Magnetization Switching Using Spin Orbit Torques from Sputtered Conductive WTex
Xiang (Shaun) Li,
Mahendra DC, Chong Bi, and S. X. WangMaterials Science and Engineering, Electrical Engineering
Peng Li, Yuri SuzukiApplied Physics
Stanford University
2019 E3S Annual RetreatUniversity of California, Berkeley, September 19-20, 2019
A Science & Technology Center
9/19/2019 Page 2
0.1
1
10
100
1000
10000
Read time (ns)
Write time (ns)
Cell size (F2)Read energy (fJ)
Write energy (fJ)
SRAMeDRAMDRAMSTT-MRAMFeFETReRAMPCM
Xiang Li, Kang L. Wang, et al., MRS Bulletin, vol. 43, pp. 970-977, 2018.
S. Salahuddin, K. Ni, and S. Datta, Nature Electronics, vol. 1, pp. 442-450, 2018.
Standby Power
Limited Endurance
Comparison of Existing and Emerging Memories
A Science & Technology Center
SOT-MRAM Towards SRAM Performance
Page 39/19/2019
Bit switching energy estimates:
~250 fJ @ 110 nm
Scaling down possibility:
~10 fJ @ 22 nm ~0.5 fJ @ 5 nm
Sato, Wang, et al., Nature Electronics, 1(9), 508, 2018
A Science & Technology Center
Leverage New Physics for More Efficient Write
Page 49/19/2019
http://www.cpfs.mpg.de/2520563/Dirac-semimetal_-Transport-by-massless-fermionsJ. Phys. Soc. Jpn. 87, 041002 (2018)https://www.eecs.mit.edu/node/6509
A Science & Technology Center
Topological Insulator and Weyl Semimetals
Page 59/19/2019
https://www.eecs.mit.edu/node/6509
K. Kuroda, et al., Physical Review B, vol. 94, Nov 18 2016.
โข High resistivity of topological insulators lowers overall on/off ratio (over 4000 ๐ฮฉ cm for 5 nm films)
โข Weyl semimetals are promising candidates, for example WTe2
A Science & Technology Center
Sputtered Weyl Semimetal WTex
Page 69/19/2019
100 150 200 250
0
100
200
300
400
500
600 A10
1 A4
276.9 nm
76.9 nm
36.4 nm
36.4 nm
27.6 nm
A5
2A
6
1
A9
1 A2
1
Inte
nsity (
arb
itra
ry u
nit)
Raman shift (cm-1)
A5
1
27.6 nm
Y. C. Jiang, J. Gao, and L. Wang, Scientific
Reports, vol. 6, p. 19624, 01/22/online 2016.
โข Sputter deposition desired for industry adoptionโข Signature Raman peaks of sputtered WTe2
Xiang Li, Shan Wang, et al., in preparation
A Science & Technology Center
High Resolution TEM Analysis
Page 79/19/2019
โข TEM shows W:Te ratio of 1:1.34 with visible WTex grains/clusters
Xiang Li, Shan Wang, et al., in preparation
A Science & Technology Center
Low Frequency Current Induced Resistance Change
Page 89/19/2019
โข Charge-to-spin conversion efficiency characterized using harmonic current induced magnetization oscillation
โข HDL is the damping-like effective field that drives switching
CoFeB
HDL
Mo
damping-like effective field
H
V
๐ฐ๐๐๐(๐๐)๐
x
y Raw data
Fitted data
-6000 -3000 0 3000 6000-15
-10
-5
0
5
10
15
= 45o
R x
y
2 (
m
)H (Oe)
I = 0.5 mA
Q Shao, Kang Wang et al., 2018 IEDM
๐ 2๐ = ๐ ๐๐ป๐น๐ฟ๐ป๐๐ฅ๐ก
๐๐๐ 2๐๐๐๐ ๐ +๐ ๐ด2
๐ป๐ท๐ฟ๐ป๐๐ฅ๐ก โ ๐ป๐พ
+ ๐ ๐กโ ๐๐๐ ๐
Xiang Li, Shan Wang, et al., in preparation
A Science & Technology Center
Charge-to-Spin Conversion Efficiency
Page 99/19/2019
โข Mo between WTe2 and CoFeB partially absorb spin-polarized electronsโข Real ๐๐๐ value of WTe2 should be larger ๐๐๐ =
2๐๐๐๐ก๐ถ๐๐น๐๐ตโ
๐ป๐ท๐ฟ๐ฝ๐๐๐2Xiang Li, Shan Wang, et al., in preparation
0.0 0.5 1.0 1.5 2.00
2
4
6
8
10
WTeX(5)/Mo(1)/CoFeB(1)
Mo(6)/CoFeB(1)
Linear Fit
Linear FitHD
L (
Oe)
I (mA)
ST= 0.50 0.03
WTeX
ST = 0.039 0.002Mo
A Science & Technology Center
Unidirectional Spin Hall Magnetoresistance (USMR)
Page 109/19/2019
โข Spin currents interaction with magnetization affects interface scattering, thus changes longitudinal resistance
-15 -10 -5 0 5 10 15
-10
-5
0
5
-5000 0 5000-4
-2
I = 0.7 mA
R x
x
2
(m
)
Hy (Oe)
C. O. Avci et al., Nature Physics, vol. 11, p. 570, 2015.
Xiang Li, Shan Wang, et al., in preparation
A Science & Technology Center
Current-Induced Field-Free Switching
Page 119/19/2019
โข Switching current density in WTex 0.77-1.41 MA/cm2
-15 -10 -5 0 5 10 15
-10
-5
0
5
-5000 0 5000-4
-2
I = 0.7 mA
R x
x
2
(m
)
Hy (Oe)
-8 -4 0 4 8
-10
-5
0
5
Ipulse
(mA)
R x
x
2
(m
)
- My initialization
My initialization
H = 0
tpulse
= 1 ms
Xiang Li, Shan Wang, et al., in preparation
A Science & Technology Center
Resistivity (๐ฮฉ โ ๐๐)
๐ ๐๐
0.1
1
10
100
100 1000 10000
Benchmark: Power Efficiency of SOT-MTJ Cell
Page 129/19/2019
Physical Review Applied, vol. 10, Sep 6 2018.
Assumes 6 nm SOT write line under 1 nm in-plane CoFeB.
Resistivity (๐ฮฉ ๐๐)
Pow
er
1
10
100
100 1000 10000
435.2
300
713
12000
Sputtered WTex
Sputtered WExfoliated WTe2*Sputtered BiSex**
Xiang Li, Shan Wang, et al., in preparation
*Yang et al., Nature
Nano, 2019.
**Wang et al.,
Nature Materials,
2018.
A Science & Technology Center
High Frequency Current Induced Magnetic Resonance
2018 NSF Site Visit Page 139/19/2019
โข Fitted resonance peak with symmetric and asymmetric Lorentzian line shapes
๐ =
Luqiao Liu, et al., PRL 106, 036601 (2011)
Raw data
Fitted Data
Symmetric Lorentzian
Asymmetric Lorentzian
200 300 400
0.0
1.0ยต
2.0ยต
3.0ยต
WTeX
Vm
ix (
V)
H (Oe)
f = 5 GHz
t = 58.2 nm
ST = 0.82
Xiang Li, Shan Wang, et al., in preparation
A Science & Technology Center
Conclusions
โข MRAM holds great promise to replace or complement SRAM for data-centric applications as high-density on-chip memory
โข Unique topological band structure gives rise to highly spin polarized electrons in Weyl semimetal WTe2
โข Sputtered 5 nm WTex at room temperature shows attractive charge-to-spin conversion efficiency (0.5), low switching current density (1 MA/cm2), and low thin film resistivity (570 ๐๐โ ๐๐)
โข Greatly improved energy/delay performance compared with other topological materials such as BiSe or exfoliated WTe2
โข Even larger charge-to-spin conversion efficiency up to 0.8
Page 159/19/2019