1
METAKAOLIN-METAKAOLIN-A SUPPLEMENTARY A SUPPLEMENTARY
CEMENTETIOUS MATERIALCEMENTETIOUS MATERIAL
BY
R.VALLISH
![Page 2: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/2.jpg)
2
INTRODUCTION
•A MATERIAL OTHER THAN CEMENT, WATER AND AGGREGATES THAT IS USED AS AN INGREDIENT OF CONCRETE AND IS ADDED TO THE BATCH IMMEDIATELY BEFORE OR DURING MIXING
ADMIXTURE
•USED TO MODIFY THE PROPERTIES OF ORDINARY CONCRETE SO AS TO MAKE IT MORE SUITABLE FOR ANY SITUATION
![Page 3: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/3.jpg)
3
POZZOLONA
• ARE THE TYPE OF ADMIXTURE , WHICH POSSESS LITTLE CEMENTISIOUS VALUE.
• IN FINELY DIVIDED FORM AND IN THE PRESENCE OF MOISTURE, CHEMICALLY REACTS WITH CALCIUM HYDROXIDE LIBERATED ON HYDRATION AT ORDINARY TEMPERATURE TO FORM COMPOUNDS POSSESSING CEMENTITIOUS PROPERTIES
• CLASSIFIED INTO NATURAL AND ARTIFICIAL POZZOLONA
![Page 4: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/4.jpg)
4
WHAT IS METAKAOLIN ?
• RELATIVELY NEW MINERAL ADMIXTURE
•HIGH REACTIVITY METAKAOLIN IS ONE OF THE RECENTLY DEVELOPED SUPPLEMENTARY CEMENTING MATERIALS FOR HIGH PERFORMANCE CONCRETE.
•PRODUCED BY CALCINING PURIFIED KAOLINITE CLAY AT A SPECIFIC TEMPERATURE RANGE TO DRIVE OFF THE CHEMICALLY BOUND WATER IN THE INTERSTICES OF KAOLINE AND DESTROY THE CRYSTALLINE STRUCTURE
![Page 5: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/5.jpg)
5
•PARTICLE SIZE OF THE METAKAOLIN IS LESS THAN 2μM
•IT IS TYPICALLY INCORPORATED INTO CONCRETE TO REPLACE 5 TO 15% BY WEIGHT OF CEMENT
•MIXTURES CONTAINING HIGH-REACTIVITY METAKAOLIN YIELD GOOD RESULTS IN TERMS OF STRENGTH,PERMEABILITY AND DRYING SHRINKAGE RESISTANCE.
![Page 6: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/6.jpg)
6
CONCRETE PROPERTIESFRESH CONCRETE
•MK, BEING VERY FINE IN SIZE GENERALLY HAS HIGHER WATER DEMAND FOR WORKABILITY.
•WITH INCREASED ADDITION OF MK WORKABILITY OF CONCRETE REDUCES
• FURTHER ADJUSTMENTS IN FINES OF CONCRETE, RETAINING COHESIVENESS, REDUCES LOSS IN WORKABILITY
![Page 7: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/7.jpg)
7
•BLEEDING WHICH IS A FUNCTION OF SEDIMENTATION DEPENDS UP ON MIX COMPOSITION AND PROPERTIES OF CEMENT FOR A GIVEN COMPOSITION.
•BLEEDING REDUCES WITH INCREASED SPECIFIC SURFACE AREA.
•THUS MK SURROUNDING THE AGGREGATE PARTICLES HELPS IN REDUCING THE BLEEDING.
BLEEDING
![Page 8: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/8.jpg)
8
•COMPRESSIVE STRENGTH OF METAKAOLIN CONCRETE CONTINUES TO INCREASE WITH REPLACEMENT LEVELS AT ALL AGES.
•IT COULD BE SEEN THAT THERE IS A SIGNIFICANT IMPROVEMENT IN EARLY AGE STRENGTH OF CONCRETE IN ADDITION TO 28-DAY STRENGTH LEVELS.
HARDENED CONCRETE
![Page 9: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/9.jpg)
9
CHEMICAL COMPOSITION OF METAKAOLIN AND CEMENT
CHEMICALS CEMENT METAKAOLIN
SIO2 21.0% 51.2%
Al2O3 5.2% 45.3%
Fe2O3 2.3% 0.60%
MgO 3.9% --
CaO 63.9% 0.05%
Na2O 0.5% 0.16%
K2O 0.5% 0.16%
SO3 2.4% --
![Page 10: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/10.jpg)
10
METAKAOLIN AS A CEMENT RELPLACEMENT MATERIAL
•GREATLY REDUCE POROSITY AND PERMIABILITY
•INCREASE COMPRESSIVE STRENGTH
HRM ADDED TO OPC AT 5-15% BY WEIGHT WILL
![Page 11: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/11.jpg)
11
•PROVIDE LONG TERM DURABILITY WHERE ASR IS A CONCERN
•REDUCE OCCURANCE OF EFFLORESENCE
•PROVIDE ENHANCED RESISTANCE TO CHEMICAL ATTACK
![Page 12: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/12.jpg)
12
PERMEABILITY
• PARTICLE SIZE OF HRM IS LESS THAN 2μm
• IT WILL SERVE TO FILL THE SPACES BETWEEN CEMENT GRAINS, PHYSICALLY TIGHTENING THE PARTICLE ARRAGEMENT
• HRM REACTS WITH CALCIUM HYDROXIDE TO FORM DURABLE BINDING PRODUCT NAMELY CALCIUM SILICATE AND CALCIUM ALUMINATE HYDRATES
•DISTINCT DENSIFICATION WHICH INCLUDE AN INCREASED STRENGHT AND DECREACED PERMIABILITY.
![Page 13: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/13.jpg)
13
POROSITY
• THE PORE SIZE DISTRIBUTION IS AFFECTED BY HRM.
•GENERALLY, THE TOTAL PORE VOLUME IS REDUCED AND THE AVERAGE PORE SIZE IS DECREASED
•SIGNIFICANT DECREASE IN THE OCCURANCE OF VERY FINE PORES IN AN HRM PASTE AS COMPARED TO OPC
![Page 14: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/14.jpg)
14
ALKALI SILICA REACTION
THE REACTION BETWEEN THE SILICIOUS MINERAL IN THE AGGREGATE AND THE ALKALINE HYDROXIDE DERIVED FROM ALKALIS IN CEMENT
RESULTS IN THE FORMATION OF UNLIMITED SWELLING TYPE
![Page 15: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/15.jpg)
15
EFFLORESCENCE
OCCURS WHEN CALCIUM HYDROXIDE(FREE LIME) BY PRODUCT OF HYDRATION OF CEMENT IS CARRIED TO THE SURFACE OF CEMENT BASED PRODUCTS BY MIGRATING WATER.
WHEN EXPOSED TO ATMOSPHERE CALCIUM HYDROXIDE REACTS WITH CARBON DIOXIDE TO FORM CALCIUM CARBONATE WHICH REMAINS AS WHITE STAINS
![Page 16: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/16.jpg)
16
ADVANTAGES AND
APPLICATIONS
![Page 17: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/17.jpg)
17
METAKAOLIN MODIFIED CONCRETE HAS A CREAMIER TEXTURE, SETS SOME WHAT FASTER, GENERATES LESS BLEED WATER AND HAS A BETTER FINISHABILITY
THE COMPRESSIVE AND FLEXURAL STRENGTH DEVELOPMENTS OF THE METAKAOLIN MIXTURES ARE SIGNIFICANTLY FASTER THAN THOSE OF THE NON POZZOLONIC CONTROL MIXTURE.
LONG TERM DRYING SHRINKAGE OF METAKAOLIN MIXTURE IS LESS THAN THAT OF PLAIN CONCRETE
ADVANTAGES
![Page 18: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/18.jpg)
18
ACCORDING TO ASTM, THE CHLORIDE PERMEABILITY OF METAKAOLIN MIXTURE IS MUCH LOWER THAN THAT OF PLAIN CONCRETE.
ELIMINATE FREE LIME FROM THE SYSTEM THROUGH RAPID POZZOLONIC REACTION
INCREASE THE DENSITY AND REDUCE THE POROSITY AND PERMEABILITY OF THE PASTE SYSTEM
REDUCE THE CEMENT CONTENT WITH POZZOLONA SUBSTITUTION 5-15%
![Page 19: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/19.jpg)
19
HIGH PERFORMANCE, HIGH STRENGTH AND LIGHT WEIGHT CONCRETE.
PRECAST CONCRETE WORKS
FIBRE CEMENT AND FERRO CEMENT PRODUCTS
MANUFACTURED REPITITIVE CONCRETE PRODUCTS
APPLICATIONS
![Page 20: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/20.jpg)
20
CASE STUDY
City college of New York
![Page 21: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/21.jpg)
21
•HIGH-REACTIVE METAKAOLIN (HRM) IS BEING USED IN CONCRETE TO RESTORE THE FACADE OF HISTORIC SHEPARD HALL AT THE CITY COLLEGE OF NEW YORK.
•THE DECISION TO USE THE CONCRETE ADDITIVE WAS BASED ON TO MEET THE PERFORMANCE REQUIREMENTS ESTABLISHED FOR THE BUILDING.
•THE PROJECT DRAMATICALLY DEMONSTRATES THE POTENTIAL OF HRM TO ENHANCE THE PERFORMANCE AND APPEARANCE OF CONCRETE.
![Page 22: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/22.jpg)
22
CONCLUSIONS
• METAKAOLIN OFFERS BETTER WORKABILITY COMPARED TO OTHER ADMIXTURES.
•STRENGTH OF METAKAOLIN MODIFIED CONCRETE INCREASE AT ALL STAGES.
•DURABILITY AND COMPRESSIVE STRENGTH ARE LIKE TWO LEGS OF HUMAN BEING, THESE TWO PROPERTIES CAN BE ENHANCED BY THE USE OF METAKAOLIN.
![Page 23: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/23.jpg)
23
REFERENCES
•A. K. Tiwari & P. Bandhyopadhyay, “Metakaolin for high performance concretes in India”, Indian Concrete Journal, April 2003.
•M. S. Shetty, “Concrete Technology”, 2002, S. Chand & Co. Ltd.
• Neville. A.M. “Properties of Concrete” Fourth Edition Wiley & Sons 1996.
• Jian-Tong Ding and Zongjin Li, “Effects of Metakaolin and Silica Fume on Properties of Concrete”, July-August 2003, pp. 393-398.
![Page 24: METAKAOLIN -SUPPLEMENTARY CEMENTETIOUS MATERIAL](https://reader037.vdocuments.us/reader037/viewer/2022100304/544e3d8aaf79595b278b4719/html5/thumbnails/24.jpg)