Rupture of deep groove ball bearing cage belongs to the occasional and non-normal failure
mode, we should analysis the causes of IKO bearing cage fracture following the five aspects
below.
1, deep groove ball bearing is poor lubrication: IKO bearing is running in a lean State, forming
adhesive wear, and deterioration of the working surface. Tear matter produced by adhesive
wear is easy to enter into the cage, so that cage is in abnormal loads, has the potential to
cause rupture of cage.
2, creep phenomena of deep groove ball bearings: creep mostly means sliding phenomenon
of finger rings, in case of insufficient interference combined with surface, the loading point
moves around due to sliding, direction ring relative to the circular shaft or housing location
deviation.
3, cage of deep groove ball bearing material defects: cracks, large blocks of metal inclusions
and shrinkage cavity defects, bubble and riveting short nails or nails, pad in half cage surface
voids, serious damage may cause, these all may cause cage fracture.
4,deep groove ball bearing cage is abnormal load: not installed in certain place, tilt, and
excessive interference, which easily caused tour gap reduced, increased friction and heat,
surface softened, prematurely appeared exception peeling. As peeling extended, peeling
foreign body entered into the frame hole, leading to the cage running block and producing
attached load, increased cage wear. Such deterioration in the loop, will may cause the cage
fracture.
5, hard foreign body invasion: intrusion of foreign body exacerbates the cage wear and
generate exception additional load, which can cause the cage fracture.
My name is Michael chower, a bearing engineer. Click http://singlerowballbearing.blogspot.com
for more details or products at http://www.hisupplier.com/a-deep-groove-ball-bearing/ or
http://www.hisupplier.com/a-single-row-ball-bearing/.