fuel cell charge transport(natha) - umons · 22 introduction charge transport completes the circuit...
TRANSCRIPT
22
INTRODUCTIONINTRODUCTION
Charge transport completes the circuit in an electrochemical system, moving charges from the electrode where they are produced to the electrode where they are consumed.
They are two major types of charges species: electrons and ions. The transport of electrons versus ions is fundamentally different, primarily due to the large difference in mass between the two. In most fuel cells, ion charge transport is far more difficult than electron charge transport.
Resistance to charge transport results in a voltage loss (given by Ohm’s law) = ohmic, or IR, loss.
These losses are minimized by making electrolytes as thin as possible and employing high-conductivity materials.
33
INTRODUCTIONINTRODUCTION
Flux J measures how much of a given quantity (ex: moles) flows through a material per unit area per unit of time.
Charge flux j measures the amount of charge that flows through a material per unit area per unit of time.
Typical units:22
cm
A
scm
C=
Charge flux = current density
44
INTRODUCTIONINTRODUCTION
Ji = flux of species i
Fk = the k different forces acting on i
Mik = coupling coefficients which reflect the relative ability of a species to respond to a given force with movement as well as the effective strength of the driving force itself
∑=
=
k
kiki
i
FMJ
JFzj
55
INTRODUCTIONINTRODUCTION
If charge transport is dominated by electrical driving forces:
dx
dVj σ=
66
CHARGE TRANSPORT : VOLTAGE LOSSCHARGE TRANSPORT : VOLTAGE LOSS
Why does charge transport result in a voltage loss?
Because fuel cell conductors are not perfect – they have an intrinsic resistance to charge flow.
σ
σ
σσ
A
L
RiA
LiV
LjV
L
Vj
=
=
==
Resistance of our conductor
77
CHARGE TRANSPORT : VOLTAGE LOSSCHARGE TRANSPORT : VOLTAGE LOSS
V is the voltage which must be applied in order to transport charge at a rate given by i.
This voltage represents a loss (Ohmic loss)= voltage which was expended or sacrificed in order to accomplish charge transport.
( )ionicelecohmicohmic RRiRi +==η
Often small compared to Rionic
88
CHARGE TRANSPORT : VOLTAGE LOSSCHARGE TRANSPORT : VOLTAGE LOSS
99
TRANSPORT RESISTANCETRANSPORT RESISTANCE
Fuel cell resistance scales with area and with thickness: for this reason fuel cell electrolytes are generally made as thin as possible.
Fuel cell resistances are additive.
Performance improvements may be won by the development of better ion conductors.
1010
TRANSPORT RESISTANCETRANSPORT RESISTANCE
Area-normalised resistance known as area-specific resistance (ASR):
RESISTANCE SCALES WITH AREA
( )
[ ]
σ
η
LASR
cmARAASR
ASRjRi
ohmic
ohmicCellfuelohmic
ohmicohmicohmic
=
=
==2
1111
TRANSPORT RESISTANCETRANSPORT RESISTANCE
The shorter the conductor length L, the lower the resistance.
RESISTANCE SCALES WITH THICKNESS
σ
LASRohmic =
Fuel cell electrolytes are designed to be as thin as possible.
The most important limitations are:
- Mechanical Integrity : Ex: membrane failure can result in catastrophic mixing of the fuel and oxidant.
- Nonuniformities: Thin electrolyte areas may become “hot spots” that are subject to rapid deterioration or failure.
- Shorting: Especially when the electrolyte is on the same order of magnitude as the electrode roughness.
1212
TRANSPORT RESISTANCETRANSPORT RESISTANCE
The shorter the conductor length L, the lower the resistance.
RESISTANCE SCALES WITH THICKNESS
σ
LASRohmic =
Fuel cell electrolytes are designed to be as thin as possible.
The most important limitations are:
- Fuel crossover : As the electrolyte thickness is reduced, the crossover of reactants may increase.
- Contact resistance : Resistance associated with the interface between the electrolyte and the electrode.
- Dielectric breakdown: When the electrolyte is so thin that the electric field across the membrane exceeds the dielectric breakdown field for the material.
1313
TRANSPORT RESISTANCETRANSPORT RESISTANCE
RESISTANCE SCALES WITH THICKNESS
Practical limitations :
Limit achievable thickness : 10 – 100 µm
1414
TRANSPORT RESISTANCETRANSPORT RESISTANCE
FUEL CELL RESISTANCES ARE ADDITIVE
It is extremely very difficult to distinguish between all the various sources of resistance loss.
1515
TRANSPORT RESISTANCETRANSPORT RESISTANCE
IONIC RESISTANCE USUALLY DOMINATES
The best electrolytes employed in fuel cell:
111.0 −−Ω≈ cmσ
21,005,0 cmASR Ω−≈At a thickness of 50 µm:
A 50-µm-thick porous carbon cloth electrode:
26105 cmASR Ω×< −
This example illustrates how electrolyte resistance usually dominates fuel cells.
Developing satisfactory ionic conductors is challenging.
1616
PHYSICAL MEANING OF CONDUCTIVITYPHYSICAL MEANING OF CONDUCTIVITY
Conductivity quantifies the ability of a material to permit the flow of charge when driven by an electric field.
Two major factors: how many carriers are available to transport charge and the mobility of those carriers within the material.
( ) iii ucFz=σ
A material’s conductivity is determined by carrier concentration Ci and carrier mobility ui.
1717
PHYSICAL MEANING OF CONDUCTIVITYPHYSICAL MEANING OF CONDUCTIVITY
ELECTRONIC VERSUS IONIC CONDUCTORS
1818
REVIEW OF FUEL CELL ELECTROLYTESREVIEW OF FUEL CELL ELECTROLYTES
Three major candidate materials classes for fuel cells: aqueous, polymer, and ceramic electrolytes
Any fuel cell electrolyte must meet the following requirements:
- High ionic conductivity
- Low electronic conductivity
- High stability (in both oxidizing and reducing environments)
- Low fuel crossover
- Reasonable mechanical strength (if solid)
- Ease of manufacturability
1919
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
Almost all aqueous/liquid electrolyte fuel cells use a matrix material to support or immobilize the electrolyte.
1. Provides mechanical strength to the electrolyte
2. Minimizes the distance between the electrodes while preventing shorts
3. Prevents crossover of reactant gases through the electrolyte
Examples: Alkaline fuel cells use concentrated aqueous KOH electrolytes; phosphoric acid fuel cells use either concentrated H3PO4 electrolytes or pure H3PO4. Molten carbonate fuel cells use molten (K/Li)2CO3 immobilizedin a supporting matrix.
IN AQUEOUS ELECTROLYTES/IONIC LIQUIDS
2020
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN AQUEOUS ELECTROLYTES/IONIC LIQUIDS
( ) iii ucFz=σ
Selected Ionic Mobilities at Infinite Dilution in Aqueous Solutions at 25°C.
2121
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN POLYMER ELECTROLYTES
For a polymer to be good ion conductor, at a minimum it should possess the following structural properties:
1) The presence of fixed charges sites;
2) The presence of free volume (“open space”).
The fixed charge sites should be opposite charge compared to the moving ions.
In a polymer structure maximizing the concentration of these charge sites is critical to ensure high conductivity.
Excessive addition of ionically charged side chains will significantly degrade the mechanical stability of the polymer.
2222
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN POLYMER ELECTROLYTES
Schematic of ion transport between polymer chains: Polymer segments can move or vibrate in the free volume, thus inducing physical transfer of ions from one charged site to one another.
2323
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN POLYMER ELECTROLYTES: Ionic Transport in Nafion
Teflon backbone = mechanical strength
Sulfonic acid functional groups:charge sites for proton transport
2424
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN POLYMER ELECTROLYTES: Ionic Transport in Nafion
In the presence of water, the protons (H+) in the pores form hydronium complexes (H3O
+) and detach from the sulfonicacid side chains. When sufficient water exists in the pores, the hydronium ions can transport in the aqueous phase.
-Under these circumstances, ionic conduction in Nafion is similar to conduction in liquid electrolytes.
-The hydrophobic nature of the Teflon backbone accelerates water transport through the membrane, since the hydrophobic pore surfaces tend to repel water.
-To maintain this extraordinary conductivity, Nafion must be fully hydrated with liquid water.
2525
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN POLYMER ELECTROLYTES: Ionic Transport in Nafion
The water content λ in Nafion = the ratio of the number of water molecules to the number of charged (SO3
-H+) sites
220 << λCompletely
dehydrated NafionFull saturation
2626
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN POLYMER ELECTROLYTES: Ionic Transport in Nafion
Water content versus water activity for Nafion 117 at 303 K
2727
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN POLYMER ELECTROLYTES: Ionic Transport in Nafion
Ionic conductivity of Nafion versus water content λ at 303 K
2828
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN POLYMER ELECTROLYTES: Ionic Transport in Nafion
Ionic conductivity of Nafion versus temperature when λ= 22
( ) ( )
−=
TT K
1
303
11268exp, 303 λσλσ
2929
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN CERAMIC ELECTROLYTES
SOFC electrolytes = are solid, crystalline oxide materials that can conduct ions
The most popular SOFC electrolyte is yttria stabilised zirconia (YSZ)
Typical YSZ electrolyte contains: 8% yttria mixed with zirconia
Zirconia = ZrO2 (zirconium oxide)
Yttria = Y2O3 (Yttrium oxide)
Yttria stabilised the zirconia crystal structure in the cubic phase (where it is most conductive).
Yttria induces high concentrations of oxygen vacancies into the zirconia crystal structure. High ion conductivity
3030
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN CERAMIC ELECTROLYTES
Charge compensation effects in YSZ lead to creation of oxygenvacancies
The addition of 8% (molar) yttria to zirconia causes about 4% of the oxygen sites to be vacant.
3131
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN CERAMIC ELECTROLYTES
The oxygen vacancies can be considered to be ionic charge « carriers ».
Carrier mobility is described by D, the diffusivity of the carrier in the crystal lattice.
Diffusivity describes the ability of a carrier to move, or diffuse, from site to site within a crystal lattice.
A material’s conductivity is determined by the combination of carrier concentration c and carrier mobility u:
( ) ( )RT
DzFcucFz
2
==σ
3232
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN CERAMIC ELECTROLYTES
There is an upper limit to doping.
Above a certain dopant or vacancy concentration, defects start to interact with each other, reducing their ability to move.
3333
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN CERAMIC ELECTROLYTES
The carrier diffusivity in SOFC electrolytes is exponentially temperature dependent:
( )RTGacteDD∆−= 0
D0 = constant (cm2/s)
∆Gact= the activation barrier for the diffusion process (J/mol)
( ) ( )
RT
eDzFcRTGact∆−
= 0
2
σ
3434
REVIEW OF FUEL CELL CLASSESREVIEW OF FUEL CELL CLASSES
IN CERAMIC ELECTROLYTES
For extrinsic carriers, c is determined by the doping chemistry of the electrolyte. In this case, c is a constant and the preceding equation can be used.
For intrinsic carriers, c is exponentially dependent on the temperature and the equation becomes:
( ) ( ) ( )
RT
eeDzFcRTGkTh
sitesactv ∆−∆−
=2
0
2
σ