Typical grade of Cellulose ethersManufacturers APPLICATIONS Cellulose ether Grade Viscosity Property
DOW
Cement-Based Tile Adhesives (CBTA) WaloCel VP-M-49125 8,000modified HPMC grade for long open time and very high slip resistance
Cement-Based Tile Adhesives (CBTA) WaloCel MKS 10000 PF 60 10,000modified HPMC grade for long open time and very high slip resistance
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 15000 PF 01 15,000medium viscosity HPMC grade recommended for standard quality polymer and non-polymer modified thin-sets
Cement-Based Tile Adhesives (CBTA) WaloCel MW 15000 PFV 15,000medium viscosity HEMC grade with delayed hydration; suitable for dry-mix and ready-to-use
Cement-Based Tile Adhesives (CBTA) MeThoCel 327 20,000 multipurpose; good open time and slip resistance
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 20000 PP 10 20,000modified heMc grade; good open time and workability
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 25000 PF 25 l 25,000modified heMc grade; long open time, good slip resistance and workability
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 40000 PF 01 40,000high viscosity heMc grade; recommended for standard quality polymer and non-polymer modified thin-sets
Cement-Based Tile Adhesives (CBTA) WaloCel MW 40000 PFV 40,000high viscosity heMc grade with delayed hydration; suitable for dry-mix and ready-to-use
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 45000 PP 10 45,000high viscosity heMc grade offering good open time, workability and moderate slip resistance
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 45000 PF 20 l 45,000modified heMc grade provides long open time, excellent workability and good slip resistance
DOW
Cement-Based Tile Adhesives (CBTA) WaloCel MKX 60000 PF 01 60,000very high viscosity heMc; high water retention/open time at low dosage rates
Cement-Based Tile Adhesives (CBTA) WaloCel MW 60000 PFV 60,000very high viscosity heMc with delayed hydration; high water retention/open time at low dosage rates
Cement-Based Tile Adhesives (CBTA) WaloCel M-20678 80,000ultra high viscosity heMc; high water retention/open time at low dosage rates
Tile Grouts WaloCel MK 3000 PF 3,000 excellent workabilityTile Grouts WaloCel MKW 4000 PF 01 4,000 easy workabilityTile Grouts WaloCel MKX 6000 PF 01 6,000 good workability and application propertiesSelf-Leveling Underlayments MeThoCel CP 7331 100 less segregation, good flowSelf-Leveling Underlayments MeThoCel CP 1119 300 less segregation, good flowSelf-Leveling Underlayments WaloCel MK 400 PF 400 less segregation, good flowSelf-Leveling Underlayments WaloCel MKW 2000 PF 01 2,000 easy workabilityMortars for EIFS/Skim Coat WaloCel MKW 4000 PF 01 4,000 easy workabilityMortars for EIFS/Skim Coat WaloCel MKX6000 PF 01 6,000 good workability and application propertiesMortars for EIFS/Skim Coat WaloCel MKS10000 PF 60 10,000 excellent open time,slip resistanceMortars for EIFS/Skim Coat WaloCel MKW 10000 PP 01 10,000 good air void stabilizationMortars for EIFS/Skim Coat WaloCel MKX 15000 PF 01 15,000 multipurposeMortars for EIFS/Skim Coat WaloCel MKW 15000 PP 30 15,000 good air void stabilization,sag resistanceMortars for EIFS/Skim Coat WaloCel MKW 20000 PP 20 20,000 good air void stabilizationMortars for EIFS/Skim Coat WaloCel MKX 20000 PP 10 20,000 easy workabilityMortars for EIFS/Skim Coat MeThoCel 327 20,000 multipurposeMortars for EIFS/Skim Coat WaloCel MKX 25000 PF 25 l 25,000 high yield, good workabilityMortars for EIFS/Skim Coat WaloCel MKX 45000 PP 10 45,000 high water retentionMortars for EIFS/Skim Coat WaloCel MKX 45000 PF 20 l 45,000 good workabilityCement-Based Plasters WaloCel MKW 15000 PP 30 15,000 air void stabilization, good standing strengthCement-Based Plasters WaloCel MKW 20000 PP 01 20,000 air void stabilization, good standing strengthCement-Based Plasters WaloCel MKW 20000 PP 20 20,000 air void stabilization, easy workabilityCement-Based Plasters WaloCel MKW 20000 PP 30 20,000 air void stabilization, sag resistanceCement-Based Plasters WaloCel MKW 20000 PP 40 20,000 air void stabilization, high yield
DOW
Cement-Based Plasters WaloCel MKW 30000 PP 01 30,000 air void stabilizationCement-Based Plasters WaloCel MKW 30000 PP 10 30,000 air void stabilization, easy workabilityCement-Based Plasters WaloCel MKW 30000 PP 30 30,000 air void stabilization, sag resistanceGypsum-Based Building Materials WaloCel MKX 20000 PF 40 20,000 reduced lump formationGypsum-Based Building Materials WaloCel MKX 30000 PF 60 e 30,000 easy workability, high yieldGypsum-Based Building Materials WaloCel MKX 35000 PP 35 35,000 multipurposeGypsum-Based Building Materials WaloCel MKX 40000 PF 20 40,000 reduced lump formationGypsum-Based Building Materials WaloCel MKX 70000 PP 01 70,000 high water retentionGypsum-Based Building Materials WaloCel MKX 70000 PP 40 70,000 easy workability, high water retention
Shinetsu
Cement tile adhesive premium Tylose® MB 10008 P410000 mPa•s Höppler
Consistency development:moderateFinal consistency:very highSag resistance:very highWater demand:very highWater retention:moderateInfluence on cement hydration:moderateHeat stability:low
Cement tile adhesive standard Tylose® MB 15009 P2 15000 mPa•s Höppler
Consistency development:moderateFinal consistency:moderateSag resistance:moderateWater demand:highWater retention:highInfluence on cement hydration:highHeat stability:low
Cement tile adhesive premium Tylose® MB 3003 P43000 mPa•s Höppler
Consistency development:moderateFinal consistency:very highSag resistance:very highWater demand:highWater retention:lowInfluence on cement hydration:highHeat stability:low
Shinetsu
Paint-stripping pastes Tylose® MB 60000 P260000 mPa•s Höppler
Biostability:noGloss:moderatePigment Compatibility:moderateAnti-spattering:moderatePseudoplasticity:moderateThickening effect:highWet scrub resistance:highWater retention:very high
Gypsum spray plasterGypsum trowelling compound
Tylose® MHS 100005 P3100000 mPa•s
Consistency development:fastFinal consistency:highSag resistance:highWater demand:highWater retention:very highInfluence on cement hydration:lowHeat stability:high
Cement one coat Tylose® MHS 10012 P610000 mPa•s
Consistency development:very fastFinal consistency:highSag resistance:moderateWater demand:highWater retention:moderateInfluence on cement hydration:moderateHeat stability:high
Cement one coat Tylose® MHS 10012 P610000 mPa•s
Consistency development: very fastFinal consistency: highSag resistance: moderateWater demand: highWater retention: moderateInfluence on cement hydration: moderateHeat stability: high
Shinetsu
Block laying adhesive Gypsum mounting binder Gypsum spray plaster
Tylose® MHS 150003 P4150000 mPa•s
Consistency development: very fastFinal consistency: moderateSag resistance: moderateWater demand: highWater retention: very highInfluence on cement hydration: moderateHeat stability: high
Cement decorative render Cement skim coat
Tylose® MHS 30007 P630000 mPa•s
Consistency development: very fastFinal consistency: lowSag resistance: moderateWater demand: moderateWater retention: highInfluence on cement hydration: lowHeat stability: high
Tylose® MHS 30024 P4 30000 mPa•s
Consistency development: fastFinal consistency: moderate
Cement render EIFS Tylose® MHS 30027 P6
Höppler30000 mPa•s
Consistency development: very fastFinal consistency: moderateSag resistance: moderateWater demand: moderateWater retention: highInfluence on cement hydration: lowHeat stability: high
Shinetsu
Emulsion tile adhesive Tylose® MHS 60000 YP460000 mPa•s
Consistency development: fastFinal consistency: lowSag resistance: lowWater demand: low Water retention:very highInfluence on cement hydration: lowHeat stability: high
Gypsum hand plaster Tylose® MO 30023 P430000 mPa•s
Consistency development: fastFinal consistency: highSag resistance: highWater demand: highWater retention: highInfluence on cement hydration: moderateHeat stability: high
Emulsion joint filler Emulsion tile adhesive
Tylose® MOT 60000 YP460000 mPa•s
Consistency development: fastFinal consistency: lowSag resistance: lowWater demand: lowWater retention:very highInfluence on cement hydration: lowHeat stability: high
Protective colloidal effect: goodParticle size controll: good
Tylose® MOBS 50 G4 50 mPa•s
Rubber gloves Seed coating
PolymerisationSuspension polymerisation (PVC)
Shinetsu
Cement one coat Tylose® MO 60016 P460000 mPa•s
Consistency development: very fastFinal consistency: lowSag resistance: moderateWater demand: moderateWater retention: very highInfluence on cement hydration: lowHeat stability: high
Pencils Tylose® MO 4000 P44000 mPa•s
Ceramic applicationsEngobes & glazes Extrusion
Tylose® CER 406001 300 mPa•s
Thickening effect: moderatePlasticity: goodTemperature stability: goodBinding effect: moderate
Ceramic applicationsExtrusion Tylose® E 407003
20000 mPa•s
Thickening effect: highPlasticity: very goodTemperature stability: goodBinding effect: good
Ceramic applicationsPowder metallurgy Tylose® E 510024
10000 mPa•s
Thickening effect: very highPlasticity: goodTemperature stability: very goodBinding effect: very good
Ceramic applicationsExtrusion Tylose® E 514016
15000 mPa•s
Thickening effect: highPlasticity: goodTemperature stability: goodBinding effect: good
Shinetsu
Further applicationsRubber gloves Personal and home careShaving products
Tylose® E 7070024000 mPa•s
Thickening effect: moderateHigher purity: yesClarity of the solution: highStabilization of foam: highPseudoplasticity: lowCompatibility with salts: moderateCompatibility with surfactants:
Paint-stripping pastes Tylose® PSO 810001150000 mPa•s
Biostability: yes Thickening effect: very high
Cement decorative render Tylose® MH 6002 P46000 mPa•s
Consistency development: fastFinal consistency: moderateSag resistance: moderateWater demand: moderateWater retention: moderateInfluence on cement hydration: lowHeat stability: standard
Cement render Cement tile adhesive standard Gypsum hand plaster Gypsum joint compound Gypsum mounting binder Gypsum spray plaster Gypsum trowelling compound
Tylose® MH 60010 P4
60000 mPa•s
Consistency development: very fastFinal consistency: highSag resistance: moderateWater demand: highWater retention: very highInfluence on cement hydration:moderateHeat stability: standard
Cement tile adhesive ordinary Tylose® MH 60004 P6 according to Höppler60000 mPa•s
Consistency development: very fastFinal consistency: moderateSag resistance: moderateWater demand: moderateWater retention: very highInfluence on cement hydration: lowHeat stability: standard
Shinetsu
Cement skim coat Tylose® MH 60001 P660000 mPa•s
Consistency development: very fastFinal consistency: lowSag resistance: moderateWater demand: moderateWater retention: very highInfluence on cement hydration: lowHeat stability:standard
Cement one coat Cement tile adhesive ordinary Gypsum mounting binder Gypsum trowelling compound
Tylose® MH 60001 P460000 mPa•s
Consistency development: very fastFinal consistency: lowSag resistance: moderateWater demand: moderateWater retention: very highInfluence on cement hydration: lowHeat stability: standard
Pet litter Tylose® MH 60000 P660000 mPa•s
Grouts Coating materials Limewash paints Powder paints
Tylose® MH 6000 YP46000 mPa•s
Consistency development: fastFinal consistency: lowSag resistance: lowWater demand:very lowWater retention: moderateInfluence on cement hydration: lowHeat stability: standard
Shinetsu
Gypsum joint compound Tylose® MH 30026 P430000 mPa•s
Consistency development: moderateFinal consistency: very highSag resistance: very highWater demand: very highWater retention: highInfluence on cement hydration: moderateHeat stability: standard
Cement paints Exterior paints Silicone resin paints
Tylose® MH 30000 YP430000 mPa•s
Biostability: yesGloss: lowPigment Compatibility: lowAnti-spattering: goodPseudoplasticity: lowThickening effect: highWet scrub resistance: moderateWater retention: high
Self levelling floor compounds Tylose® MH 300 P2 300 mPa•s
Consistency development: slowFinal consistency: very lowSag resistance: lowWater demand: very lowWater retention: lowInfluence on cement hydration: lowHeat stability: standard
Block laying adhesive
Cement render
Tylose® MH 15002 P615000 mPa•s
Consistency development: fastFinal consistency: moderateSag resistance: moderateWater demand:highWater retention: highInfluence on cement hydration: lowHeat stability: standard
Shinetsu
Cement tile adhesive premium Tylose® MH 10016 P410000 mPa•s
Consistency development: fastFinal consistency: very highSag resistance: very highWater demand: very highWater retention: moderateInfluence on cement hydration: moderateHeat stability: high
Cement tile adhesive premium Tylose® MH 10015 P410000 mPa•s
Consistency development: fastFinal consistency: very highSag resistance: very highWater demand: very highWater retention: moderateInfluence on cement hydration: moderateHeat stability: high
Cement decorative render
EIFS
Tylose® MH 10007 P410000 mPa•s
Consistency development: fastFinal consistency: moderateSag resistance: moderateWater demand: moderateWater retention: moderateInfluence on cement hydration: moderateHeat stability: moderate
Cement skim coat Cement tile adhesive ordinary
Tylose® MH 100001 P6100000 mPa•s
Consistency development: very fastFinal consistency: lowSag resistance: moderateWater demand: moderateWater retention: very highInfluence on cement hydration: lowHeat stability: standard
Shinetsu
Toilet cleaners / WC-gels Tylose® MH 10000 KG410000 mPa•s
Thickening effect: moderateHigher purity: noClarity of the solution: moderateStabilization of foam: highPseudoplasticity: moderateCompatibility with salts: moderateCompatibility with surfactants: moderate
Gypsum joint compound Tylose® MH 10013 P410000 mPa•s
Consistency development: fastFinal consistency: very highSag resistance: very highWater demand: very highWater retention: moderateInfluence on cement hydration: moderateHeat stability: high
Akzo nobel
admixture in gypsum and cement BERMOCOLL® CCA 612
(Brookfield LV) 5500 – 7 500 mPa.s
BERMOCOLL CCA 612 prolongs the working time and effectively counteracts the sagging tendency of the plaster.
admixture in gypsum-based mortars BERMOCOLL® CCA 4702 500 – 3 500 mPa·s
BERMOCOLL CCA 470 ensures good water retention and gives a mortar with suitable working time.
gypsum based mortars BERMOCOLL® CCA 3285 000 – 7 000 mPa.s
BERMOCOLL CCA 328 effectively counteracts the sagging tendency of glue.
admixture in gypsum and cement BERMOCOLL® CCA 3122 300 – 3 000 mPa.s
BERMOCOLL CCA 312 prolongs the open time and effectively counteracts the sagging tendency of the plaster
latex paints BERMOCOLL® E 230 FQ260 - 360 mPa.s
BERMOCOLL E 230 FQ is easily dispersed in cold water of pH 7 or less
Akzo nobel
thickening and stabilizing effects in mortars and other building glues
BERMOCOLL® E 230X260 - 360 mPa.s
The simultaneous viscosity increase is moderate. Normal dosage is 0.4 - 0.8 % calculated on the dry mortar weight.
latex paints BERMOCOLL® E 320 FQ1 850 – 2 650 mPa.s
It improves the consistency, the stability, and the water retention of water based products.
stabilize aqueous dispersions BERMOCOLL® E 320 G1 850 – 2 650 mPa.s
It improves the consistency, the stability, and the water retention of water based products.
cement-based tile fix and joint mortars BERMOCOLL® E 351 X4 250 – 6 000 mPa.s
It improves the consistency, the stability, and the water retention of water based products.
cement-based tile fix and joint mortars BERMOCOLL® E 431 X1 700 – 2 400 mPa.s
improve workability, consistency, water retention and adhesion
cement-based tile fix and joint mortars BERMOCOLL® E 481 FQ4 250–6 000 mPa.s
It improves the consistency, the stability, and the water retention of water based products.
cement-based tile fix and joint mortars BERMOCOLL® E 511 X6 500-8000 mPa.s
It improves the consistency, the stability, and the water retention of water based products.
latex paints forthickening and stabilizing effects
BERMOCOLL® EBM 55005 000 – 6 500 mPa.s
It improves the consistency, thestability, and the water retention of water basedproducts.
latex paints forthickening and stabilizing effects,
BERMOCOLL® EBM 80007 000 – 9 000 mPa.s
It improves the consistency, the stability,and the water retention of water based products.
latex paints for thickening and stabilizing effects
BERMOCOLL® EBM 75907 500- 9 000 mPa.s
It improves the consistency, the stability, and the water retention of water based products.
latex paintsfor efficient thickening and stabilizing effects
BERMOCOLL® EBM 10 00010000 – 15000 mPa.s
It improves the consistency, the stability,and the water retention of water based products.
latex paints for thickening and stabilizing effects
BERMOCOLL® EBS 351 FQ5 000 – 6 000 mPa.s
It improves the consistency, the stability, and the water retention of water based products.
latex paints for thickening and stabilizing effects
BERMOCOLL® EBS 451FQ3 000 – 4 000 mPa.s
It improves the consistency, the stability, and the water retention of water based products
latex paints for thickening and stabilizing effects
BERMOCOLL® EBS 481FQ4 000 – 6 000 mPa.s
It improves the consistency, the stability, and the water retention of water based products.
Akzo nobel
a thickener in all types of latex paints BERMOCOLL® EHM 200min 350 mPa.s
improves high shear viscosity, roller spatter, flow and levelling
thickener in all types of latex paints BERMOCOLL® EHM 3001 700 – 3 000 mPa.s
improves high shear viscosity, roller spatter, flow and levelling.
thickener in all types of latex paints BERMOCOLL® EHM 5007000 - 10000 mPa.s
improves high shear viscosity, roller spatter, flow and levelling
thickener in all types of latex paints BERMOCOLL® EHM Extra250 - 450 mPa.s
improves high shear viscosity, roller spatter, flow and leveling.
latex paints for thickening and stabilizing effects
BERMOCOLL® EM 7000 FQ6 000 – 8 §000 mPa.s
It improves the consistency, the stability, and the water retention of water based products.
cement-based tile fix and joint mortars BERMOCOLL® M10750 – 1 200 mPa.s
intended as a water retaining and consistency improving additive to cement based mortars.
cement-based tile fix and joint mortars BERMOCOLL® M302 500 – 3 500 mPa.s
giving a unique balance between workability and strength.
cement-based tile fix and joint mortars BERMOCOLL® M30 Q2 500 – 3 500 mPa.s
giving a unique balance between workability and strength.
cement-based tile fix and joint mortars BERMOCOLL® ML 111 100 - 1 600 mPa.s
giving a unique balance between workability and strength.
cement-based tile fix and joint mortars for improvement of workability,consistency, water retention and adhesion.
BERMOCOLL® ML 312 900 – 3 900 mPa.s
giving a unique balance between workability and strength
cement-based tile fix, adhesives and plasters
BERMOCOLL® M 706 000 – 9 000 mPa.s
retaining and consistency improving additive to cement based mortars.
cement-based tile fix and joint mortars BERMOCOLL® ML 716 200 – 9 200 mPa.s
giving a unique balance between workability and strength.
cement based tile-fix BERMOCOLL® BCM 0503 500 – 6 000 mPa.s
giving unique balance between workability and strength.
Akzo nobel
cement based tile adhesive BERMOCOLL® BCM 0513 500 – 6 000 mPa.s
giving a unique balance between workability and strength
tile fix and joint mortars BERMOCOLL® BCM 1073 400 – 4 600 mPa.s
giving a unique balance between workability and strength
tile fix and joint mortars BERMOCOLL® BCM 1081 200 – 1 600 mPa.s
giving a unique balance between workability and strength
cement-based tile fix and joint mortars BERMOCOLL® M800 X11 000 – 15 000 mPa.s
It improves the consistency, the stability, and the water retention of water based products.
admixture in gypsum based plaster BERMOCOLL® CCM 81212 000 mPa.s
It improves the consistency and the water retention of gypsum based plaster
cement and gypsum based mortars BERMOCOLL® CCM 82510 000 – 14 000 mPa.s
improving additive to cement and gypsum based mortars
gypsum based mortars BERMOCOLL® CCM 87912 000 mPa.s
improving additive to gypsum based mortars.
gypsum based mortars BERMOCOLL® CCM 89410 000 – 14 000 mPa.s
improvement of workability, consistency and water retention, leading to a prolongation of the open time
cement-based tile fix and joint mortars BERMOCOLL® ME 1000 X11 000 – 15 000 mPa.s
It improves the water retention, the consistency and the stability of water based products.
gypsum based mortars BERMOCOLL® CCM 107910 000 – 15 000 mPa.s
rheology modifier in all types of latex paints
BERMOCOLL® Prime 1000500 - 900 mPa.s
It improves the consistency, the stability, and the water retention of water based paints.
rheology modifier in all types of latex paints
BERMOCOLL® Prime 25002 200 – 3 200 mPa.s
It improves the consistency, the stability, and the waterretention of water based paints.
Akzo nobel
rheology modifier in all types of latex paints
BERMOCOLL® Prime 35003,000 – 4,000 mPa.s
It improves the consistency, the stability, and the waterretention of water based paints.
Lotte fine chemical
Normal Tile Cement
Mecellose FMC-2400634,000 – 44,000
High water retardationExcellent open timeGood heat resistance
Mecellose FMC-2400733,000 – 43,000
High adhesion strengthExcellent open timeHigh water retention
Mecellose FMC-2500245,000 – 55,000
Excellent open timeGood water retentionGood heat resistance
Mecellose FMC-2600253,000 – 63,000
High adhesion strengthExcellent open timeHigh water retention
Mecellose FMC-2370133,000 – 43,000
standard tile cement(c1)
Mecellose FMC-207014,000 – 22,000
Overall good performanceLong open timeLess retardation of cement hydration
Mecellose FMC-2250118,000 – 26,000
Good open timeGood slip resistanceGood heat resistance
Mecellose FMC-2300727,000 – 35,000
Less retardation of cement hydrationLong open timeGood workabilit
Mecellose FMC-2350232,000 – 40,000
Excellent open timeGood workabilityGood heat resistance
Mecellose FMC-2450240,000 – 50,000
High water retentionGood Heat ResistanceGood slip resistance
Lotte fine chemical
standard tile cement(c1)
Mecellose FMC-2450342,000 – 52,000
High water retentionLong open timeGood heat resistance
High Performance Tile Cement
Mecellose FMC-2101012,000 – 18,000
Excellent slip resistanceLess retardation of cement hydrationVery good open time
Cement plaster
Mecellose FMC-20717,000 – 13,000
Excellent workabilityLess retardation of cement hydration
Mecellose FMC-210277,000 – 13,000
Excellent crack resistanceFast setting timeExcellent water retentionGood workability
Mecellose FMC-2151011,000 – 17,000
Fast thickening effectGood water retentionGood workabilityGood air stability
Mecellose FMC-2201315,000 – 23,000
Excellent workabilityGood water retentionLess stickiness
Skim coat
Mecellose FMC-2350528,000 – 40,000
Excellent workabilityLong pot lifeGood water retention
Mecellose FMC-2500245,000 – 55,000
Excellent workabilityLong pot lifeLess water absorption
Joint Compound
Mecellose PMB-40HS3,500 – 5,600
Good workabilityLess retardation of cement hydrationGood heat resistance
Mecellose PMB-40H 3,500 – 5,600
Excellent PressureVery good Green-body hardnessGood Surface state
Lotte fine chemical
Joint Compound
Mecellose FMC-5300130,000 – 40,000
Long retarded gradeExcellent workabilityGood water retention
Mecellose PMH-986030,000 – 40,000
Excellent workabilityGood water retention
Ready-to-use Tile Adhesive
Mecellose FMC-882145,000 – 55,000
Long retarded gradeExcellent water retentionGood open time
Mecellose FMC-5300130,000 – 40,000
Long retarded gradeExcellent workabilityGood water retention
Putty
Mecellose FMC-5150213,000 – 22,000
Very low air contentsGood sag resistanceEasy handling
Mecellose PMC-40US35,000 – 45,000
Very high water retentionHigh thickening efficiencyGood open timeEasy handling
Joint CompoundHecellose H 100K 100000Hecellose H 30K 30000Hecellose H 50K 50000
MonocapaMecellose FMC-2051Mecellose FMC-22013
Tile grout
Mecellose FMC-2101012,000 – 18,000
Excellent workabilityLess Retardation of Cement HydrationHigh water demand
Mecellose FMC-2300727,000 – 35,000
Excellent workabilityHigh water demandLong working time
Mecellose PMB-40HS3,500 – 5,600
Good workabilityLess retardation of cement hydrationGood heat resistance
Lotte fine chemical
self leveling compoundMecellose FMC-20101Mecellose FMC-60150Hecellose H300
Masonry mortar
Mecellose FMC-2101012,000 – 18,000
Excellent workabilityHigh water demandGood compressive strength
Mecellose FMC-2300727,000 – 35,000
Excellent water retentionGood workabilityLess stickiness
Mecellose FMC-2400634,000 – 44,000
Excellent workabilityLess stickinessGood sag resistance
Mecellose FMC-2400733,000 – 43,000
Excellent workabilityExcellent water retentionLess stickiness
EIFS
Mecellose FMC-207014,000 – 22,000
Excellent wetting capabilityGood workabilityGood adhesion strength
Mecellose FMC-2101012,000 – 18,000
Less stickinessExcellent adhesion strengthGood workability
Mecellose FMC-2300727,000 – 35,000
Excellent workabilityLess stickinessExcellent wetting capability
Mecellose FMC-2400634,000 – 44,000
High water retardationExcellent open timeGood heat resistance
Mecellose FMC-2350427,000 – 39,000
Mecellose FMC-2450342,000 – 52,000
Excellent workabilityLess stickinessExcellent open time
Lotte fine chemical
Gypsum Machine Plaster
Mecellose FMC-715030,000 – 40,000
High water demandGood sag resistanceGood workability & water retention
Mecellose FMC-7351628,000 – 38,000
Excellent WorkabilityExcellent sag resistanceGood water retention
Mecellose FMC-7550248,000 – 62,000
Excellent water retentionHigh water demandGood workability & sag resistance
Gypsum hand plaster
Mecellose FMC-711728,000 – 38,000
Excellent WorkabilityExcellent sag resistanceGood water retention
Mecellose FMC-7400435,000 – 43,000
Excellent water demandExcellent sag resistanceGood water retention
Mecellose FMC-7550347,000 – 61,000
Excellent water demandExcellent sag resistanceGood water retention
Gypsum Finishing Plaster
Mecellose FMC-711527,000 – 37,000
Good workabilityGood sag resistanceHigh water demand
Mecellose FMC-7250725,000 – 35,000
Good water retentionLess lump formationHigh water demand
Joint filler
Mecellose FMC-711527,000 – 37,000
Good workabilityGood sag resistanceHigh water demand
Mecellose FMC-510029,000 – 15,000
Excellent workabilityLess lumpingGood wet adhesion
Lotte fine chemical
Joint filler
Mecellose FMC-2400634,000 – 44,000
High water retentionExcellent workabilityGood sag resistance
Ashland
self leveling compound MHPC400
Economical Gypsum plaster
Culminal C835218500-23000
Excellent workabilityHigh wetabilityHigh sag resistance
Culminal C838135000-47000
Excellent workabilityHigh wetabilityHigh water retentionGood sag resistance
Superior Gypsum plaster
Culminal C870627000-36000
Reduced lump formationFor plasters with lower water demand
Culminal C838134000-46000
Excellent workabilityHigh wetabilityHigh water retentionGood sag resistance
Skim coat
Culminal C838135000-47000
Long open timeGood sag resistance
Combizel M402535000-45000
Combizel LH40M34000-46000
Combizel LH70M63000-72000
PREMIUM C2TEBrookfield RVT 2%
Culminal C9166 25000 Outstanding open timeSuperior water resistanceVery high strength valuesHigh sag resistance
Culminal C9167 9000Culminal C9168 8000
SUPERIOR C2T/C1 TE
Culminal C856410000-15000
Increased open timeExcellent water retentionHigh sag resistanceGood workability
Ashland
SUPERIOR C2T/C1 TE Culminal C916420000-30000
High water retentionOutstanding open timeHigh sag resistanceGood heat resistance
Culminal C9166 25000
Outstanding open timeSuperior water resistanceVery high strength valuesHigh sag resistance
Tile adhesive C1NPD/C1/C1T
Culminal C836732000-43000
Outstanding correctionHigh sag resistanceGood water retentionHigher strength
Culminal C911562000-75000
Outstanding correction timeExcellent heat resistanceGood water retentionSufficient sag resistance
Culminal C838135000-47000
long open time good sag resistance
Other related products
Culminal C811422000-30000
Culminal C855517000-23000
Culminal C910417000-25000
Culminal C911562000-75000
Culminal C9133 4000-6000
MHEC15000PFF18000-24000
MHEC 6000PFS 6000
Economical EIFS Culminal C8352 21000Excellent sag resistanceExcellent workability
Ashland
Superior EIFS Culminal C9164 2000-30000Long embedding timeCreamy workability
Premium EIFS Culminal C9166 25000Very long embedding timeCreamy workability
Other related products
Culminal C835517000-23000
Culminal C910417000-25000
Culminal C911562000-75000
Culminal C915525000-35000
MHEC15000PFF18000-24000
MHEC 6000PFS 6000
Combizel LH20M 18000-24000
Combizel LH40M 38000-55000
Combizel LH70M >60000
Gypsum joint filler
Culminal C8475 35000 Improved wetabilityExcellent water demandHigh sag resistanceSpecial dissolution property
Culminal C849517000-22500
Culminal C8713 65000
High efficiencyHigh water demandHigh water retentionVery strong thickening effect
Culminal C8715 65000
High efficiencyHigh water demandHigh water retentionStrong thickening effect
Ashland
Economical Renders Culminal C838135000-47000
High water retentionHigh sag resistance
Superior Renders Culminal C856410000-15000
Increased open timeUniversal application properties
Premium Renders
Culminal C830112000-17000
Very good workabilityUsed for one-coat render application
Culminal C8352 21000 Excellent workabilityExcellent sag-resistanceReduced stickinessCulminal C8355
17000-23000
Other grades
Culminal C405165000-85000
Culminal C405338000-51500
Culminal C807022000-30000
Culminal C831518000-24000
Culminal C8344 2000-26500
Culminal C835015000-20500
Culminal C835125000-30000
Culminal C835324000-32000
Culminal C838455000-75000
Culminal C870435000-45000
Culminal C836033000-45000
Culminal C837628000-38000
Ashland
Other grades
Culminal C871157000-67000
Culminal C9111 7500-10500