LAMINATED METAL–INTERMETALLIC
COMPOSITES BY EXPLOSIVE WELDING AND ANNEALING
I. A. Bataev1, A. A. Bataev1, V. I. Mali2, M. A. Esikov2, P. S. Yartsev1, A.S. Gontarenko1
1. Novosibirsk State Technical Univestity2. Lavrentyev Institute of Hydrodynamics SB RAS
![Page 2: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/2.jpg)
1. Motivation 2. Structure of Al-Ti composite produced by
explosive welding 3. Peculiarities of Al3Ti layer formation
during annealing 4. Some results of mechanical tests 5. Conclusion
Outline
![Page 3: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/3.jpg)
Motivation High specific stiffness High heat resistance Low density Good results in fatigue and impact tests Combining the properties of both the hard
and refractory intermetallics and the ductile matrix
“Dilution” of titanium with cheaper aluminum reduces the cost of material
![Page 4: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/4.jpg)
Vecchio KS. Synthetic multifunctional metallic–intermetallic laminate composites. JOM 2005;57:25–31.
![Page 5: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/5.jpg)
Scheme of explosive welding
Al plate – 1mm
Ti plate – 0,5 mm
HE – Ammonite 6GV
![Page 6: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/6.jpg)
Cross-section of explosively welded Al-Ti composite (optical microscopy)
![Page 7: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/7.jpg)
Interface appearance in the upper and lower parts of the composite
Upper part of composite
lower part of composite
![Page 8: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/8.jpg)
TEM investigation of the interface
![Page 9: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/9.jpg)
Vortexes arised during explosive welding Al distribution
Ti distribution
![Page 10: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/10.jpg)
Vortexes structure (TEM)
![Page 11: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/11.jpg)
Dynamic of Al3Ti layer growth(630 oC annealing)
1 hour 5 hours 100 hours
Wavy interfaces
plane interfaces
![Page 12: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/12.jpg)
Al3Ti layer thickness at different interfaces after annealing at 630 oC
5 hours annealing
100 hours annealing
![Page 13: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/13.jpg)
5 hours at 630 oC, layer thickness
![Page 14: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/14.jpg)
Growth of Al3Tiat the position of former vortexes
Growth of Al3Tiat plane interface
630 oC annealing, 30 min
![Page 15: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/15.jpg)
Scheme of Al3Ti layer growth
![Page 16: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/16.jpg)
Dependence of intermetallic layer thickness on annealing time
![Page 17: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/17.jpg)
XRD pattern after 100 hours at 630o
![Page 18: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/18.jpg)
TEM of intermetallic layer
Al3Ti
![Page 19: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/19.jpg)
Differences in Al3Ti grain size in different zones
Near Al Middle of the Al3Ti layer Near Ti
Al Al3Ti Ti
![Page 20: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/20.jpg)
Iron-reach intermetallic precipitations (100 hours 630 oC)
Dark field OM Btight field OM Btight field OM,Iron-rich precipitation in the Al-layer
![Page 21: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/21.jpg)
Impact behavior of Al –Al3Ti – Ti composite
Al –Al3Ti – Ti Al – Ti
Al3Ti Ti
![Page 22: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/22.jpg)
Scheme of fatigue cracks propagation
![Page 23: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/23.jpg)
Fatigue fracture of Al3Ti layer
![Page 24: I. A. Bataev 1, A. A. Bataev 1, V. I. Mali 2, M. A. Esikov 2, P. S. Yartsev 1, A.S. Gontarenko 1 1. Novosibirsk State Technical Univestity 2. Lavrentyev](https://reader035.vdocuments.us/reader035/viewer/2022081515/551811825503467b258b4588/html5/thumbnails/24.jpg)
Explosive welding of Ti and Al plates with subsequent annealing is effective technological process for MIL composites production.
Titanium trialuminide (Al3Ti) is the only intermetallic compound between Al and Ti formed under annealing.
The most favorable place for Al3Ti growth are former vortexes
The best intermetallic structure is on the Ti-Al3Ti boundary. On Al-Al3Ti boundary pores and microcracks were found
One of the most important goals arisen during explosive welding and annealing is addressing the causes of residual stresses, pores and microcracks formation
Conclusion