Chapter 2
Preparation and Characterization of ZnF2–PbO–TeO2: TiO2 glass ceramics
In this chapter the detailed description of the methods used in the
preparation of glasses and glass ceramics and the apparatus used and
methods adopted for the characterization of the ZnF2–PbO–TeO2: TiO2
glass ceramics are presented. The characterization of the samples by SEM,
TEM, XRD and DSC techniques have indicated that the samples contain
well defined and randomly distributed grains of different crystalline
phases.
Preparation and Characterization of ZnF2–PbO–TeO2: TiO2 glass ceramics
2.1 Introduction
In this chapter the detailed description of the methods used in the
preparation of glasses and glass ceramics and the apparatus used and methods
adopted for the characterization of the ZnF2–PbO–TeO2: TiO2 glass ceramics are
presented. The methods include X-Ray diffraction (XRD), scanning electron
microscopy (SEM) and transmission electron microscopy (TEM), differential
scanning calorimetry (DSC). These studies are intended to obtain the
information regarding the chemical composition, size and the concentration of
different crystalline phases that are formed in the bulk samples due to
crystallization. This information is essential for understanding different physical
properties of the samples that are presented in the subsequent chapters.
2.2 Glass preparation
2.2.1 Composition of the glass
Within the glass forming region of ZnF2–PbO–TeO2 system (Fig. 2.1), the
following compositions are chosen for the present study:
TC0 : 30ZnF2–10.0PbO– 60TeO2
TC5 : 30ZnF2–9.50PbO–60TeO2:0.5TiO2 TC7 : 30ZnF2–9.30PbO–60TeO2:0.7TiO2
TC10: 30ZnF2–9.00PbO–60TeO2:1.0TiO2 TC15: 30ZnF2–8.50PbO–60TeO2:1.5TiO2
85
TC20: 30ZnF2–8.00PbO–60TeO2 :2.0TiO2
Fig. 2.1 Approximate glass forming region of ZnF2–PbO–TeO2 system. Circle indicates the composition of the present study.
2.2.2 Preparation of the glass and glass ceramics
The glasses used for the present study are prepared by the melting and
quenching techniques [1–3]. The starting chemicals used for the preparation of
the glasses were analytical grade reagents of ZnF2, PbO, TeO2 (METALL, China,
4N pure) and TiO2. The compounds of required compositions were thoroughly
mixed in an agate mortar and melted in a platinum crucible. The furnace used was
a proportional–integral–derivative (PID) temperature controlled furnace (Fig. 2.2).
The glasses were melted at about 700–750 oC for an hour till a bubble free liquid
86
was formed. The resultant melt was then poured in a brass mould (containing
smooth polished inner surface) and subsequently annealed from 250 oC with a
cooling rate of 1ºC/min in another furnace.
Crystallization
For the crystallization, the glasses were heat treated at crystallization
temperature of the corresponding amorphous material identified from the DSC
traces of the glasses for 72 h. After heat treatment in the furnace at specified
temperature, the samples were sharply chilled in air to room temperature.
Automatic controlling furnace was used for raising the temperature to the required
level and for maintaining it for the specified duration.
Fig. 2.2 (a) PID controller and the photographs of (b) Melting furnace (c) Annealing furnace and (d) Casting of glass sample.
87
The photographs of some of ZnF2–PbO –TeO2 :TiO2 glass samples (as quenched) are shown below:
Fig. 2.3 Photographs of pre-polished ZnF2 –PbO –TeO2: TiO2 glass samples
The glasses were then ground and optically polished. The approximate final
dimensions of the glasses used for studying the electrical and optical properties are
1 cm x 1 cm x 0.2 cm.
2.3 Physical properties
The density (d) of the glasses and glass ceramics was determined to an
accuracy of 0.0001 g/cm3 by the standard principle of Archimedes’ with o-xylene
(99.99 % pure) as the buoyant liquid using Ohaus digital balance Model AR2140
fitted with density measurement kit. The density of the samples was determined by
weighing the bulk glasses in the liquid and in air. The refractive index (nd) of the
glasses was measured (at λ = 589.3 nm) at room temperature using Abbe
88
refractometer (Fig.2.4) with monobromo naphthalene as the contact layer between
the glass and the refractometer prism.
From the measured values of the density and average molecular weight M
of the samples, various other physical parameters such as titanium ion
concentration Ni, mean titanium ion separation Ri, polaron radius Rp in ZnF2–PbO–
TeO2: TiO2 glass ceramic samples which are useful for understanding the physical
properties of these glasses are evaluated using conventional formulae [3,4]
mentioned in the Chapter 1 and presented in Table 3.1. The density of the samples
is observed to decrease slightly with the concentration of TiO2. However due to
the crystallization a slight increment in the density compared to that of
corresponding amorphous samples is observed.
The average errors in these physical parameters were calculated and given below.
Density, d (g/cm3) ±0.0001
Fig. 2.4 Abbe refractometer (Model NAR-4T)
89
Dopant ion concentration, Ni (1020/cm3) ±0.01
Inter-ionic distance of dopant ions, Ri (Å) ±0.01
Polaron radius, Rp(Å) ±0.01
Field strength, Fi (1015 cm-2) ±0. 01
Refractive index ±0. 001
Table 2.1 Physical parameters of ZnF2–PbO–TeO2: TiO2 glass ceramic samples
• Density values given in the parenthesis are those of corresponding amorphous samples
The progressive introduction of crystallizing agent TiO2 caused a slight
decrease in the density of the samples. The degree of structural compactness, the
modification of the geometrical configuration of the glassy network, the size of the
Sample
Density (g/cm3)
Dopant ion conc (Ni)
( x 1020 ions/cm3)
Inter ionic distance(Ao)
Polaron radius (Ao)
Refractive index
TCo
TC5
TC7
TC10
TC15
TC20
5.660
(5.565)
5.617 (5.506)
5.517
(5.499)
5.499 (5.496)
5.486
(5.486)
5.467 (5.405)
……..
1.14
1.57
2.24
3.55
4.505
……..
20.62
18.53
16.46
14.12
13.04
………
8.309
7.468
6.632
5.689
5.256
1.662
1.655
1.653
1.649
1.642
1.633
90
nano-crystals formed, change in the coordination of the glass forming ions and the
fluctuations in the dimensions of the interstitial holes might have influenced the
density of the glass ceramic samples.
2.4 Scanning electron microscopy (SEM)/Transmission electron microscopy (TEM) studies
Scanning electron microscopy studies were carried out on these glasses to
check the crystallinity in the samples using HITACHI S-3400N Scanning Electron
Microscope (Fig. 2.5 (a)).
In a typical SEM, electrons are thermionically emitted from a tungsten or
lanthanum hexaboride (LaB6) cathode and are accelerated towards an anode. The
electron beam, which typically has an energy ranging from a few hundred eV to
Fig. 2.5 (a) HITACHI S-3400N Scanning Electron Microscope
91
100 keV, is focused by one or two condenser lenses into a beam with a very fine
focal spot sized 0.4 nm to 5 nm. The beam passes through pairs of scanning coils
or pairs of deflector plates in the electron optical column, typically in the objective
lens, which deflect the beam horizontally and vertically so that it scans in a raster
fashion over a rectangular area of the sample surface. When the primary electron
beam interacts with the sample, the electrons lose energy by repeated scattering
and absorption within a teardrop-shaped volume of the specimen known as the
interaction volume, which extends from less than 100 nm to around 5 µm into the
surface. The size of the interaction volume depends on the electrons' landing
energy, the atomic number of the specimen and the specimen's density. The energy
exchange between the electron beam and the sample results in the emission of
electrons and electromagnetic radiation, which can be detected to produce an
image.
The transmission electron microscopic pictures were recorded for some
of the glass ceramic samples using Tecnai T20 microscope (Fig. 2.5 (b)). The FEI
Tecnai TF20 is a 200kV FEG high resolution Transmission Electron Microscope
(TEM), suitable for cryo single particles and semi-thick frozen cells or sections
(up to 200 nm) electron microscopy and electron tomography. The microscope is
fitted with a W-source and an ultra high resolution pole piece with a point-point
resolution of 1.9 A. The TF20 is equipped with a Field Emission Gun (FEG) and
+/-80 degrees tilted computer controlled LiN cryostage. This microscope features
a TIETZ F415MP 4k x 4k multiport CCD camera with a 4-port readout and 15m
92
pixel size. Images could be recorded on plain film camera as well. In the main
body of the EM, the column, are located, from top to bottom, Field Emission Gun
(FEG), Condenser lenses and condenser apertures (C1 and C2), Objective lens,
Compustage, Objective aperture (OA), Selective aperture (SA), Projectors,
Viewing camera, Plain film camera and CCD camera. The High Voltage Tank
produces 80 – 200kV Accelerating voltage applied to the FEG and the Anode,
which produces a coherent beam of accelerated electrons. The condenser lenses
and apertures control spot size and beam size.
Fig. 2.5 (b) Tecnai T-20 High Resolution- Transmission Electron Microscope.
The objective lens focuses the beam transmitting the specimen, the objective
aperture selects the electrons close to optical axis improving image contrast and
projectors form the final magnification. The post magnification factor for the CCD
93
camera is 1.4. All the microscope functions, including CCD imaging, are provided
by the Main Computer supplied with dedicated FEI and TIETZ software
The scanning microscopic pictures of some of the crystallized samples are
shown in Fig. 2.6 (a), whereas in Fig. 2.6 (b) transmission electron microscopic
pictures are presented for some of the samples. The pictures clearly indicate that
well defined, randomly distributed crystals of different sizes (varying from 50 to
500 nm) are ingrained in glassy matrix. The residual glass phase is acting as
interconnecting zones among the crystallized areas, making the samples free of
voids and cracks. The pictures further indicate a gradual increase in the volume
fraction of crystallites in the samples with increasing concentration of TiO2. Thus,
from these pictures it can also be concluded that TiO2, enhanced the phase
separation tendency of various crystalline phases. The SEM or TEM pictures of
pre-heated samples exhibited virtually no crystallinity.
Fig. 2.6 (a) ZnF2–PbO–TeO2 glasses heat treated with different concentrations of TiO2.
TC2 TC5 TC7
TC10 TC15 Amorphous sample TA5
94
Fig. 2.6 (b) TEM pictures of ZnF2–PbO–TeO2: TiO2 glass ceramic samples
2.5 X-ray diffraction studies (XRD)
The crystalline nature of the heat treated samples was checked by X-ray
diffraction spectra recorded on Xpert PRO’panalytical X-ray diffractometer (Fig.
2.7 (a)) with CuKα radiation. Fig. 2.7 (b) represents the schematic diagram of
general X-ray diffractometer.
It may be noted here that the XRD pattern of pre-heated samples have not
exhibited any sharp peaks.
TC10
TC5
TC20
Pre Crystallized
95
X-ray diffraction patterns for the ZnF2–PbO–TeO2 glass ceramic doped with 1.0
wt% of TiO2 is shown in Fig. 2.8 (a).
Fig. 2.7 (a) Xpert PRO’panalytical X-ray diffractometer.
Fig. 2.7 (b) Schematic representation of X-ray diffractometer.
96
The patterns exhibited peaks due to variety of crystal phases; some of them are
Pb5Ti3F19, PbTiO3, PbTi2O6, PbTeO3, Pb3TeO5 and TiTe3O8; the details JCPDS
card numbers for these crystalline phases can be found in the ref. [6]. The XRD
patterns for all the crystallized glasses are shown in Fig. 2.8 (b).
Fig. 2.8 (a) XRD pattern of ZnF2–PbO–TeO2 glass ceramics doped with 1.0 wt % of TiO2 showing different possible crystalline phases. Most interestingly we have observed diffraction peak with significant intensity and
full width at half maximum due to Pb5Ti3F19 crystal phase at about 2θ = 25.00°,
27.84° and 29.65° due to reflections from (3 2 1), (4 1 1) and (2 2 2) crystal planes,
4
5 10 15 20 25 30 35 40 45 50 55
2θ (deg)
Inte
nsity
(rel
. uni
ts)
(1)
(1)
(1)
(2)
(2)
(3)
(3)
(3)
(4)(5)
(5)
(6)(6)
97
respectively. The presence of such phase clearly suggests that a fraction of the
titanium ions exists in Ti3+ valence state. However, as the concentration of TiO2
increased up to 1.0 wt% the intensity of these peaks is found to increase and
beyond this concentration a slight decreasing trend is observed.
Fig. 2.8 (b) XRD pattern of ZnF2–PbO–TeO2 glass ceramics doped with different concentrations of TiO2. For the sake of comparision, the XRD pattern of one of the pre-crystallized samples (TA5) is also included.
5 10 15 20 25 30 35 40 45 50 55
2θ (deg)
TA5
TC5
TC7
TC10
TC15
TC20
98
The structure composed of infinite chains of eclipsed corner-sharing TiF6
octahedra as well as individual octahedra. The arrangement consists of number of
octahedra, PbFn polyhedra and non-octahedral F- ions. A structural fragment of
Pb5Ti3F19 is illustrated in Fig.2.9.
Distortions from regularity in the independent TiF6 octahedral phase result
in the development of appreciable electric dipoles in these crystal phases that will
contributing to NLO effects which will be discussed in chapter 5. The gradual
increase in the intensity of the diffraction peaks due to these crystallites (especially
in the pattern of the samples containing TiO2 upto1.0 wt %) indicates larger
concentration of such crystal phases.
Fig. 2.9 An illustration of Pb5Ti3F19 structural fragment.
99
In fact ferroelectric behaviour of this type of crystals was reported earlier [7, 8].
Another interesting feature of XRD pattern is, presence of clear diffraction peaks
at 2θ = 22.77° and 31.97° corresponding to PbTiO3 orthorhombic crystal phases;
this observation points out that the titanium ions do exist in Ti4+ state and
participate as a network former in the glass network. Additionally, the intensity of
the diffraction peaks due to PbTiO3, PbTeO3 phases is also found to be maximal
for the samples crystallized with 1.0 wt % of TiO2 indicating the concentration of
such crystal phases is higher in this sample. The presence of PbTiO3 crystal phases
points out that the titanium ions also exist in Ti4+ state and participate as a network
former in the glass network. Additionally, it should be further emphasized that the
XRD patterns of pre-heated samples have exhibited virtually no sharp peaks (see
XRD pattern of the sample TC5, Fig. 2.8 (b)).
2.6 Differential scanning calorimetric (DSC) studies
Thermal analysis of the samples was carried out by Netzsch Simultaneous
DSC/TG Thermal Analyzer STA409C (Fig. 2.10(a)) with 32-bit controller to
determine the glass transition temperature and crystalline peaks. High temperature
furnace together with a sample carrier suitable for Cp measurements and Al2O3
crucibles were used. Apparatus was calibrated both for temperature and for
sensitivity with melting temperatures and melting enthalpies of the pure metals:
Ga, In, Sn, Zn, Al, Ag, Au. All the recordings were carried out in argon (of 5N
pure) atmosphere to prevent samples from oxidation. Heating rate was 10 �C/min
in the temperature range 303–1500 K.
100
The glass transition temperature and other glass forming ability parameters are
evaluated to an accuracy of ± 1 K. The schematic sketch of Netzsch Simultaneous
DSC/TG Thermal Analyzer STA409C is also presented in Fig. 2.10 (b).
In Figs. 2.11(a–e) differential scanning calorimetric (DSC) scans in the
temperature region 300-1500 K for ZnF2–PbO–TeO2 glasses crystallized with
different concentrations of TiO2 are presented, whereas in Fig. 2.12 the
comparison plot for all the samples is presented. For the crystallized glasses, a
weak endothermic effect (due to glass transition) in the temperature range 590 to
610 K is observed. At about 770 K, the DSC thermogram of each glass ceramic
sample exhibited well-defined exothermic effects with multiple steps of
Fig. 2.10 (b) The sketch of Netzsch Simultaneous DSC/TG Thermal Analyzer STA409C.
Fig. 2.10 (a) Netzsch Simultaneous DSC/TG Thermal Analyzer STA409C.
101
crystallization temperatures; the auxiliary peaks appear to be weak and spread
over a region of approximately 50 K. These results clearly support the view point
that the samples are composed of different crystalline phases. The enthalpy
associated with the primary crystallization peak with the concentration of
crystallizing agent appears to decrease with the concentration of crystallizing
agent TiO2. It may be noted here that no multiple steps of crystallization are
observed in the thermograms of pre-crystallized samples. To observe the mass
change effects during heating process, we have also recorded thermal gravimetric
traces for all the samples; in Fig. 2.11 (a–e), thermal gravimetric (TG) traces for
all the samples along with corresponding DSC traces are also shown. The analysis
exhibits virtually no change in the mass of the samples upto 1100 K.
103
Fig. 2.11 (a –e) DSC scans of ZnF2–PbO–TeO2 glasses crystallized with different concentrations of TiO2. In the DSC scan of sample TC10 the corresponding thermogram of pre-crystallized sample (TA10) is also presented. Multiple weak exothermic effects could clearly be observed in the thermograms of crystallized samples.
(d)
(e)
104
Fig. 2.12 Comparison plots of DSC traces of ZnF2–PbO–TeO2 glass ceramics doped with different concentrations of TiO2 (a) In the low temperature region, (b) In the high temperature region.
The appearance of different exothermic peaks in the DSC pattern obviously
suggests the presence of different phases of crystallization in the samples. The
crystallization in the glass samples may take place following the surface and
bulk nucleations. The general shape of the crystallization peak in DSC curves
reflects the variation of enthalpy. A decrease in the value of enthalpy
associated with the crystallization with increase in the concentration of
nucleating agent suggests that the crystallization starts initially from the
surface of the material and extended in to volume of the material. The
calorimetric exothermic effects (peaks) caused by crystallization have been
suppressed by mutual movement and revolution (aggregation) of metal–oxygen
octahedral (endothermic) in the plastic (flexible) phase, at temperature range
which appear in the same temperature as the crystallization; this affects
decrease of actual enthalpy of crystallization as observed. Thermal gravimetric
analysis confirms high stability and lacks of symptom of decomposition up to
1100 K of all the crystallized samples.
105
106
2.7 Conclusions
ZnF2–PbO–TeO2 glasses doped with different concentrations of TiO2
were prepared. Later they were crystallized by heat treating them at
crystallization temperature identified from DSC studies. The samples were
characterized by SEM, XRD and DSC techniques. The characterization of the
samples by SEM, XRD and DSC techniques have indicated that the samples
contain well defined and randomly distributed grains of different crystalline
phases viz., Pb5Ti3F19, PbTiO3
and PbTeO3. Interestingly the concentration of Pb5Ti3F19 tetragonal crystalline
phases in which the titanium ions exist as Ti3+ state is found to increase in the
glass ceramics with increase in the concentration of TiO2.
107
References [1] James E Shelby, Introduction to Science and Technology of Glass
Materials Royal Society of Chemistry, London 2005.
[2] W. Vogel, Glass Chemistry, Springer Verlag, Berlin 1994.
[3] S.R. Elliot, Physics of Amorphous Materials. Longman, Essex1990.
[4] M.J. Weber, R.A. Saroyan, R.C. Ropp, J. Non-Crst. Solids 4 (1981) 137.
[5] M.J. Weber, J. Chem. Phys. 48 (1968) 4774.
[6] Powder Diffraction File, Alphabetical Index, Inorganic Compounds, JCPDS, International Centre for Diffraction Data, Newtown Square, PA 19073, 2003.
[7] S.C. Abrahams, J. Ravez, H. Ritter and J. Ihringer, Acta Cryst. B59
(2003) 557. [8] V. Andriamampianina, P. Gravereau, J. Ravez, S.C. Abrahams, Acta
Cryst. B50 (1994) 135.