Mari Cruz García Gutiérrez
Instituto de Estructura de la Materia, CSIC
SAXS Workshop
Barcelona, 1st October 2014
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
Hierarchical structures and techniques
Basics about X-ray scattering and polymers
Wide angle X-ray scattering (WAXS) and small angle X-ray
scattering (SAXS)
Microfocus X-ray scattering (mWAXS y mSAXS)
Grazing incidence X-ray scattering (GIWAXS y GISAXS)
Crystallography Microstructure Structure
Proteins Virus
Bacterias
Granular
structures
Polymers
Atomic
structure
Porous
materials
10-11 10-9 10-7 10-5 10-3
Size (meters)
Length scales
SEM
Optic microscopy Techniques
WAXS SAXS Scanning X-ray
microdiffraction
Neutron
diffraction TEM
Electron
diffraction
AFM STM
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
10-8 m
5x10-10 m
Tg <T < Tm
X-ray scattering (WAXS)
Neutron scattering
SAXS; SANS;
AFM
10-5 m
Light scattering
Optic microscopy
AFM
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
sample X-ray source
2
SAXS interface : WAXS interface
2’
WAXS
SAXS
q (nm -1
)
0.0 0.5 1.0 1.5 2.0
I (a
rbb
itra
ry u
nits)
0.0
0.5
1.0
1.5
2.0
~ 10nm
s(nm-1)
1.0 1.5 2.0 2.5 3.0 3.5
I(a
.u.)
PBT
S (nm-1)
~ 5Å
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
Detector SAXS Detector WAXS Sample environment
Vacuum chamber
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
X-ray beam
rotating
cilinder
sample
detector
movement
at rest
PS in methanol
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
WAXS SAXS
: I Sics et al, Rev. Sci. Instrum.
71,1733 (2000)
DS
WAXS
q (Å-1
)
0.8 1.2 1.6 2.0
Inte
nsid
ad
SAXS
q (Å-1
)
0.02 0.04 0.06 0.08 0.10
I×q
2
DS
Log10
[F/Hz]
3 4 5 6
"
0.06
0.08
0.10
0.12
0.14
0.16
0.18
0.20
0.22
0.24
0.26
10
120
10
120
10
120
tie
mp
o
tie
mp
o
tie
mp
o
Structure Dynamics
Uniaxial deformation
SAXS/WAXS +
Raman
X-rays
Camera
Raman
Stress-strain
S. Ran et al, Rev. Sci. Instrum. 74, 3087 (2003)
Complementary information about
the structural evolution of
molecular chain in the amorphous
phase, mesophase and crystalline
phase.
BNL, Spring-8
Processing
SAXS/WAXS
S. Ran et al, Colloid Polym. Sci. 282, 802 (2004)
BNL
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
strain (%)
0 50 100 150 200 250 300 350 400 450
Str
ess (
MP
a)
0
2
4
6
8
10
12
14
(PBT-PTMO)
(PBT-PTMO)+0.2%SWCNT
(PBT-PTMO): 75.8 MPa
(PBT-PTMO)+SWCNT: 87.6 MPa
Young’s Modulus:
(PBT-PTMO): 8.4 MPa
(PBT-PTMO)+SWCNT: 9.1 MPa
Yield Strength:
(PBT-PTMO): 420%
(PBT-PTMO)+SWCNT: 170%
Elongation-to-break:
“Deformation behavior during cold drawing of nanocomposites based
on single wall carbon nanotubes and poly(ether ester) copolymers” J.J.
Hernández, M.C. García-Gutiérrez, et al.; Polymer 48, 3286 (2007)
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
strain (%)
0 50 100 150 200 250 300 350 400 450
Str
ess (
MP
a)
0
2
4
6
8
10
12
14
(PBT-PTMO)
(PBT-PTMO)+0.2%SWCNT
relaxed
Str
ess (
MP
a)
1 2 5 4 3 relaxed
SAXS
WAXS
2
3
4
5
1
3
4 5
2
6
relaxed
1 2 3 5
6 relaxed 4
(PBT-PTMO)
equator +- +-
(PBT-PTMO)+SWCNT
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
A
B
C
D
E
L
Leq
r
e
l
a
x
e
d
L’
Leq’
L>L’ Leq<Leq’
A
B
E
D
C
F
Copolymer Nanocomposite
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
focalized X-ray beam ( 0.5 mm)
video-microscope
scan in xyz
CCD
sample
Scanning set-up @ ID13 (ESRF)
SAXS
WAXS
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
3*3 mm
compression
6 1
2 UHMW-PE
C. Riekel, M.C. García-Gutiérrez, et al.;
Anal. & Bioanal. Chem. 376, 594 (2003)
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
2A 3
M. Kastler et al. Adv. Mater.
18, 2255 (2006)
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
30 mm
SEM
AAO Membrane + solution (30wt% PVDF-Dimethylacetamide)
5 mm
PVDF nanofibers
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
“Confinement-induced one-dimensional ferroelectric polymer
arrays” M.C. García-Gutiérrez, et al.; Nano Letters 10, 1472 (2010)
bulk nanoarray
q (nm-1
)
0 5 10 15 20 25 30 35
Inte
nsity (
a.
u.)
0
500
1000
1500
2000
2500
3000
3500
q (nm-1
)
0 5 10 15 20 25 30 35
Inte
nsity (
a.
u.)
0
50
100
150
200
250
300
bulk nanoarray
100
020
110
200 002
a form g form 020
002 / 110
022
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
2 mm SAXS
b
020
022 002 / 110
“Probing the internal structure of high-performance fibers by on-axis scanning
diffractometry” R. Davies et al. Macromolecules 40, 5038 (2007)
Tamaño de haz =
500nm
“X-ray microdiffraction study of SWCNT alignment
across a fiber” V. Pichot et al. EPL 79, 46002 (2007)
Beam size< 100 nm
“Coherent X-ray diffraction imaging with nanofocus illumination”
C.G. Schroer et al. PRL 101, 090801 (2008)
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
qz
qy
qz
qy
2p/d
qz
qy
2p/d
qz=2p/l sin (ai+af)
qy=2p/l sin(w)cos(af)
ai << 1
ai ~ ac
• GIWAXS/GISAXS → similar to WAXS/SAXS but in reflection geometry
• Length scales range: from Angstroms to several microns
• Structure and morphology: size, shape and order
• Depth sensibility (buried structures)
• Average of illuminated area (~ cm2)
• Real time experiments
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
X-rays
Detector
BW4 beamline @ HASYLAB, Hamburg
Sample environment
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
y
y=0mm Au Dy=50 mm
300mm 200mm 400mm
600mm
0.205
0.300
0.395
0.110
PS 3500mm
0 -0.098 0.098
qy [Å-1]
qz [Å-1]
800mm 900mm
X-ray
5mm
“Combinational investigation of the isolated nanoparticle to coalescent layer transition in a gradient
sputtered gold nanoparticle layer on top of polystyrene” S. Roth, et al.; Appl. Phys. Lett. 88, 021910 (2006)
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
Thin films: Spin-Coating
Thickness(~nm) : concentration; w
LIPSS: Interference between the incident light and the light dispersed by the surface.
L
Periodicity:
Laser parameters:
Wavelength (266 nm)
Fluence (~ mJ/cm2)
Number of pulses
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
Laser-Induced Periodic Surface Structures (LIPSS)
Laser-Induced Periodic Surface Structures (LIPSS)
Fluence:
7 mJ/cm2 100 pulses 600 pulses 3000 pulses
(a) (b)(a) (b)
Poly (trimethylene terephthalate) (PTT),
x=3
600 pulses
AFM
I. Martín-Fabiami, et al.; Langmuir 28, 7938 (2012)
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
Laser-Induced Periodic Surface Structures: GISAXS
Simulated GISAXS
H; R; W: Measured by AFM
H
2R
2W
In order to assess the level of order we used a one-
dimensional paracrystalline lattice
L
The probability of finding a particle at a distance L
is defined by a probabilistic function p(x)
paracrystalline distortion parameter: g= DL/L
DL
IsGISAXS http://www.insp.jussieu.fr/axe2/Oxydes/IsGISAXS/isgisaxs.htm, 2002
g→ 0
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
Nanoimprint lithography (NIL)
Clean room (IMB-CSIC)
RIE
Fabrication of mould:
Nanoimprint:
5x5 mm2
Mould
5x5 mm2
NIL
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
GISAXS: NIL vs LIPSS
LIPSS
Mould NIL
Experimental GISAXS:
Simulated GISAXS:
D.R. Rueda et al.; J. Appl. Cryst. 45, 1038 (2012)
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
• Europe: - ESRF: ID2, ID10, ID13, BM26
- Alba:NCD
- Diamond: I22
- Soleil: SWING
- BESSY: mSpot
- Elettra: BL5.2L
• UUEE: - APS: 1-ID, 8-ID, 18-ID
- ALS: 7.3.3
• Asia: - Spring-8: BL08B2, BL40B2, BL45XU
SAXS Workshop. Barcelona, 1st October 2014 [email protected]
Condensed Matter Physics, G. Strobl, Springer.
Neutrons, X-rays and Light: Scattering Methods Applied to Soft
Condensed Matter P. Lindner, T. Zemb Ed., Elsevier: 2002.
Small Angle X-ray Scattering, O. Glatter, O. Kratky Ed., Academic
Press, London (1982).
Synchrotron Light to Explore Matter, ISBN 3-540-14888-4 ©
Copyright IMediaSoft® (Bucharest and Meylan) ESRF (Grenoble)
and Springer-Verlag (Berlin, Heidelberg) 2001.
Applications of Synchrotron Light to Scattering and Diffraction in
Materials and Life Sciences, T.A. Ezquerra, M.C. García-Gutiérrez, A.
Nogales, M.A. Gómez Ed., Lect. Notes Phys. 776 Springer, (Berlin,
Heidelberg) 2009.
AUSE: http://auseweb.wordpress.com/
ESUO:http://www.elettra.trieste.it/ELISA/index.php?n=Main.EuropeanSy
nchrotronUserOrganization
SAXS Workshop. Barcelona, 1st October 2014 [email protected]