Anisotropic Kondo Effect in a 3d transition metal compoundAhmad Us Saleheen1 , Tapas Samanta1, Daniel L. Lepkowski1, Alok Shankar1, Joseph Prestigiacomo1, Igor Dubenko2, Abdiel Quetz2, Iain W. H. Oswald3, Gregory T.
McCandless3, Julia Y. Chan3, Philip W. Adams1, David P. Young1, Naushad Ali2, and Shane Stadler1
1Department of Physics & Astronomy, Louisiana State University, Baton Rouge, LA 70803 2Department of Physics, Southern Illinois University, Carbondale, IL 62901 3Department of Chemistry, The University of Texas at Dallas, Richardson, TX 75080
Abstract
Background
Results Results Results
Conclusion
OPTIONAL
LOGO HERE
We report an anisotropic Kondo effect in purely 3d
transition metal ferromagnetic (FM) system (i.e., not rare-
earth-based). The isostructural alloying of two compounds
having collinear magnetic structure has resulted in a FM
Kondo lattice system, Mn1-xFexCoGe in the proximity of a
noncollinear FM state with x = 0.2. Resistivity, magnetic
susceptibility and heat capacity studies on single crystal
sample indicate that the Kondo effect is anisotropic. An
increase in resistivity along two principal direction at low-
temperature has been observed with the decrease in T,
which follows a lnT behavior below the Kondo minimum
(TK) due to Kondo scattering. However, TK along i∥c is
about two times higher than that of along i⊥c. Directional
dependence of magnetization also mimics the similar
behavior by showing pronounced Kondo screening along
c-axis. Large saturation magnetization at low-temperature
indicates that it is a underscreened Kondo Effect.
Underscreening of moments may lead to the coexistence
of FM and Kondo behavior.
For x=0.2 composition Kadowaki-Woods ratio of
𝐴 𝛾2~43 μΏ.cm.mol2.K2.J-2 was observed. This
indicates strong electron correlation in
Mn1-xFexCoGe system. According to Rhodes-
Wohlfarth model large PC/MS value indicates
itinerant behavior (Rhodes and Wohlfarth,
Proc.Roy.Soc.London 273,247, 1963). We can see
a transition to more itinerant behavior with the
increase in Fe content. At x=0.2 composition, a
transition from localized to itinerant behavior is
expected (Samanta et
al.,Appl.Phys.Lett.103,042408, 2013).
Resistivity:
We observed an increase in ρ at low temperature
with the decrease in T. It follows a lnT behavior
below the Kondo minimum due to Kondo
scattering (inset).
TK along i∥c is around two times greater than that of
along i⊥c. This behavior may indicate a more
pronounced Kondo behavior along c axis.
Magnetization:
Structure:
Single crystals of Mn0.8Fe0.2CoGe were grown using Sn flux.
XRD data indicates a Ni2In type hexagonal structure. Lattice
parameters are: a=4.06 A0 and c= 5.20A0 .
Strong anisotropy in both directions is evident from
magnetization measurements.
Heat Capacity:
After fitting the low temperature data a large value of
γ= 25.3 mJ/mol K2 was found, indicating the formation of
heavy quantum particle with effective mass enhancement
of approximately 30 times that of free electrons.
𝐷0 𝐸𝐹 = 15.1 states/eV/f.u. was estimated from the γ
value and which is three times larger than that of the
parent compound MnCoGe (Samanta et al., 2013).
We observed two different Kondo minima in two different axial
directions. Until now, the reason for this behavior is not entirely
clear to us. We can also see high MS in both directions in spite
of Kondo type increase in ρ below TK . From low temperature
magnetization data it was revealed that it is an S=1 system.
Underscreening of moments may lead to the coexistence of FM
and Kondo behavior.