Natural fibres are hygroscopic and they are able to
absorb water molecules from a moist atmosphereand to give up water to a dry atmosphere;
The properties of many textile fibres such as mass,tensile strength, elongation, elastic recovery,electrical resistance, fibre dimensions and rigidity arestrongly affected by the amount of moisture in theair;
Moisture content can have a significant effect on themass of the material. Commercially, it is important toknow the amount of moisture contained in thematerials.
-
7/29/2019 6 Textiles and Moisture
2/15
Dimensional
Mechanical
Electrical
Thermal
-
7/29/2019 6 Textiles and Moisture
3/15
The behaviour of the fibre (swelling and deswelling) to changes in the relative
humidity of the environment is responsible for the dimensional stability
problems of certain fabrics
-
7/29/2019 6 Textiles and Moisture
4/15
Some fibres, such as wool and viscose, lose strength
when they absorb water and some, such as cotton, flax,
hemp and jute, increase in strength;
The extensibility, that is the extension at a given load,can increase for some fibres when wet;
Wool fibre (like most protein fibres) loses strength but
gains in elongation when wet compared with a drysample;
Besides tensile strength other properties such as fabric
tearing strength are affected by fibre strength.
-
7/29/2019 6 Textiles and Moisture
5/15
o The moisture content of fibres has animportant effect on their electricalproperties;
o The electrical resistance decreases andcapacitance increases with increasingmoisture content;
o Static electrical charges are more readilydissipated when the atmospheric relativehumidity is high.
-
7/29/2019 6 Textiles and Moisture
6/15
When moisture is absorbed by the fibre(esp wool), heat (heat of absorption orwetting, when fibre wets), is generated;
The thermal conductivity of the fibreincreases with moisture;
The application of both facts is importantin the design of clothing in coldenvironment.
-
7/29/2019 6 Textiles and Moisture
7/15
Therelative humidity is a ratio of the mass of watervapour in a given volume of air to mass of water vapourrequired to saturate this volume (100% humidity) at thesame temperature and is expressed as a percentage;
It can also be defined as the ratio of the actual vapourpressure to the saturated vapour pressure at the sametemperature;
The absolute humidity is defined as the weight of waterpresent in moist air (g/m3);
The amount of moisture contained by fibres that are inequilibrium with the atmosphere appears to depend onthe relative rather than the absolute humidity.
-
7/29/2019 6 Textiles and Moisture
8/15
The relative humidity affects the moisture content oftextile fibres and their properties;
It is thus necessary to specify the atmosphericconditions in which any testing is carried out;
A standard atmosphere for testing purposes is definedas a relative humidity of 65% and a temperature of2OoC;
In practice, certain tolerances in these values areallowed so that the testing atmosphere is RH 65% 2%,20 2oC. In tropical regions a temperature of 27 2oCmay be used;
Hygrometer is used to measure relative humidity.
-
7/29/2019 6 Textiles and Moisture
9/15
The amount of moisture in a fibre sample can beexpressed as eitherregain ormoisture content.Regain, popularly used in the textile industry, is theweight of water in a material expressed as a
percentage of the oven dry weight:
Regain,% = (10O x W) / D ;
where D is the dry weight and W is the weight ofabsorbed water
Moisture content is the weight of water expressedas a percentage of the total weight:
Moisture content, % = (100 x W) / ( D + W)
-
7/29/2019 6 Textiles and Moisture
10/15
Hysteresis: If two identical samples of fibre, one wet and
one dry, are placed in a standard atmosphere of 65% RH,the one that was originally wet is found to have a higher
regain than the one that was originally dry.
Equilibrium
Time
Regain, %
When samples are being conditioned, it is necessary for reproducibility of moisture
content for a sample to approach equilibrium in the std testing atm from the same
direction every time. The samples are dried in an oven at a low temperature (5OoC)
before conditioning in the std atmosphere
absorption
desorption
Regain, %
Relative humidity, %
-
7/29/2019 6 Textiles and Moisture
11/15
To measure the regain of a sample of textilematerial it is necessary to weigh the material, dry itand then weigh it again. The difference betweenthe masses is then the mass of water in the sample.
Regain, % = (mass of water x 100) / oven dry mass
Regain is based on the oven dry mass, which formost fibres is the constant mass obtained by drying
at a temperature of 105 2oC for most fibres forabout 1-2 hours. Constant mass is achieved bydrying and weighing repeatedly, at short intervals,until successive weighings differ by less than 0.05%.
-
7/29/2019 6 Textiles and Moisture
12/15
A conditioning oven is a large oven which contains the fibre
sample in a mesh container which is connected to a balance.This ensures that the weight of the sample can be monitoredwithout the need to remove it from the oven
A continual flow of air at the correct relative humidity is passedthrough the oven which is maintained at 105oC. The use of a
conditioning oven to dry a sample is the correct standardprocedure;
-
7/29/2019 6 Textiles and Moisture
13/15
A 'correct invoice weight' has to be determined when textile
materials, affected by RH, are bought and sold by weight;
A sample (~200 g), stored in air tight container, is taken from theconsignment and tests are made to give the correct invoiceweight;
The samples are weighed and then the oven dry weight isdetermined as described above.
The oven dry mass of the consignment, C = (M x D) / S ;
M is the mass of consignment at time of sampling, D is the oven dry mass
of sample, and S is the original mass of sample.
To the oven dry mass is added an official or standard regainallowance (as set out in BS 4784) for moisture depending on thenature and type of the material;
In the case of a blend the overall allowance is calculated fromthe fraction of each component in the blend multiplied by its
regain value.
-
7/29/2019 6 Textiles and Moisture
14/15
Testing laboratories require the atmosphere to be maintained at65 2% RH and 20 20oC in order to carry out accurate physicaltesting of textiles;
The temperature is controlled in the usual way with a heater/refrigeration and thermostat;
The relative humidity is controlled by a hygrometer whichoperates either a humidification or a drying plant;
The laboratory enclosure should be such (adequate insulation,air-tight doors and windows) that it helps to maintain theatmosphere within the tolerance bands;
When a fully conditioned testing laboratory is not available,testing should be carried out in a room in which ambientconditions are as uniform as possible throughout the year;
Small cabinets may be used to condition samples before testing,the actual tests being carried out in a normal atmosphere
straight after removal from the conditioned atmosphere.
-
7/29/2019 6 Textiles and Moisture
15/15
Tendency of fibers getting charged with static electricity changes according to
surface resistivity of them. Relative humidity directly affects surface resistivity.