gmaw troubleshooting guide

11Copyright Copyright 2004 Lincoln Global Inc. 2004 Lincoln Global Inc.

Gas Metal Arc WeldingGas Metal Arc Welding

Weld Troubleshooting Weld Troubleshooting GuideGuide

22

Copyright Copyright 2004 Lincoln Global Inc. 2004 Lincoln Global Inc.

Possible CausesPossible Causes Corrective ActionsCorrective Actions* Drive Rolls in Poor Condition* Drive Rolls in Poor Condition*Tighten, Clean, or Replace Drive*Tighten, Clean, or Replace Drive

RollsRolls

* Excessive Welding Voltage* Excessive Welding Voltage * Reduce Voltage* Reduce Voltage

* Insufficient Electrical Stickout* Insufficient Electrical Stickout * Increase Contact Tip to Work* Increase Contact Tip to Work

Piece DistancePiece Distance

* Contact Tip in Poor Condition* Contact Tip in Poor Condition * Clean or Replace Contact Tip* Clean or Replace Contact Tip

* Liner in Poor Condition* Liner in Poor Condition * Blow Out Liner with Compressed* Blow Out Liner with Compressed

Air or Replace LinerAir or Replace Liner

* Excessive Burn-back Time* Excessive Burn-back Time * Reduce Burn-back Time* Reduce Burn-back Time

* Spatter on Contact Tip* Spatter on Contact Tip * Remove Spatter at Regular * Remove Spatter at Regular

Intervals of Time, Use Anti-SpatterIntervals of Time, Use Anti-Spatter

Compounds in GunCompounds in Gun

Wire BurnbackWire Burnback

33


Possible CausesPossible Causes Corrective ActionsCorrective Actions* Excessive Run-In Speed * Excessive Run-In Speed *Reduce Run-In Speed*Reduce Run-In Speed

* Excessive Welding Amperage* Excessive Welding Amperage * Reduce Amperage (WFS)* Reduce Amperage (WFS)

* Insufficient Welding Voltage* Insufficient Welding Voltage * Increase Voltage* Increase Voltage

* Excessive Electrical Stickout* Excessive Electrical Stickout * Decrease Contact Tip to Work* Decrease Contact Tip to Work


* Contact Tip in Poor Condition* Contact Tip in Poor Condition * Clean or Replace Contact Tip* Clean or Replace Contact Tip

* Poor Work Piece Connection * Poor Work Piece Connection * Tighten Work Piece Connection* Tighten Work Piece Connection

or in Poor Condition or in Poor Condition or Replace Cables or Replace Cables

* Excessive Inductance/Insufficient* Excessive Inductance/Insufficient * Decrease Inductance Control* Decrease Inductance Control

Pinch ControlPinch Control

* Contaminants on Base Material* Contaminants on Base Material * Clean Work Piece Prior to * Clean Work Piece Prior to

WeldingWelding

Inconsistent Arc StartingInconsistent Arc Starting

44


Possible CausesPossible Causes Corrective ActionsCorrective Actions* Excessive Amperage* Excessive Amperage *Reduce Amperage (WFS)*Reduce Amperage (WFS)

* Poor Joint Fit-Up (Excessive* Poor Joint Fit-Up (Excessive * Reduce Root Openings or Gaps* Reduce Root Openings or Gaps

GapGap

* Improper Travel Angle* Improper Travel Angle * Use a Push Angle* Use a Push Angle

* Travel Speed Too Low* Travel Speed Too Low * Increase Travel Speed or Speed* Increase Travel Speed or Speed

of Positionerof Positioner

* Improper Shielding Gas* Improper Shielding Gas * Use a Lower Percentage of CO2* Use a Lower Percentage of CO2

in Shielding Gas (Use Argon Mix)in Shielding Gas (Use Argon Mix)

* Improper Mode of Metal Transfer* Improper Mode of Metal Transfer * Use Short Circuit Mode of Metal* Use Short Circuit Mode of Metal

TransferTransfer

* Insufficient Electrical Stickout* Insufficient Electrical Stickout * Increase Contact Tip to Work * Increase Contact Tip to Work


BurnthroughBurnthrough

55


Possible CausesPossible Causes Corrective ActionsCorrective Actions* Insufficient Amperage * Insufficient Amperage *Increase Amperage (WFS)*Increase Amperage (WFS)

* Improper Travel Angle* Improper Travel Angle * Use Less of a Drag Angle* Use Less of a Drag Angle



* Improper Shielding Gas * Improper Shielding Gas * Use a Shielding Gas With a* Use a Shielding Gas With a

Higher Percentage of CO2Higher Percentage of CO2

* Improper Wire Selection* Improper Wire Selection * Choose the Correct Wire/Consult* Choose the Correct Wire/Consult

the Manufacturer if Necessarythe Manufacturer if Necessary

* Improper Mode of Metal Transfer* Improper Mode of Metal Transfer * Use Spray Arc or Pulse Spray* Use Spray Arc or Pulse Spray

Arc Mode of Metal TransferArc Mode of Metal Transfer

* Weld Joint Too Narrow* Weld Joint Too Narrow * Increase the Opening of the Weld* Increase the Opening of the Weld

JointJoint

Incomplete PenetrationIncomplete Penetration

66


Possible CausesPossible Causes Corrective ActionsCorrective Actions* Excessive Amperage* Excessive Amperage * Decrease Amperage (WFS)* Decrease Amperage (WFS)

* Uneven Heating of Work Piece* Uneven Heating of Work Piece * Distribute Heat Evenly Over * Distribute Heat Evenly Over Both Both Pieces of Metal Being Welded Pieces of Metal Being Welded

* Improper Welding Procedures* Improper Welding Procedures * Consult Manufacturer’s* Consult Manufacturer’s

Recommendations Recommendations

* Improper Mode of Metal Transfer* Improper Mode of Metal Transfer * Use Short Circuit Mode of Metal* Use Short Circuit Mode of Metal

TransferTransfer

DistortionDistortion

77


Possible CausesPossible Causes Corrective ActionsCorrective Actions* Excessive Welding Voltage* Excessive Welding Voltage * Reduce Voltage* Reduce Voltage

* Insufficient Inductance/Slope* Insufficient Inductance/Slope* Increase Inductance (Add Droop)* Increase Inductance (Add Droop)

* Insufficient Electrical Stickout* Insufficient Electrical Stickout * Increase Contact Tip to Work* Increase Contact Tip to Work

* Improper Shielding Gas* Improper Shielding Gas * Use a Higher Percentage of * Use a Higher Percentage of

Argon in the Shielding GasArgon in the Shielding Gas

* Excessive Gas Flow Rate* Excessive Gas Flow Rate * Reduce Gas Flow Rate* Reduce Gas Flow Rate

* Contaminants on Base Material* Contaminants on Base Material * Clean the Work Piece Prior to* Clean the Work Piece Prior to

WeldingWelding

* Contact Tip Recessed Too Much* Contact Tip Recessed Too Much * Use Longer Contact Tip, Shorter* Use Longer Contact Tip, Shorter

Nozzle, or Adjustable NozzleNozzle, or Adjustable Nozzle

Excessive SpatterExcessive Spatter

88


Possible CausesPossible Causes Corrective ActionsCorrective Actions* Inadequate Gas Coverage* Inadequate Gas Coverage * Increase Flow Rate if Too Low* Increase Flow Rate if Too Low

* Decrease Flow Rate if Weld * Decrease Flow Rate if Weld

Turbulence OccursTurbulence Occurs

* Eliminate Drafts that Can Disrupt* Eliminate Drafts that Can Disrupt

the Shielding Gas Coveragethe Shielding Gas Coverage

* Ensure that Hoses are in Good* Ensure that Hoses are in Good

Repair & Connections are tightRepair & Connections are tight



* Contaminants on Base Material* Contaminants on Base Material * Use a Higher Deoxidizing Wire and/or* Use a Higher Deoxidizing Wire and/or

Clean Base MaterialClean Base Material

* Contaminated Shielding Gas or * Contaminated Shielding Gas or * Eliminate Leaks in Gas Lines* Eliminate Leaks in Gas Lines

ElectrodeElectrode * Store and Handle Electrodes* Store and Handle Electrodes

ProperlyProperly

PorosityPorosity

99


Possible CausesPossible Causes Corrective ActionsCorrective Actions* Insufficient Welding Voltage* Insufficient Welding Voltage * Increase Voltage* Increase Voltage

* Excessive Amperage * Excessive Amperage * Reduce Amperage (WFS)* Reduce Amperage (WFS)

* Excessive Travel Speed* Excessive Travel Speed * Reduce Travel Speed or Speed* Reduce Travel Speed or Speed


* Improper Gun Angle* Improper Gun Angle * Reduce Drag Angle* Reduce Drag Angle

* Excessive Electrical Stickout* Excessive Electrical Stickout * Decrease Contact Tip to Work * Decrease Contact Tip to Work


* Improper Polarity* Improper Polarity * Ensure DC+ Polarity* Ensure DC+ Polarity

* Improper Shielding Gas* Improper Shielding Gas * Use a Higher Percentage of * Use a Higher Percentage of

Argon in the Shielding GasArgon in the Shielding Gas

* Insufficient Inductance* Insufficient Inductance * Increase Inductance Control* Increase Inductance Control

Convex Weld BeadConvex Weld Bead

1010


Possible CausesPossible Causes Corrective ActionsCorrective Actions* Excessive Welding Voltage* Excessive Welding Voltage * Reduce Voltage* Reduce Voltage

* Insufficient Amperage* Insufficient Amperage * Increase Amperage (WFS)* Increase Amperage (WFS)

* Excessive Travel Speed* Excessive Travel Speed * Decrease Travel Speed or Speed* Decrease Travel Speed or Speed


* Improper Gun Angle* Improper Gun Angle * Increase Drag Angle* Increase Drag Angle

* Poor Electrode Manipulation* Poor Electrode Manipulation * Improve Technique/Hold the * Improve Technique/Hold the

Corners in Out-of-Position Corners in Out-of-Position Welding Welding

Concave Weld Bead / UndercutConcave Weld Bead / Undercut

1111


Possible CausesPossible Causes Corrective ActionsCorrective Actions* Excessive Amperage* Excessive Amperage * Reduce Amperage (WFS)* Reduce Amperage (WFS)

* Excessive Welding Voltage* Excessive Welding Voltage * Reduce Voltage* Reduce Voltage

* Improper Gun Angle* Improper Gun Angle * Increase Drag Angle* Increase Drag Angle

* Excessive Travel Speed* Excessive Travel Speed * Reduce Travel Speed or * Reduce Travel Speed or SpeedSpeed


* Improper Joint Design* Improper Joint Design * Increase Corner Joint Angle* Increase Corner Joint Angle

Arc BlowArc Blow

1212


Possible CausesPossible Causes Corrective ActionsCorrective Actions* Improper Technique in Crater* Improper Technique in Crater * Increase Crater Fill Time* Increase Crater Fill Time

* Reduce WFS During Crater Fill* Reduce WFS During Crater Fill

* Insufficient Weld Bead Size* Insufficient Weld Bead Size * Decrease Travel Speed* Decrease Travel Speed

Concave Weld(Restraint Crack)Concave Weld(Restraint Crack) * Decrease Travel Angle* Decrease Travel Angle

* “Tramp” Elements in Base * “Tramp” Elements in Base * Reduce Amperage (WFS)* Reduce Amperage (WFS)

MaterialMaterial

* Insufficient Preheat in Certain* Insufficient Preheat in Certain * Increase Preheat Time and/or* Increase Preheat Time and/or

Base Materials (i.e. High Carbon) Base Materials (i.e. High Carbon) Temperature Temperature

* Cooling Rate of Weld Too Fast* Cooling Rate of Weld Too Fast * Insulate/Slow Cool Weld* Insulate/Slow Cool Weld

* Excessive Contaminants on Base* Excessive Contaminants on Base * Clean Work Piece Prior to * Clean Work Piece Prior to

MaterialMaterial Welding Welding

Solidification CrackingSolidification Cracking

gmaw troubleshooting guide