Examen de Evaluación ASME SECTION V
1.-The correct filmside IQI designation for a weld that is 1.56" thicks is_________.
30
50
12
8
2.-A dark image of the "B" on a lighter background is___________.
acceptable
rejectable
sometimes rejactable
acceptable when OK ed by the inspector
3.-One of the procedural requirements for conducting PT is to address the processing details for______________.
keeping temperature within 50 to 125 °F
documenting results of examination
maximum light intensity
applying the penetrant
4.-The accurancy of a piece of magnetizing equipment that is equipped with an ammeter shall be verified____________.
each year
each two years
when pssoble
every 6 months
5.-When using fluorescent particles, the examiner shall be in a darkened area for a least__________ minutes prior to performing the examination.
7
10
9
5
6.-An MT field strength indicator is composed of___________ low carbon steel pie sections, furnace brazed together.
2
6
10
8
7.-Which of the following must be identified on a written Magnetic Particle Testing procedure?
NDE technician
temperature limitations set by particle manufacture
prod manufacture
last calibration date
8.-Certification of contaminants shall be obtained for all PT materials used on_________.
carbon steels
ferritic stainless steels
copper
austenitic stainless steels
9.-Black linght intensity shall be meansured with a _____________ when conducting fluorescent PT.
dark room mater
phot-meter
black light meter
none of the above
10.-What is the maximum prod spacing permitted when using the MT prod technique?
3"
8"
1 foot
6"
11.-D.C yokes may be used for detecting____________ discontinuities.
near surface
surface
volumetric
any
12.-How many total liquid penetrant techniques are listed in ASME V?
4
6
2
1
13.-Prior to examination using PT, each adjacent surface shall be cleaned within at least________ of the area to be examined.
1"
1.5"
2"
3"
14.-Watre washable penetrant shall be removed with a __________.
steam spray not to exceed 50 psi and 125°F
water spray not to exceed 50 psi and 110°F
emulsifier not to excced 60 psi
solvent
15.-Emulsification time shall not exceed_________ minutes, unless other times have been qualified by actual test.
5
10
15
none of the above
16.-Densitometers shall be calibrated by verification with a calibrated_________.
densitometer
step wedge Calibration Film
Light Meter
Transmission monitor
17.-For the MT Prod technique the minimum amo/in. Of current for a section thickness of 1/2" is:?
1000 amp/in.
90 amp/in.
125 amp/in.
200 amp/in.
18.-Parts are demagnetized to remove residuak magnetization __________ the examination.
before
after
at least once during
throungh out
19.-When a penetrant test cannot be conducted betwwen 40°F- 125°F, what must be done, per ASME V?
the procedure must be cualified at the proposed test temperature
the surface must be re-cleaned
the test cannot be conducted
none of the above
20.-The sulfur content of a penetrant residue is measured to be less than .0025g. This material is accpetable for use on:
nickel-base alloys
carbon steel
ferritic steel
all of the above
21.-All indications are to be evaluated in accordance with__________.
ASME VIII
ASME V
the rererencing Code section
the written procedure
22.-Dry particle MT shall not be performed is the surface tenperature of the part exceeds____________.
500 F
those set by the particle manufacturer
60 F
50 F
23.-The ammeter on MT equipment shall not vary by more than_________ of full scale.
plus or minus 10%
10 amps
plus or minus 1%
5 amps
24.-Wire diameter 0.032 in. Is common to which of the following ASTM SETS:
A & B
C & D
B & C
none of the above
25.-Surfaces may be dried after preparation for PT examination by:
normal evaporation
forced Hot Air
forced Cold Air
all of the above
26.-A______________ is a device used to determine the required sentitivity of a radiograph.
a step wedge comparison film
a densitometer
an IQI
a sizemometer
27.-In accordance with Section V, intensifying screens:
can always be used if screens are on source side
may be used when performing radiographic examination in accordance with Article 2
can never be used
can be used only with Type 1 film
28.-A single film technique was used to make a radiographic using a Cobalt-60 source. The minumum permitted density in the area of interest is:
4
1.8
2
1.3
29.-A radiograph is made using an X-ray source, and two films in each film holder. If the film is to be viewed separately the minimum permitted density would be:
4
1.8
2
1.3
30.-A weld with a nominal thickness of 1.5 inch is to be rediographed using a film side IQI. The IQI designation should be:
25
30
35
both a and b are acceptable?
31.-Which of the following is used to detect both surface and near surface flaws?
liquid penetrant testing?
magnetic particle testing?
visual examination?
pneumatic testing?
32.-What is a densitometer used to determine?
magnetic flux
decibels
density
weight
33.-All MT examinations will be conduced with sufficient over lap to assure an minimum of_________ coverage?
99%
100%
80%
90%
34.-Liquid penetrant testing is captable of detecting:
elongated slag inclusions
surface discontinuities
subsurface laminations
any of the above
35.-Which of the following inspection techniques require visual examination of the test specimen during testing?
readiography testing
ultrasonic testing
magnetic particle
eddy current
36.-Penetrameters are used:
to measure thickness of a weld
to check the image quality of the radiograph
to measure the weld reinforcement
to check for back scatter
37.-In radiography the purpose of a shim is to:compensate for the excess thickness throungh the weld relative to the base material when the penetrameter is placed adjacent to the weld
level the piece being radiographed
compensate for the excess thickness throungh the base metal
change the density from 2.0 to 2.6
38.-Shims are made from which of the following:
any carbon steel material
material which is a radiographically similar to the weld material
austenitic stainless steel type 304
material which is radiographically similar to the base material
39.-If in viewing radiographs a light letter "B" indicates:
nothing
the radiograph is better than most
the radiograph may have been demaged by chemicals when processing
the protection from backscatter is insufficient
40.-Which of the following inspection methods is principally used to determine surface defects:
radiography
ultrasonic
liquid penetrant
eddy current
41.-Which of the following applies when qualifying a penetrant precedure lower than 50°F?qualifying at a temperature lower than 50°F qualifies from the lower temperature to 50°F
qualifying at the upper and lower ranges to be used temperature
qualifying at a temperature lower than 50°F qualifies from the lower temperature to 125°F
qualifying at any temperature between 50°F and the lower temperature
42.-An ASTM wire penetrameter has been used in the radiographic examination of a vessel seam if the weld is 2 in. Thick and placed on the source side, the required wire diameter is___________.
0.04
0.032
0.025
0.25
43.-When performing a radiograph of a weld on a vessel seam, where should the lead letter B be placed?
on the front of the film holder
on the outside surface of the vessel
on the back of the film holder
on the inside surface of the vessel
44.-SE-797 is limited to which of the following maximum temperature?
500°F
700°F
200°F
1000°F
45.-UT instruments are divided into three groups, one of these is:
direct thickness readount
flaw detectors whitout URT readout
flaw detectors with screen readout
direct thickness readout with CRT screen
46.-What is the lead symbol "B" used to determine during radiography examination?
the grade of film used
that the best film is being used
if backscatter radiation is exposing the film
if there is adequate backscatter radiation exposing the film
47.-Which of the following is not usually found a radiographic report?
film brand or designation
minimum source to film distance
name of the IQI manufacturer
effective focal spot size
48.-When using fluorescent penetrant the examiner shall be in the darkened area for at least__________ prior to performing the examination
5 minutes
1 minute
15 minutes
10 minutes
49.-When radiographing a vessel, where are location markers to be placed which are to appear as images on a radiographic film when the source to material distance is greater than the inside radius:
source side
film side
either source
neither side
50.-When the density of the radiograph varies by more the minus______% or plus______% from the density through the body of the hole IQI within the minimum/maximum allowable density ranges specified then an additional IQI shall be used
15, 40
20, 30
15, 30
30, 30
51.-The __________________ is responsibile for examination equipment calibration records.
manufacturer
NDE technician calibrates his own equipment
company that manufactures the NDE equipment
authorized inspector
52.-At least_________ copy(ies) of an NDE procedure must be available to the manufacturers nondestructive examination personnel at the work site.
two
one
none
there is not requirement
53.-The difference between an inspection and an examination per Section V of the ASME Code is:
inspections are non NDE functions, other Q.C. functions are examinations
"examinations" are performed bye the Al
"inspections" are performed by the manufacturer s personnel
examinations are performed by the manufacturer s personnel & inspections are performed by the Al
54.-On the four step standardization block fQr SE-792 what is the thickness of the third step?
1.000 in.
0.750 in
0.250 in
1.500 in
55.-Which of the following is not part of the minimum content of a written radiographic preocedure?
type of screens used if any
type of emulsion used
film brand & designation
maximum X-ray voltage or isotope used
56.-How can compliance with a written radiographic procedure be demonstrated?
by showing the film to the A.I.
be confirming the accurancy of the radiographs with welder or welding foreman
bye verifying the proper density and demostrating the IQI image requirements
bye demostrating the required sentitivity by showing the "3T" hole in a hole typpe IQI
57.-What finished surface is required of butt welds?
all surface cracks must run vertically in the center
all surface cracks must run horizontally in the center
the must not have any irregularities or contours than will mask defects or interfere with interpretationthey must not have any undercut or pinholes that will mask defects interfere with interpretation
58.-One reason for a system of radiographic film identification is:
to identify the film manufacturer
so the location of defects will be traceable to the weldment
to keep track of how much film is used for billing purposes
so the welders will know where to have the film placed by the radiographer
59.-What type films is to be used for radiographs?
kodak +
polaroid XXX
industrial radiography film
any of the above
60.-IQI s may be what types?
wire
hole
slit
1 & 2 above
61.-Viewing facilities for the radiographs shall_______________________________.
be small, warm and confortableenough for afternoon naps
have adjustable lighting with variable temperature control for film storage
be bright and airy with lots or ferns and plants
subdued background lighting that will not cause glare on the film
62.-The direction of the central beam of radiation should be____________ the area of interest whenever practical.
as close as possible to
centered on
no more than 18" from
at least 36" from
63.-Where are the hole type IQI(s) normally placed?
in the center of the weldment
adjacent to the weld but not in the area of interest
on the film side
outside the area of interest
64.-What designation is used to indicate the IQI is on the film side?
it is only noted on the radiographic report-there is no other designation used
the welder noted it on the weld map
the IQI may not be placed on the film side
a lead letter "F" placed next to or on the
65.-How many IQI s should appear on each radiograph?there must always be one on every radiograph and it the must appear as a radiographic imagethere must always be one on every radiograph but it need not appear as a radiographic image
there must always be two on every radiograph and it must appear as a radiographic imageit depends on the configuration used to set up the shot (panoramic multifilm, single shots, etc…)
66.-Shims may be placed under IQI s to simulate weld reinforcement to assure the density in the area of interest is not less than__________lighter than the density throungh the IQI.
10%
25%
15%
5%
67.-Which the following blemishes is permittd on the filmas a long as they do not interfere with interpretation and do not mask or become confused with discontinuities in the area of interest?
fogging & false indications from defective screens
scratches, crimps,static marks & dirtiness
processing defects such as streaks & water marks
all of the above
68.-The basic minumum density requirements for single film viewing are:
1.8 for film made with an isotope and 2.0 for film made with an X-ray machine
4.0 for film made with an isotope and 4.0 for film made with an X-ray machine
2.0 for film made with an isotope and 1.8 for film made with an X-ray machine
no more than 25% lighter in any area than the density in the darkest area
69.-What are the essential indications of sensitivity for image quality of a radiograph?
display of the "1T" hole
clearly visible location markers
display of the specified hole or wire of the IQI used
proper density variations
70.-Which of the following information is not required to be included in the documentation accompanying the radiographs:
minimum source to film distances and film brand & designation
number of exposure & film identification
isotope & effective focal spot sizes
development time & exact shim material specifications
71.-When the radiographs are presented to the Autorized Inspector______________________________________.
he will interpret them and indicate the disposition of each film on the report
he will view them only after a good luch paid for by the NDE technician
the amnufacturer will have interpreted all the film and will have indicated the disposition of each on the report and will have also included all the other information required to be on the reportthe radiographs will be marked with a permanent marker or by other means to indicate which technician processed them
72.-For measuring thin sections which type of search init is generally used?
highly damped, high frequency
highly attenuated, low frequency
highly damped, low frequency
5 MHz single element
73.-When calibrating a UT instrument using Case II , what minimum number of test blocks should be used when the instrument must be completely calibrated with the delay line search init?
3
4
2
1
74.-Which type of search unit may be used effectively with rough surface conditions?
delay line single element
direct contact single element
dual search unit
direct contact double element
75.-When measuring materials at high temperatures the readings are high by a factor of:
1% per 50°F
1% per 10°F
5% per 50°F
1% per 100°F
76.-Which following is not a type of discontinuiy liquid penetrant examination is effective in detecting.
cold shuts & laminations
sbsurface cracks
pinholes
seams
77.-Which of the following need not be included in a Liquid penetrant procedure?
post examination cleaning details
materials, shapes & sizes to be examined
temperature of penetrant after the examination
processing datails for removal of excess penetrant
78.-Revisions to PT procedures would be required if there is
a change in the post examination cleaning technique
a change or substitution in type or family of penetrant materials
a change or substitution is made in the precleaning materials or process
all of the above
79.-What materials require the use of tested and certified liquid penetrants as to the contaminants in the penetrant?
carbon steels with > 3% chrome
aluminum
nickel base alloys & titanium
copper
80.-What condition must the surface to by examined be in the prior to conducting the examination?
dry & free of all remedial demagnetization effects
dry & free of any grease, lint or scale for 1" on all sides of the area to be methods
free of all subsurface defects previously detected by other methods
dry & free of extraneous matter for 2" on all sides of the area to be examined
81.-The minimum period of drying time after initial cleaning is_____________.at least 5 minutes to assure that all the cleaning solution has evapored prior to applying the penetranta minimum time established to assure that all the cleaning solution has evaporated prior to applying the penetrantat least 15 minutes to assure that all the cleaning solutions has evaporated prior to applying the penetrantat least 10 minutes to assure that all the cleaning solution has evaporated prior to applyng the penetrant
82.-Without special qualification penetrant testing can be performed between______________.
50 degress F to 125 degress F
60 degress F to 125 degress F
72 degress F to 130 degress F
50 degress F to 130 degress F
83.-Fluorescent penetrant examination shall not follow__________________.
UT thickness measurement
radiography because the residual radiation will cause false indications
eddy current examination
color contrast PT examination
84.-Water washable and post emulsifying penetrants may be dried using circulated air as lon as the surface of the part does not exceed:
100 degress F
110 degress F
212degress F
125 degress F
85.-How shall PT indications be evaluated per ASME Article 6?
per universal acceptance standards in ASNT SNT-TC-1A
in terms of the acceptance standards of the referencing code section
per the specific requirements in appendix N. 5.3 of API-789
per the ower/user procedures NDE
86.-Five typical discontinuities detectable by magnetic particle method are:
seams, low carbon content, cold shuts, laminations, and bad developing
cracks, caustic embrittlement, seams, and silicon isotope matrix syndrome
excessive weld seam reinforcement, cracks, cold shuts, seams, and low viscosity
cracks, laps, seams, cold shuts and laminations
87.-What is the magnetic particle examination medium?
the surfaces of ferromagnetic work pieces
dry, wet or fluorescent ferromagnetic particles
any type of small metal particles
high iron content enamel or latex coatings
88.-If coatings are left in place during MT examination________________________.
the particles used must be the same color as the coating
coatings are not allowed to be left in place-all coatings must be removed
the procedure must be demonstrated as capable of detecting indications through the
maximum thickness of the coating appliedall indications must be verified with penetrant examination in addition to the magnetic particle examination
89.-What type of discontinuity is the magnetic particle method most sentitive to?
subsurface discontinuities
slag inclusions not open to the surface
linear discontinuities perpendicular to the lines of flux
high nickel alloy weld defects
90.-The intensity of the black ligh used shall be minumum of:
800 µw/cm² 12" from the surface of the part being examined
600 µw/cm² on the surface of the part being examined
1800 µw/cm² 18" from the surface of the part being examined
1000 µw/cm² on the surface of the part being examined
91.-Magnetic field strength may be verified on all techniques except prod and yoke by using_____________.
an amp meter to determine if the field is within ± 10% of full scale
the proper IQI manufactured using all magnetically identical materials
an ohm meter to determine if the field is within ± 5% of full scale
magnetic particle field indicator
92.-AC yokes must be able to lift_________ pounds at a maximum spacing of_____________.
40 pounds at the maximum spacing to be used during examinations
10 pounds at a maximum spacing of 18 inches or 1 1/2 feet
40 pounds at a maximum spacing of 1.5 times the length of the yoke legs
10 pounds at the maximum spacing to be used during examiantions
93.-MT equipment with ammeters must be calibrated to a standard___________
supplied by the MT equipment manufacturer
supplied by the ISO MT standards committee
traceable to a national standard
welded by qualified welder or welding operator qualified in accordance with Section V
94.-What is the area of wire identity number 16?
0.008 sq.in.
0.320 sq.in.
0.049 sq.in.
1.000 sq.in.
95.-What would be the equivalent 4T hole-Type designation if the 2T hole-Type designation is # 20?
30
20
15
40
96.-Densitometers shall be calibred at least every_____ days.
120
180
90
365
97.-Periodic calibration verifications shall be performed on densitometers?
beginning of each shift
after 8 hours of continuous use
after change of apertures
whichever of the abovw occurs first
98.-Wire diameter 0.008 in.has a wire identity of?
#11
#21
#5
#6
99.-Direct visual examination may usually be made when access is sufficient to place the eye within__________ of the surface to be examined.
12 inches
24 inches
6 inches
3 feet
100.-Which of the following is a technique used for visual examination of metal pipe?
translucent
direct visual
remote visual