orientation imaging microscopy (oim) - some case studies
DESCRIPTION
ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES. EML 5930 (27-750) Advanced Characterization and Microstructural Analysis A. D. Rollett, P.N Kalu, D. Waryoba Spring 2006. OUTLINE. REVIEW OF OIM CASE STUDIES - PowerPoint PPT PresentationTRANSCRIPT
![Page 1: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/1.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
1
ORIENTATION IMAGING MICROSCOPY (OIM)
- SOME CASE STUDIES
EML 5930 (27-750)
Advanced Characterization and Microstructural Analysis
A. D. Rollett, P.N Kalu, D. Waryoba
Spring 2006
![Page 2: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/2.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
2
OUTLINE REVIEW OF OIM
CASE STUDIES
Development of Polishing Technique For OIM Study of
Heavily Deformed OFHC Copper
Recrystallization in Heavily Deformed OFHC Copper
Heavily Deformed Cu-Ag
Deformed and Annealed OFHC Copper
Deformed and Annealed Cu-Nb
Other Examples
![Page 3: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/3.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
3
INTRODCUTION TO OIM - Diffraction
Diffraction of inelastically scattered electrons by lattice planes (hkl) according to Bragg’s law:
Sections of a pair of Kossel cones form a pair of parallel straight Kikuchi lines on the flat phosphor screen.
For maximum intensity, the specimen surface is steeply tilted at an angle of 20°-30° from grazing incidence.
![Page 4: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/4.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
4
INTRODCUTION TO OIM - EBSP formation
![Page 5: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/5.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
5
INTRODCUTION TO OIM - Data acquisition
![Page 6: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/6.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
6
TECHNIQUE DEVELOPMENT
![Page 7: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/7.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
7
TECHNIQUE DEVELOPMENT
(a) OIM grain boundary map and (b) EBSD patterns
EBSPs from a sample prepared by standard metallographic technique: Polished
![Page 8: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/8.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
8
TECHNIQUE DEVELOPMENT
(a) OIM grain boundary map and (b) EBSD patterns
(b)(a)
EBSPs from a sample prepared by standard metallographic technique: Polished + etched
![Page 9: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/9.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
9
TECHNIQUE DEVELOPMENT
(a) OIM grain boundary map and (b) EBSD patterns
(b)(a)
EBSPs from a sample prepared by Novel technique - Polished + Etched + Polished
![Page 10: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/10.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
10
Image Quality
Image Quality
Confidence Index
Confidence Index
![Page 11: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/11.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
11
TECHNIQUE DEVELOPMENT
IPF of wire drawn OFHC copper deformed to = 3.2, obtained via (a) OIM and (b) X-ray diffraction techniques
CONCLUSIONS Polishing by the novel technique, which consists
of polishing+etching+polishing, produced high
quality EBSPs leading to excellent OIM image.
IPF from OIM were consistent with the IPF from
X-ray diffraction
![Page 12: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/12.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
12
Rex in HEAVILY DEFORMED OFHC COPPER
![Page 13: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/13.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
13
Rex in HEAVILY DEFORMED OFHC COPPER
Optical micrograph showing microstructure after deformation to = 3.2, = 405 MPa. Arrows show pockets of recrystallized grains.
Microstructure
Optical micrograph showing microstructure after deformation to = 1.3, = 392 MPa. No recrystallization
![Page 14: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/14.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
14
Rex in HEAVILY DEFORMED OFHC COPPER
OIM map showing grain orientations at (a) p = 2.3, UTS = 411.5 MPa, and (b) p = 3.2, UTS = 405 MPa. The lines represent high angle boundaries, with misorientation > 15o.
U
X
V
Y
W
DD
(b)(a)
![Page 15: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/15.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
15
Rex in HEAVILY DEFORMED OFHC COPPER
![Page 16: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/16.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
16
1
10
1112
13
<313>85°{184}<-12 17 2>
<12-6>40°{-4-19}<-46-3>
<213>75°{-3 11 6}<-65-2>
<1-1-3>48°{-8713}<25-3>
<1-21>26°{-212}<-34-5>
<112>54°{-265}<-12 22 –7>
<-4-13>45°{1 11 18}<7 29 2>
<-1-12>60°{198}<12 23 2>
<1-1-1>64°{-201}<23-8>
<144>60°{-6 13 5}<-24-2>
<-1-15>56°{-2 14 23}<13 11 –1><-211>63°
{3-4 11}<6 10 3>
<112>65°
<-210>36°
<-210>32°
<133>65° <4-2-1>42° <313>66°
<-1-12>60°
<2-1-2>52°<2-1-1>65°
<2-1-3>55°
![Page 17: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/17.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
17
Rex in HEAVILY DEFORMED OFHC COPPER
OIM map showing grain orientations after deformation to p = 3.6, UTS = 390.5 MPa.
![Page 18: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/18.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
18
Color Key
![Page 19: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/19.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
19
Sh/B in HEAVILY DEFORMED OFHC COPPER
1
2
OIM maps of a heavily drawn Cu ( = 3.2) showing regions of shear bands.
Shaded IQ map of a heavily drawn Cu ( = 3.2) showing regions of shear bands.
![Page 20: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/20.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
20
![Page 21: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/21.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
21
Rex in HEAVILY DEFORMED OFHC COPPER CONCLUSION
Three regions were identified: Low processing strain < 2.5: No recrystallization,
elongated structure.
Intermediate strain 2.5 < < 3.2: Nucleation of recrystallization, shear bands formation. Shear bands occurred in grains with S{123}<634> orientation, and were inclined at 54° to the drawing direction. Their misorientation was between 5°s10°.
High strain > 3.2: Extended recrystallization, recrystallized grains were mainly of Cube {001}<100> and S{123}<624> orientations.
OIM proved to be a viable tool in the study of heavily deformed materials.
![Page 22: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/22.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
22
HEAVILY DEFORMED Cu-Ag
![Page 23: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/23.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
23
Optical micrograph of a heavily drawn CuAg ( = 3.2) showing regions of shear bands.
Shaded IQ map of a heavily drawn CuAg ( = 3.2) showing regions of shear bands.
HEAVILY DEFORMED CuAg
![Page 24: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/24.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
24
HEAVILY DEFORMED Cu-Ag
1
2
OIM maps of a heavily drawn CuAg ( = 3.18) showing regions of shear bands. The Grain boundaries were constructed with a misorientation criteria of 15°.
![Page 25: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/25.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
25
DEFORMED AND ANNEALED OFHC COPPER
![Page 26: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/26.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
26
ANNEALED OFHC COPPER - Microstructure
(a) Optical micrograph of annealed Cu, p = 3.1, 350°C
(a) Optical micrograph of annealed Cu, p = 3.1, 750°C
![Page 27: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/27.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
27
ANNEALED OFHC COPPER
OIM tiled IPF map showing grain orientations for Cu wire drawn to a strain of 3.1 and annealed at 250°C for 1 hr.
![Page 28: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/28.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
28
Color Key
![Page 29: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/29.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
29
ANNEALED OFHC COPPER
OIM tiled IPF map showing grain orientations for Cu wire drawn to a strain of 3.1 and annealed at 300°C for 1 hr.
![Page 30: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/30.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
30
ANNEALED OFHC COPPER
OIM tiled IPF map showing grain orientations for Cu wire drawn to a strain of 3.1 and annealed at 500°C for 1 hr.
![Page 31: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/31.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
31
ANNEALED OFHC COPPER
OIM tiled IPF map showing grain orientations for Cu wire drawn to a strain of 3.1 and annealed at 750°C for 1 hr.
![Page 32: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/32.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
32
ANNEALED OFHC COPPER: OIM-IPF
(a) Deformed Cu, p = 2.3 (b) Deformed Cu, p = 3.1
![Page 33: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/33.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
33
(a) Annealed Cu, p = 3.1, 250°C (b) Annealed Cu, p = 3.1, 300°C
(c) Annealed Cu, p = 3.1, 500°C (d) Annealed Cu, p = 3.1, 750°C
![Page 34: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/34.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
34
DEFORMED AND ANNEALED Cu-Nb/Ti
![Page 35: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/35.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
35
DEFORMED AND ANNEALED Cu-Nb/Ti
SEM micrograph of a heavily drawn Cu-Nb ( = 3.2) annealed at 500°C.
SEM micrograph of a heavily drawn Cu-Nb ( = 3.2) showing elongated Cu and Nb phases.
![Page 36: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/36.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
36
DEFORMED AND ANNEALED Cu-Nb/Ti
Annealed CuNb, p = 3.1, 250°C
(Nb phase extracted)
![Page 37: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/37.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
37
DEFORMED AND ANNEALED Cu-Nb/Ti
Annealed CuNb, p = 3.1, 300°C
![Page 38: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/38.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
38
DEFORMED AND ANNEALED Cu-Nb/Ti
Annealed CuNb, p = 3.1, 500°C
![Page 39: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/39.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
39
DEFORMED AND ANNEALED Cu-Nb/Ti
Annealed CuNb, p = 3.1, 750°C
![Page 40: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/40.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
40
Other Examples
![Page 41: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/41.jpg)
FAMU-FSU College of EngineeringDepartment of Mechanical Engineering
41
![Page 42: ORIENTATION IMAGING MICROSCOPY (OIM) - SOME CASE STUDIES](https://reader035.vdocuments.us/reader035/viewer/2022062315/56815702550346895dc4a81a/html5/thumbnails/42.jpg)