Download - V.V. Kedrov, N.V. Klassen, G.V. Strukov ( ISSP RAS ), D.V. Orlinskyi (“ Kurchatov Institute ”),
Development of the first mirrors for ITER plasma diagnostics based on rhodium
nanocrystalline coatings
V.V. Kedrov, N.V. Klassen, G.V. Strukov (ISSP RAS), D.V. Orlinskyi (“Kurchatov Institute”),A.F. Bardamid, O.G. Kolesnik, K.I. Iakimov (Kiev University),V.S. Voitsenia, V.G. Konovalov, I.V. Ryjkov, S.I. Solodovchenko, A.F. Shtan’ (Kharkov Institute of Physics and Engineering)
Reflectivity of various metals
Rhodium is one of the best materials for the first mirrors due to:● high melting point ● low rate of sputtering;● good reflectivity
0
20
40
60
80
100
200 300 400 500 600 700 800 R
efl
ec
tio
n c
oe
ffic
ien
t,
%
Wavelength , nm
Al
Rh Cu Ag
W
Mo
Disadvantages of bulk Rh mirrors high cost of the bulk material (more than
100,000 USD/ kilogram), resulting in the cost of one bulk mirror more than 30,000 USD;
inevitable deterioration of the optical smoothness of the reflecting surface due to its vapor etching during sputtering (the mean dimensions of the grains are in the range 1 – 10 micrometers, so evaporation of the material from the surface results in etching of intergrain boundaries and corresponding scattering of the light)
First experiments on Rh film mirrors
50
55
60
65
70
75
80
85
0 0.5 1 1.5 2 2.5
Rh on Cu R
efle
ctan
ce, %
Thickness of sputtered layer, um
650nm
#3 #4
#3 #4
400nm Res. pow.
Res
olu
tio
n p
ow
er, l
ine/
mm
Differences in sputtering perfomance of surfaces of various mirrors
Good mirror Bad mirror
The both of these problems are solved by preparation of the rhodium mirrors based on thin
film Rh coatings (with the thickness about 10 μm)
The total volume of rhodium and its cost are decreased by about 100 times;
The optical smoothness of the reflecting surface during sputtering of several micrometers can be stabilized by preparation of nanocrystalline structure of the rhodium coating. In this case the distances between intergrain boundaries are much less than the light wavelength, so scattering of the light by the boundaries can be neglected).
This opportunity has been confirmed by our experiments on sputtering of Rh coatings deposited by electroplating
In these experiments we varied
Material of substrate (copper, brass, copper – nickel alloys, stainless steel, )
Procedure of substrate preparation (abrasive polishing, deformation polishing) Concentration of the electrolythe (from 10% to 40 % of water solution
of sulfur acid) Concentration of rhodium in the electrolythe (by dissolving of rhodium
sulfate) Material and dimensions of the anode (rhodium, platinum, nickel) The distance between the anode and the substrate Procedure of the chemical activation of the substrate Procedure of deposition of intermediate layer (nickel, nickel-silver alloy) Current density Rate of the barbotage of the solution Temperature of the solution Procedure of finishing processing of the coating
Testing of the mirrors with Rh coatings
The samples were subjected to bombardment in deuterium plasma (0.1 – 1000 eV) The optical characteristics were measured as functions of the bombardment duration and thickness of the sputtered layer:
Spectroscopy of optical reflection Integral optical reflection In parallel the morphology of the surface was studied as
the function of the sputtering time by means of scanning electron microscopy
X-Ray diffractometry and adhesion measurements have been made as well
Correlation between the degree of stability the optical parameters, surface morphology and parameters of
nanocrystalline structure has been found
The most stable mirrors have nanocrystalline structure of Rh coating with mean dimensions of the grains between 10 and 30 nm
40
45
50
55
60
65
70
75
80
0 50 100 150 200 250 300
Rh film mirrors, λ = 600им
96
85
98
76
87
93
82
97
94
Reflection coefficient, %
Bombardment duration, minutes
.
Correlation between the degree of stability the optical parameters, surface morphology and parameters of
nanocrystalline structure has been found
Good mirror Moderate mirror Bad mirror
Now we are ready to develop the technological chain for mass production of the first mirrors of this kind for ITER:
Preparation of substrates. Cleaning of the substrates in ultrasonic
baths. Activation of the substrates in acid
solutions. Rhodium deposition by electroplating. Finishing processing of the mirrors. Cleaning of the mirrors. Exit control of the mirrors (optical
reflectometry and X-Ray diffractometry)
Scheme of electroplating deposition of Rh film
Rh solutionsubstrate anode
Development of technology of mass production of Rh film mirrors
The total duration of the work: 12 months The final results: the experimental
technological line with optimized technological procedures at each step
Amount of specialists involved: 7 persons Total cost of the work: about 100,000 USD Estimation of production cost of one mirror
(100 mm diameter): 500 USD
Deformation polishing of mirrors resulting in surface passivation
die
surface
Radiation hard scintillators based on nanoscopic oxides
radiation defects are attracted to the surface and annihilated
light guide
nanoscintillator
γn
Conclusions
Laboratory technology of electroplating deposition of nanocrystalline rhodium coatings onto substrates from copper alloys has been developed
The first mirrors manufactured by electroplating deposition of nanocrystalline rhodium films onto substrates from copper alloys demonstrate high reflectivity and its good stability under sputtering of several micrometers.
Technology of mass production of the first mirrors by means of rhodium deposition onto substrates from copper alloys can be developed in one year.
The production cost of the rhodium film mirror with 100 mm diameter stable to ion sputtering is estimated as 500 USD
Application of finishing deformation polishing of rhodium anf other mirrors can decrease significantly the rate of deposition of carbon – hydrate films due to effective passivation of the surface of the mirror.