In: Nanocellulose, Cellulose Nanofibers … ISBN: 978-1-63483-860-3
Editor: Md. Ibrahim H. Mondal © 2016 Nova Science Publishers, Inc.
Chapter 20
SYNTHESIS AND ASSESSMENT OF PEPTIDE-
NANOCELLULOSIC BIOSENSORS
J. Vincent Edwards, Krystal R. Fontenot,
Nicolette Prevost, Sunghyun Nam, Monica Concha
and Brian Condon Southern Regional Research Center,
USDA, New Orleans, LA, US
ABSTRACT
Nanocellulose is an ideal transducer surface for biosensors: it provides a high surface
area, easily derivatized with bioactive molecules, and abrogates binding of proteins
present in biological fluids where analytes and clinical biomarkers are of interest. Here
we consider approaches to biosensors of human neutrophil elastase (HNE), a biomarker
for chronic wounds and a therapeutic target for a variety of inflammatory diseases.
An unchecked influx of neutrophils degrades growth factors and collagen formation,
thereby indefinitely delaying the healing of chronic wounds. Over the years, the use of
cellulose and other polysaccharides as matrices for wound care has grown. Among these,
nanocellulose is suitable for both wound dressing and point of care diagnostic sensor
applications.
Synthetic approaches to nanocellulose derivatization include esterification of the
transducer surface for the covalent immobilization of peptides and enzymes, and
numerous pathways for annealing peptides and proteins. Nanocellulosic transducers,
which are considered here, include cotton cellulose nanocrystals (cCNC) and wood
cellulose nanocrystals (wCNC). The cCNC and wCNC provide transducer surfaces of
varying reactivity and specific surface area. The comparison of cCNC and wCNC
matrices illustrates the relative efficacy of putative transducer surfaces as colorimetric
and fluorescent peptide conjugate sensors of HNE. Here we discuss routes to their
synthesis and analysis. The resulting peptide-nanocellulose conjugates demonstrate
promise for application to diagnostic technologies with the potential to interface with
therapeutic paradigms in advanced wound dressings.
E-mail: [email protected].
No part of this digital document may be reproduced, stored in a retrieval system or transmitted commercially in any form or by any means. The publisher has taken reasonable care in the preparation of this digital document, but makes no expressed or implied warranty of any kind and assumes no responsibility for any errors or omissions. No liability is assumed for incidental or consequential damages in connection with or arising out of information contained herein. This digital document is sold with the clear understanding that the publisher is not engaged in rendering legal, medical or any other professional services.
J. Vincent Edwards, Krystal R. Fontenot, Nicolette Prevost et al. 476
Keywords: sensors, peptides, cotton and wood cellulose nanocrystals, human neutrophil
elastase
INTRODUCTION
Point-of-care protease detection has been receiving increasing interest and adopted
clinically in some countries to enable chronic wound treatment decisions [1, 2]. The
combination of detection with wound dressing treatment of chronic wounds in a single
dressing is not available at this time. Thus, the ability to combine measurable protease
detection with a dressing motif that removes harmful proteases from chronic wounds is a
current goal of wound healing biomaterial design.
Biosensors at a molecular level are designed with a receptor-like recognition component
that can be activated by a cellular or biochemical event, which in turn prompts a signal that
can be detected electrically (evanescent field), optically (fluorescence and colorimetric), and
mechanically (quartz crystal microbalance) [3]. Of the different types of biosensors,
fluorescence based detection is one of the most sensitive.
A biosensor is comprised of a bio-molecule such as an enzyme or peptide, i.e., a ligand-
like molecule as appended to a matrix, and a transducer surface where the ligand is
immobilized [4]. The application of biosensors in the biomedical, industrial, or military field
is growing [4]. High sensitivity of detectors is required to improve the efficiency in complex
biological fluids [5].
Cellulose is an abundant polymer composed of repeat glucose units connected by beta-
glycosidic linkages to form long chains that typically aggregate into crystalline or amorphous
domains. The anhydroglucose unit of nanocellulose is covalently modifiable principally at the
hydroxymethyl position. An important benefit of cellulose when applied to sensors is its low
propensity to absorb proteins making it favorable in biological milieus [6]. An acid treatment
of cellulose produces nanocellulosic systems that have a greater propensity of hydroxymentyl
groups.
Natural sources of nanocellulose include plants, trees, and bacteria [7, 8]. Processing of
naturally occurring cellulosic sources into nanocellulose systems has given rise to a number
of beneficial materials that afford potential sensor transducer surfaces. These include
aerogels, cellulose nanofibrils, cellulose nanocrystals, microfibrillated cellulose, nanopaper,
and thin films from different sources of cellulose [9]. These nanocellulose systems are highly
versatile, abundant, biocompatible, and biodegradable [10] with unique utility including high
specific surface area.
NANOCELLULOSE TRANSDUCERS AS OPTICAL SENSORS
Nanocellulose systems functionalized with covalent or non-covalent attachment of
fluorescent molecules enables sensitive detection in potential biomedical applications
including optical bioimaging, biosensors, and photodynamic therapy [11]. Previously
reported fluorophores anchored to nanocellulose include fluorescein-5‘-isothiocyanate (FITC,
bioimaging) [12], terpyridine and terpyridine-modified perylene fluorophore (bioimaging)
Synthesis and Assessment of Peptide-Nanocellulosic Biosensors 477
[13], 5-(and-6)carboxyfluorescein succinimidyl ester (FAM-SE, pH sensing) and Oregon
Green 488 carboxylic acid – succinimidyl ester (OG-SE, pH sensing) [14], polyethylenimine-
chlorin p6 derivatives (PEI-chlorin p6, photodynamic therapy) [15], 5-(4, 6-dichlorotriazinyl)
aminofluorescein (DTAF, bioimaging) [16], and 7-amino-4-methylcoumarin (AMC,
bioimaging) [17].
The covalent attachment of biomolecular substrates to nanocellulose as a sensor
transducer surface [11], offers specificity for biological recognition by enzymes or receptor
proteins. For example, DNA oglionucleotides grafted onto nanocellulose that gives rise to a
biocompatible material, which behaves as a biosensor for enzyme/protein immobilization [11,
18]. Furthermore, nanocellulose transducers of peptide-cellulose conjugates can function in
concert with the peptide as a molecular recognition element of proteases by negative charge
and surface polarity interaction with positively charged HNE.
Human Neutrophil Elastase in Chronic Wounds and Methods of Detection
Chronic wounds are severe wounds that typically do not heal within four to six weeks (up
to three months) or alternatively the wound size does not reduce by 20 – 40% after two to
four weeks of treatment [19-21]. These wounds may occur due to a variety of pathologies
including diabetes, repeated damage to tissues, insufficient pressure relief treatment or lack
thereof in the initial stages of wounding. It has also been noted that the body‘s production of
abnormally low levels of proteases inhibitors are etiological to chronic wound development
[19, 22]. Wounds heal through four overlapping stages of hemostasis, inflammation,
proliferation, and maturation [19, 23]. However, chronic wounds remain in the inflammation
stage, and can secrete harmful proteases that have a deleterious effect on the non-healing
wounds [22].
Human neutrophil elastase (HNE) is an elevated serine protease released from
neutrophils, a type of white blood cell, which is present in the inflammation stage of a chronic
wound [22, 24]. The HNE and matrix metalloproteases (MMPs) are required for debridement
of wounds during the healing process, but when HNE and MMP levels are unchecked, they
breakdown growth factors and collagen inhibiting the formation of new tissue [25, 26].
The sensor-based detection of elastase has varied from a microchip [27], microdialysis
probe [28], fluorometric supramolecular pore sensor [29], immobilization of peptides on
quantum dots [30], immobilization of HNE on a biosensor chip for surface plasma resonance
[31], and the use of a colorimetric and fluorometric peptides coupled to cotton cellulose
nanocrystals [25, 32]. However, enhancing the detection limits of HNE released from chronic
wounds continues to be of importance.
Peptide Analogs That Detect HNE
The serine protease, HNE, has specificity for small-uncharged amino acids including
alanine (A) and valine (V) [33-36]. An example is seen in the protein elastin, which can be
degraded as a result of pathologies associated with the lungs and connective tissue. Elastin is
subject to breakdown by HNE especially where alpha-antitrypsin is depleted in some
inflammatory disease states. Elastin contains repeat amino acid motifs of alanine and valine
J. Vincent Edwards, Krystal R. Fontenot, Nicolette Prevost et al. 478
residues that are segmented by proline (P) which constitutes the substrate-recognition sites for
HNE binding and hydrolysis [34].
Synthetic peptide substrates containing these hydrophobic amino acids vary in size,
sequence, and have a detectable signal, which can be associated with a sensor, that is
mediated through release of a chromophore or fluorophore upon HNE hydrolysis between the
COOH-terminal valine or alanine and respective signal molecule. The HNE selective peptide
sequences have a minimum of 3 – 4 hydrophobic uncharged amino acids with sequences of
Ala-Ala-Ala, Ala-Pro-Ala, and Ala-Ala-Pro-Val. As shown in this study some of these
sequences AAA [37], APA [38], and AAPV [39] have a high propensity to form β-turn
motifs. The amino and carboxyl termini of these peptides have also been derivatized with a
succinic acid linker and a chromophore or fluorophore (the signal molecules), respectively.
Figure 1 show the minimized low β-turn conformational energy of the tetrapeptide (Suc-
AAPV) with the 4-paranitroaniline (pNA, chromophore) and 7-amino-4-methylcoumarin
(AMC, fluorophore) attached to the esterified cellotriose chain as a portrayal of the motif that
is assembled on the surface of the cellulose nanocrystal.
Figure 1. The minimization energy of the tetrapeptide (Suc-AAPV) with the pNA (A) or AMC
fluorophore (B).
Synthesis and Assessment of Peptide-Nanocellulosic Biosensors 479
Cotton and Wood Cellulose Nanocrystals
Cellulose nanocrystals (CNC), which are referred to in the literature as nanocrystalline
cellulose, cellulose whiskers, cellulose microcrystallites, and microcrystals [40] are typically
generated from acid hydrolysis, which gives rise to cellulose crystallites that are less
accessible to acid degradation, and can be isolated through repeated dialysis of the acid [41-
45].
Cotton CNC (cCNC) has beneficial properties including high surface area, mechanical
robustness, and is characterized by geometrical rod-like or whisker shape nanocrystals with
fibril diameters of 15 nm, a length of 159 nm, and a density of 1.5 gcm-3
[25, 46].
Nanocrystals made from wood (wCNC), are prepared in a similar way to cCNC but during
the wood pulping process, more of the amorphous regions remain intact. Cotton cellulose
nanocrystals contain cellulose I nanocrystals, and wCNC contains both cellulose I and II [47].
The wCNC has similar properties to cCNC and has rod-like particles that are comparable to
cCNC but it differs in the fibril diameter (10 nm), length (112 nm), and density (1.6 gcm-3
)
[48-50]. Applications of wCNC are currently being explored in the automotive, aerospace,
electronics, and medical industries [48, 51].
Elastase Biosensor In Situ Paradigm for Wound Dressing Motif
Commercial applications of wound dressings that utilize bacterial nanocellulose are
beginning to emerge [52]. It is notable that nanocrystalline silver has also been applied to
dressings (used to prevent and treat infection) in the late 1990s [53], the system contained
high-density polyethylene sandwiching a layer of rayon/polyester gauze where the outer layer
contains a nanocrystalline form of silver coating [53]. These types of dressings have been
found to both inhibit matrix metalloproteases and wound specific bacteria. Nanofiber-based
wound dressings (NFD) have been applied to burn wounds, and confer high filtration, liquid
absorption efficiency, semi-permeability, conformability, functional ability, and confer scar
free properties [21,53]. Recently, we have proposed a system for the use of peptide
derivatized cellulose nanocrystals as biosensors interfaced within the dressing material [25].
Cotton and Wood Nanocellulose Systems as HNE Biosensors
Here we contrast the design, synthesis, and characterization of cotton and wood
nanocellulosic sensors, which shed light on the relationship of contrasting material properties
including specific surface area, degree of substitution and protease detection sensitivity by
examining two nanocellulosic transducer surfaces. The cCNC and wCNC transducer surfaces
immobilized with colorimetric and fluorescent elastase peptide substrates, Suc-AAPV-pNA
and Suc-AAPV-AMC, are contrasted as HNE sensors. This is with a view to further
understanding surface chemistry properties necessary to interface sensors with dressings.
J. Vincent Edwards, Krystal R. Fontenot, Nicolette Prevost et al. 480
EXPERIMENTAL
Materials
Chemicals N‘N-dimethylformamide (DMF), dichloromethane (DCM), and filter paper
were purchased from VWR. All chemicals were used as received without further purification.
Ethylcyanoglyoxylate-2-oxime (Oxyma Pure), diisopropylcarbodiimide (DIC), N,N-
diisopropylethylamine (DIPEA), 4-dimethylaminopyridine (DMAP), and N-(1-naphthyl)
ethylenediamine dihydrochloride (NEDH) were purchased from Sigma Aldrich. The 9-
fluorenylmethoxycarbonyl-glycine (Fmoc-Gly) was purchased from Peptides international,
Louisville, KY, USA. The peptide substrates succinyl-Ala-Ala-Pro-Val-para-nitroanilide
(Suc-AAPV-pNA) and succinyl-Ala-Ala-Pro-Val-7-amino-4-methylcoumarin (Suc-AAPV-
AMC) was purchased from Bachem without further purification. Human neutrophil elastase
was purchased from Athens Research Technologies. Electrospray liquid chromatography
mass spectrometry (ESI-LC/MS) data was collected on an Agilent 6520 QTOF LC-MS/MS
instrument. The cotton cellulose nanocrystals (cCNC) were provided as a freeze-dried powder
supplied by Dr. Quiglin Wu from Louisiana State University, Baton Rouge, LA. A solution of
wCNC was provided as a solution supplied by David Haldane, Innovatech. The wCNC was
freeze-dried into a powder form.
Methods
Esterification of Transducers
In a 50 mL centrifuge tube Oxyma Pure (0.75 mmol), DIC (0.75 mmol), and DMAP
(0.075 mmol) in DMF were added to Fmoc-Gly-OH (0.75 mmol). The cCNC or wCNC (0.75
mmol) was added to the centrifuge tube and sonicated at 25 – 30˚C for 3 h. The esterified
nanocrystals were washed thrice with DMF by centrifuging and decanting with a pasture
pipette. Deprotection of the Fmoc protected glycine on nanocrystals was accomplished by
soaking in 20% piperidine/DMF deblock solution for 15 mins while sonicating, see loading
substitution section. The deprotected esterified nanocrystals were washed thrice with DMF by
centrifuging and decanting with a pasture pipette. After which, the deprotected surfaces were
prepared for peptide coupling or washed thrice with methanol, air dried, and stored for further
use.
Immobilization of the Peptide Substrate on the Transducers
To a 50 mL centrifuge tube Oxyma Pure (0.68 mmol), DIC (0.68 mmol), and DMAP
(0.068 mmol) in DMF were added with the respective peptide substrate (Suc-AAPV-pNA or
Suc-AAPV-pNA) (0.052 mmol) in minimal DMF. The esterified cCNC-Gly or wCNC-Gly
(0.67 mmol) were added to the solution and swirled. The centrifuge tube was sonicated at 25
– 30 ˚C for 3 h and then placed in the refrigerator overnight. The biosensors cCNC-Pep or
wCNC-Pep was purified by washing with thrice with DMF and methanol using vacuum
filtration or centrifuged and decanted using a pasture pipette. The biosensors were allowed to
air dry and stored at ~ 4 – 8 ˚C until further use. Note biosensor will be defined as the
transducers immobilized with glycine and the peptide.
Synthesis and Assessment of Peptide-Nanocellulosic Biosensors 481
Upon the completion of drying, 10 mg of each biosensor was subject to peptide removal
by adding a cleavage cocktail of TFA/water/triisopropylsilane (95/2.5/2.5) to the biosensor
for three hours. The solution for each biosensor were diluted with water (1:10) and submitted
for ESI-LC/MS. The generation of the biosensors was confirmed via its molecular weight.
Loading Substitution
The supernatant from the deblock solution was measured using ultraviolet visible
spectroscopy (UV-VIS) and the loading substitution of the different transducers was
calculated [54]. The supernatant of each matrix were transferred to a quartz cuvette and the
absorbance was measure at 301 nm. The loading substitution was calculated using Equation
1.
Loading (mmol/g) = (Abssample) / (mg of sample x 1.75) Equation 1
Elemental Analysis
All samples were submitted as solids to Midwest Microlabs for carbon (C), hydrogen
(H), and nitrogen (N) analysis. Nitrogen content calculations for peptide mass (μg) and
peptide (μg/mg) were performed in Excel 2007 using equations 2 and 3. The peptide mass
determines the amount of peptide on the surface of biosensor by multiplying the nitrogen
mass by the nitrogen factor of 6.25, Equation 2. The amount of peptide per μg/mg of support
was achieved by dividing the peptide mass by the weight of the biosensor, Equation 3.
Peptide mass (μg) = N mass*6.25 Equation 2
Peptide (μg/mg) = peptide mass/weight of biosensor Equation 3
Attenuated Total Reflectance Infrared Imaging (ATR-IR)
A Platinum Alpha ATR-IR Bruker spectrometer, A220/D01 was used to determine the
functional groups of the cCNC, and wCNC transducers and biosensors. The OPUS 6.5
software was used to collect; sixty-four scans at a resolution of 4 cm-1
between the 4000 –
500 cm-1
region and to analyzed the spectra. All spectra were graphed using Microsoft Excel.
Degree of Substitution
Degree of substitution (DS) of the biosensors was calculated using the Touzinsky and
Gordon method where the percent nitrogen was determined using elemental analysis.[55] The
application of DS herein is as follows: PC1 is the percent nitrogen, MWu is the molecular
weight of one cellulose unit, MW1 is the molecular weight of one nitrogen atom, N1
represents the number of nitrogens, and MWG1 is the molecular weight of the peptide with
the glycine linker.
dS1 = PC1(MWu) / [(MW1)(N1)(100) – (MWG1)] Equation 4
J. Vincent Edwards, Krystal R. Fontenot, Nicolette Prevost et al. 482
Specific Surface Area
The specific surface area of the cCNC was calculated with a density of 1.5 gcm-3
a width
of 15 nm and length of 159 nm and wCNC with a density of 1.6 gcm-3
using width of 10 nm
and a length of 112 nm [25]. The volume of cylinder (Equation 5), density formula (Equation
6), number of particles (Equation 7), the surface area of a cylinder (Equation 8), and the
specific surface area formula (Equation 9) were used to estimate the specific surface area
formula.
ν = π * r2 * h Equation 5
V = m/ρ Equation 6
N = V/ ν Equation 7
Sa = 2πrh + 2πr2 Equation 8
SA = N * sa Equation 9
Molecular Modeling
Computational studies were used to compute the minimization energy of the tetrapeptides
(Suc-AAPV-pNA and Suc-AAPV-AMC) anchored to cellotriose. The peptide substrate
models were built using GaussView 5.0.9 and optimized using a semiempirical Hamiltonian
method [Stewart 89, Steward89a] (PM3) contained in Gaussian 09 revision A.02 molecular
orbital software [56].
Microscopy
Hirox Optical Microscope equipped with a MGX lens was used to obtain high range
images with a 350x magnification, a resolution of 0.5 μm, and a scale of 200 μm of the
transducers. The iridescence of the transducers was observed with polarized filters. The
samples were placed onto the microscope stage and imaged without further processing.
The field emission scanning electron microscopy (FE-SEM) matrices were imaged using
a FEI Quanta 3D FEG FIB/SEM with magnifications of 65000, 80000, and 100000x with a
500nm scale. The samples were sputter coated with a thin 4 nm layer of gold-palladium using
a Leika EM ACE600. A thin layer of coating was used to ensure the surface morphology of
the matrices was not altered.
Spectroscopy
The phosphate buffer solution (PBS) consists of 0.1 M sodium dihydrogen phosphate
(NaH2PO4) and 0.5M sodium chloride (NaCl) in millipore water and the pH was adjusted to
7.4 with 1N sodium hydroxide (NaOH) or 1N hydrochloric acid (HCl). The PBS buffer was
filtered with a 0.45 μm filter for all assays.
The absorbance spectroscopy of the pNA peptide substrate with 2 U/mL of HNE and its
amplification with the NEDH chromogen was performed as previously reported [25]. The
emission spectrometry measurements of the AMC peptide substrate were obtained using
RF5301 spectrofluorometer. The peptide substrate solutions 0 – 0.5 μmol/mL were prepared
Synthesis and Assessment of Peptide-Nanocellulosic Biosensors 483
using the aforementioned PBS solution and 100 μL were added to the centrifuge tube. A 2 mg
sample of biosensor wCNC-Pep and a 4 mg sample of FP-Pep were placed into centrifuge
tube with 100 μL of PBS. A volume of 100 μL of the elastase enzyme 1 U/mL was added to
the wells containing the substrate and biosensors for a total volume of 200 μL. The centrifuge
was placed onto an Accu block digital dry bath heating element from Labnet International for
30 min at 37˚C. These samples were diluted (15x) with PBS and fluorescence measurements
were scanned from 405 – 625 nm with an excitation at 390 nm.
HNE Activity Assay
Stock solutions of the chromophore were prepared as previously reported [25] and the
fluorescent peptide substrate were prepared from which serial dilutions were made using a
PBS buffer solution. A standard curve of the substrate was prepared with a serial dilution
ranging from 1 to 0.0156 μmol/mL. The biosensor stock solutions were prepared by
suspending 20 mg of the cCNC-Pep or wCNC-Pep in 1 mL of PBS, which equals ~ 2 mg of
sample. To start the reaction, 50 μL of human neutrophil elastase at various concentrations
ranging from 2 - 0.015 U/mL was added to the standard curve and to biosensor to provide a
total well volume of 150 μL.
Measurement commenced immediately at 37˚C and continued for 1 h at 1-min intervals.
The 96 well plate was shaken before each measurement for 3 seconds. The fluorescent
substrate was excited at 360 nm and the emission was recorded at 460 nm to measure the
increase in fluorescence of the amidolytic activity.
RESULTS AND DISCUSSION
Synthesis and Characterization of Biosensors
Conjugation of the tetrapeptide containing either a chromophore (p-nitroaniline) or
fluorophore (7-amino-4-methylcoumarin) to the transducer surface occurs in two steps. The
esterification of the transducer surface with glycine via the primary hydroxyl group of
cellulose was accomplished using carbodiimide coupling (Figure 2).
The loading substitution of the first amino acid (glycine, three letter abbreviation Gly)
anchored on the transducer surface is measured by base-mediated deprotectiion of the Fmoc-
amino protecting group, which releases flourescent dibenzofulvene (through β-1 elimination).
The absorbance intensity of the chromophore is employed to calculate the loading substitution
of glycine, which averages ~ 0.16 mmol/g for both the cCNC-Gly and wCNC-Gly.
It is noteworthy that the biosensor is defined by the transducer immobilized with glycine-
linked tetrapeptide. Esterification of the cellulose nanocrystals with Fmoc-Gly provides an
anchor for the covalent immobilization of the tetrapeptide to the transducers where an amide
bond is formed between the N-terminus of the alpha amino glycine and the N-terminus of the
succinyl carboxylate of the peptide substrates (Suc-AAPV-PNA or Suc-AAPV-AMC). The
peptide nanocellulose conjugates were confirmed via its molecular weight using ESI-LC/MS,
the parent ion value (m/z) of the peptide adducts is reported in Table 1.
J. Vincent Edwards, Krystal R. Fontenot, Nicolette Prevost et al. 484
Figure 2. Esterification and immobilization of peptides on transducers.
Table 1. The ESI-LC/MS, average nitrogen percent and peptide content as determined
by elemental analysis, calculated concentration, and sensitivity concentration
of the biosensors
ESI-LC/MSb Average N% Peptide Calc. conc. Namea (m/z) (mg) (μg/mg) (μg/mL)
cCNC-Gly 1.06
cCNC-Pep [M] 633.6590 1.46 27.56 35.73c
wCNC-Gly 2.17 wCNC-Pep [M+H] 671.3005 2.54 88.13 134.86d
aThe abbreviation Pep indicates the peptide with glycine (G-Suc-AAPV-pNA or AMC).
bThe [M]
calculated for C32H42N6O10 m/z 670.72 and includes the glycidyl link attached to the peptide. cThe
absorbance concentration for cCNC-Pep and the dfluorescence calculated concentration for wCNC-
Pep are based on measurements of released chromophore and flourophore from peptide conjugate
in the HNE assay at 1-2U HNE/mL.
Elemental analysis of the biosensors identified the percent of nitrogen present on the
biosensor from which the level of peptide incorporation was calculated (Table 1). The wCNC
has a 2-fold increase in esterified glycine and peptide immobilized surfaces compared to the
cCNC. As a result, the level of peptide attachment in μg/mg for the wCNC is 88.13 μg/mg,
which is higher than the peptide attachment for the cCNC of 27.56 μg/mg. The higher-level
of percent nitrogen and peptide attachment for the wCNC may be due to the smaller size of
the wood nanocrystals, which in turn accounts for a higher specific surface area that
accommodates more peptide.
Synthesis and Assessment of Peptide-Nanocellulosic Biosensors 485
Spectroscopy
The calculated concentration of the absorbance and fluorescence intensity of the
biosensors with 1 – 2 U/mL of HNE is provided in Table 1. The pNA absorbs at 405 nm and
AMC is excited at 360 and emits at 460 nm.
Figure 3. HNE pathway of hydrolysis for A) the pNA biosensor and its amplification with NEDH and
B) the AMC biosensor.
The cCNC-peptide analog has an absorbance-calculated concentration of 35.73 μg/mL
and the emission calculated concentration of the wCNC-peptide is 134.86 μg/mL. All faces of
the cCNC-Pep and wCNC-Pep nanocrystal surfaces freely interact with HNE, thereby
promoting access of the substrate peptides to the HNE enzyme active site.
A
B
J. Vincent Edwards, Krystal R. Fontenot, Nicolette Prevost et al. 486
The higher concentration of the wCNC-peptide is due to increased peptide substitution on
the nanocrystals and the higher sensitivity of the fluorescent AMC. The detection signals of
the chromophore and fluorophore with human neutrophil elastase varies. Figure 3 shows the
pathway of A) pNA amplification with NEDH and B) the AMC fluorescence pathway. Figure
3A portrays HNE hydrolyzing the amide bond between valine and pNA, which is further
reacted with NEDH. An azide bond forms between pNA and NEDH, which results in a red
shift in absorbance to 545 nm. The low detection signal of the pNA chromophore is amplified
with NEDH, which increases the colorimetric response [25]. Figure 3B demonstrates the one-
step reaction that occurs upon HNE hydrolysis of the amide bond between valine and AMC
subsequently resulting in a strong fluorescence signal.
Surface Analysis
Attenuated total reflection infrared (ATR-IR) identified different characteristic bands
present on the surface of the cellulose nanocrystals, see Figure 4. The ATR-IR of bands of
cellulose has been well studied for its functional groups [57-59] and contains similar bands to
nanocrystalline cellulose (Table 2) [57-61].
Table 2. Characteristic ATR-IR bands of the nanocellulose transducers
Sample Wavenumber
(cm -1)
Literature
(cm -1)
Assignments
Transducers 3489 and 3439a 3486 and
3439
Intramolecular hydrogen bonding
cCNC and
wCNC
3335 -3200 3570 – 3200 ν(O―H) stretching vibration
2900 – 2893 3000 - 2800 ν(C―H, C―CH3, C―H2) stretching
1636 1633 ν(H2O) absorbed molecules
1428 1429 ν(C―H) wagging - in-plane bending
1370 – 1314 1372, 1336, ν(C―H) bending, ν(O―H) in-plane
1205 1204, 1320 bending, and ν(C―H) wagging
1055 – 1031 1042 ν(C―O) stretching vibration
899 – 895 898 ν(C―H) bending and (C―H2) stretching
666-664 700 – 600 ν(C―C) stretching vibration
Biosensors
cCNC-Pep
and
wCNC-Pepa
3489 and 3439a 3486 and
3439
Intramolecular hydrogen bonding
3334 - 3200 3570 – 3200 O―H stretching vibration
2898 – 2892 3000 - 2800 C―H, C―CH3, C―H2 stretching
1652 – 1650 1650 amide I band(C―O stretching)
weak 1568 1540 amide II band (C―N stretching and N―H bending)
1636 1633 ν(H2O) absorbed molecules
1428 1429 ν(C―H) wagging - in-plane bending
1360 – 1315 1372, 1336, ν(C―H) bending, ν(O―H) in-plane
1204 1204, 1320 bending, and ν(C―H) wagging
1055 – 1031 1042 ν(C―O) stretching vibration
899 – 895 898 ν(C―H) bending and (C―H2) stretching
662 700 – 600 ν(C―C) stretching vibration
The transducers represent the cCNC and wCNC without any modification and the biosensors represent
the cCNC-Pep and wCNC-Pep with that are functionalized with the peptide. aThe additional peaks
observed for the nanocellulose matrices.
Synthesis and Assessment of Peptide-Nanocellulosic Biosensors 487
a
b
Figure 4. ATR-IR spectra of the transducers (A) and biosensors (B) with cCNC (pink) and wCNC
(blue) without and with the peptide.
Differences in the ATR-IR spectrums between the cCNC and wCNC and the cCNC-Pep
and wCNC-Pep are notable, Table 2. Figure 4A shows the additional bands present for the
cCNC and wCNC including the 3489 cm-1
and 3439 cm-1
and these spectra have equal
intensities. The 3489 cm-1
and 3439 cm-1
bands are ascribed to intramolecular hydrogen
bonding [62-64].
The ATR-IR spectrum of the biosensors show an additional peak at 1652 – 1650 cm-1
,
which represents the amide I stretch from the peptide [65], see Figure 4B. The peak intensity
of the cCNC increases after peptide immobilization on the surface. In comparison to
previously reported cellulose spectra the bands for the nanocellulose transducers are sharper
and may indicate a higher density of hydroxyl groups present on the surface of the
nanocrystals [62]. Furthermore, the ATR-IR results support the ESI-MS findings that the
tetrapeptide is anchored on the surface of the biosensor.
60012001800240030003600
Wavelength (cm-1)
cCNC
wCNC
60012001800240030003600
Wavelength (cm-1)
cCNC-Pep
wCNC-PepA
J. Vincent Edwards, Krystal R. Fontenot, Nicolette Prevost et al. 488
Degree of Substitution and Specific Surface Area
Degree of substitution (DS) levels, which measure ratio of derivatized anhydroglucose
hydroxyls, were calculated for the esterified transducers cCNC-G and wCNC-G and
biosensors cCNC-Pep and wCNC-Pep based on the Touzinsky and Gordon method (Table 3)
[55]. The glycine-esterified transducers have DS levels of 0.128 (cCNC-Pep) and 0.276
(wCNC-Pep), respectively. The high DS level for glycine is expected since glycine is a small
molecule with limited steric hindrance. The peptide on the transducer surfaces has DS levels
of 0.025 (cCNC-Pep) and 0.061 (wCNC-Pep). This indicates that approximately 2 – 6
peptides are linked per 100 anhydroglucose units (AGU) for the biosensors. The wCNC-Pep
has a 2.3 fold increase in peptide substitution compared to the cCNC-Pep. These findings are
further supported by the elemental analysis (percent nitrogen and peptide incorporation) and
the absorbance and fluorescence intensity results. The low DS of the cCNC-Pep and wCNC-
Pep in comparison to cCNC-Gly and wCNC-Gly, as previously reported by Edwards et al.
[25] is partially due to the synthetic modification that occurs at the surface.
Table 3. Degree of substitution, specific surface area, and the sensitivity values for
cellulose nanocrystals
Name DSa Specific surface areab
(m2g-1)
Sensitivity conc.c
(U/mL)
cCNC 186.2
cCNC-Gly 0.128
cCNC-Pep 0.025 0.050
wCNC 261.2
wCNC-Gly 0.276
wCNC-Pep 0.061 0.015 \aDS is the degree of substitution as calculated by Touzinsky and Gordon method.
bThe specific surface
area was calculated using the Equations 5 – 9 in the experimental section. cThe activity of the
biosensors towards HNE.
The specific surface area (SSA) of the transducers was calculated based on the surface
area and volume formula of a cylindrical shape [25] Table 3. The transducer cCNC has a
specific surface area of 186.2 m2g
-1 when calculated with a density of 1.5 gcm
-3, a width of 15
nm, and a light of 159 nm while the wCNC has a specific surface area of 261.2 m2g
-1 with a
density of 1.6 gcm-3
, a width of 10 nm, and a length of 112 nm.
The SSA of wCNC has a 1.4 fold increase in the total surface area of the cCNC. The
higher surface area of the wCNC compared to the cCNC is due to the differences in diameter
and length (diameter of 5 – 10 nm and length of 50 – 60 nm) and (diameter of 15 nm and
length of 159 nm), respectively.
The elemental analysis and degree of substitution further supports that the wCNC has a
higher SSA and accounts for the higher percent nitrogen and peptide incorporation. Smaller
size nanocrystals lead to higher surface area and increased hydroxymethyl titer for peptide
attachment.
Synthesis and Assessment of Peptide-Nanocellulosic Biosensors 489
Microscopy
Images of the transducer were obtained with a polarized optical microscope and field
emission scanning electron microscope (FE-SEM), Figure 5. The polarized optical images
reveal the iridescent nature of the nanocellulose transducers, Figure 5A [9].
Figure 5. The microscopy images A) polarized optical images of cCNC and wCNC with polarizer and
magnification of 350X, resolution of 0.5 μm, and a scale of 200 μm and B) the FE-SEM images of
cCNC and wCNC at 65000 x with at 500 nm scale.
The images show the rod-like shapes of the crystals, which appear to emit a
purplish/bluish hue in both the cCNC and wCNC. This photonic property may represent
reflection bands with a shorter wavelength [66]. Nanocellulose is known to exhibit photonic
properties including selective reflection of left-handed circularly polarized light with the pitch
of the chiral nematic phase varying within the wavelengths of visible light [67]. The FE-SEM
images reveal whisker-like crystals of cCNC and wCNC with an uneven disbursement as
shown in Figure 5B.
HNE Activity with Cellulose Nanocrystals
As shown in Table 3, the activity of the peptide-cellulose nanocrystal conjugates in the
presence of various concentrations of HNE revealed that the wCNC-Pep had the greatest
sensitivity levels (0.015 U/ml) towards HNE whereas the cCNC-Pep had a lower sensitivity
wCNC
200 μm 200 μm
cCNC
500 nm500 nm
cCNC wCNC
A
B
J. Vincent Edwards, Krystal R. Fontenot, Nicolette Prevost et al. 490
level (0.05 U/ml) yet still within the range of that found for chronic wound exudate titer of
HNE. The higher sensitivity of the wCNC supports the findings from the higher peptide
loading, degree of substitution, the calculated concentration from fluorescence spectroscopy,
and the higher surface area.
CONCLUSION
The synthesis and application of peptide-nanocellulose from wood nanocellulose as a
biosensor for HNE is reported and contrasted with cotton nanocellulose. Esterification and
immobilization of the cotton and wood cellulose nanocrystals with glycine and the
tetrapeptide was confirmed using ESI-MS, elemental analysis, and spectroscopy. Surface
analysis using ATR-IR revealed sharp peaks present for the nanocrystals and additional peaks
representing the tetrapeptide-nanocellulose conjugate. The higher DS levels and specific
surface area observed for wCNC results in the high florescence levels and a high
concentration of the peptide, which provided enhanced sensitivity levels towards human
neutrophil elastase. Although the cCNC has a lower surface area in comparison to the wCNC
both nanocrystals show promise as transducer surfaces that can be functionalized with
peptides to serve as potential point of care diagnostic sensor to detect HNE in chronic wound
fluid.
ACKNOWLEDGMENTS
This project was funded by the U.S. Department of Agriculture. We thank Zhongqi He
and Dorselyn Chapital for allowing us to use their UV-VIS instrument and Dr. Casey Grimm
for collecting mass spectral analysis.
REFERENCES
[1] Serena, T. E. (2014). Development of a novel technique to collect proteases from
chronic wounds. Adv. Wound Care 3, 729-732.
[2] Harding, K. (2011). International concensus. The role of proteases in wound
diagnostics. An expert working group review. Wounds Intern. 1 - 13.
[3] Edwards, J. V., Prevost, N., French, A. D., Concha, M., DeLucca, A., Wu, Q. (2013).
Nanocellulose-based biosensors: Design, preparation, and activity of peptide-linked
cotton cellulose nanocrystals having fluorimetric and colorimetric elastase detection
sensitivity. Eng. 5, 20 – 28.
[4] Mohanty, S. P., Kougianos, E. (2006). Biosensors: a tutorial review. Potentials, IEEE
25, 35-40.
[5] Reimhult, E., Höök, F. (2015). Design of Surface Modifications for Nanoscale Sensor
Applications. Sensors 15, 1635-1675.
[6] Ciolacu, D., Ciolacu, F., Popa, V. I. (2011). Amorphous Cellulose - Structure and
Characterizatoin. Cellul. Chem. Technol. 45, 13-21.
Synthesis and Assessment of Peptide-Nanocellulosic Biosensors 491
[7] Fu, L., Zhou, P., Zhang, S., Yang, G. (2013). Evaluation of bacterial nanocellulose-
based uniform wound dressing for large area skin transplantation. Mater. Sci. Eng. C
Mater. Biol. Appl. 33, 2995-3000.
[8] Eichhorn, S.J. (2011). Cellulose nanowhiskers: promising materials for advanced
applications. Soft Matter 7, 303-315.
[9] Xiong, R., Han, Y., Wang, Y., Zhang, W., Zhang, X., Lu, C. (2014). Flexible, highly
transparent and iridescent all-cellulose hybrid nanopaper with enhanced mechanical
strength and writable surface. Carbohydr. Polym. 113, 264-271.
[10] Azizi Samir, M. A. S., Alloin, F., Dufresne, A. (2005). Review of Recent Research into
Cellulosic Whiskers, Their Properties and Their Application in Nanocomposite Field.
Biomacromolecules 6, 612-626.
[11] Lin, N., Dufresne, A. (2014). Nanocellulose in biomedicine: Current status and future
prospect. Eur. Polym. J. 59, 302-325.
[12] Dong, S., Roman, M. (2007). Fluorescently Labeled Cellulose Nanocrystals for
Bioimaging Applications. J. Am. Chem. Soc. 129, 13810-13811.
[13] Hassan, M. L., Moorefield, C. M., Elbatal, H. S., Newkome, G. R., Modarelli, D. A.,
Romano, N. C. (2012). Fluorescent cellulose nanocrystals via supramolecular assembly
of terpyridine-modified cellulose nanocrystals and terpyridine-modified perylene.
Mater Sci. Eng. B 177, 350-358.
[14] Nielsen, L. J., Eyley, S., Thielemans, W., Aylott, J. W. (2010). Dual fluorescent
labelling of cellulose nanocrystals for pH sensing. Chem. Commun. 46, 8929-8931.
[15] Drogat, N., Granet, R., Le Morvan, C., Bégaud-Grimaud, G., Krausz, P., Sol, V. (2012).
Chlorin-PEI-labeled cellulose nanocrystals: Synthesis, characterization and potential
application in PDT. Bioorg. Med. Chem. Lett. 22, 3648-3652.
[16] Abitbol, T., Palermo, A., Moran-Mirabal, J. M., Cranston, E.D. (2013). Fluorescent
Labeling and Characterization of Cellulose Nanocrystals with Varying Charge
Contents. Biomacromolecules 14, 3278-3284.
[17] Huang, J. -L., Li, C. -J., Gray, D. G. (2013). Cellulose Nanocrystals Incorporating
Fluorescent Methylcoumarin Groups. ACS Sustainable Chem. Eng. 1, 1160-1164.
[18] Mangalam, A. P., Simonsen, J., Benight, A. S. (2009). Cellulose/DNA Hybrid
Nanomaterials. Biomacromolecules 10, 497-504.
[19] Suvarna, K., Munira, M. (2013). Wound healing Process and Wound Care Dressings: A
Detailed Review. J. Pharma. Res. 2, 6 - 12.
[20] Skórkowska-Telichowska, K., Czemplik, M., Kulma, A., Szopa, J. (2013). The local
treatment and available dressings designed for chronic wounds. J. Am. Acad. Dermatol.
68, e117-e126.
[21] Abrigo, M., McArthur, S. L., Kingshott, P. (2014). Electrospun Nanofibers as Dressings
for Chronic Wound Care: Advances, Challenges, and Future Prospects. Macromol.
Biosci. 14, 772-792.
[22] McCarty, S. M., Percival, S. L. (2013). Proteases and Delayed Wound Healing. Adv.
Wound Care 2, 438-447.
[23] Sharma, S., Dua, A., Malik, A. (2014). Third Generation Materials for Wound
Dressings. Int. J. Pharma. Sci. Res. 5, 2113 - 2124.
[24] Diegelmann, R. F., Evans, M. C. (2004). Wound healing: an overview of acute, fibrotic
and delayed healing. Front. Biosci. 9, 283-289.
J. Vincent Edwards, Krystal R. Fontenot, Nicolette Prevost et al. 492
[25] Edwards, J. V., Prevost, N., Sethumadhavan, K., Ullah, A., Condon, B. (2013). Peptide
conjugated cellulose nanocrystals with sensitive human neutrophil elastase sensor
activity. Cellulose 20, 1223-1235.
[26] Korkmaz, B., Horwitz, M. S., Jenne, D. E., Gauthier, F. (2010). Neutrophil Elastase,
Proteinase 3, and Cathepsin G as Therapeutic Targets in Human Diseases. Pharmacol.
Rev. 62, 726-759.
[27] Henares, T. G., Takaishi, M., Yoshida, N., Terabe, S., Mizutani, F., Sekizawa, R.,
Hisamoto, H. (2006). Integration of Multianalyte Sensing Functions on a Capillary-
Assembled Microchip: Simultaneous Determination of Ion Concentrations and
Enzymatic Activities by a ―Drop-and-Sip‖ Technique. Anal. Chem. 79, 908-915.
[28] Wang, Y., Zagorevski, D. V., Stenken, J. A. (2008). In Situ and Multisubstrate
Detection of Elastase Enzymatic Activity External to Microdialysis Sampling Probes
Using LC−ESI-MS. Anal. Chem. 80, 2050-2057.
[29] Das, G., Talukdar, P., Matile, S. (2002). Fluorometric detection of enzyme activity with
synthetic supramolecular pores. Science (New York, N.Y.) 298, 1600-1602.
[30] Hyungki, K., Petryayeva, E., Algar, W. R. (2014). Enhancement of Quantum Dot
Forster Resonance Energy Transfer within Paper Matrices and Application to
Proteolytic Assays. IEEE J. Sel. Top. Quantum Electron. 20, 141-151.
[31] Shen, B., Shimmon, S., Smith, M. M., Ghosh, P. (2003). Biosensor analysis of the
molecular interactions of pentosan polysulfate and of sulfated glycosaminoglycans with
immobilized elastase, hyaluronidase and lysozyme using surface plasmon resonance
(SPR) technology. J. Pharm. Biomed. Anal. 31, 83-93.
[32] Edwards, J. V., Prevost, N. T., French, A. D., Concha, M., Condon, B. D. (2015).
Kinetic and structural analysis of fluorescent peptides on cotton cellulose nanocrystals
as elastase sensors. Carbohydr. Polym. 116, 278-285.
[33] Aimetti, A. A., Tibbitt, M. W., Anseth, K. S. (2009). Human Neutrophil Elastase
Responsive Delivery from Poly(ethylene glycol) Hydrogels. Biomacromolecules 10,
1484-1489.
[34] Meers, P. (2001). Enzyme-activated targeting of liposomes. Adv. Drug Del. Rev. 53,
265-272.
[35] Yoshimura, T., Barker, L. N., Powers, J. C. (1982). Specificity and reactivity of human
leukocyte elastase, porcine pancreatic elastase, human granulocyte cathepsin G, and
bovine pancreatic chymotrypsin with arylsulfonyl fluorides. Discovery of a new series
of potent and specific irreversible elastase inhibitors. J. Biol. Chem. 257, 5077-5084.
[36] Wiesner, O., Litwiller, R. D., Hummel, A. M., Viss, M. A., McDonald, C. J., Jenne, D.
E., Fass, D. N. Specks, U. (2005). Differences between human proteinase 3 and
neutrophil elastase and their murine homologues are relevant for murine model
experiments. FEBS Lett. 579, 5305-5312.
[37] Tashiro, S., Kobayashi, M., Fujita, M. (2006). Folding of an Ala-Ala-Ala Tripeptide
into a β-Turn via Hydrophobic Encapsulation. J. Am. Chem. Soc. 128, 9280-9281.
[38] Kleinpeter, E., Ströhl, D., Peinze, S. (1995). Solution conformation of tripeptides by
NMR spectroscopy and force-field calculations. Struct. Chem. 6, 377-382.
[39] Liang, G. B., Rito, C. J., Gellman, S. H. (1992). Thermodynamic analysis of .beta.-turn
formation in Pro-Ala, Pro-Gly, and Pro-Val model peptides in methylene chloride. J.
Am. Chem. Soc. 114, 4440-4442.
Synthesis and Assessment of Peptide-Nanocellulosic Biosensors 493
[40] Lavoine, N., Desloges, I., Dufresne, A., Bras, J. (2012). Microfibrillated cellulose – Its
barrier properties and applications in cellulosic materials: A review. Carbohydr. Polym.
90, 735-764.
[41] Espino-Pérez, E., Domenek, S., Belgacem, N., Sillard, C., Bras, J. (2014). Green
Process for Chemical Functionalization of Nanocellulose with Carboxylic Acids.
Biomacromolecules 15, 4551-4560.
[42] Schyrr, B., Pasche, S., Voirin, G., Weder, C., Simon, Y.C., Foster, E.J. (2014).
Biosensors Based on Porous Cellulose Nanocrystal–Poly(vinyl Alcohol) Scaffolds. ACS
Appl. Mats. Interf. 6, 12674-12683.
[43] Bondeson, D., Mathew, A., Oksman, K. (2006). Optimization of the isolation of
nanocrystals from microcrystalline cellulose by acid hydrolysis. Cellulose 13, 171-180.
[44] Dong, X., Revol, J. -F., Gray, D. (1998). Effect of microcrystallite preparation
conditions on the formation of colloid crystals of cellulose. Cellulose 5, 19-32.
[45] Beck-Candanedo, S., Roman, M., Gray, D. G. (2005). Effect of Reaction Conditions on
the Properties and Behavior of Wood Cellulose Nanocrystal Suspensions.
Biomacromolecules 6, 1048-1054.
[46] Yue, Y., Zhou, C., French, A., Xia, G., Han, G., Wang, Q., Wu, Q. (2012).
Comparative properties of cellulose nano-crystals from native and mercerized cotton
fibers. Cellulose 19, 1173-1187.
[47] Reiner, R. S., Rudie, A. W. (2013). Process Scale-Up of Cellulose Nanocrystal
Production to 25 kg per Batch at the Forest Products Laboratory. In Production and
applications of Cellulose nanomaterials, Postek, M. T., Moon, R. J., Rudie, A. W.,
Bilodeau, M. A. (Eds), TAPPI Press, Inc., Peachtree Corners, GA, USA, pp. 21 - 24.
[48] Dodson, B. (2012). Wood Pulp Extract Stronger than Carbon Fiber or Kevlar.
http://www.gizmag.com/cellulose-nanocrystals-stronger-carbon-fiber-kevlar/23959/.
[49] Sehaqui, H., Zhou, Q., Ikkala, O., Berglund, L. A. (2011). Strong and Tough Cellulose
Nanopaper with High Specific Surface Area and Porosity. Biomacromolecules 12,
3638-3644.
[50] R. R. Lahiji, R. R., R. J. Moon, A. Rudie (2008). Characterization of Cellulose
Nanocrystals by SPM. Conference proceeding of NSTI Nanotechnology Conference
and Trade Show: Life Sciences, Medicine & Bio Materials, June 1 - 5, 2008, Boca
Raton, FL, USA, pp. 704 - 707.
[51] Ferguson, W. (2012). Why wood pulp is world's new wonder material?
http://www.newscientist.com/article/mg21528786.100-why-wood-pulp-is-worlds-new-
wonder-material.html#.VYg9ilZOmM8.
[52] Stanislaw, B., Halina, K., Alina, K., Katarzyna, K., Marek, K. O., Manu de, G. (2012).
Wound Dressings and Cosmetic Materials from Bacterial Nanocellulose. In: Bacterial
NanoCellulose, Gama, M., Gatenholm, P., Klemm, D. (Eds), CRC Press, Inc., Boca
Raton, FL, USA, pp. 157-174.
[53] Karthik, D., Wasif, A. I. (2014). Wound care materials. Medical Textiles 61, 53 - 59.
[54] Chan, W. C., White, P. D. (2000). Basic Procedures. In Fmoc Solid Phase Peptide
Synthesis: A Practical Approach, Chan, W. C., White, P. D. (Eds), Oxford University
Press, Inc., Oxford, New York, USA, pp. 41 - 76.
[55] Touzinsky, G. F., Gordon, S. M. (1979). Degree of subsitution of cellulose derivatives
containing n different substituent groups. Carbohydr. Res. 69, 327 – 329.
J. Vincent Edwards, Krystal R. Fontenot, Nicolette Prevost et al. 494
[56] Bolton, K., Gustavsson, S., Rosen, A. A comparison of PM3 semiempirical and B3LYP
density functional methods for calculating carbon nanotube-hydrocarbon bond
strengths, Conference Proceeding of Nanotechnology, 2003. IEEE-NANO 2003. 2003
Third IEEE Conference on, 12-14 Aug. 2003 2003, pp. 615-618 vol. 612.
[57] Chen, R., Jakes, K. A. (2002). Effect of pressing on the infrared spectra of single cotton
fibers. Appl. Spectrosc. 56, 646-650.
[58] Gilbert, C., Kokot, S., Meyer, U. (1993). Application of DRIFT spectroscopy and
chemometrics for the comparison of cotton fabrics. Appl. Spectrosc. 47, 741-748.
[59] Roeges, N. P. G., (1994). A guide to the complete interpretation of infrared spectra of
organic structures. John Wiely & Sons, Inc., Chichester, UK, pp. 356.
[60] Chung, C., Lee, M., Choe, E. K. (2004). Characterization of cotton fabric scouring by
FT-IR ATR spectroscopy. Carbohydr. Polym. 58, 417-420.
[61] Wang, S., Liu, Q., Luo, Z., Wen, L., Cen, K. (2007). Mechanism study on cellulose
pyrolysis using thermogravimetric analysis coupled with infrared spectroscopy. Front.
Energy Power Eng. China 1, 413-419.
[62] Xu, X., Liu, F., Jiang, L., Zhu, J. Y., Haagenson, D., Wiesenborn, D. P. (2013).
Cellulose Nanocrystals vs. Cellulose Nanofibrils: A Comparative Study on Their
Microstructures and Effects as Polymer Reinforcing Agents. ACS Appl. Mats. Interf. 5,
2999-3009.
[63] Kadla, J. F., Kubo, S. (2003). Miscibility and hydrogen bonding in blends of
poly(ethylene oxide) and kraft lignin. Macromolecules 36, 7803-7811.
[64] Kondo, T., Sawatari, C., Manley, R. S. J., Gray, D. G. (1994). Characterization of
hydrogen bonding in cellulose-synthetic polymer blend systems with regioselectively
substituted methylcellulose. Macromolecules 27, 210-215.
[65] Orlandin, A., Formaggio, F., Toffoletti, A., Peggion, C. (2014). Cotton functionalized
with peptides: characterization and synthetic methods. J. Pept. Sci. 20, 547-553.
[66] Beck, S., Bouchard, J., Chauve, G., Berry, R. (2013). Controlled production of patterns
in iridescent solid films of cellulose nanocrystals. Cellulose 20, 1401-1411.
[67] Cheung, C. C. Y., Giese, M., Kelly, J. A., Hamad, W. Y., MacLachlan, M. J. (2013).
Iridescent chiral nematic cellulose nanocrystal/polymer composites assembled in
organic solvents. ACS Macro. Letters 2, 1016-1020.