Modipur US 569 B Isocyanate US 13 Core Foam System
Product Data Description Modipur US 569 B / US 13 is a CFC-free foam system used for making low density ski/snowboard cores. It has excellent flowing properties under suitable processing conditions. It can also be used as a core in sandwich constructions or as block foam. Mix ratio 100 parts by weight component 1 (polyol) 170 parts by weight component 2 (isocyanate) Processing data The two components can be processed on conventional high and low pressure foaming machines. To improve the flowing properties of the reacting foam-mixture and to achieve an even cellular structure of the foam, sufficient air nucleation in the raw materials, preferably by using a suitable air nucleation device, has to be ensured prior to processing. Component 1 (polyol) has to be homogenized prior to use (approx. 10 min, 1000 - 2000 rev./min). In the machine tank component 1 has to be homogenized continually (approx. 60 rev./min). Processing temperatures
Raw materials 20 30 C component 1 (polyol) 20 30 C component 2 (isocyanate)
Mould 45 - 60 C Reaction times hand mix
starting time sec 60 5 setting time sec 240 6
density, free rise kg/m 100 5 density, mould-foamed 150 300
Mould release properties After processing in tempered metal moulds (45 - 60 C) mouldings can be released after 8 min (10 mm wall-thickness, density 300 kg/m).
-
Modipur US 569 B
Properties
Nominal Density
ASTM D-1622
kg/m3
150 Compression Strength
ASTM B-1621
Mpa
2,05
Compression Modulus
ASTM B-1621
Mpa
77
Tensile Strength
ASTM B-1623
Mpa
1,26
Tensile Modulus
ASTM B-1623
Mpa
94
Shear Strength
ASTM C-273
Mpa
1,02
Shear Modulus
ASTM C-273
Mpa
35
Shear Elongation
ASTM C-273
%
3,7
Heat Distortion
C
170
Thermal Conductivity
W/mK
0,03-0,04
Colour
beige or black
Storage If protected from moisture and kept at a temperature of 20 -24 C in closed containers the raw materials are stable for 6 months after delivery. Component 2 (isocyanate) is prone to partial crystallization at temperatures below 5 C. The product can be brought back into the liquid state by careful warming of the entire content up to a maximum of 70 C. After warming the sediment content in the container may have increased, but will not affect the quality of the foam. Safety Precautions during Processing The system contains a small percentage of amines and 4,4'diphenylmethane-diisocyanate. When the raw materials come into direct contact with the skin irritation may occur. Always wear safety goggles and protective gloves (rubber or PVC) when working with the system. Splashes on the skin must be wiped off, and the contaminated areas must be thoroughly washed with soap and water. Subsequently these areas should be treated with a good barrier cream. Splashes in the eyes must be removed immediately by careful and thorough rinsing with plenty of water. A doctor should then be consulted. Contaminated clothing must be changed immediately. The material must be kept away from foodstuffs.
-
Modipur US 569 B
Important All information is believed to be accurate but is given without acceptance of liability. All users should make their own assessment of the suitability of any product for the purposes required. All sales are made subject to our standard terms of sale which include limitations on liability and other terms.
Copyright Hexcel Corporation E US 569B / 13 May 09
For More Information Hexcel is a leading worldwide supplier of composite materials to aerospace and other demanding industries. Our comprehensive product range includes: Carbon Fibre Structural Film Adhesives RTM Materials Honeycomb Sandwich Panels Honeycomb Cores Engineered Core Carbon, glass, aramid, and hydbrid prepregs Reinforcement Fabrics HexTOOL composite tooling material For US quotes, orders and product information call toll-free 1-800-688-7734 For other worldwide sales office telephone numbers and a full address list please go to: http://www.hexcel.com/contact/salesoffices Fr US Angebote, Bestellungen und Produktinformationen bitte rufen Sie gebhrenfrei 1-800-688-7734. Fr Informationen ber unsere weiteren Verkaufsbros weltweit besuchen Sie unsere Website: http://www.hexcel.com/contact/salesoffices
DescriptionMix ratioProcessing dataProcessing temperaturesReaction timeshand mix
Mould release propertiesPropertiesStorageSafety Precautions during ProcessingImportant