fracture mechanics lecture 1 recap by visiting student from sktech (moscow), dmitrii (dima) vasilev...
DESCRIPTION
The procedure to answer the question is the following What is the maximum stress in the body? What is the strength of material? When τ(max) = X(Material Strength) – material fracturesTRANSCRIPT
![Page 1: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/1.jpg)
Fracture Mechanics Lecture 1Recap
By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev
18.10.2012
![Page 2: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/2.jpg)
We started with the problem to be solved in fracture mechanics
• What is the magnitude of the load that will cause the body (material) to fracture?
Let us assume we are creating a new material
Then,
![Page 3: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/3.jpg)
The procedure to answer the question is the following
• What is the maximum stress in the body?
• What is the strength of material?
• When τ(max) = X(Material Strength) – material fractures
![Page 4: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/4.jpg)
To proceed we need to use Theory of Linear Elasticity
Let’s assume we found each stress component for each particle
Then we find maximum stresses from eigenvalues
![Page 5: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/5.jpg)
Stress concentration• It turns out that in some specific areas of the
body the stresses may be higher than the applied load
F
F
Stress concentration
Stress concentration
![Page 6: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/6.jpg)
Due to linearity…• τ(max)=c*τ(app)
F
F
Stress concentration
Stress concentration
C=3 C=1+2a/b
![Page 7: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/7.jpg)
Strength of material
• Theory cannot accurately predict strengthBut
• We can conduct experiments
![Page 8: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/8.jpg)
However…
• The maximum stress in a body is sensitive to the shape of the flaw
• The shape of the flaw inside the body is seldom known
• We assume linear elasticity• Strength depends on the sample shape
![Page 9: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/9.jpg)
Griffith attempts
Some experiments were conducted on the glass sample. Conclusions:1) In a body of glass cracks pre-exist.2) The tip of such crack concentrate stresses.3) The intense stress breaks atomic bonds one
by one, like opening a zipper.4) As the crack advances,
![Page 10: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/10.jpg)
The main conclusion is that there is a competition between 2 factors while the crack advances: releasing elastic energy forces the crack to grow, while surface crack energy (which grows) is trying to stop the crack expansion (to heal the crack). U
a
a*=2γE/πσ^2
![Page 11: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/11.jpg)
Why the discussed material is tremendously important?
![Page 12: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/12.jpg)
My previous work
300 tons of liquid
steelNew material for ladle lining – Carbonized Periclase,which has a thermal expansion coefficient significantly higher than previous materials
![Page 13: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/13.jpg)
What I found
![Page 14: Fracture Mechanics Lecture 1 Recap By visiting student from SkTech (Moscow), Dmitrii (Dima) Vasilev 18.10.2012](https://reader036.vdocuments.us/reader036/viewer/2022081512/5a4d1b617f8b9ab0599adafc/html5/thumbnails/14.jpg)
Video of numerical methods that I used to solve that problem