Specification sheet

Customer: Qatar Petroleum

P.O. Box 47Doha State of Qatar

Project:

Area:

Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2

Area size:

Coating Schedule 1Un (Revision 1) : General exposure to atmosphere : Uninsulated newly constructed items : temperature range = 0oC to 120oC

sqm 100

Hempel Paints (Qatar) W.L.L

Surface preparation:

Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure3000psi) fresh water hosed in order to remove salts and other contaminants. When thesurface is dry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1:2007.Surface profile corresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0G/S, or ISO Comparator Rough Medium (G), QP requirement 50 to 75µm.Dust off residues.

Product name (including quality number)

Treated area% Colour

Shade no.

Film thickness

(micron)

Wet Dry (sqm/ltr) Brush

Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure

Application methodsTheoretical spreadingrate

HEMPADUR ZINC 15350 100 Metal grey 19840 100 50 .017"-.021" 150 bar 9.4 (X) Xf/c

HEMPADUR MIO 47950 100 Grey 12130 125 100 .019"-.021" 225 bar 7.6 X Xf/cHEMPADUR MIO 47950 100 Grey 13480 125 100 .019"-.021" 225 bar 7.6 X Xf/c

HEMPATHANE ENAMEL 55100 100 To Be Advised T.B.A 100 50 .017"-.019" 100 bar 10.4 X Xf/c

t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 300 X: Recommended (X): Possible

Recoating intervals. Ample ventilation Hrs=Hour(s) Mth=Month(s) N/R=Not Recommended

Quality no

D.F.T.

(micron)

Recoated withquality no

40°C 30°C 20°C 10°C 0°C -10°C

Min. Max. Min. Max. Min. Max. Min. Max. Min. Max. Min. Max.

100 Min None 3 Hrs None 5 Hrs None 13 Hrs None N/R N/R N/R N/R4795015350 50

2 Hrs Ext 3 Hrs Ext 5 Hrs Ext 9 Hrs Ext 21 Hrs Ext N/R N/R4795047950 100


Hempel's PreSale System 2.6.17 (Build 790)

Printed at: Environment :

1Page:

01.10.2013 13:42

User name:

Department name:

Created/Last modified: 17.09.2013 14:23

Quality Code:Cheryl Leitch

Admin Severe

QACHL1858N

Remarks and Product information see next page.

HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 1Un (Revision 1) : General exposure to atmosphere : Uninsulated newly constructed items : temperature range = 0oC to 120oC

sqm 100


Product information:

Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume

Pot life Dry to touch Application restrictions

Thinner

Flashpoint Min. Temp. Max. RH%

20°C 20°C °C °C

HEMPADUR ZINC 15350 19840 47 95350 4 : 1 8 h 45 min 25 08450 10

HEMPADUR MIO 47950 12130 76 98140 5 : 1 1 h 2 h 24 08450 0

HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0

HEMPATHANE ENAMEL 55100 T.B.A 52 95370 7 : 1 2 h 4 h 35 08080 -10

Remarks:

When the interval is denoted "Extended", the coated structure can possibly be overcoated even after longer periods. This will depend on the actual exposure conditions, such aslimited exposure to sun, and on the condition and cleanliness of the paint surface. The evaluation of the specific situation must be based on local experience, contact HEMPEL for advice.Stripe coat by brush all edges, welds, inaccessible areas etc. prior to application of primer and in between each subsequent coat.



2Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N

The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.

HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 1Un (Revision 1) : General exposure to atmosphere : Uninsulated newly constructed items : temperature range = 0oC to 120oC "EXTERNAL OF TANKROOF"

sqm 100






Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPADUR ZINC 15350 100 Metal grey 19840 100 50 .017"-.021" 150 bar 9.4 (X) Xf/cHEMPADUR MIO 47950 100 Grey 13480 125 100 .019"-.021" 225 bar 7.6 X Xf/c

HEMPADUR MIO 47950 100 Grey 12130 125 100 .019"-.021" 225 bar 7.6 X Xf/c






3Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C








4Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C


HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0

HEMPADUR MIO 47950 12130 76 98140 5 : 1 1 h 2 h 24 08450 0

HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0


Remarks:




5Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 1In (Revision 1) : General Exposure to atmosphere : Insulated newly constructed items : temperature range = minus 46oC to 120oC

sqm 100






Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPADUR ZINC 15350 100 Metal grey 19840 100 50 .017"-.021" 150 bar 9.4 (X) Xf/c

HEMPADUR MIO 47950 100 Grey 12130 125 100 .019"-.021" 225 bar 7.6 X Xf/cHEMPADUR MIO 47950 100 Grey 13480 125 100 .019"-.021" 225 bar 7.6 X Xf/c



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C






6Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 1In (Revision 1) : General Exposure to atmosphere : Insulated newly constructed items : temperature range = minus 46oC to 120oC

sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C


HEMPADUR MIO 47950 12130 76 98140 5 : 1 1 h 2 h 24 08450 0

HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0

Remarks:




7Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 1F (Revision 1) : General Exposure to atmosphere : Fireproofed newly constructed items : temperature range minus 46oC to 120oC

sqm 100



Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure3000psi) fresh water cleaned in order to remove salts and other contaminants. When thesurface is dry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1:2007, usingsuitably sized abrasive to produce a surface profile equivalent to 35 to 50microns.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPADUR FAST DRY 17410 100 Red 50630 75 50 .019"-.021" 225 bar 14.8 (X) (X) Xf/c




Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C


N/R N/R 1 Hrs 15½ Day 80 Min 21 Day 3 Hrs 42 Day 6 Hrs 90 Day N/R N/R4795017410 50



8Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 1F (Revision 1) : General Exposure to atmosphere : Fireproofed newly constructed items : temperature range minus 46oC to 120oC

sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPADUR FAST DRY 17410 50630 74 98410 4 : 1 h 30 m 1 h 30 min 27 08450 -10

HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0

Remarks:




9Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 2Un (Revision 1) : General Exposure to atmosphere : Uninsulated existing items maintenance : temperature range 0oC to 120oC

sqm 100



Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (highpressure3000psi) fresh water cleaned in order to remove salts and other contaminants.When the surface is dry utilise the appropriate surface preparation method as indicated :

1)No visible coating breakdown Ri 0 (ASTM No 10) level (where overcoating for aestheticor other reasons). = Abrade pretreated surfaces with emery paper for good topcoatadhesion.

2)Partial or variable coating breakdown with primer intact or localised under rusting to nomore than Ri 3 (ASTM No 6) level = Locally blast clean degraded areas to Sa 2.5standard as per ISO 8501-1 plus supplement or where blast cleaning is impractical,power tool clean to St 3 standard. At the QP engineer's discretion, fully blast clean the

surfaces to Sa 2.5 standard.

3)More extensive coating breakdown to Ri 4 (ASTM No 4) level or worse = Fully blastclean surfaces to Sa 2.5 standard per ISO 8501-1 plus supplement. Power tool cleaningto St 3 standard is only acceptable for small areas and areas that are impractical for blastcleaning by agreement. use suitable blast cleaning abrasive to give a surface profile of 50- 75microns.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPADUR MASTIC 45881 100 Red 50630 150 125 .017"-.023" 250 bar 6.4 (X) Xf/c






10Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C


3 Hrs Ext 5 Hrs Ext 6 Hrs Ext N/R N/R N/R N/R N/R N/R4795045881 125




11Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPADUR MASTIC 45881 50630 80 95881 3 : 1 3 h 3 h 39 08450 15

HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0


Remarks:




12Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 2Un (Revision 1) : General Exposure to atmosphere : Uninsulated existing items maintenance : temperature range 0oC to 120oC "EXTERNAL OF TANKROOF"

sqm 100




1)No visible coating breakdown Ri 0 (ASTM No 10) level (where overcoating for aestheticor other reasons). = Abrade pretreated surfaces with emery paper for good topcoatadhesion.

2)Partial or variable coating breakdown with primer intact or localised under rusting to nomore than Ri 3 (ASTM No 6) level = Locally blast clean degraded areas to Sa 2.5standard as per ISO 8501-1 plus supplement or where blast cleaning is impractical,

power tool clean to St 3 standard. At the QP engineer's discretion, fully blast clean thesurfaces to Sa 2.5 standard.




Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure




HEMPADUR MIO 47950 100 Grey 13480 125 100 .019"-.021" 225 bar 7.6 X Xf/cHEMPATHANE ENAMEL 55100 100 To Be Advised T.B.A 100 50 .017"-.019" 100 bar 10.4 X Xf/c




13Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C







14Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C


HEMPADUR MIO 47950 12130 76 98140 5 : 1 1 h 2 h 24 08450 0HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0


Remarks:




15Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 2In (Revision 1) : General Exposure to atmosphere : Insulated existing items maintenance : temperature range minus 46oC to 120oC

sqm 100




1)No visible coating breakdown Ri 0 (ASTM No 10) level = No overcoating required.

2)Partial or variable coating breakdown with primer intact or localised under rusting to nomore than Ri 3 (ASTM No 6) level = Locally blast clean degraded areas to Sa 2.5standard as per ISO 8501-1 plus supplement or where blast cleaning is impractical,power tool clean to St 3 standard. At the QP engineer's discretion, fully blast clean thesurfaces to Sa 2.5 standard.




Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure







16Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C





17Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C


HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0

Remarks:


AREAS THAT PROTRUDE THROUGH THE INSULATION ALSO REQUIRE 50micron THICK COAT OF ALIPHATIC POLYURETHANE HIGH GLOSS TOPCOAT "HEMPATHANEENAMEL 55100"



18Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 2F (Revision 1) : General Exposure to atmosphere : Fireproofed existing items maintenance : temperature range 0oC to 120oC

sqm 100




1)No visible coating breakdown Ri 0 (ASTM No 10) level = No overcoating required.





Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure






19Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 2F (Revision 1) : General Exposure to atmosphere : Fireproofed existing items maintenance : temperature range 0oC to 120oC

sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C


Remarks:


AREAS THAT PROTRUDE THROUGH THE INSULATION ALSO REQUIRE TO BE COATED WITH AN ADDITIONAL 125µm OF MIO PIGMENTED EPOXY MIDCOAT PAINT PLUS A 50µm THICK COAT OF ALIPHATIC POLYURETHANE HIGH GLOSS TOPCOAT PAINT = HEMPADUR 47950-13480 AT 125µm + HEMPATHANE ENAMEL 55100-T.B.A. AT50µm.



20Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 3 (Revision 1) : Uninsulated steel items with a design temperature of 120oC to 400oC

sqm 100



Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (highpressure3000psi) fresh water cleaned in order to remove salts and other contaminants.When the surface is dry: Abrasive blasting to minimum Sa 3.0 according to ISO8501-1:2007, using a suitably sized abrasive blast media to produce a surface profile of between 35 and 50microns.

Maintenance :

1)If the primer is intact, lightly blast clean or mechanically abrade to remove damagedtopcoat paint and thoroughly fresh water wash using a stiff bristle brush to remove solublezinc salts.

2)If the primer has suffered breakdown or a marked reduction in film thickness, blastclean affected areas to Sa 3.0 standard as per ISO 8501-1 plus supplement using asuitable sized abrasive to give a surface profile of 35 to 50µm.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPEL'S GALVOSIL 15700 100 Metal grey 19840 75 50 .019"-.023" 100 bar 12.8 (X) Xf/c

HEMPEL'S SILICONE ACRYLIC 56940 100 Light alu 19000 75 25 .017" 125 bar 12.0 (X) Xf/c

HEMPEL'S SILICONE ACRYLIC 56940 100 Light alu 19000 75 25 .017" 125 bar 12.0 (X) Xf/c




21Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C


1) 1) 1) 1) 1) 1) 1) 1) 1) 1) 1) 1)5694015700 50

12 Hrs None 18 Hrs None 24 Hrs None 43 Hrs None 72 Hrs None 6½ Day None5694056940 25



22Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPEL'S GALVOSIL 15700 19840 64 97170 7.4 : 2.6 4 h 30 min 14 08700 0

HEMPEL'S SILICONE ACRYLIC 56940 19000 30 1 h 25 08080

HEMPEL'S SILICONE ACRYLIC 56940 19000 30 1 h 25 08080

Remarks:

1) See product data sheet and / or APPLICATION INSTRUCTIONS regarding drying time and recoating intervals.RESPECTFULLY SUGGEST MODIFIED SILICONE ALUMINIUM PRODUCTS CAN NOW BE REPLACED BY PURE SILICONE MOISTURE CURING RESIN BASED PRODUCTSSUCH AS :HEMPEL SILICONE ALUMINIUM 56914-19000



23Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 3HT (Addition) :Uninsulated steel items operating at temperatures above 400oC " metal sprayed items"

sqm 100



Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water cleaned in order to remove salts and other contaminants.When the surface is dry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1,with a suitable sized abrasive to give a surface profile of 75 to 100 microns.Followed by metal (aluminium) spraying to dry film thickness of at least 200microns.

Maintenance :

1)If metal coating is intact : sweep blast clean and fresh water wash to remove aluminiumsalts.

2)If metal coating has suffered breakdown, blast clean affected areas to Sa 3.0 standard

to ISO 8501-1 plus supplement using a suitable abrasive to give a surface profile of 50 to75microns.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPEL'S SILICONE ALUMINIUM 56914 100 Light alu 19000 50 25 0.017" 125 bar 17.2 (X) Xf/c

HEMPEL'S SILICONE ALUMINIUM 56914 100 Light alu 19000 50 25 0.017" 125 bar 17.2 (X) Xf/c

t/u: touch up f/c: full coat s/c: stripe coat Total d.f.t. 50 X: Recommended (X): Possible



24Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C


12 Hrs None 18 Hrs None 24 Hrs None 43 Hrs None 72 Hrs None 6½ Day None5691456914 25



25Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPEL'S SILICONE ALUMINIUM 56914 19000 43 1 h 30 08080

HEMPEL'S SILICONE ALUMINIUM 56914 19000 43 1 h 30 08080

Remarks:

A flash-coat before applying the full coat is strongly recommended when recoating Metal Sprayed Coatings.



26Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 4 (Revision 1) : Insulated ferrous items with a design temperature of 120oC to 250oC

sqm 100



Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water cleaned in order to remove salts and other contaminants. When the surface isdry:1)No visible coating breakdown Ri 0 (ASTM No 10) level = No overcoating required.


3)More extensive coating breakdown to Ri 4 (ASTM No 4) level or worse = Fully blast

clean surfaces to Sa 2.5 standard per ISO 8501-1 plus supplement. Power tool cleaningto St 3 standard is only acceptable for small areas and areas that are impractical for blastcleaning by agreement. use suitable blast cleaning abrasive to give a surface profile of 35to 50microns.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPEL'S SILVIUM 51570 100 Light alu 19000 125 50 .017'' 100 bar 7.6 (X) Xf/c

HEMPEL'S SILVIUM 51570 100 Light alu 19000 125 50 .017'' 100 bar 7.6 (X) Xf/c




27Page:

01.10.2013 13:42

User name:

Department name:



Admin Medium

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C


10 Hrs None 15 Hrs None 20 Hrs None 40 Hrs None N/R N/R N/R N/R5157051570 50



28Page:

01.10.2013 13:42

User name:

Department name:



Admin Medium

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPEL'S SILVIUM 51570 19000 38 5 h 38

HEMPEL'S SILVIUM 51570 19000 38 5 h 38

Remarks:

STRONGLY RECOMMEND DUE TO VERY SLOW CURING OF OLEORESINOUS HIGH TEMPERATURE PRODUCTS THEIR APPLICATION IS BEST SUITED TO MAINTENANCEPROJECTS ONLY.



29Page:

01.10.2013 13:42

User name:

Department name:



Admin Medium

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Shedule 5 (Revision 1) : Items exposed to seawater and seaspray in the splash zone (excluding riser lines which is covered by QP:SPC:L:003)

sqm 100



Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1:2007. Surface profilecorresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISOComparator Rough Medium (G), profile amplitude of 75 to 100microns.Dust off residues.

Repair of damaged coatings : vacuum or spot blast to ISO 8501-1 plus supplement usinga suitably sized abrasive to give a surface profile of 75 to 100µm. Power tool cleaning isnot acceptable for even local repair of this coating system when fully cured. Sweep blastcleaning may be used by agreement.

Maintenance : Unless no visible coating breakdown is evident. Blast clean the surfaces toSa 2.5 standard as per ISO 84501-1 plus supplement using a suitably sized abrasive togive a surface profile amplitude of 75 to 100µm. Power tool cleaning is not acceptable for this schedule.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPADUR MULTI-STRENGTH GF 35870 100 Red 50630 575 500 .023"-.027" 250 bar 1.7 Xf/c

HEMPADUR MULTI-STRENGTH GF 35870 100 Black 19990 575 500 .023"-.027" 250 bar 1.7 Xf/c




30Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C


2 Hrs 9 Day 4 Hrs 15 Day 8 Hrs 30 Day 20 Hrs 75 Day N/R N/R N/R N/R3587035870 500



31Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPADUR MULTI-STRENGTH GF35870

50630 87 98870 3 : 1 1 h 2 h 30 min 35 08450 5

HEMPADUR MULTI-STRENGTH GF35870

19990 87 98870 3 : 1 1 h 2 h 30 min 35 08450 5

Remarks:

Stripe coating with brush before or after spray application of each coat is to be carried out on areas difficult to cover properly by spray as eg edges, corners, flanges, cutouts,handwelds and other rough surfaces.



32Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:

Coating Schedule 6 (Revision 1) : Internal surfaces of steel, hydrocarbon, and water storage tanks.

sqm 100



Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry:1)NEW CONSTRUCTION : Abrasive blasting to minimum Sa 3.0 according to ISO8501-1:2007. Surface profile corresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISO Comparator Rough Medium (G) using suitably sizedabrasive to give a surface profile of 75 to 100 microns.Dust off residues.2)Repair of Damaged Coating : Vacuum or spot blast clean to ISO 8501-1 plussupplement using a suitable sized abrasive to give a surface profile amplitude of 75 to100 microns. Power tool cleaning to St 3 standard is only acceptable by agreement for areas that are inaccessible or impractical for blast cleaning .

3)Maintenance : Unless no visible coating breakdown is evident, blast clean the surfacesto Sa 2.5 standard as per ISO 8501-1 plus supplement using a suitable sized abrasive togive a surface profile amplitude of 75 to 100µm. Power tool cleaning to St 3 is onlyacceptable for small and inaccessible areas.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPADUR 35600 100 Light red 50900 300 300 .017"-.021" 250 bar 3.3 (X) Xf/c

HEMPADUR 35600 100 Cream 20320 300 300 .017"-.021" 250 bar 3.3 (X) Xf/c




33Page:

01.10.2013 13:42

User name:

Department name:



Admin Immersion

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C


22 Hrs 36 Hrs 36 Hrs 60 Hrs 72 Hrs 5 Day 7½ Day 12½ Day N/R N/R N/R N/R3560035600 300



34Page:

01.10.2013 13:42

User name:

Department name:



Admin Immersion

QACHL1858N


HEMPEL



Specification sheet



Project:

Area:


Area size:


sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPADUR 35600 50900 100 98600 14.8 : 5.2 h 30 m 24 h 93 08450 15

HEMPADUR 35600 20320 100 98600 14.8 : 5.2 h 30 m 24 h 93 08450 15

Remarks:

Stripe coating with brush before or after spray application of each coat is to be carried out on areas difficult to cover properly by spray as eg edges, corners, flanges, cutouts,handwelds and other rough surfaces.DEPENDANT UPON THE TANK STORAGE SERVICE VARIOUS OTHER EPOXY PRODUCTS MAY PROVE ACCEPTABLE PLEASE CONSULT HEMPEL OFFICE FOR DETAILEDRECOMMENDATION.



35Page:

01.10.2013 13:42

User name:

Department name:



Admin Immersion

QACHL1858N


HEMPEL

S ifi ti h t



Specification sheet



Project:

Area:


Area size:

Coating Schedule 6 (Revision 1) : Internal surfaces of steel hydrocarbon and water storage tanks "OPTION FOR HYDROCARBON STORAGE ONLY"

sqm 100



Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry:1)NEW CONSTRUCTION : Abrasive blasting to minimum Sa 3.0 according to ISO8501-1:2007. Surface profile corresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISO Comparator Rough Medium (G) using suitably sizedabrasive to give a surface profile of 75 to 100 microns.Dust off residues.2)Repair of Damaged Coating : Vacuum or spot blast clean to ISO 8501-1 plussupplement using a suitable sized abrasive to give a surface profile amplitude of 75 to100 microns. Power tool cleaning to St 3 standard is only acceptable by agreement for areas that are inaccessible or impractical for blast cleaning .

3)Maintenance : Unless no visible coating breakdown is evident, blast clean the surfacesto Sa 2.5 standard as per ISO 8501-1 plus supplement using a suitable sized abrasive togive a surface profile amplitude of 75 to 100µm. Power tool cleaning to St 3 is onlyacceptable for small and inaccessible areas.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPADUR 35760 100 Light red 50900 300 300 .021" 250 bar 3.3 (X) (X) Xf/c

HEMPADUR 35760 100 Cream 20320 300 300 .021" 250 bar 3.3 (X) (X) Xf/c




36Page:

01.10.2013 13:42

User name:

Department name:



Admin Immersion

QACHL1858N


HEMPEL

S ifi ti h t



Specification sheet



Project:

Area:


Area size:


sqm 100



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C





37Page:

01.10.2013 13:42

User name:

Department name:



Admin Immersion

QACHL1858N


HEMPEL

S ifi ti h t



Specification sheet



Project:

Area:


Area size:


sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPADUR 35760 50900 100 98760 6.4 : 3.6 40 min 65 10

HEMPADUR 35760 20320 100 98760 6.4 : 3.6 40 min 65 10

Remarks:




38Page:

01.10.2013 13:42

User name:

Department name:



Admin Immersion

QACHL1858N


HEMPEL

S ifi ti h t



Specification sheet



Project:

Area:


Area size:

Coating Schedule 7 (Revision 1) : Underside surface of Steel Storage Tank Floor Plates

sqm 100



Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1:2007. Surface profilecorresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISOComparator Rough Medium (G), using suitably sized abrasive to give a surface profileamplitude of 75 to 100microns.Dust off residues.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPADUR QUATTRO 17634 100 Red 50630 275 200 .021"-.025" 250 bar 3.6 Xf/c

HEMPADUR QUATTRO 17634 100 Black 19990 275 200 .021"-.025" 250 bar 3.6 Xf/ct/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 400 X: Recommended (X): Possible


Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C


2 Hrs Ext 3 Hrs Ext 4 Hrs Ext 8 Hrs Ext 18 Hrs Ext 36 Hrs Ext1763417634 200



39Page:

01.10.2013 13:42

User name:

Department name:



Admin buried

QACHL1858N


HEMPEL

S ifi ti h t



Specification sheet



Project:

Area:


Area size:

Coating Schedule 7 (Revision 1) : Underside surface of Steel Storage Tank Floor Plates

sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPADUR QUATTRO 17634 50630 72 97334 4 : 1 2 h 4 h 27 08450

HEMPADUR QUATTRO 17634 19990 71 97334 4 : 1 2 h 4 h 27 08450

Remarks:




40Page:

01.10.2013 13:42

User name:

Department name:



Admin buried

QACHL1858N


HEMPEL

S ifi ti h t



Specification sheet



Project:

Area:


Area size:

Coating Schedule 8A (Addition) : Internal surfaces of Vessels in Corrosive service at low pressure/temperature up to 70oC

sqm 100



Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry:1)NEW CONSTRUCTION :Abrasive blasting to minimum Sa 3.0 according to ISO8501-1:2007. Surface profile corresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISO Comparator Rough Medium (G), using a suitably sizedabrasive to produce a surface profile of 75 to 100µm.Dust off residues.2)Repair of damaged coating : Vacuum or spot blast to ISO 8501-1 plus supplement withsuitably sized abrasive to give a surface amplitude of 75 to 100µm. Power tool cleaning isnot acceptable for even local repair of this coating. Abrade partially damaged coatingswith emery paper and solvent wipe them.

3)Maintenance : Unless no visible coating breakdown is evident, blast clean the surfacesto Sa 3 standard as per ISO 8501-1 plus supplement using a suitably sized abrasive togive a surface amplitude of 75 to 100 microns. Power tool cleaning is not acceptable for this schedule.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPADUR 35900 100 Light red 50900 300 300 .018'' - .021'' 250 bar 3.3 Xf/c

HEMPADUR 35900 100 Cream 20320 300 300 .018'' - .021'' 250 bar 3.3 Xf/c




41Page:

01.10.2013 13:42

User name:

Department name:



Admin Immersion

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:


sqm 100



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C


N/R N/R ½ Day 30 Day 1 Day 60 Day 2½ Day 90 Day N/R N/R N/R N/R3590035900 300



42Page:

01.10.2013 13:42

User name:

Department name:



Admin Immersion

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:


sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPADUR 35900 50900 100 95900 3 : 1 1 h 65 08450 10

HEMPADUR 35900 20320 100 95900 3 : 1 1 h 65 08450 10

Remarks:




43Page:

01.10.2013 13:42

User name:

Department name:



Admin Immersion

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:

Coating Schedule 8B (Addition) : Internal surfaces of Vessels in Corrosive service at high pressure/temperature in excess of 70oC

sqm 100



Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry:1)NEW CONSTRUCTION :Abrasive blasting to minimum Sa 3.0 according to ISO8501-1:2007. Surface profile corresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISO Comparator Rough Medium (G), using a suitably sizedabrasive to produce a surface profile of 75 to 100µm.Dust off residues.2)Repair of damaged coating : Vacuum or spot blast to ISO 8501-1 plus supplement withsuitably sized abrasive to give a surface amplitude of 75 to 100µm. Power tool cleaning isnot acceptable for even local repair of this coating. Abrade partially damaged coatingswith emery paper and solvent wipe them.

3)Maintenance : Unless no visible coating breakdown is evident, blast clean the surfacesto Sa 3 standard as per ISO 8501-1 plus supplement using a suitably sized abrasive togive a surface amplitude of 75 to 100 microns. Power tool cleaning is not acceptable for this schedule.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPADUR 35900 100 Light red 50900 300 300 .018'' - .021'' 250 bar 3.3 Xf/c

HEMPADUR 35900 100 Cream 20320 300 300 .018'' - .021'' 250 bar 3.3 Xf/c




44Page:

01.10.2013 13:42

User name:

Department name:



Admin Immersion

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:


sqm 100



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C


N/R N/R ½ Day 30 Day 1 Day 60 Day 2½ Day 90 Day N/R N/R N/R N/R3590035900 300



45Page:

01.10.2013 13:42

User name:

Department name:



Admin Immersion

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:


sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPADUR 35900 50900 100 95900 3 : 1 1 h 65 08450 10

HEMPADUR 35900 20320 100 95900 3 : 1 1 h 65 08450 10

Remarks:




46Page:

01.10.2013 13:42

User name:

Department name:



Admin Immersion

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:

Coating Schedule 9 (Revision 1) : Zinc Coated Steel Surfaces

sqm 100



Remove oil and grease and any other contamination using a water soluble degreasingagent, followed by thorough fres water washing.

NEW CONSTRUCTION : Remove soluble zinc corrosion products by scrubbing with astiff bristle brush during fresh water washing. At QP engineer's discretion, lightly roughenthe surface by sweep blast cleaning using a fine abrasive or, if pretreatment primer is tobe applied, abrade with emery paper.

REPAIR OF DAMAGED COATING : If zinc is intact, remove soluble zinc corrosionproducts by scrubbing with stiff bristle brush during fresh water washing. If rusting of thesteel is evident, remove the rust by lightly abrading affected areas with emery cloth beforescrubbing with a stiff bristle brush during fresh water washing.

MAINTENANCE : As for repair of damaged coating but lightly sweep blast clean rustedareas to Sa 2.5 standard



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure







47Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:


sqm 100



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C


3 Hrs 36 Hrs 5 Hrs 54 Hrs 6 Hrs 72 Hrs N/R N/R N/R N/R N/R N/R5510045881 125



48Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:


sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C



Remarks:

When the interval is denoted "Extended", the coated structure can possibly be overcoated even after longer periods. This will depend on the actual exposure conditions, such aslimited exposure to sun, and on the condition and cleanliness of the paint surface. The evaluation of the specific situation must be based on local experience, contact HEMPEL for advice.



49Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:

Coating Schedule 10 (Revision 1) : Helideck & Walkway Non Skid Surfaces

sqm 100



Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1, Using suitableabrasive media to give a surface profile amplitude of 75 to 100µm.Dust off residues.REPAIR OF DAMAGED COATING : Vacuum or spot blast clean to ISO 8501-1 plussupplement using a suitably sized abrasive to give a surface profile amplitude of 75 to100µm. Power tool cleaning to St-3 standard is only acceptable by agreement for areasthat are inaccessible or impractical for blast cleaning.MAINTENANCE : Blast clean areas of coating breakdown or, at QP Engineer' sdiscretion, fully blast clean surfaces to Sa 2.5 standard as per ISO 8501-1 plussupplement using a suitable sized abrasive to give a surface profile of 75 to 100µm.Power tool cleaning is only acceptable for small areas.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPADUR SPRAY-GUARD 35490 100 Grey 11480 1500 1500 0.0 bar 0.7 (X) Xf/c

HEMPADUR MULTI-STRENGTH 35530 100 To Be Advised T.B.A 300 300 .019"-.031" 250 bar 3.3 (X) Xf/c



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C





50Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:

Coating Schedule 10 (Revision 1) : Helideck & Walkway Non Skid Surfaces

sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPADUR SPRAY-GUARD 35490 11480 100 95690 5.6 : 1 1 h 8 h 60 10

HEMPADUR MULTI-STRENGTH 35530 T.B.A 100 95530 3 : 1 1 h 24 h 100 10 85

Remarks:

Helideck Markings to CAP437 shall be made with brush applied aliphatic polyurethane topcoat paint, applied over the epoxy seal coat.



51Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:

Coating Schedule 11(Revision 1) : Buried/Fully Immersed Pipelines (Field Joint Coating/Maintenance Painting)

sqm 100



Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry: Abrasive blasting to minimum Sa 3.0according to ISO 8501-1. Surface profilecorresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISOComparator Rough Medium (G), surface profile 75 to 100µmDust off residues.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPADUR 85531 100 Red 50890 325 275 .021"-.023" 250 bar 3.1 (X) Xf/c

HEMPADUR 85531 100 Red 50630 350 275 .021"-.023" 250 bar 2.9 (X) Xf/c



Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C


6 Hrs 48 Hrs 11 Hrs 3½ Day 16 Hrs 5 Day 36 Hrs 11 Day N/R N/R N/R N/R8553185531 275



52Page:

01.10.2013 13:42

User name:

Department name:



Admin Buried

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:

Coating Schedule 11(Revision 1) : Buried/Fully Immersed Pipelines (Field Joint Coating/Maintenance Painting)

sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPADUR 85531 50890 84 97531 4 : 1 1 h 6 h 14 08450 5

HEMPADUR 85531 50630 81 97531 4 : 1 1 h 6 h 14 08450 5

Remarks:




53Page:

01.10.2013 13:42

User name:

Department name:



Admin Buried

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:

Coating Schedule 12 (Revision 1) : Stainless Steel and Non Ferrous Metal Surfaces

sqm 100



Remove oil and grease, etc. with suitable detergent. Remove salt and other contaminantsby (high pressure) fresh water hosing. When the surface is dry:

Abrasive sweep blasting with mineral (non metallic) abrasive to an evenly flattenedsurface with a dense profile of between 35 and 50µm.Dust off residues.



Shade no.

Film thickness

(micron)


Roller

Spray

Nozzleorifice

Recommended

Nozzlepressure


HEMPADUR 15553 100 Off white 11630 100 50 .017"-.019" 175 bar 11.0 (X) Xf/c





Quality no

D.F.T.

(micron)


40°C 30°C 20°C 10°C 0°C -10°C


N/R N/R 5 Hrs Ext 6 Hrs Ext 12 Hrs Ext 27 Hrs Ext 54 Hrs Ext4795015553 50




54Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N


HEMPEL

Specification sheet



Specification sheet



Project:

Area:


Area size:

Coating Schedule 12 (Revision 1) : Stainless Steel and Non Ferrous Metal Surfaces

sqm 100



Shade no.

Volumesolids %

Curingagent

Mixing ratiovolume


Thinner


20°C 20°C °C °C

HEMPADUR 15553 11630 55 98021 3 : 1 2 h 3 h 30 08450 5

HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0


Remarks:

When the interval is denoted "Extended", the coated structure can possibly be overcoated even after longer periods. This will depend on the actual exposure conditions, such aslimited exposure to sun, and on the condition and cleanliness of the paint surface. The evaluation of the specific situation must be based on local experience, contact HEMPEL for advice.



55Page:

01.10.2013 13:42

User name:

Department name:



Admin Severe

QACHL1858N