Pair distributionfunction analysis
The Analytical X-ray Company
Total scattering experiments using high-energy X-rays on a laboratory system
SummaryAnalyzing powder diffraction data of nanocrystalline and amorphous materials using the atomic pair distribution function (PDF) method provides useful information about the long- and short-range ordering of the atoms in the materials. We have developed the application of PDF analysis on a standard laboratory system employing an X-ray tube with either a silver or a molybdenum anode as X-ray source. Data obtained from a variety of samples are shown. Meaningful results have been achieved, that allowed extracting structural information for comparison with data reported in literature.
Introduction Recent years have shown an increased interest in the study of nanocrystalline materials due to their specific properties for application in e.g. semiconductors, pharmaceuticals and polymers. Structural information about these materials is present as broad, not well defined features in a diffractogram. Analysis of nanomaterials therefore requires a total scattering approach, including both Bragg peaks and diffuse scattering. One of the most promising analytical methods used is atomic pair distribution function (PDF) analysis.Originally, this method was used to study primarily amorphous and highly disordered materials. More recently, it has been used for the analysis of nanostructured materials. Since the method requires short wavelengths to obtain high resolution in real space (well defined interatomic distances), often the measurements are performed at synchrotron facilities, making use of both the high photon energies and the high photon flux that these facilities offer.We have investigated the possibility to apply the pair distribution technique on an in-house system, using Ag or Mo Kα radiation. This application note describes typical results on nanocrystals, liquids and amorphous materials.
G [
Å]
-2
r [Å]10 2 3 4 5 6
XRD APPLICATION NOTE
Schematic representation of the constructionof the atomic pair distribution function from asquare array of atoms [2]. The colored circles (a)indicate the distance from a central atom wherea neighboring atom can be found. The arrowsindicate the corresponding peaks in the pairdistribution function.
(a)
(b)
Pair distribution function analysis
The pair distribution function G(r) describes the probability of finding two atoms separated by a distance r in the material under investigation. The PDF method extracts structure-related information from powder diffraction data [3].Since the technique takes both Bragg and diffuse scattering into account, it provides information not only about the long-range (>10 nm) atomic ordering but also about the short-range ordering in materials. The method is performed in the following steps: (i) the diffraction pattern is corrected for background (using a separate diffraction measurement of an empty sample
container), Compton scattering, detector dead time, absorption, diffraction geometry and polarization;(ii) the corrected X-ray diffraction data is scaled into electron units and the reduced structure function [4] is calculated;(iii) the structure function is Fourier transformed to obtain the atomic pair distribution function:
G(r) = 4πr (ρ(r) - ρ0)
in which ρ(r) is the local atom number density, and ρ0 is the mean atom number density.Since the method does not assume periodicity in the material, it is widely applied for the study of nanocrystalline andamorphous materials. The data can be used for full-profile fitting to refine structural models [5].
Empyrean goniometer with programmable divergence slit and incident beam anti-scatter slit, capillary spinner, programmable receiving slit with programmable anti-scatter slit and scintillation detector
PreFIX mounting
The optics and sample stage are designed according to the PreFIX concept; they are interchangeable with all other available modules for Empyrean without the need for realignment. The capillary spinner stage uses a goniometer head to allow precise alignment of the capillary tube on the goniometer axis.
Beam path of the used configuration
Instrumental configurations
X-ray diffraction measurements were performed on a PANalytical Empyrean system equipped with a programmable divergence slit, a capillary spinner, a dedicated anti-scatter device, and either X’Celerator detector or a scintillation detector with a programmable receiving slit. The X-ray source was a tube with either silver or molybdenum anode delivering Kα radiation with a wavelength of 0.0561 or 0.0709 nm, respectively.
Additional shielding was applied to the optical path in order to achieve a feature-free background.The samples were prepared in glass capillaries with a diameter of 2 mm.Scans along the 2θ axis were made up to an angle of 160 degrees corresponding to a scattering vector Q of 22 A-1 when a silver anode is used. The scattering vector is given by:
Q = 4π sinθ / λ
Initial data treatment, including background subtraction and optional Kα2 stripping, was done using X’Pert HighScore.For PDF analysis and fitting, we used the software RAD [6] and PDFgui [5].
Experimental setup
Instrument EmpyreanX-ray tube Empyrean Tube with silver (Ag) or molybdenum (Mo)
anode, long fine focus
Incident beam optics Divergence slit with incident beam anti-scatter slit and rhodium (Rh) or zirconium (Zr) beta-filters, focusing beam X-ray mirrors
Sample stage Capillary spinnerReflection-transmission spinnerFlat sample stage
Diffracted beam optics Programmable receiving slit with programmable anti-scatter slit or a dedicated anti-scatter device
Detector X’Celerator, scintillation detector
Scan parameters Typically 2 - 160° 2θ, 0.06° step size
Total scan time 8-24 hours depending on the material and the configuration used for the experiment
Results and discussion
Inte
nsi
ty [
cou
nts
]F(
Q)
[Å-1
]
(Q) [Å-1]
2 theta [deg.] (Ag radiation)
62500
40000
22500
10000
2500
010 20 30 40 50
Empty containerExperiment data
60 70 80 90 100 110 120 130
-20
-10
0
10
20
30
40
0 5 10 15 20
Inte
nsi
ty [
cou
nts
]F(
Q)
[Å-1
]
(Q) [Å-1]
2 theta [deg.] (Ag radiation)
62500
40000
22500
10000
2500
010 20 30 40 50
Empty containerExperiment data
60 70 80 90 100 110 120 130
-20
-10
0
10
20
30
40
0 5 10 15 20
Radial distance [Å]
10
5
0
-5
10 20 30 40 50 60
GdiffGobsGcalc
G(r
) [Å
-2]
Radial distance [Å]
GdiffGobsGcalc
10
5
0
-5
5 10 15 20 25
ab
c
d a: ¼<111>b: ½<110>c: <100>d: ¼<331>
GdiffGobsGcalc
G(r
) [Å
-2]
Samples of different nature – crystalline, nanocrystalline, amorphous solid and liquid – were selected to test the applicability of PDF analysis on a standard XRD system. The results of these experiments are described below.
Silicon carbide Figure 1a shows a diffraction pattern of silicon carbide powder in a capillary, together with a measurement of an empty capillary. The reduced structure function obtained from the corrected intensity data is shown in Figure 1b. After Fourier transformation the PDF as shown in Figure 2 was obtained. Figure 2b shows the short distances of the PDF in more detail. The maxima in this graph could be identified as the interatomic distances Si-C, Si-Si and C-C, derived from the sphalerite crystal structure of SiC [6]. The relation between the orientation and the interatomic distances in SiC is shown in Table 1.
Figure 1. (a) XRD measurement and (b) reduced structure function of silicon carbide
Figure 2. Experimental (circles) and calculated atomic PDF (red line) of SiC
SiC crystal structure
Table 1. Interatomic distances of SiC calculated determined from the experimental PDF (Fig.2)
(a)
(a)
(b)
(b)
Atoms Orientation Interatomic distance [Å]
Si - C ¼ <111> 1.89
Si - Si, C - C ½ <110> 3.08
Si - C ¼ <311> 3.61
Si - Si, C - C <100> 4.36
Si - C ¼ <331> 4.75
Si - Si, C - C ½ <211> 5.34
Variable counting time Measurements performed for PDF analysis typically require long-range scans up to high 2θ angles, where the diffracted intensities are low. Variable counting time (VCT) methods can be applied to spend longer counting times at the high-angle, low-intensity region of the diffractogram at the cost of time spent on the low-angle region. Schematically the redistribution of measurement times is shown in Figure 3. The total measurement time is the same for both situations. In order to investigate the improvement of data quality at high Q-values, measurements were performed on nanocrystalline anatase (TiO2) with an average particle size of 15 nm using constant and variable measurement times according to the scheme given in Figure 3. The resulting diffractograms and reduced structure functions are shown in Figure 4 and 5 respectively.
Figure 3. Constant counting time (left) and variable counting time (right) as a function of 2θ angle
Figure 4. XRD measurements on nanocrystalline anatase measured using (a) constant counting time and (b) variable counting time
Results and discussion ctd.
(b)
20 40 60 80 100 120 140
20 40 60 80 100 120 140
2theta [deg.]
0
50000
100000
150000
200000
Inte
nsi
ty [
cou
nts
]
2theta [deg.]
0
10000
20000
30000
Inte
ns
ity
[co
un
ts]
(a)
Figure 5. Reduced structure functions of anatase, measured using variable and constant counting times
The noise level at high Q-values of the variable counting time measurement is improved in comparison with the constant counting time measurement allowing the observation of additional structure-related features. No reduction in data quality has been observed in the low Q-range. The experimental PDF derived from the VCT experiment is in good agreement with the calculated PDF, as is shown in Figure 6.
Anatase - constant counting time
-5
0
5
10
0 5 10 15 20
Anatase - variable counting time
-5
0
5
10
0 5 10 15 20
F(Q
) [Å
-1]
F(Q
) [Å
-1]
G(r
) [Å
-2]
Radial distance [Å]
4
2
0-1
0 10 20 30 40
GdiffGobsGcalc
3
1
-2
-3
Figure 6. Experimental (circles) and calculated atomic PDF (red line) of nanocrystalline anatase
Focusing mirrors for high-energy X-rays (Ag and Mo)The graded multilayer focusing X-ray mirror is a beam conditioner, which is able to convert the divergent X-ray beam from a tube in line focus position to an intense monochromatic beam that is focused onto the goniometer circle.
Experimental configurations for PDF analysis using slit and mirror optics are graphically compared in Figure 7 and 8.
Results and discussion ctd.
Figure 8: configuration with a focusing X-ray mirror using convergent X-ray beam
Sample in horizontalorientation
Line- or pointdetector - X’Celeratoror scintillation counter
Line- or pointdetector - X’Celeratoror scintillation counter
Figure 7: standard configuration using divergent X-ray beam
The performance of the focusing X-ray mirror for diffraction measurements in transmission geometry (including PDF analysis) was tested using silicon powder (NIST SRM 640b) prepared in a 0.3 mm glass capilary. Experiments showed that the intensity and angular resolution of the diffraction data collected with the focusing mirror for Mo radiation are suitable for PDF analysis as well as traditional diffraction applications, such as phase analysis.
Results and discussion ctd.
Figure 9: silicon 640b: raw measurements. Data collected using a focusing mirror for Mo radiation (λ = 0.7093 Å)
Figure 10: experimental PDF of silicon (blue dots) compared with a calculated PDF using the known structure of Si (red line).
Figure 11: angular resolution is comparable to focusing mirror for Cu radiation.
10 20 30 40 50 60 70 80 90 100 110 120 130 1400
10000
40000
90000
160000
Inte
nsi
ty [
cou
tns] Experimental data
Empty capillary 0.3 mm
2theta [deg]
6000
4000
2000
Inte
nsi
ty [
cou
nts
]
21.6 21.7 21.8 21.9 22.0 22.1 22.2 22.3 22.4 22.5 22.6
21.9962 (°), 6800.6 (counts)
0.0474 (°)
2theta [deg]
10
5
0
-5
G(r
) (Å
-2)
Radial distance [Å]
10 20 30 40 50 60
GdiffGobsGcalc
-10
70
10 20 30 40 50 60 70 80 90 100 110 120 130 1400
10000
40000
90000
160000
Inte
nsi
ty [
cou
tns] Experimental data
Empty capillary 0.3 mm
2theta [deg]
6000
4000
2000In
ten
sity
[co
un
ts]
21.6 21.7 21.8 21.9 22.0 22.1 22.2 22.3 22.4 22.5 22.6
21.9962 (°), 6800.6 (counts)
0.0474 (°)
2theta [deg]
10
5
0
-5
G(r
) (Å
-2)
Radial distance [Å]
10 20 30 40 50 60
GdiffGobsGcalc
-10
7010 20 30 40 50 60 70 80 90 100 110 120 130 1400
10000
40000
90000
160000
Inte
nsi
ty [
cou
tns] Experimental data
Empty capillary 0.3 mm
2theta [deg]
6000
4000
2000
Inte
nsi
ty [
cou
nts
]
21.6 21.7 21.8 21.9 22.0 22.1 22.2 22.3 22.4 22.5 22.6
21.9962 (°), 6800.6 (counts)
0.0474 (°)
2theta [deg]
10
5
0
-5
G(r
) (Å
-2)
Radial distance [Å]
10 20 30 40 50 60
GdiffGobsGcalc
-10
70
Figure 12. XRD measurement of vanadium oxide xerogel using Mo radiation. Background intensity has been subtracted from the data.
Figure 13. Reduced structure function of vanadium oxide xerogel
Figure 14. Atomic PDF of vanadium oxide xerogel. Experimental (circles) and calculated (red line)
Vanadium oxide xerogelVanadium oxide xerogel (V2O5 nH2O) does not form crystals, that can be analyzed with the use of traditional crystallographic methods. The diffraction pattern (see Figure 12) only shows a combination of Bragg-like peaks and broad diffuse features. The reduced structure function is shown in Figure 13.The PDF, derived from the measurement was compared with the PDF obtained from a structure model described by Petkov et al. [8]. This model describes the crystallites consisting of bilayers of V2O5, made of square pyramidal VO5 units and separated by water molecules. PDF analysis in Figure 14 shows a good fit at distances in the intralayer region(r < 11 Å) and a not so good agreement in the interlayer region(r > 11 Å). The same observation by Petkov et al. [8] was attributedto the fact that the bilayer slabs are not perfectly stacked, but are turbostratically disordered.
Results and discussion ctd.
-2
2 6 10 14 184 8 12 16 20
0
2
4
6
-5
0 2 4 6 8 10 12 14 16
0
5
10
100
0 20 40 60 80 100 120 140
1000
10000
Inte
nsi
ty [
arb
. un
its]
F(Q
) [Å
-1]
G(r
) [Å
-2]
2theta [deg]
Scattering vector Q [Å-1]
Interatomic distance r [Å-1]
G(r
) [Å
-2]
Interatomic distance r [Å-1]
8
6
4
2
0
-2
-40 5 10 15 20
GtruncGdiffGcalc
-2
2 6 10 14 184 8 12 16 20
0
2
4
6
-5
0 2 4 6 8 10 12 14 16
0
5
10
100
0 20 40 60 80 100 120 140
1000
10000
Inte
nsi
ty [
arb
. un
its]
F(Q
) [Å
-1]
G(r
) [Å
-2]
2theta [deg]
Scattering vector Q [Å-1]
Interatomic distance r [Å-1]
G(r
) [Å
-2]
Interatomic distance r [Å-1]
8
6
4
2
0
-2
-40 5 10 15 20
GtruncGdiffGcalc
-2
2 6 10 14 184 8 12 16 20
0
2
4
6
-5
0 2 4 6 8 10 12 14 16
0
5
10
100
0 20 40 60 80 100 120 140
1000
10000
Inte
nsi
ty [
arb
. un
its]
F(Q
) [Å
-1]
G(r
) [Å
-2]
2theta [deg]
Scattering vector Q [Å-1]
Interatomic distance r [Å-1]
G(r
) [Å
-2]
Interatomic distance r [Å-1]
8
6
4
2
0
-2
-40 5 10 15 20
GtruncGdiffGcalc
Figure 16. Atomic PDF of fumed silica
Figure 1. Fumed silica powder prepared in a glass capillary
Amorphous solidsFumed silica powder was used as an example of applying PDF analysis to amorphous materials. Traditional structure analysis does not give much information; only a few ’humps‘ can be seen in the scan in Figure 15a. After calculating the reduced structure function in Figure 15b more structure can be observed.
PDF analysis of these data helps to reveal the short range order by determining average distances between the nearest neighbouring atoms.
The PDF in Figure 16 shows five clear peaks that could be determined as first and second order Si-Si, O-O or Si-O interatomic distances in silica as given by Mozzi and Warren [9].
Figure 15b. Reduced structure function calculated from the experimental data from Figure 15a.
Figure 15a. XRD measurement of fumed silica (red line) and empty glass capillary (blue line) performed with Mo radiation
-2
1
1
23 4 5
2 3 4 5 6 7 8
-1
0
1
2
3
4
5
-2
0 2 4 6 8 10 12 14 16
0
2
-1
1000 20 40 60 80 100 120 140
1000
10000
Inte
nsi
ty [
arb
. un
its]
F(Q
) [Å
-1]
G(r
) [Å
-2]
2theta [deg]
Scattering vector Q [Å-1]
Interatomic distance r [Å]
-2
1
1
23 4 5
2 3 4 5 6 7 8
-1
0
1
2
3
4
5
-2
0 2 4 6 8 10 12 14 16
0
2
-1
1000 20 40 60 80 100 120 140
1000
10000
Inte
nsi
ty [
arb
. un
its]
F(Q
) [Å
-1]
G(r
) [Å
-2]
2theta [deg]
Scattering vector Q [Å-1]
Interatomic distance r [Å]
-2
1
1
23 4 5
2 3 4 5 6 7 8
-1
0
1
2
3
4
5
-2
0 2 4 6 8 10 12 14 16
0
2
-1
1000 20 40 60 80 100 120 140
1000
10000
Inte
nsi
ty [
arb
. un
its]
F(Q
) [Å
-1]
G(r
) [Å
-2]
2theta [deg]
Scattering vector Q [Å-1]
Interatomic distance r [Å]
(a)
(b)
LiquidsAs in amorphous materials, liquids do not have a periodic arrangement of the atoms, and therefore no sharp diffraction maxima are observed in the diffractogram. Figure 18a shows the XRD measurement of tap water as an example. PDF analysis helps to observe the average distance betweens atoms.Calculation of the reduced structure function from this diffractogram reveals the structural information, as can be seen in Figure 18b.
The PDF in Figure 19 shows a relatively narrow peak for the first O-O distance (ca. 2.8 Å). The maxima for the second and third coordination spheres are less sharp. These results are in accordance with the synchrotron data reported by Hura et al. [10].
Figure 19. Atomic PDF of liquid water
Results and discussion ctd.
Figure 18b. Reduced structure function calculated from the experimental data from Figure 17a.
Figure 18a. XRD measurement of liquid water (red line) and empty glass capillary (blue line) performed with Mo radiation
-1
Inte
nsi
ty [
arb
. un
its]
F(Q
) [Å
-1]
G(r
) [Å
-2]
2theta [deg]
Scattering vector Q [Å-1]
Interatomic distance r [Å]
-31
1
2 3
2 3 4 5 6 7 8 9 10
-2
-1
0
1
2
3
4
-2
0 2 4 6 8 10 12 14 16
0
2
4
1000 20 40 60 80 100 120 140
1000
10000
-1
Inte
nsi
ty [
arb
. un
its]
F(Q
) [Å
-1]
G(r
) [Å
-2]
2theta [deg]
Scattering vector Q [Å-1]
Interatomic distance r [Å]
-31
1
2 3
2 3 4 5 6 7 8 9 10
-2
-1
0
1
2
3
4
-2
0 2 4 6 8 10 12 14 16
0
2
4
1000 20 40 60 80 100 120 140
1000
10000
-1
Inte
nsi
ty [
arb
. un
its]
F(Q
) [Å
-1]
G(r
) [Å
-2]
2theta [deg]
Scattering vector Q [Å-1]
Interatomic distance r [Å]
-31
1
2 3
2 3 4 5 6 7 8 9 10
-2
-1
0
1
2
3
4
-2
0 2 4 6 8 10 12 14 16
0
2
4
1000 20 40 60 80 100 120 140
1000
10000
(a)
(b)
Figure 20. Water sample prepared in a glass capillary
ConclusionResults of PDF analysis on a range of samples measured on a standard laboratory XRD system, equipped with an X-ray tube with a silver or molybdenum anode, were shown. Meaningful results were achieved, that allowed for comparison with data reported in literature. Empyrean allows performing experiments with both high-energy X-ray radiation and a wide 2θ measurement range and this permitted to obtain data with good quality up to scattering vectors of 17Å-1 (Mo anode) or 22Å-1 (Ag anode). Larger Q-vectors can be obtained by using X-rays with higher energy at synchrotron facilities although in practice values higher than 30 A-1 are rarely used.
The flexibility and the accessibility of the Empyrean system make it the ideal tool for preparation and pre-screening for valuable synchrotron beam time.
References1. J. te Nijenhuis, M. Gateshki, M. J. Fransen, Z. Kristallogr. Suppl. 2009, 30, 163.2. Billlinge, S.J.L., 2007, Z. Kristallog. Suppl., 26, 17.3. Egami, T & Billinge, S.J.L, 2003, Underneath the Bragg peaks: StructuralAnalysis of Complex Materials (Amsterdam, The Netherlands: ElsevierScience B.V.).4. Klug, H. P. & Alexander, L. E., 1974, X-ray Diffraction Procedures forPolycrystalline Materials (New York, NY, USA: Wiley).5. Farrow, C. L., Juhas, P., Liu, J. W., Bryndin, D., Bozin, E. S., Bloch, J.,Proffen, Th. & Billinge, S. J. L., 2007, J. Phys.: Condens. Matter, 19,335219.6. Petkov, V., 1989, J. Appl. Cryst., 22, 387.7. Braekken, H., 1930, Z. Kristallog, 75, 572-573.8. Petkov, V., Bozin, E., Billinge, S.J.L., Vogt, T., Trikalitis, P. & Kanatzidis, M.,2002, J. Am. Chem. Soc., 124, 10157.9. Mozzi, R.L. & Warren, B.E., 1969, J. Appl. Cryst., 2, 164.10. Hura, G., Sorenson, J., Glaeser, R.M. & Head-Gordon, T., 2000, J. Chem.Phys., 113, 9140.
AcknowledgementsThe authors gratefully acknowledge Prof. V. Petkov, Central Michigan University, Mt. Pleasant, MI, USA and Prof. B. Palosz, Institute of High Pressure Physics, Polish Academy of Sciences, Warsaw, Poland respec-tively for providing the vanadium oxide xerogel and silicon carbide samples described in this paper.
Alt
ho
ug
h d
ilig
ent
care
has
bee
n u
sed
to
en
sure
th
at t
he
info
rmat
ion
her
ein
is a
ccu
rate
, no
thin
g c
on
tain
ed h
erei
n c
an b
e co
nst
rued
to
imp
ly a
ny
rep
rese
nta
tio
n o
r w
arra
nte
e as
to
th
e ac
cura
cy, c
urr
ency
or
com
ple
ten
ess
of
this
info
rmat
ion
. Th
e co
nte
nt
her
eof
is s
ub
ject
to
ch
ang
e w
ith
ou
t fu
rth
er n
oti
ce.P
leas
e co
nta
ct u
s fo
r th
e la
test
ver
sio
n o
f th
is d
ocu
men
t o
r fu
rth
er in
form
atio
n. ©
PA
Nal
ytic
al B
.V. [
2009
]
Prin
ted
in T
he
Net
her
lan
ds
on
50%
rec
ycle
d, c
hlo
rin
e-fr
ee p
aper
. 949
8 70
2 15
512
PN
7258
PANalytical PANalytical is the world’s leading supplier of analytical instrumentation and software for X-ray diffraction (XRD) and X-ray fluorescence spectrometry (XRF), with more than half a century of experience. The materials characterization equipment is used for scientific research and development, for industrial process control applications and for semiconductor metrology. PANalytical, founded in 1948 as part of Philips, employs around 900 people worldwide. Its headquarters are in Almelo, the Netherlands. Fully equipped application laboratories are established in Japan, China, the USA, and the Netherlands. PANalytical’s research activities are based in Almelo (NL) and on the campus of the University of Sussex in Brighton (UK). Supply and competence centers are located on two sites in the Netherlands: Almelo (development and production of X-ray instruments) and Eindhoven (development and production of X-ray tubes). A sales and service network in more than 60 countries ensures unrivalled levels of customer support. The company is certified in accordance with ISO 9001:2000 and ISO 14001.
The product portfolio includes a broad range of XRD and XRF systems and software widely used for the analysis and materials characterization of products such as cement, metals and steel, nanomaterials, plastics, polymers and petrochemicals, industrial minerals, glass, catalysts, semiconductors, thin films and advanced materials, pharmaceutical solids, recycled materials and environmental samples.
Visit our website at www.panalytical.com for more information about our activities.
PANalytical is part of Spectris plc, the precision instrumentation and controls company.
PANalytical B.V.Lelyweg 1, 7602 EA AlmeloThe NetherlandsT +31 (0) 546 534 444F +31 (0) 546 534 [email protected]
Regional sales offices
AmericasT +1 508 647 1100 F +1 508 647 1115
Europe, Middle East, AfricaT +31 (0) 546 834 444 F +31 (0) 546 834 499
Asia PacificT +65 6741 2868 F +65 6741 2166
Global and near