscosity of the liquid metal: It is a function of superheat that is the degree of overheating above the melting temperature. Since the pouring process is essentially a problem of fluid flow, lower viscosity is beneficial.

b) Surface Tension: It affects the wetting of inclusions and also limits the minimum radius that can be filled without pressure (typically to 0.1 mm in cavity casting).

c) Oxide Films: Surface of the liquid metal quickly oxidizes and metals act as if it is flowing in an envelope. Aluminum produces many problems due to quick formation of strong oxides.

d) Fluidity: It is material plus mold property. It is the ability to fill the cavity in the mold.

ME 333 PRODUCTION PROCESSES II

Page 29: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

29

ME 333 PRODUCTION PROCESSES II

Fluidity is a measure of the capability of a metal to flow into and to fill the mold before freezing. It defines to the great extend the quality of casting.

Factors affecting fluidity:

1. Œ Pouring temperature2. Metal composition3. Ž Heat transfer to the surroundings4. Viscosity of the liquid metal

In the foundry practice, test for fluidity is carried out for each ladle just before pouring the molten metal into the mold

Page 30: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

30

2.9 HEATING THE METAL

ME 333 PRODUCTION PROCESSES II

Heat energyrequired

Heat to riseTm

Heat to fusion(solid→liquid)

Heat to riseTpouring

= + +

{ })()( mpefoms TTCHTTCVH −++−= ρwhere

H : Total heat required, Btu (J)

ρ : Density, lbm/in2 (g/cm3)

sC : Weight specific heat for solid, Btu/lb-°F (J/g- °C)

V : Volume of metal, in3 (cm3)

mT : Melting temperature, °F (°C)

oT : Room temperature, °F (°C)

fH : Heat of fusion, Btu/lb-°F (J/g- °C)

eC : Weight specific heat for liquid, Btu/lb-°F (J/g- °C)

pT : Pouring temperature, °F (°C)

Page 31: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

31

2.10 POURING ANALYSIS

ME 333 PRODUCTION PROCESSES II

2

222

21

211

1 22F

g

VPhF

g

VPh +++=+++

ρρ

021 == PP Atmospheric pressure

021 == FF Neglected

02 =h Base (Datum) point

01 =V

1

2

*

*ghVg

Vh 2

2 2

22

1 =⇒=⇒

Speed at the beginning of pouring

Sum of the energies from Bernoulli eqn.

Head + Press.+ Kinetic E. + Fric.

Page 32: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

32

For continuity law

2211 AVAVQ == (Volumetric flow rate)

Q

VMFT =

MFT = Mold filling time (sec)V = Volume (cm3)Q = Volumetric flow rate (cm3/sec)

Volume rate of flow remains constant

Page 33: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

33

2.11 RISER (FEEDER) DESIGN

ME 333 PRODUCTION PROCESSES II

Several riser designs are used in practice as shown in the figure. The riser must remain molten until after the casting solidifies.The Chvorinov’s Rule is used to calculate the riser’s dimensions.

Possible types and positions for risers in sand casting

Page 34: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

34

2.11 RISER (FEEDER) DESIGN

ME 333 PRODUCTION PROCESSES II

Chvorinov’s rule:

nm AVCTST )(=

TST : Total Solidification Time (min)Cm : Mold Constant (min/cm2)V : Volume (cm3)A : Surface area (cm2)n : Exponent (n=2)

Page 35: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

35

Tf

TST

Tp

Tm

Liq.

V/A ↑ TST ↓

TSTcasting<TSTriser

Lower V/A located away from risers

So that: riser remains liquid until after the casting solidity

Page 36: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

36

EXAMPLE

5 cm

15 cm

10 cm

A cylindrical riser with dimensions of D=h must be designed. Previous observations show TST=1.6 min. for casting. Determine dimension of riser.

TSTriser=2 min. suggested as.

Sol’n: n

m AVCTST )(=

375051015 cmVc =××=2550)5105151015(2 cmAc =×+×+×=

2)550750(6.1 mC=

→2min86.0 cmCm =

32

44DhDVr

ππ ==

22

4

6

4

2DDDhAr

πππ =+=

646

42

3 D

D

D

A

V

r

r ==ππ

2)6(86.02 D=cmD 15.9= cmh 15.9=

Page 37: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

37

There are numerous opportunities in the casting operation for different defects to appear in the cast product. Some of them are common to all casting processes:

Misruns: Casting solidifies before completely fill the mold. Reasons are low pouring temperature, slow pouring or thin cross section of casting.Cold shut: Two portions flow together but without fusion between them. Causes are similar to those of a misrun.Cold shots: When splattering occurs during pouring, solid globules of metal are entrapped in the casting. Proper gating system designs could avoid this defect.Shrinkage cavity: Voids resulting from shrinkage. The problem can often be solved by proper riser design but may require some changes in the part design as well.Microporosity: Network of small voids distributed throughout the casting. The defect occurs more often in alloys, because of the manner they solidify.Hot tearing: Cracks caused by low mold collapsibility. They occur when the material is restrained from contraction during solidification. A proper mold design can solve the problem.

2.12 CASTING QUALITY

Some defects are typical only for some particular casting processes, for instance, many defects occur in sand casting as a result of interaction between the sand mold and the molten metal. Defect found primarily in sand casting are gas cavities, rough surface areas, shift of the two halves of the mold, or shift of the core, etc.

Page 38: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

38

Page 39: Ch2 foundaryproc

02/11/14 CHAPTER 2 FOUNDARY PROCESSES

39