SPRINT COMPOSITES |TECHNICAL CATALOGUE
3
A LARGE COMPANY AT A HUMAN SCALE
The wide range of solutions offered by the company is designed by a team of specialized technicians,
who aim to achieve the best in terms of technological innovation, performance and cost/benefi t ratio.
Present in more than 100 countries worldwide, strong, stable and constantly growing, ICR is an
International company which remains faithful to its vocation for tailor-made products. This is clear not
only in the care spent in developing and manufacturing each single product but also in the
open approach it has towards each customer, providing assistance in each stage of the purchase.
1980
1969
4 SPRINT COMPOSITES | TECHNICAL CATALOGUE
MADE IN ITALY EXCELLENCE
ICR was founded and was immediately committed in the manufacturing of chemical products for car refi nishes, marble and stones.
1961
1962
The associated company, ICR Ibérica, is incorporated in Spain.
ICR’s operations develop in the Western and Eastern Europe markets.
The Sprint brand is launched onto the market, and it immediately stands out in the fi eld of car refi nish.
2011
5
2001
2004/2005
ICR acquires a 30,000sm plant in Lodi, which is active in the exclusive production of paints.
ICR enters the colour world, taking over Brenen Italiana, whose headquarters are in Perugia and holds an historical brand of liquid industrial paints.
ICR entered the composites sector. The major Italian shipyards started certifying ICR products.
STRUCTURAL ADHESIVES
X07 EXTREME - ACRYLIC-URETHANE STRUCTURAL ADHESIVE
8 SPRINT COMPOSITES | TECHNICAL CATALOGUE
DescriptionA Urethane-acrylate thixotropic structural adhesive. Excellent structural adhesive properties on FRP (Fibre Reinforced Polymers) and metal substrates, such as steel, aluminum and its light alloys.
Main Features- remarkable elasticity- elevated mechanical properties- low linear shrinkage- very high chemical/ physical resistances
Certifi cationX07 Extreme obtained the RINA (Registro Italiano Navale e Aeronautico) certifi cate as structural adhesive: Certifi cate N° DIP147011CS released on 2011-08-09.
HardenersKetanox B18 (MEK Peroxide solution at 50%) or C08 (Cyclohexanone Peroxide Solution).
Catalysis ratio1-3%
General featuresPROPERTY UNIT VALUE
Colour - Blue ViracolorGel Time1 min 50
Fixture Time2 hours 6Specifi c Weight Kg/l 1,15
Thermal and Mechanical DataPROPERTY U.M. VALUE
Elastic modulus MPa 140Strain at break MPa 9,6
Tg °C 95Exotermic Peak °C 66
Properties RESISTANT TO DIESEL FUELLap shear strength tests, 12 hr conditioning, 2 hr at 80° C, immersion in diesel fuel for 7 days at 23° C
PackagingX07 Extreme is supplied in the following containers:- 4 Liters- 20 Liters- 200 Liters
StorageExtreme should be stored in its original container and out of direct sunlight. The recommended storage temperature is under 20 °C. In those condition the shelf-life of Extreme is 12 month from the expedition date.
NotesApplication should be carried out at temperatures above 15 °C.
1Catalysis at 2% with Ketanox B18, at 25 °C, on 20g of product.2Time at 23 °C to achieve 1,5 MPa strenght in lap-shear test according to ASTM D6868.
POLIFIBRE STRUCTURAL VEVINYLESTER FLEX PUTTY P40EXTREME - ACRYLIC-URETHANE
STRUCTURAL ADHESIVE
9
DescriptionStructural adhesive based on special vinylester resin, with excellent mechanical properties, like fl exibility and adhesion power. Suitable for adhesion with FRP, metals (steel, aluminum, light allows).
Main Features- white colour- easy to sand- very good chemical resistance
Recommended usesRecommended for FRP (Fibre Reinforced Polymers) structures and metals, such as steel, aluminum and light alloys.It is used in sectors like marine, railways, truck industry, etc.Thanks to its capacity of deformation, it favours the structural adjustment, counteracting delamination/cracking problems in the bonding points.
PropertiesP40 has high bond strength, excellent fl exibility, high mechanical properties (see table), low linear shrinkage, good chemical and physical resistance. It is suitable for mechanical application.
PROPERTY U.M. VALUE
Colour - Blue colour-changing
Gel Time 2% M50 (MEKP 50%)at 25°C min 60 ± 10
Gel Time 2% C08 (CEP) at 25°C min 65 ± 10
Specifi c weight Kg/l 1,40 - 0,10
Surface preparationDegrease and clean the surface with V09, in order to remove traces of pollutants and sand.
HARDENERS CATALYSIS RATIO
M50 (MEK 50%) 1-3%
Thermal and Mechanical DataPROPERTY U.M. VALUE
Deformation % 17Strain at break MPa 8,5
Linear shrinkage % 0,2Tg °C 71
PackagingP40 is supplied in: - pails 25kg net- drums 250 kg net
StorageStore the product in the original, sealed packaging at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 4 months from the date of shipment..
NotesApplication should be carried out at temperatures above 15 °C.
POLYESTER ADHESIVES
Recommended usesP05 is a bonder formulated for use on fi breglass parts. It can be used for:- fi lling of edges and curves of medium-small radius
HardenersP05 is a two-component bonder which must be accuratelymixed with the specifi c C08 liquid hardener (Cyclohexanone peroxide).
Catalysis ratioP05 should be mixed with a percentage of hardener that takes into account the ambient temperature, never less than 5°C, in which the process is carried out.
CATALYSIS AND TEMPERATURE C08 LIQUID HARDENERbetween 5 and 10° C 3,0%
between 10 and 20° C 2,0%over 20° C 1,0%
PropertiesWhen the product is applied, it will assume mechanicalproperties that depend on the type of hardener used and thetemperature at which the process has been carried out. Thecharacteristics measured at 20°C are:
Reinforced putty P05 with Liquid Hardener C08PROPERTY U.M. VALUE
Colour - viracolourGel Time min 55 ± 15
Specifi c weight kg/l 1,35 ± 0,05Linear shrinkage1 % 0,19Shore Hardness D D 73
Tg (after 2 hours at 80°C)2 °C 56HDT (after 2 hours at 80°C)3 °C 55Tensile Modulus of elasticity4 MPa 3027Flexural Modulus of elasticity5 MPa 3917
PackagingP05 is supplied in:- drums containing 25 kg net
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 1 year from the date of shipment.
P05 POLIVIR WITH FIBRESLOW-SHRINKAGE FILLING BONDER
DescriptionColours-changing bonder based on unsaturated polyester resins and fi bres.
Main Features- shrinkage near to zero- easy to apply- high degree of hardness
12 SPRINT COMPOSITES | TECHNICAL CATALOGUE
1DSC Test at 20°C/min under N2, ISO 113572DMA Test, ASTM D648-013Dynamometer Test, ISO 527-14Dynamometer Test, UNI EN ISO 178
Recommended usesP23 is a specially-formulated fi ller bonder for the production and repair of fi breglass items. It is excellent when used for:- fi lling edges and small-medium radius.
HardenersP23 is a two-component fi ller bonder and must be mixedthoroughly with the specifi c liquid hardener C08(Cyclohexanone peroxide).
Catalysis ratioP23 bonder must be mixed with a percentage of hardenertaking the current room temperature where it will be usedinto account. Never work at temperatures below 5°C.
CATALYSIS AND TEMPERATURE HARDENER LIQUID C08between 5 and 10° C 3,0%
between 10 and 20° C 2,0%above 20° C 1,0%
PropertiesAfter application, the properties of the bonder vary according to the type of hardener used and the working temperature. At 20° C, the specifi cations of P23 bonder are illustrated in the table below.
P23 fi ller bonder with C08 Liquid HardenerPROPERTY U.M. VALUE
Colour - Light Blueviracolour
Gel Time min 60 ± 20Specifi c weight kg/l 1,45 ± 0,05
Linear shrinkage1 % 0,4Shore Hardness D D 73
Tg (after 2 hours at 80°C)2 °C 72HDT (after 2 hours at 80°C)3 °C 67Tensile modulus of elasticity4 MPa 1930
PackagingP23 is supplied in:- 4 L tins- 25 kg drums- drums containing 250 kg net
Storage Store in the original, saled packaging at a temperature below 20°C. Do not expose to heat or sunlight. The product will remain stable for 1 year after shipment in these conditions.
POLIVIR WITH FIBRES SOFTSOFT LOW-SHRINKAGE FILLING BONDER P23POLIVIR WITH FIBRES
LOW-SHRINKAGE FILLING BONDER
DescriptionColour-changing fi ller bonder made with unsaturated polyester resins and fi bres.
Main Features- shrinkage close to zero- very easy to apply- optimum hardness- good fl exibility
13
1After 2 h at 80°C2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-014Dynamometer Test, ISO 527-1
14 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesP26 is a specifi cally-formulated fi ller bonder for the production and repair of fi breglass items. It is excellent when used for:- fi lling of edges and curves of medium-small radius.
HardenersP26 is a two-component fi ller bonder and must be mixedthoroughly with the specifi c liquid hardener MEKp (methylethyl ketone peroxide).
Catalysis ratioP26 bonder must be mixed with a percentage of hardenertaking the current room temperature where it will be usedinto account.Never work at temperatures below 5° C.
CATALYSIS AND TEMPERATURE MEKP LIQUID HARDENERbetween 5 and 10° C 3,0%
between 10 and 20° C 2,0%above 20° C 1,0%
PropertiesAfter application, the properties of the bonder vary according to the type of hardener and the working temperature. At 20° C, the specifi cations of P26 bonder are illustrated in the table below.
P26 fi ller bonder with 2% MEKp Liquid HardenerPROPERTY U.M. VALUE
Colour - neutralGel Time min 65 ± 15
Specifi c weight kg/l 1,50 ± 0,5Linear shrinkage1 % 0,3Shore Hardness D D 73
Tg (after 2 hours at 80°C)2 °C 91HDT(after 2 hours at 80°C)3 °C 64Tensile modulus of elasticity
(after 2 hours at 80°C)4 MPa 4215
PackagingP26 fi ller bonder is supplied in:- 25 kg drums (net weight)
StorageStore in the original, sealed packaging at a temperature ofless than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 4 months from the date of shipment.
DescriptionFiller bonder consisting of unsaturated polyester resins and fi bres.
Main Features- no vertical dripping- very easy to apply- optimum hardness- good fl exibility
1After 2 h at 80°C2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-014Dynamometer Test, UNI EN ISO 178
P26 POLYFIBRE SOFT TXLOW-SHRINKAGE MULTIPURPOSE BONDER
POLIFIBRE SOFT TX FASTFAST LOW-SHRINKAGE MULTIPURPOSE BONDER P28
15
POLYFIBRE SOFT TXLOW-SHRINKAGE MULTIPURPOSE BONDER
Recommended usesP28 is specially-formulated for the production,repair and adhesion of FRP items. It is excellentwhen used for:- fi lling small to medium radius edges and curves- assembly of FRP products
HardenersP28 is two-components and must be mixedaccurately with the specifi c liquid hardener,MEKP (methyl ethyl ketone peroxide).
Catalysis ratioMix with a percentage of hardener taking the current room temperature where it will be used into account. Never work at temperatures below 5°C.
CATALYSIS AND TEMPERATURE MEKP LIQUID HARDENERbetween 5 e 10° C 3,0%
between 10 e 20 °C 2,0%above 20 °C 1,0%
PropertiesAfter application, the properties vary according to the type of hardener used and the working temperature. At 20°C, the specifi cations are illustrated in the following table.
P28 Polifi bre with 2% Liquid Hardener MEKPPROPERTY U.M. VALUE
Colour - neutralGel Time min 30± 5
Specifi c weight kg/l 1,49 ± 0,05Linear shrinkage1 % 0,3Shore Hardness D D 73
Tg (after 2 hours at 80°C)2 °C 91HDT(after 2 hours at 80°C)3 °C 64Tensile modulus of elasticity
(after 2 hours at 80°C)4 MPa 4215
PackagingP28 is supplied in:- 25 kg pails.
StorageStore in the original, sealed packaging at atemperature below 20°C. Do not expose to heator sunlight. The product will remain stable for 1 year from the date of production.
DescriptionAdhesive-Filler based on unsaturated polyesterresins and glass fi bres.
Main Features- does not sag on vertical application- easy to apply by spatula.- high degree of hardnes- good fl exibilty- rapid hardening
1After 2 h at 80°C2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-014Dynamometer Test, UNI EN ISO 178
P30 POLIFIBRE MF AMCFLUID PUTTY WITH MICROFIBRES
16 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesP30 is a specially-formulated for generaladhesion on fi breglass reinforced plastic items. It is excellent when used for:- Production of FRP items.- Filling edges and small medium radius
HardenersP30 is two-component and must be mixedthoroughly with liquid or paste hardener.
Catalysis ratioP30 must be mixed with a percentage of hardener taking the current room temperature where it will be used into account. Never work at temperature below 5°C.
HARDENERS GEL TIME2% (MEKP) B180 / M50 40 ± 3’
2% (PB) Paste 18 ± 3’
PropertiesAfter application, the properties vary according to the type of hardener used and the working temperature. At 20°C, the specifi cations of P30 are illustrated in the following table.
P30PROPERTY U.M. VALUE
Colour - Light blueSpecifi c weight kg/l 1,35 ± 0,05Elastic modulus1 MPa 2175
PackagingP30 is supplied in:- Pails or drums containing 25 and 230 kg net
Storage Store in the original, sealed packaging at a temperature below 20°C. Do not expose to heat or sunlight. The product will remain stable for 1 year from the date of production in these conditions.
DescriptionAdhesive with colour changing, based on unsaturated polyester resins and glass microfi bres.
Main Features- suitable to mechanical application- good adhesion- good fl exibility- low shrinkage
1Dynamometer Test, ISO 527-1
TEX FIBREGLASS PUTTY GENERAL PURPOSE PUTTY WITH FIBRES P50POLIFIBRE MF AMC
FLUID PUTTY WITH MICROFIBRES
17
Recommended usesP50 has been formulated for assembling glass-reinforcedplastic and different materials together. It can be used inprocesses such as:- Positioning bulkheads when the interiors are assembled- Gluing match-moulds, walls and ceilings- Stoppering the hull and parts in fi breglass-reinforced plastic
HardenersP50 is a two-component reinforced putty which must beaccurately mixed with the specifi c C10 paste hardener(Dibenzoyl peroxide).
Catalysis ratioP50 should be mixed with a percentage of hardener that takes into account the ambient temperature, never less than 5°C, in which the process is carried out.
CATALYSIS AND TEMPERATURE C10 PASTE HARDENERbetween 5 and 10° C 3,0%between 10 and 20° C 2,0%
over 20° C 1,0%
Do not exceed these percentages. Excessive amounts of hardener can lead to peroxide stains during the fi nishing phase.
PropertiesWhen the product is applied, it will assume mechanicalproperties that depend on the temperature at which the process has been carried out. The characteristics measured at 20°C are:
Reinforced putty P50 with Paste Hardener C10PROPERTY U.M. VALUE
Colour - grey-greenGel Time min 6
Specifi c weight kg/l 1,60 ± 0,10Linear shrinkage1 % 0,35Shore Hardness D D 65Min. sanding time min 40
Tg (after 2 hours at 80°C)2 °C 97HDT (after 2 hours at 80°C)3 °C 82Flexural modulus of elasticity4 MPa 3670
PackagingP50 is supplied in:- 750 ml tins- 4 L tins- drums containing 25 kg net
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 4 months from the date of shipment.
DescriptionPutty based on unsaturated polyester resins, reinforced with glass fi bres and mineral fi llers.
Main Features- optimum workability- easily sanded- good degree of hardness- optimum mechanical strength
1After 2 h at 80°C2DSC Test at 20°C/min under N2 ISO 113573DMA Test, ASTM D648-014Dynamometer Test, UNI EN ISO 178
Recommended usesP54 has been formulated for assembling glass-reinforcedplastic panels and joining different materials. It can be used in processes such as:- Bulkheads positioning- Tacking longitudinal members to the hull whilst it is being laminated- Bulwarks, walls and ceilings positioning
HardenersP54 is a two-component reinforced putty which must beaccurately mixed with the specifi c C10 paste hardener(Dibenzoyl Peroxide) or C08 liquid hardener (Cyclohexanone peroxide).
Catalysis ratioP54 should be mixed with a percentage of hardener that takes into account the ambient temperature, never less than 5° C, in which the process is carried out.
CATALYSIS ANDTEMPERATURE
C10 PASTE HARDENER
C08 LIQUID HARDENER
between 5 and 10° C 3,0% 3,0%between 10 and 20° C 2,0% 2,0%
over 20° C 1,0% 1,0%
If the C10 hardener is used, do not exceed these percentages. Excessive amounts of hardener can lead to peroxide stains during the fi nishing phase.
PropertiesWhen the product is applied, it will assume mechanicalproperties that depend on the type of hardener used and thetemperature at which the process has been carried out. The characteristics measured at 20°C are:
P54 Reinforced putty C10 Paste Hardener
C08 Liquid Hardener
PROPERTY U.M. VALUEColour - grey
Gel Time min 7,5 ± 2,5 28 ± 7,0Specifi c weight kg/l 1,66 ± 0,10
Linear shrinkage1 % 0,400 0,400Shore Hardness D D 70 70Min. sanding time min 30 120Exothermic peak °C 78 62
Tg (after 2 hours at 80°C)2 °C - 74HDT (after 2 hours at 80°C)3 °C - 57Tensile Modulus of elasticity4 MPa - 3535Flexural Modulus of elasticity5 MPa - 5431
PackagingP54 is supplied in:- drums containing 25 kg net
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 4 months from the date of shipment.
P54 P/L GREY POLIFIBREREINFORCED PUTTY WITH FIBRES
DescriptionPutty based on unsaturated polyester resins, reinforced with organic fi bres, glass fi bres up to 3 mm in length and mineral fi llers.
Main Features- optimum mechanical properties- high bond- good thixotropy
18 SPRINT COMPOSITES | TECHNICAL CATALOGUE
1After 2 h at 80°C2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-014Dynamometer Test, ISO 527-15Dynamometer Test, UNI EN ISO 178
POLIFIBRE SOFT SOFT FILLING PUTTY P64P/L GREY POLIFIBRE
REINFORCED PUTTY WITH FIBRES
19
Recommended usesP64 is suitable for general adhesion; it is used for:- Assembling FRP parts.- Filling of edges and medium curves.- Suitable for eliminating defects on FRP surfaces
HardenersP64 is two-components and must be mixed thoroughly with paste hardener C10 (Benzoyl peroxide) or liquid hardeners C08 (Cyclohexanone peroxide) or MEKP.
Catalysis ratioP64 must be mixed with a percentage of hardener taking into account the current room temperature where it will be used. Never work at temperature below 5°C.
HARDENERS GEL TIME2% (MEKP) B180 / M50 22’ ± 2’
2% (MEKP) C28 120’± 10’2% (CEP) C08 60’ ±10’
2% ((BPO) Paste 13’ ± 2’
PropertiesAfter application, the properties vary according to the type of hardener used and the working temperature. At 20°C, the specifi cations of P64 are illustrated in the following table:
P64PROPERTY U.M. VALUE
Colour - Light blueSpecifi c weight kg/l 1,5 ± 0,1
Linear shrinkage1 % 1,5 ± 0,1Tensile elastic modulus2 (after 2 hours at 80°C) MPa 4770
PackagingP64 is supplied in:- Pails or drums containing 25 and 230 kg net
Storage Store in the original, sealed packaging at a temperature below 20°C. Do not expose to heat or sunlight. The product will remain stable for 1 year from the date of production in these conditions.
DescriptionTo be used as adhesive and fi llers, based onunsaturated polyester resins and mineral fi llers.
Main Features- soft aspect- good adhesion- good verticality
1After 2 h at 80°C2Test with INSTRON 5582, Iso 527-1
P69 POLIERRE VIRACOLOR FILLING PUTTY WITH FIBRES
20 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesP69 is specially-formulated for assembling ofFRP items and bonding of other materials; it isexcellent when used for:- Spars and Bulkheads fi xing- Assembling the structure of the model
HardenersP69 is two-components and must be mixed thoroughly with the specifi c paste hardener C10 (Benzoyl peroxide) or liquid hardener C08 (Cyclohexanone peroxide).
Catalysis ratioP69 must be mixed with a percentage of hardener taking the current room temperature where it will be used into account. Never work at temperature below 5°C.
CATALYSIS ANDTEMPERATURE
C10 PASTE HARDENER
C08 LIQUID HARDENER
between 5 and 10° C 3,0% 3,0%between 10 and 20° C 2,0% 2,0%
over 20° C 1,0% 1,0%
If the C10 hardener is used, do not exceed thesepercentages. Excessive amount of hardener can lead to peroxide stains during the fi nishing phase.
PropertiesAfter application, the properties vary according to the type of hardener used and the working temperature. At 20°C, the specifi cations of P69 are illustrated in the following table.
P69 with hardener C10 Paste Hardener
C08 Liquid Hardener
PROPERTY U.M. VALUEColour - Blue
Gel Time min 4,5 ± 1,5 27 ± 5,0Specifi c weight kg/l 1,70 ± 0,10
Linear shrinkage1 % 0,950 0,950Shore Hardness D D 78 78Min. sanding time min 70 360
Tg (after 2 hours at 80°C)2 °C 65 65HDT(after 2 hours at 80°C)3 °C 62 59
PackagingP69 is supplied in:- pails containing 4 kg net- pails containing 25 kg net
StorageStore in the original, sealed packaging at a temperature below 20°C. Do not expose to heat or sunlight. The product will remain stable for 1 year from the date of production in these conditions.
DescriptionBased on unsaturated polyester resins, glassfi bres and mineral fi llers.
Main Features- very good application by spatula- good mechanical properties
1After 2 h at 80°C2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-01
POLYESTER PUTTY WITH FIBRESFILLING PUTTY FOR LEVELLING P71POLIERRE VIRACOLOR
FILLING PUTTY WITH FIBRES
21
Recommended usesIt is a putty formulated for fi lling / levelling and repairing fi breglass and metal surfaces which are not submerged, where higher than the normal thicknesses provided by common putties are required. The optimum balance of its features allows the repair of wide surfaces, for thicknesses up to 4mm. After sanding, the levelled application of autobody / nautical putty is recommended before successive jobs.
HardenersIt is a two-component putty and must be mixed thoroughly with the specifi c liquid hardener methyl ethyl ketone peroxide (MEKP).
Catalysis ratioMix with a percentage of hardener between 1 – 3% taking into account the current room temperature where it will be used. Never work at temperatures below 5°C.
Reactivity% MEKP 50% T°C GEL TIME
2 22 9’ – 12’2 15 20’ – 28’
Properties
General features with 2% MEKP Hardener Liquid 50%PROPERTY U.M. VALUE
Colour - Light blue Viracolor
Specifi c weight kg/l 1,57 ± 0,10Linear shrinkage % 0,3 ± 0,1
PackagingThe putty is supplied in:- 25 kg (net) drums
StorageStore in the original, closed packaging at a temperature below 20°C. Do not expose to heat or sunlight. In these conditions the product will remain stable for 6 months from the shipping date.
DescriptionUnsaturated polyester and mineral-based fi llingputty with soft consistency.
Main Features- excellent spatola application- good sanding- good fl exibilty
P73 POLIERRE VIRACOLOR SOFTSOFT FILLING MULTIPURPOSE PUTTY
22 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended uses P73 is ideal for the assembly of fi breglass items for the adhesion of various materials, and for small fi llings.
HardenersP73 is a two-component fi ller bonder and must be accurately mixed with the specifi c hardener paste C10 (benzoyl peroxide) or liquid hardener C08 (cyclohexanone peroxide), or liquid MEKP 50%.
Catalysis ratioP73 bonder must be mixed with a percentage of hardener taking the current room temperature where it will be used into account. Never work at temperatures below 5°C.
CATALYSIS ANDTEMPERATURE
C10 PASTE HARDENER
C08 LIQUID HARDENER
between 5 and 10° C 3,0% 3,0%between 10 and 20° C 2,0% 2,0%
over 20° C 1,0% 1,0%
In the case of using C10 Hardener, do not exceed the stated percentages. Excessive hardener can cause peroxide staining in the fi nishing stage.
PropertiesAfter application, the properties of the bonder vary according to the type of hardener used and the working temperature. At 20° C, the specifi cations of P73 bonder are illustrated in the table below.
P73 Bonder fi ller C10 Paste Hardener
C08 Liquid Hardener
PROPERTY U.M. VALUEColour - Light blue
Gel Time min 4,5 ± 1,5 27 ± 5,0Specifi c weight kg/l 1,70 ± 0,10
Linear shrinkage1 % 0,950 0,790Shore Hardness D D 78 78Min. sanding time min 70 360
Tg (after 2 hours at 80°C)2 °C 65 66HDT (after 2 hours at 80°C)3 °C 62 59
PackagingP73 is supplied in: 25 kg (net) drums
StorageStore in the original, closed containers at a temperature below 20°C. Do not expose to heat or sunlight. The product will remain stable for 1 year after production in these conditions.
DescriptionColour-changing unsaturated polyester-based fi lling bonder, reinforced with special microfi bres and lamellar fi llers.
Main Features- high softness- notable hardness- good mechanical resistance.- brush appliable
1Internal method2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-01
POLIERRE VIRACOLOR SOFTSOFT FILLING MULTIPURPOSE PUTTY
23
VINYLESTER ADHESIVES
P13 FILLING ADHESIVE VE AMC FLUID VINYLESTER ADHESIVE
24 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesP13 is excellent when used for:- general bonding of FRP items- fi lling edges and small medium curves- repairing of damaged surfaces
HardenersP13 is two-component and must be mixed thoroughly with liquid hardeners.
Catalysis ratioP13 must be mixed with a percentage of hardener taking the current room temperature where it will be used into account. Never work at temperature below 5°C.
HARDENERS GEL TIME2% (MEKP) B18 / M50 35’ ± 5’
2% (CEP) C08 60’± 10’
PropertiesAfter application, the properties vary according to the type of hardener used and the working temperature. At 25°C, the specifi cations of P13 are illustrated in the following table.
P13 with 2% MEKPPROPERTY U.M. VALUE
Colour - Olive greenviracolour
Specifi c weight kg/l 1,5 ± 0,1Tg (after 2 hours at 80°C)1 °C 78
Linear Shrinkage2 % 0,9 ± 0,1HDT(after 2 hours at 80°C)3 °C 74.5
Elastic modulus4 MPa 1546 ± 110
PackagingP13 is supplied in:- Pails and drums containing 25 and 230 kg net
Storage Store in the original, sealed packaging at a temperature below 20°C. Do not expose to heat or sunlight. The product will remain stable for 4 months from the date of shipment in these conditions.
DescriptionAdhesive-Filler with colour changing, based onunsaturated polyester resins.
Main Features- suitable for machine application- very good adhesion- good chemical and osmosys resistance- good fl exibility
1DSC Test at 20°C/min under N2, ISO 113572After 2 h at 80°C3DMA Test, ASTM D648-01 4Dynamometer Test, ISO 527-1
ADHESIVE WITH FIBRES VEVINYLESTER ADHESIVE WITH FIBRES P14FILLING ADHESIVE VE AMC
FLUID VINYLESTER ADHESIVE
25
Recommended usesFor general adhesion on FRP. It is excellent when used for:- general glueing of FRP parts.- fi lling edges and medium radius curves- repairing damaged surfaces
HardenersMix accurately with liquid hardener (MEKP 50%).
Catalysis ratioMix with a percentage of hardener taking the current room temperature where it will be used into account. Never work at temperatures below 5°C.
PropertiesAfter application, the properties vary according to the type of hardener used and the working temperature. At 20°C, the specifi cations are illustrated in the following table.
HARDENERS GEL TIME2% (MEKP) B180/ M50 22 ± 2’
P14 with 2% MEKPPROPERTY U.M. VALUE
Colour - Olive greenSpecifi c weight kg/l 1.5 ± 0,1
Tg (after 2 hours at 80°C)1 °C 89HDT(after 2 hours at 80°C)2 °C 87
Linear Shrinkage3 % 0.6 ± 0,2Tensile modulus of elasticity
in fl exure4 MPa 3844
PackagingP14 is supplied in:- 25 kg pails- Drums containing 250 kg net
Storage Store in the original, sealed packaging at a temperature below 20°C. Do not expose to heat or sunlight. The product will remain stable for 4 months from the date of shipment.
DescriptionAdhesive-Filler with colour-changing, based on vinylester resins, reinforced with glass microfi bres. Soft look, does not undergo rheological modifi cation with hardening.
Main Features- suitable for machine application- very good adhesion- chemical and osmosys resistance.- does not sag on vertical application
- low shrinkage- good fl exibilty
1DSC Test at 20°C/min under N2, ISO 113572DMA test, ASTM D648-013After 2 h at 80°C4Dynamometer Test, UNI EN ISO 178
P15 ADHESIVE WITH FIBRES VE FASTFAST VINYLESTER ADHESIVE WITH FIBRES
26 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesFor general adhesion. It is excellent when used for:- glueing of FRP parts- fi lling edges and medium radius curves- repairing damaged surfaces
HardenersMix accurately with liquid hardener (MEKP 50%).
Catalysis ratioMix with a percentage of hardener taking the current room temperature where it will be used into account. Never work at temperatures below 5°C.
PropertiesAfter application, the properties vary according to the type of hardener used and the working temperature. At 20°C, the specifi cations are illustrated in the following table.
HARDENERS GEL TIME2% (MEKP) B180/ M50 11 ± 1’
P15 with 2% MEKPPROPERTY U.M. VALUE
Colour - Olive greenSpecifi c weight kg/l 1,5 ± 0,1
Tg (after 2 hours at 80°C)1 °C 89HDT(after 2 hours at 80°C)2 °C 87
Linear shrinkage3 % 0,6 ± 0,2Tensile modulus of elasticity
in fl exure4 MPa 3884
PackagingP15 is supplied in:- 25 kg pails- drums containing 250 kg net
Storage Store in the original, sealed packaging at a temperature below 20°C. Do not expose to heat or sunlight. The product will remain stable for 4 months from the date of shipment.
DescriptionAdhesive with colour-changing, based on vinylester resin with glass fi bres, for glueing and fi lling. P15 does not undergo rheological deformation with hardening.
Main Features- suitable for machine application- high adhesion power- chemical and osmosys resistance.- does not sag on vertical application
- low shrinkage- good fl exibilty
1DSC Test at 20°C/min under N2, ISO 113572DMA Test, ASTM D648-013After 2 h at 80°C4Dynamometer Test, UNI EN ISO 178
POLIVIR WITH FIBRES VEFILLING VINYLESTER PUTTY WITH FIBRES P25ADHESIVE WITH FIBRES VE FAST
FAST VINYLESTER ADHESIVE WITH FIBRES
27
- low shrinkage- good fl exibilty
Recommended usesP25 is expressly formulated to repair anti-osmosis laminates. It can be used in processes such as:- Hulls’ joining- Repairing of surfaces damaged by osmosis- Filling of small-medium radius edges and curving
HardenersP25 is a two-component reinforced putty which must beaccurately mixed with the specifi c C08 hardener(Cyclohexanone peroxide).
Catalysis ratioP25 should be mixed with a percentage of hardener that takes into account the ambient temperature, never less than 5°C, in which the process is carried out.
CATALYSIS AND TEMPERATURE C08 LIQUID HARDENERbetween 5 and 10° C 3,0%
between 10 and 20° C 2,0%over 20° C 1,0%
PropertiesWhen the product is applied, it will assume mechanicalproperties that depend on the temperature at which the process has been carried out. The characteristics measured at 20°C are:
Reinforced putty P25 with Liquid Hardener C08PROPERTY U.M. VALUE
Colour - viracolourGel Time min 40 ± 5,0
Specifi c weight kg/l 1,25 ± 0,05Linear shrinkage1 % 0,4Shore Hardness D D 70Min. sanding time min 270
Tg (after 2 hours at 80°C)2 °C 105HDT (after 2 hours at 80°C)3 °C 97
PackagingP25 is supplied in:- drums containing 25 kg net- drums containing 250 kg net
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 4 months from the date of shipment.
DescriptionVinylester resins reinforced with organic fi bres, glass fi bres (max length 3 mm) and mineral fi llers.
Main Features- high resistance to osmosis- thixotropic, no sagging by vertical application- high mechanical properties- optimum adhesion- optimum fl exibility
1After 2 h at 80°C2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-01
28 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesIdeal for fi lling and levelling of fi breglass and metal surfaces where higher than the normal thicknesses are required with repairs up to 4mm. After sanding, the level-led application of VE nautical putty, S11 or S12, is recommended before successive jobs.
HardenersIt is a two-component putty and must be mixed accurately with the specifi c liquid hardener methyl ethyl ketone peroxide (MEKP 50%).
Catalysis ratioMix with a percentage of hardener between 1 – 2%. Never work at temperatures below 5°C.
Reactivity at 23°C, catalysis in weight% CAT. GEL TIME SANDABLE
1 ~ 40’ > 180’2 ~ 34’ > 130’
General featuresPROPERTY U.M. VALUE
Colour - white (Ral 9016)Specifi c weight kg/l 1,60 ± 0,10
G. Time 26°C 2% MEKP min 27’Linear shrinkage % 0,2 ± 0,1
Tg (after 2 hr 80°C)1 °C 87HDT (after 2 hours at 80°C)2 °C 78
PackagingThe putty is supplied in: - 25 kg (net) drums
StorageStore in the original, closed packaging at a temperature below 20°C. Do not expose to heat or sunlight. In these conditions the product will remain stable for 4 months from the shipping date.
DescriptionSoft-consistancy white putty, based on vinylester resin, mineral fi ller, reinforced with microfi bres.
Main Features- good spatola application- high adhesive power- low shrinkage- good sanding
P72 VINYLESTER PUTTY WITH FIBRESFILLING VINYLESTER PUTTY FOR LEVELLING
1DSC Test at 20°C/min under N2, ISO 113572DMA test, ASTM D648-01
VINYLESTER PUTTY WITH FIBRESFILLING VINYLESTER PUTTY FOR LEVELLING
PUTTIES
SM1 ULTRALIGHT PUTTY ULTRA LIGHTWEIGHT PUTTY FOR MODELS
30 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesSM1 is a putty formulated for the fi lling of wood and fi breglass handworks. It is used mainly in the marine sector for models shaping. Excellent venting and spreading without any porosity.
HardenersSM1 is a two-component putty which must be accurately mixed with the specifi c C10 paste hardener (Dibenzoyl Peroxide).
Catalysis ratio
CATALYSIS AND TEMPERATURE C10 PASTE HARDENERbetween 5 and 10° C 3,0%between 10 and 20° C 2,0%
over 20° C 1,0%
Do not exceed these percentages. Excessive amounts of hardener can lead to peroxide stains during the fi nishing phase.
PropertiesWhen the product is applied, it will assume mechanical properties that depend on the temperature at which the process has been carried out. The characteristics measured at 20°C are:
SM1 Putty with 2% C10 Hardener PastePROPERTY U.M. VALUE
Colour - beigeGel Time min 4 ± 1
Specifi c weight kg/l 1 ± 0,05Linear shrinkage1 % 0,80Min. sanding time min 15/30
PackagingSM1 is supplied in:- 4L tins
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 2 years from the date of shipment.
DescriptionLow weight high-performances putty based on unsaturated polyester resins and very fi ne mineral fi llers.
Main Features- beige colour- easy to apply- excellent to sand
1After 2 h at 80°C
GEL FILLER FOR FINISHING VE/PVINYLESTER PUTTY FOR BODYWORK S12ULTRALIGHT PUTTY
ULTRA LIGHTWEIGHT PUTTY FOR MODELS
31
Recommended usesS12 is a putty formulated for fi lling and repairing hullslaminated with vinylester resins; ideal for levelling andfi nishing hulls before the gel-coat fi nal touch. S12 can be used for:- fi nishing hulls- fi nishing aesthetic joints
HardenersS12 is a two-component putty which must be accurately mixed with the specifi c C10 paste hardener (Dibenzoyl Peroxide).
Catalysis ratioS12 should be mixed with a percentage of hardener that takes into account the ambient temperature, never less than 5°C, in which the process is carried out.
CATALYSIS AND TEMPERATURE C10 PASTE HARDENERbetween 5 and 10° C 2,0%between 10 and 20° C 1,5%
over 20° C 1,0%
Do not exceed these percentages. Excessive amounts ofhardener can lead to peroxide stains during the fi nishingphase.
PropertiesWhen the product is applied, it will assume mechanicalproperties that depend on the temperature at which the processhas been carried out. The characteristics measured at 20°Care:
Putty S12 with Paste Hardener C10PROPERTY U.M. VALUE
Colour - whiteGel Time min 6 ± 1
Specifi c weight kg/l 1,67 ± 0,05Linear shrinkage1 % 0,67Shore Hardness D D 64Min. sanding time min 15 - 30
Tg (after 2 hours at 80°C)2 °C 103Tensile Modulus of elasticity3 MPa 10672Flexural Modulus of elasticity4 MPa 9226
PackagingS12 is supplied in:- 750 ml tins- 4 L tins- drums containing 25 kg net
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 4 months from the date of shipment.
DescriptionHigh-performances putty based on vinylester resins and very fi ne mineral fi llers.
Main Features- very easy to apply- no shrinkage- high hardness
1After 2 h at 80°C 2DSC Test at 20°C/min under N2, ISO 113573Dynamometer Test, ISO 527-14Dynamometer Test, UNI EN ISO 178
GEL FILLER FOR FINISHING PE/PHIGH PERFORMANCES POLYESTER PUTTY FOR BODYWORKS14 GEL FILLER FOR FINISHING PE/L
HIGH PERFORMANCES POLYESTER PUTTY FOR BODYWORK
32 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesS14 is a putty formulated for fi nishing glass reinforced plastic panels. S14 can be used for:- fi nishing fi breglass reinforced plastic handworks- fi nishing aesthetic joints- eliminating imperfections and scratches from bodywork
Do not exceed 12-14 mm thickness (to be reached after severalcoats)
HardenersS14 is a two-component putty which must be accurately mixed with the specifi c C08 liquid hardener (Cyclohexanoneperoxide).
Catalysis ratioS14 should be mixed with a percentage of hardener that takes into account the ambient temperature, never less than 5° C, in which the process is carried out.
CATALYSIS AND TEMPERATURE C08 LIQUID HARDENERbetween 5 and 10° C 2,0%
between 10 and 20° C 1,5%over 20° C 1,0%
PropertiesWhen the product is applied, it will assume mechanicalproperties that depend on the temperature at which the process has been carried out. The characteristics measured at 20°C are:
White Putty S14 with Liquid Hardener C08PROPERTY U.M. VALUE
Colour - whiteGel Time min 40 ± 5
Specifi c weight kg/l 1,30 ± 0,05Linear shrinkage1 % 1,20Shore Hardness D D 60Min. sanding time min 120
Tg (after 2 hours at 80°C)2 °C 67HDT (after 2 hours at 80°C)3 °C 54Tensile modulus of elasticity4 MPa 4854
PackagingS14 is supplied in:- 4 L tins- drums containing 25 kg net
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 2 years from the date of shipment.
DescriptionMedium weight high-performances putty based on unsaturated polyester resins and very fi ne mineral fi llers.
Main Features- white colour- easy to sand- high resistance to chemical agents
1After 2 h at 80°C2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-014Dynamometer Test, ISO 527-1
GEL FILLER FOR FINISHING PE/PHIGH PERFORMANCES POLYESTER PUTTY FOR BODYWORK S15GEL FILLER FOR FINISHING PE/L
HIGH PERFORMANCES POLYESTER PUTTY FOR BODYWORK
33
Recommended usesS15 is a putty formulated for fi nishing fi breglass surfaces.S15 can be used for:- fi nishing fi breglass handiworks- eliminating imperfections and scratches from bodywork
Do not exceed 6-8 mm thickness (to be reached after several coats).
HardenersS15 is a two-component putty which must be accurately mixed with the specifi c C10 paste hardener (Dibenzoyl Peroxide).
Catalysis ratioS15 should be mixed with a percentage of hardener that takes into account the ambient temperature, never less than 5°C, in which the process is carried out.
CATALYSIS AND TEMPERATURE C10 PASTE HARDENERbetween 5 and 10° C 3,0%between 10 and 20° C 2,0%
over 20° C 1,0%
Do not exceed these percentages. Excessive amounts ofhardener can lead to peroxide stains during the fi nishingphase.
PropertiesWhen the product is applied, it will assume mechanicalproperties that depend on the temperature at which the process has been carried out. The characteristics measured at 20°C are:
White Putty S15 with Paste Hardener C10PROPERTY U.M. VALUE
Colour - whiteGel Time min 3 ± 1
Specifi c weight kg/l 1,30 ± 0,05Linear shrinkage1 % 0,90Shore Hardness D D 60Min. sanding time min 30
Tg (after 2 hours at 80°C)2 °C 89HDT (after 2 hours at 80°C)3 °C 73
PackagingS15 is supplied in:- 750 ml tins- 4 L tins- drums containing 25 kg net
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 2 years from the date of shipment.
DescriptionMedium weight high-performances putty based on unsaturated polyester resins and very fi ne mineral fi llers.
Main Features- white colour- easy to sand- high resistance to chemical agents
1After 2 h at 80°C2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-01
S22 EASY TOP WHITE WHITE POLYESTER PUTTY
34 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesS22 is a putty formulated for fi nishing wood andFRP parts; it can be used for:- shaping models with by spatula.- fi nishing FRP parts.- fi nishing aesthetic FRP joints.
HardenersS22 is two-components, which must be accurately mixed with the specifi c C10 paste hardener (BPO).
Catalysis ratioS22 should be mixed with a percentage of hardener that takes into account the ambient temperature, never less than 5°C, in which the process is carried out.
CATALYSIS AND TEMPERATURE C10 PASTE HARDENERbetween 5 and 10° C 3,0%between 10 and 20 °C 2,0%
over 20 °C 1,0%
Do not exceed these percentages. Excessive amounts of hardener can lead to peroxide stains during the painting fi nishing.
PropertiesWhen the product is applied, it will assume mechanical properties that depends on the temperature at which the process has been carries out. The characteristics, measured at 20°, are reported in the following table.
S22 with 2% Paste Hardener C10PROPERTY U.M. VALUE
Colour - whiteGel time 20°C min 4 ± 1Specifi c weight kg/l 1,95 ± 0,05
Linear shrinkage1 % 0,61Shore Hardness D D 57Min. sanding time min 40
Tg (after 2 h at 80°C)2 °C 80HDT (after 2 h at 80°C)3 °C 78
PackagingS22 is supplied in- 750 ml net tins- Tins containing 3 L- pails containing 25 kg net
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 2 years from the date of shipment.
DescriptionHigh-performance putty, based on unsaturatedpolyester resins and mineral fi llers.
Main Features- white colour- very easy to sand- high chemical resistance
1After 2 h at 80°C2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-01
EASY TOP PUTTY GREYMULTIPURPOSE GREY PUTTY S71EASY TOP WHITE
WHITE POLYESTER PUTTY
35
Recommended usesS71 is a putty formulated for the use on different surfacessuch as wood and fi breglass. S71 can be used for:- models shaping- fi nishing of fi breglass handiworks
HardenersS71 is a two-component putty which must be accurately mixed with the specifi c C10 paste hardener (Dibenzoyl Peroxide).
Catalysis ratioS71 should be mixed with a percentage of hardener that takes into account the ambient temperature, never less than 5°C, in which the process is carried out.
CATALYSIS AND TEMPERATURE C10 PASTE HARDENERbetween 5 and 10° C 3,0%between 10 and 20 °C 2,0%
over 20 °C 1,0%
Do not exceed these percentages. Excessive amounts ofhardener can lead to peroxide stains during the fi nishingphase.
PropertiesWhen the product is applied, it will assume mechanicalproperties that depend on the temperature at which the process has been carried out. The characteristics measured at 20°C are:
Grey Putty S71 with Paste Hardener C10PROPERTY U.M. VALUE
Colour - greyGel time 20°C min 4 ± 1Specifi c weight kg/l 1,97 ± 0,05
Linear shrinkage1 % 1,22Shore Hardness D D 57Min. sanding time min 40
Tg (after 2 h at 80°C)2 °C 69HDT (after 2 h at 80°C)3 °C 69
PackagingS71 is supplied in:- 750 ml tins- 820 ml cartridge- 4 L tins- drums containing 25 kg net
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 2 years from the date of shipment.
DescriptionHigh-performances putty based on unsaturated polyesterresins and very fi ne mineral fi llers.
Main Features- grey colour- easy to sand- high resistance to chemical agents
1After 2 h at 80°C2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-01
POLIBONDERS
P01 POLIBONDER SOFT LIGHT LIGHT BONDER FOR PANELS
38 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesP01 is a bonder formulated for gluing core materials andfi breglass panels, where high bonding capacity and low weight are important. It can be used for:- gluing open-cell PVC parts- gluing panels made of termanto
HardenersP01 is a two-component bonder which must be accuratelymixed with the specifi c C08 liquid hardener (Cyclohexanoneperoxide).
Catalysis ratioP01 should be mixed with a percentage of hardener that takes into account the ambient temperature, never less than 5°C, in which the process is carried out.
CATALYSIS AND TEMPERATURE C08 LIQUID HARDENERbetween 5 and 10° C 3,0%
between 10 and 20° C 2,0%above 20° C 1,0%
Yield1,5 L/m2
PropertiesWhen the product is applied, it will assume mechanicalproperties that depend on the temperature at which the process has been carried out. The characteristics measured at 20°C are:
Light Bonder P01 with 2% Liquid Hardener C08PROPERTY U.M. VALUE
Colour - viracolourGel time 20°C min 75 ± 25Specifi c weight kg/l 1,0 ± 0,1
Linear shrinkage1 % 0,5Shore Hardness D D 60
Tg (after 2 hours at 80°C)2 °C 78HDT (after 2 hours at 80°C)3 °C 76
Tensile elastic modulus4
(after 2 hours at 80°C) MPa 5486
PackagingP01 is supplied in:- drums containing 15 kg net- drums containing 175 kg net
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 4 months from the date of shipment.
DescriptionSpecial bonder based on unsaturated polyester resins,with light reinforcing fi ller and micro-spheres.
Main Features- very light specifi c weight (1,0 kg/l)- easy o apply- high bonding power
1Post-curing: 48 h r.t.2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-014Dynamometer Test, ISO 527-1
POLIBONDER SOFT LIGHT AMCFLUID BONDER FOR PANELS P02POLIBONDER SOFT LIGHT
LIGHT BONDER FOR PANELS
39
Recommended usesP02 is a specially-formulated bonder for the adhesion of core material, for structural sandwiches where limited weight and high adhesion capacity are essential requirements for quality application. It is excellent when used for:- gluing PVC foams and other core materials
HardenersP02 is a two-components bonder and must be mixed thoroughly with the specifi c liquid hardener C08 (Cyclohexanone peroxide).
Catalysis ratioP02 bonder must be mixed with a percentage of hardener taking the current room temperature where it will be used into account. Never work at temperature below 5°C.
CATALYSIS AND TEMPERATURE C08 LIQUID HARDENERbetween 5 e 25° C 2,0%
above 25 °C 1,0%
PropertiesAfter application, the properties of the bonder vary according to the type of hardener used and the working temperature. At 20°C, the specifi cations of P02 bonder are illustrated in the following table.
P02 light bonder with C08 Liquid HardenerPROPERTY U.M. VALUE
Colour - Light blueviracolour
Gel time 20°C min 120±25Specifi c weight kg/l 1,0 ± 0,1
Linear shrinkage1 % 0,5Shore Hardness D D 60
Tg (after 2 hours at 80°C)2 °C 78HDT (after 2 hours at 80°C)3 °C 76
Tensile elastic modulus4
(after 2 hours at 80°C) MPa 3552
PackagingP02 is supplied in:- pails containing 15 kg net- drums containing 175 kg net
StorageStore in the original, sealed packaging at a temperature below 20°C. Do not expose to heat or sunlight. The product will remain stable for 1 year from the date of production in these conditions.
DescriptionSpecial bonder based on unsaturated polyesterresins, light fi llers and micro-spheres.
Main Features- light specifi c weight 1.0 g/l- easy to apply by spatula- high bonding power
1Value refers to sample with 2% C08 liquid hardener post-hardened 2 hours at 80°C2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-014Dynamometer Test, ISO 527-1
P07 ULTRA LIGHT POLIBONDER LIGHTWEIGHT PANEL BONDER
40 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesP07 is a specifi cally formulated fi ller bonder for bondingcore materials where limited weight and high adhesionproperties are essential prerequisites for the quality of theapplication. P07 is the ideal product for:- bonding expanded PVC components- bonding panels in termanto
HardenersP07 is a two-component fi ller bonder and must be mixedthoroughly with the specifi c liquid hardener C08(Cyclohexanone peroxide).
Catalysis ratioP07 bonder must be mixed with a percentage of hardeneraccording room temperature.Never work at temperatures below 5°C.
CATALYSIS AND TEMPERATURE C08 LIQUID HARDENERbetween 5 and 10° C 3,0%
between 10 and 20° C 2,0%above 20° C 1,0%
Yield1,5 L/m2
PropertiesAfter application the mechanical properties of the bondervary according to the working temperature. At 20°C thespecifi cations of P07 are illustrated in the table below.
Ultra-Light weight Border P07 with Liquid Hardener C08PROPERTY U.M. VALUE
Colour - whiteGel Time 20°C min 40 ± 10Specifi c weight kg/l 0,67 ± 0,03
Linear shrinkage1 % 1,06Shore Hardness D D 60
Tg (after 2 hours at 80°C)3 °C 63HDT (after 2 hours at 80°C)4 °C 47
PackagingP07 ultra lightweight bonder is supplied in:- 10 kg drums (net weight)- 135 kg drums (net weight)
StorageStore in the original, saled packaging at a temperature below 20°C. Do not expose at heat or sunlight. The product will remain stable for 4 months after shipment in these conditions.
DescriptionSpecial bonder consisting of unsaturated polyester resins,with ultra lightweight reinforcement components and micro-spheres.
Main Features- ultra lightweight, with a specifi c weight of 0.7 kg/l- very easy to apply- strong adhesive power
1After 2 h at 80°C2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-01
POLIBONDER LIGHT VELIGHT VINYLESTER BONDER FOR PANELS P11ULTRA LIGHT POLIBONDER
LIGHTWEIGHT PANEL BONDER
41
Recommended usesP11 is a bonder formulated for gluing core materials andfi breglass panels, where high bonding capacity and low weight are important. It can be used for:- gluing open-cell PVC parts- gluing panels made of balsa and termanto
HardenersP11 is a two-component bonder which must be accuratelymixed with the specifi c liquid hardener (MEKpMethylethylketone peroxide).
Rapporto di catalisiP11 should be mixed with a percentage of hardener that takes into account the ambient temperature, never less than 5°C, in which the process is carried out.
CATALYSIS AND TEMPERATURE C08 LIQUID HARDENERbetween 5 and 10° C 3,0%
between 10 and 20° C 2,0%above 20° C 1,0%
Yield1,5 L/m2
PropertiesWhen the product is applied, it will assume mechanicalproperties that depend on the temperature at which the process has been carried out. The characteristics measured at 20°C are:
Light Border P11 with Liquid Hardener MEKpPROPERTY U.M. VALUE
Colour - viracolourGel Time1 min 50 ± 10
Specifi c weight kg/l 1,00 ± 0,03Linear shrinkage2 % 0,60Water absorption3 % 0,7
Tg (after 2 hours at 80°C)4 °C 100HDT (after 2 hours at 80°C)5 °C 85
Tensile strain at break6 % 1,4
Tests performed with 2% cyclohexanone peroxide. Peeling tests confi rm that the core material fails before delamination occurs.
PackagingP11 is supplied in:- drums containing 15 kg net- drums containing 175 kg net
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 4 months from the date of shipment.
DescriptionSpecial bonder based on unsaturated vinylester resins, with light reinforcing fi ller and micro-spheres.
Main Features- very light specifi c weight- good resistance to high temperature- easy to apply- high bonding power
1Gel time 20°C 60 ± 10 min. with 2% hardener C082After 2 h at 80°C3UNI EN ISO 624DSC Test at 20°C/min under N2, ISO 113575DMA Test, ASTM D648-016Dynamometer Test, ISO 527-1
P24 POLIBONDER SOFT GENERAL PURPOSE BONDER
42 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesP24 is a bonder especially formulated for gluing parts offi breglass and other materials, where use of medium-lightproducts is advisable. It can be used for:- gluing core materials of a medium and small size
HardenersP24 is a two-component bonder which must be accuratelymixed with the specifi c C08 liquid hardener (Cyclohexanone peroxide).
Catalysis ratioP24 should be mixed with a percentage of hardener that takes into account the ambient temperature, never less than 5°C, in which the process is carried out.
CATALYSIS AND TEMPERATURE C08 LIQUID HARDENERbetween 5 and 10° C 3,0%
between 10 and 20° C 2,0%over 20° C 1,0%
Yield1,5 L/m2
PropertiesWhen the product is applied, it will assume mechanicalproperties that depend on the temperature at which the process has been carried out. The characteristics measured at 20°C are:
Border P24 with Liquid Hardener C08PROPERTY U.M. VALUE
Colour - viracolourGel Time 20°C min 40 ± 10Specifi c weight kg/l 1,49 ± 0,05
Linear shrinkage1 % 0,35Shore Hardness D D 70
Tg (after 2 hours at 80°C)2 °C 78HDT (after 2 hours at 80°C)3 °C 74
PackagingP24 is supplied in:- drums containing 25 kg net- drums containing 250 kg net
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 1 year from the date of shipment.
DescriptionColour-changing bonder based on unsaturated polyester resins, suitable for many conditions in which fi breglassreinforced plastic parts are glued together.
Main Features- easy to apply- high degree of hardness- shrinkage near to zero
1After 2 h at 80°C2DSC Test at 20°C/min under N2, ISO 113573DMA Test, ASTM D648-01
POLIBONDER SOFT GENERAL PURPOSE BONDER
43
MILLABLE COMPOUNDS
PE100 EPOXY MILLABLE COMPOUND
44 SPRINT COMPOSITES | CATALOGO TECNICO
Recommended uses- small and large scale modelling industries- modelling for nautical, windturbine and general composite sectors
Chemical-physical properties
PROPERTY U.M. VALUEColour - Blue-green
Specifi c weight kg/l ≈ 0.60Use ratio - 1:1 w/w o v/v
Thermal and mechanical data
PROPERTY U.M. VALUETime to peak1 min 70
Exothermic Peak1 °C 53Tg2 °C 47
Hardness3 Shore-D 51-54Hardness4 Shore-D 51-54
Linear shrinkage5 % 0.25Compressive stress
at break6 MPa > 37
Application parameters
PROPERTY U.M. VALUEUsage ratio - 1:1 w/w o v/v
Pot-life1 min 30Maximum applicable
thickness mm 30
Time before milling2 h 24
PrecautionsThe temperature of the materials and of the environment must not be below 18°C. Do not apply thicknesses over 30 mm in a single layer. Thicknesses over 30 mm are achieved with more applications, leaving the fi rst layer to harden.
PackagingPE100 Epoxy millable compound 120 Kg net drumsCE200 Hardener 120 Kg net drums
StorageThe product in its original closed container must be stored at a temperature between 15 and 35°C.
DescriptionEpoxy thixotropic paste, specifi cally for modelling surfaces with numerical controlled milling of wood, fi breglass,polyurethane foam and polystyrene. Easy application. Allows thin to high thicknesses with even and rapidhardening.
Main Features- applicable in high thickness, up to a maximum of 30 mm- low and controlled heat production- high degree of cross-linkage within 24 hr- easy application- easy CNC machine milling with low dust emission
1On 60 g 25 °C adiabatic container2After 7 days rt, DSC Q100 (TA Instruments), 2°heating scan, -50°C ÷ +180 °C, 20 °C/min, ISO 113573After 7 days rt4After 14h a 52 °C5Internal method, after 14h at 52 °C6After 14h at 52 °C, Instron 5582, ISO 604, cell 100KN, compression speed 0.6 mm/min
HARDENER FOR EPOXY MILLABLE COMPOUND CE200EPOXY
MILLABLE COMPOUND
45
Recommended uses- small and large scale modelling industries- modelling for nautical, windturbine and general composite sectors
Chemical-physical properties
PROPERTY U.M. VALUEColour - Light yellow
Specifi c weight kg/l ≈ 0.60Use ratio - 1:1 w/w o v/v
PrecautionsThe temperature of the materials and of the environment must not be below 18 °C. Do not apply thicknesses over 30 mm in a single layer. Thicknesses over 30 mm are achievedwith more applications, leaving the fi rst layer to harden.
PackagingCE200 Hardener 120 Kg net drums
StorageThe product in its original closed container must be stored at a temperature between 15 and 35°C.
DescriptionHardener for Epoxy thixotropic paste, specifi cally for modelling surfaces with numerical controlled milling of wood, fi breglass, polyurethane foam and polystyrene. Easy application. Allows thin to high thicknesses with even andrapid hardening.
Main Features- applicable in high thickness, up to a maximum of 30 mm- low and controlled heat production.- high degree of cross-linkage within 24 hr- easy application- easy CNC machine milling with low dust emission
PRIMERS
FAF03 HP018 CARBON LOOK PRIMER2K TRANSPARENT PRIMER FOR CARBON FIBRES
48 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesFAF03 HP018 is a transparent acrylic primer formulated for the fi lling of defects (tiny holes) in carbon fi bre fabrics.The very fast drying allows the quick application of 2-3 coats. HardenersSM1 is a primer which must be accurately mixed with the specifi c CP003 hardener and DP001 thinner.
Catalysis ratio
CATALYSIS LIQUID HARDENER30% CP003
10 - 20% DP001
WEIGHTFAF03 HP018 2K Primer 1,000 Kg
CP003 Hardener 300DP001/2/3 Thinner 100-200
Spray application
Application viscosity 25-30 sNozzle diameter 1,7 mm
Air pressure 2-3 barFlash-off at 20° C 15-20 min
Technical recommendations
Recommended fi nal thickness (2-3 coats) 40-80 µm
Theoretic yield 9 m2/kgAir drying 12-14 hr
Stove drying at 50° C 60 min
PackagingFAF03 HP018 spray fi ller is supplied in:- 25 kg net drums- 4.8 kg net tin cans
StorageStore in the original, sealed containers at a temperature below 20°C. Do not expose to heat or sunlight. The product will remain stable for 2 years after the production date in these conditions.
DescriptionTransparent acrylic primer with high fi ller power ideal for paint cycles.
Main Features- it is ideal to fi ll the imperfections that can characterize carbon fi bre surfaces- fast drying
SPRAY FILLER GREYPOLYESTER SPRAY FILLER F18HP018 CARBON LOOK PRIMER
2K TRANSPARENT PRIMER FOR CARBON FIBRES
49
Recommended usesF18 is a specially-formulated spray fi ller used as a topcoat for a variety of surfaces. It is excellent when used for:- a model-making topcoat
HardenersF18 is a two-component fi ller and must be mixedthoroughly with the specifi c C12 liquid hardener(Cyclohexanone peroxide).
Catalysis ratioF18 fi ller must be mixed with a percentage of hardener, considering the current room temperature where it will be used. Never work at temperatures below 5°C.
CATALYSIS LIQUID HARDENER5% C12
DilutionIf necessary dilute with D12 Spray Thinner forpolyester or pure acetone max 5 %.
PropertiesAfter application, the mechanical properties of the fi ller vary according to the working temperature. At 20°C, the specifi cations of F18 fi ller are illustrated in the following table.
F18 polyester spray fi ller with C12 liquid hardenerPROPERTY U.M. VALUE
Colour - greyGel Time at 20°C min 20 ± 8Specifi c weight kg/l 1,60 ± 0,10
Min time before sanding min 180
PackagingF18 spray fi ller is supplied in:- 25 kg net drums- 4.8 kg net tin cans
StorageStore in the original, sealed containers at a temperature below 20°C. Do not expose to heat or sunlight. The product will remain stable for 2 years after the production date in these conditions.
DescriptionSpray fi ller based on unsaturated polyester resinsand mineral fi llers.
Main Features- allows high thickness, to be reached after several coats- fast drying- polishable
RUBBING COMPOUNDS
LPM/LPMO/LPME MORDANT RUBBING COMPOUND FOR GELCOAT
52 SPRINT COMPOSITES | TECHNICAL CATALOGUE
Recommended usesLPM is a compound formulated for compounding gelcoat panels. Due to its mordanting characteristics, LPM compound can be used for:- polishing handiworks- polishing moulds and plugs
Polishing process- make sure that the gelcoat is cold before polishing- remove impurities such as dirt or grease from the gelcoat with a cloth soaked in soap and water- place a small quantity of paste on a wool or foam polishing pad- spread the paste evenly over the surface, with the polisher still off- switch on the polisher and adjust the speed to between 800 and 1,500 rpm- start polishing by exercising a light pressure, then progressively reduce it until the paste begins to dry- make several crossed runs in order to remove all the scratches. Do not polish in the same area for very long or the surface will become overheated
This process will achieve a fi nish high level of gloss whichcan be improved if required by a successive treatment withpolishing compound.
Physical propertiesColour whiteSpecifi c weight 1,65 ± 0,10 kg/l
Chemical composition- special paraffi ns- emulsifi ers- aliphatic solvents- silica-free abrasives in aluminium oxide
ThinningDue to its viscosity, the compound may need thinning. Use petroleum.
PackagingLPM compound is supplied in:- 2 l tins
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 2 years from the date of shipment.
DescriptionStabilized emulsion in combination with special abrasives with controlled granulometry. LPMO mordant - LPME extra mordant.
Main Features- high mordant power. Removes sanding marks or scratches of medium depth- high viscosity, allows very hard surfaces to be quickly polished- special formula for processes on gelcoat
POLISHING RUBBING COMPOUND LPV2MORDANT RUBBING
COMPOUND FOR GELCOAT
53
Recommended usesLPV is a polishing compound formulated for polishing gelcoat and fi breglass panels. It can therefore be used to advantage for:- polishing handiworks- polishing moulds
Polishing process- make sure that the gelcoat is cold before polishing- remove impurities such as dirt or grease from the gelcoat with a cloth soaked in soap and water- place a small quantity of paste on a wool or foam polishing pad- spread the paste evenly over the surface, with the polisher still off- switch on the polisher and adjust the speed to between 1,500 and 2,000 rpm- start polishing by exercising a light pressure, then progressively reduce it until the paste begins to dry- make several crossed runs in order to remove all the scratches. Do not polish in the same area for very long or the surface will become overheated
This process will achieve the maximum high level of glosswhich can only be improved by just one successive treatmentwith polishing compound.
Physical propertiesColour whiteSpecifi c weight 1,78 ± 0,10 kg/l
Chemical composition- esterifi cated waxes- emulsifi ers- aliphatic solvents- polishing abrasives
ThinningOwing to its viscosity, the abrasive paste may need thinning.Use petroleum.
PackagingLPV2 is supplied in:- 2 l tins
StorageStore the product in the original, closed cans at a temperature of less than 20°C, well away from heat sources and sunlight. In these conditions, the product will remain stable for 2 years from the date of shipment.
DescriptionStabilized highly polishing emulsion in combination with special abrasives with fi ne granulometry.
Main Features- high mordant power. Removes sanding marks or scratches of medium depth- high viscosity, allows very hard surfaces to be quickly polished- special formula for processes on gelcoat
Main Features- provides the utmost gloss thanks to the special mixture of esterifi cated waxes- removes sanding marks or low depth scratches
54 SPRINT COMPOSITES | TECHNICAL CATALOGUE
ON-DEMAND PRODUCTS
Vinylester putty S0522009M1 Dark greyVinylester putty S0822009M1 WhiteVinylester putty S1122009M1 WhitePolyester putty S1622009M1 WhitePolyester putty S1822009M1 White
Polyester putty S2722009M1 Light YellowPolyester putty S9722009M1 Yellow
Polyester bonder P2722009M1Polyester adhesive P2122009M1Polyester adhesive P5222009M1Polyester adhesive P5322009M1Polyester adhesive P6222009M1
Spray putty F2122007M1 Dark grey
The above-mentioned products are available upon request for a minimum order quantity of 600/800 kg.Orders will be fulfi lled in 20/30 days.
ON-DEMAND PRODUCTS
INDUSTRIA CHIMICA REGGIANA - I.C.R. S.p.A - 42124 Reggio Emilia - Italy - Via M. Gasparini, 7 - Tel. +39 0522 517803 - Fax +39 0522 51438426817 S. Martino in Strada (LO) - Italy - Via del Commercio, 1 - Tel. +39 0371 475313 - Fax +39 0371 475370 - [email protected] - www.icrsprint.it ICR Ibérica S.A. - Pol. Ind. Sta. Magdalena, C/ Guillem Rovirosa 18-24 - 08800 Vilanova i la Geltrú, España - Tel. +34 93 8932695 - Fax +34 93 [email protected]