materials of carbon and graphite

Carbon - Graphite Materials

Chemical FormulaC

Topics CoveredIntroduction

Types of Carbon

Amorphous Carbon

Graphite

Carbon-Graphites

Processing Carbon-Graphites

Carbon-Graphites vs Traditional Lubricants

Chemically Aggressive Environments

High Load Applications

Design Factors

Carbon-Graphite Seals

Impregnation of Carbon-Graphite Seals

Blistering

Carbon-Graphite Seals in Aerospace Applications

Materials Selection and Suitability

IntroductionCarbon-graphites offer the design engineer a unique family of mechanical materials. Manufactured entirely from

carbon and including high temperature carbonaceous bonding, these materials combine the strength, hardness

and wear resistance of carbon with the corrosion resistance and self lubricating properties of graphite. The

precisely controlled inherent porosity of carbon-graphites can be filled with a variety of impregnants to enhance

chemical, mechanical and tribological properties.

Types of Carbon

The terms ‘carbon’ and ‘graphite’ are often used interchangeably. This is unfortunate since each form of the

element carbon offers specific properties that can be used to benefit different types of applications.

Amorphous Carbon

Amorphous carbon is a very hard, strong compound. The crystals exhibit a turbostratic disorder which makes the

material extremely resistant to wear. The strength and wear resistance properties of this material make it of

interest in some applications. However, these strengths can also be a weakness -carbon generates high friction

when rubbed against another surface.

Graphite

Graphite, on the other hand, is softer and relatively weak because of the crystalline order and closer spacing

between the monoplanes and stacks. A graphite structure can be compared to a deck of cards with individual

layers able to easily slide off the deck. This phenomenon gives the material a self lubricating ability which is

matched by no other material. External lubricants are simply not necessary.

Carbon-Graphites

It is possible to combine amorphous carbon and graphite to take full advantage of the strengths and weaknesses

of each of these two types of carbon, table 1. The proper mixture of the two materials is strong and hard and has

low friction. At the same time, this composite has excellent corrosion resistance and is capable of operating at


Saved from URL: http://www.azom.com/article.aspx?ArticleID=516P

/51

http://www.azom.com/article.aspx?ArticleID=516

temperatures in excess of 315°C for extended periods of time, depending on the specific grade. The ability to

create materials that have these properties is the basis of the manufactured mechanical carbon materials that

perform well in difficult tribological situations such as pumps.

Table 1. Properties of typical carbon and graphite materials.

Carbon

100%

Carbon-graphite

(70%-30%)

Carbon-graphite

(30%-70%)

Graphite

100%

Apparent density

(g.cm-3)1.70 1.72 1.75 1.80

Hardness 100 85 65 40

Compressive strength

(MNm-2)300 208 145 55

Flexural strength

(MNm-2)62 62 52 28

Modulus of elasticity

(GNm-2)21 17 14 10

Thermal conductivity

(W/m.°C)5 9 12 85

Temp limit in air (°C) 315 315 315 455

Processing Carbon-Graphites

Carbon-graphites are created by combining the two forms of carbon with coal tar pitch. The coal tar pitch acts as

a temporary binder that holds the two structures together during the compression moulding process in which near

net shapes are formed. Following the moulding operation, the parts are sintered at temperatures high enough to

carbonise the coal tar pitch. The result is a structure that is completely carbon bound and contains both carbon

and graphite. This structure is extremely strong in compression and will not creep under load. The carbonisation

of the temporary binder leaves holes in the structure - on a micro scale the sintered body is a black sponge.

The formation of holes during the processing of a carbon-graphite composite has various advantages. The holes

can be filled with resins, metals, carbon, or inorganic salts, depending on the planned use of the material, table 2.

These fillers serve to improve the strength, thermal conductivity and tribological characteristics of the material.

Additionally, carbon-graphite can be sintered to an even higher temperature to convert the entire structure to

graphite to provide especially good performance in very high temperature, high speed applications.

Impregnation Application

Thermoset resin General duty to 260°C in water, coolants, fuels, oils.

Light chemical solutions, food and drug.

Antimony Hot water, steam, light hydrocarbons.

Copper or silver High pressure service to 20.7MNm-2.

Carbon Highly corrosive environments.

Film formers (fluorides etc) Extremely dry environments, vacuum or cryogenic.

Oxidation inhibitors (phosphates etc) High temperature and/or high speed (to 538°C and

240ms-1).

Carbon-Graphites vs Traditional Lubricants

Carbon-graphites are used in a wide range of applications where traditional lubricating methods are not

appropriate. For example, a typical oil lubricated bearing struggles at temperatures below -40°C because of the

high viscosity of the oil. Above 200°C oils carbonise, making them abrasive and ineffective. Graphite bearings are

capable of extended use at temperatures above 600°C.

Chemically Aggressive Environments

Chemically aggressive applications represent another application niche for carbon-graphite. For instance,



/52


sterilisation processes tend to leach the oil from the structure of an oil lubricated bearing. Also, solvents and

radiation can break down lubricating oils, and low pressures can cause the oil to vaporise. Carbon-graphite

materials are inherently stable and chemically resistant, making them ideally suitable for these types of

application, figure 1.

Figure 1. Inside of a pump. The four vanes on the rotor are made of carbon-graphite, and are consequently self

lubricating, temperature resistant and impermeable to gases and liquids.

High Load Applications

Lubricants are inappropriate in other applications for a variety of reasons. High loads can squeeze the lubricant

from a surface. Without the hydrodynamic layer of lubricant, failure is imminent if the material cannot provide self

lubrication. In some applications, such as those involving food handling, lubricants can contaminate the

surrounding environment. Specific grades of carbon-graphites are approved for use in food handling applications.

Design Factors

Carbon-graphite bearings are used in both wet and dry operating conditions. Carbon-graphite allows the designer

to specify the bearing close to the boundary lubricated condition without the risk of seizure. Permissible loads and

running speeds depend on the allowable wear rate. Shaft materials and surface finishes are important factors in

the wear rates of carbon-graphite materials. As a rule of thumb, the harder and more polished the surface, the

lower the wear. Where possible, aluminium and bronze should be avoided for use as shaft materials.

Carbon-graphite materials are also widely used as rotating shaft and face seal materials, figure 2. They perform

well when running against metal and ceramic counterfaces. Seals are manufactured from solid rings, split rings

and segmented rings for use in both liquid and dry-running applications in the aerospace, nuclear, petrochemical

and general marine industries.



/53


Figure 2. Carbon-graphite seals are self lubricating, resistant to chemical corrosion, and capable of running at

temperatures up to 538°C.

Carbon-Graphite Seals

Seal materials require high strength and a relatively high modulus of elasticity to withstand deformation at the

interface. Carbon-graphite seal materials provide the strength and rigidity which are especially important in high

pressure, zero leakage mechanical end-face seals. High thermal conductivity is essential in removing heat from

the interface.

Seal wear is a result of adhesive wear, chemical wear, erosive wear and sometimes radioactive wear.

Carbon-graphite is inert to most chemical reagents so it survives where other materials fail. However, chemical

wear is evidenced in certain strong oxidising environments or where the additives are attacked by specific

oxidising reagents.

Impregnation of Carbon-Graphite Seals

Impregnation of carbon seals can be done with a variety of materials to control permeability. In addition to

thermoset resins, other types of impregnants include thermoplastics, metals, and inorganic salts or glasses. The

temperature limit of the impregnant places an upper limit on the operating temperature of the carbon parts.

Metals such as antimony, silver, copper, nickel, and babbitt can improve the strength, thermal conductivity, and

tribological characteristics of the materials. Impregnants made of inorganic salts usually phosphate or borate -

and glasses are used in high temperature applications. Carbons impregnated with soluble salts must be handled

carefully to avoid exudation, especially under humid conditions, but loss of impregnant rarely affects any physical

property of a seal other than permeability.

Blistering

Blistering is a critical concern with carbon seal materials. Strangely, the reason why blistering occasionally occurs

is not clear. One of the most popular explanations is that a certain amount of fluid becomes absorbed in the

carbon substrate and expands due to frictional heat, creating a subsurface pressure and eventual crater in the

seal face. Another theory is that softer mating materials can tend to tear pieces from the carbon-graphite in the

presence of heavy hydrocarbons. Blistering is most often found in applications involving hydrocarbons or cyclical

temperature service such as air conditioning compressors. In some cases, the use of silicon carbide as a mating

surface will reduce or even eliminate a blistering problem, possibly because of its high thermal conductivity and

hardness.

Carbon-Graphite Seals in Aerospace Applications



/54


Carbon-graphite and graphites are excellent materials for aircraft turbine engine mainshaft seals. The mainshaft

in a turbine engine rotates at very high speeds and operates in an environment of changing high temperature

conditions. Mainshaft bearing compartment seals are used to protect rotor support bearings from hot gases

flowing through the engine and to prevent the loss of lubricant in the bearing compartments.

Materials Selection and Suitability

Loads, speeds, temperatures, mating materials, cost constraints and projected volume are critical factors to be

kept in mind when selecting materials. Scores of base carbon materials are available with hundreds of

modifications that can be customised for specific designs and environments. General service carbon-graphites are

usable up to 260°C while special grades are available that provide resistance up to 538°C. Special carbons and

impregnants are used for seal applications in the 260-538°C temperature range.

These materials are chemically inert, temperature resistant, lightweight, resilient, dimensionally stable, and

impermeable to gases and liquids. They can be moulded to size or machined to close tolerances, impregnated,

plated, vulcanised to rubber, and cemented or shrunk into housings or retainers - a truly versatile set of

materials.

Primary author: Joe Boylan

Source: Materials World, Vol. 4, no. 12 pp. 707-8, December 1996.

For more information on Materials World please visit The Institute of Materials.

Date Added: May 29, 2001