Basic dental materials
From the above properties it is clear that there is no appreciable advantage of using metal modified GIC over conventional GIC.
Bahan dasar gigi Dari sifat-sifat di atas jelas bahwa tidak ada keuntungan yang cukup menggunakan logam diubah GIC atas GIC konvensional.
Anticariogenic property
Both metal modified ionomers have anticariogenic capability due to leaching of fluoride. However less fluoride is released from cermet cement than type II GIC, since the glass particle is metal coated. On the other hand the admixed cement releases more fluoride than type II GIC. Here the metal filler particles are not bonded to the cement matrix and thus there are pathways for fluid exchange. This increases leaching of fluoride.
Properti antikariogenik
Kedua logam diubah ionomer memiliki kemampuan antikariogenik karena pencucian fluoride. Namun kurang fluoride dilepaskan dari semen keramik logam dari tipe II GIC, karena partikel kaca logam dilapisi. Di sisi lain rilis semen dicampur lebih fluoride dari tipe II GIC. Berikut partikel filler metal tidak terikat pada matriks semen dan dengan demikian ada jalur untuk pertukaran cairan. Hal ini meningkatkan pencucian fluoride.
Resin-modified glass ionomer
These are relatively new materials having various names like compomer,resin-ionomers,RMGI (resin modified glass ionomer), light cured GIC,dual cure GIC,tricure GIC,reinforced GIC,hybrid ionomers,etc. These materials were developed to over come some of the drawbacks of conventional GIC like.- moisture sensitivity-low initial strength-fixed working times
Resin modified glass ionomer
Ini adalah bahan yang relatif baru yang memiliki berbagai nama seperti kompomer resin-ionomer, RMGI (modifikasi resin ionomer kaca), cahaya sembuh GIC, dual menyembuhkan GIC, tricure GIC, diperkuat GIC, ionomers hybrid, dll. Bahan-bahan ini dikembangkan untuk menanggulangi beberapa kelemahan dari konvensional GIC seperti.
Sensitivitas kelembaban -
Kekuatan awal-rendah
-Tetap kali bekerja
![Page 2: Dental Materials](https://reader036.vdocuments.us/reader036/viewer/2022082415/5695d2c41a28ab9b029ba72f/html5/thumbnails/2.jpg)
ClassificationDependingon which is the predominant component. These materials may be classified as (mcClean et al)A.resin-modified glass ionomer cement (RMGI), e.g., Fuji II LC (Figs 7.21 A to C) , vitremer,photac Fil , etc.B. Compomers or polyacid-modified composites (pmc), e.g, dyract variglass VLC (this category will be discussed subsequently under the heading compomers).
Klasifikasi
Tergantung yang merupakan komponen dominan. Bahan-bahan ini dapat diklasifikasikan sebagai (McClean et al)
A.resin-dimodifikasi glass ionomer semen (RMGI), misalnya, Fuji II LC (Gambar 7.21 A ke C), vitremer, photac Fil, dll
B. Kompomer atau komposit poli-dimodifikasi (PMC), misalnya, varioglass dyract VLC (kategori ini akan dibahas selanjutnya di bawah Kompomer judul).
Uses
1.Restoration of class I,III, or V cavities.2.Bases and liners3.As adhesives for orthodontic brackets.4.Cementation of crowns and FPDs.5.Repair of damaged amalgam cores or cuspa6.Retrograde root filling
Penggunaan
1.Restoration kelas I, III, atau rongga V.
2.Bases dan liners
3.As perekat untuk kurung ortodontik.
4.Cementation mahkota dan FPDs.
5.Repair core amalgam rusak atau cuspa
6.Retrograde mengisi akar
Note uses vary according to brand
Supplied asThey are supplied as*chemical cure (acid-base setting reaction of the glass ionomer portion)*dual cure (combines acis-base setting reaction of the GIC portion and light curing of the resin portion)
![Page 3: Dental Materials](https://reader036.vdocuments.us/reader036/viewer/2022082415/5695d2c41a28ab9b029ba72f/html5/thumbnails/3.jpg)
*tricure (combines acid base setting reaction,chemical and light cured polymerization of the resin portion)
Menggunakan catatan bervariasi sesuai dengan merek
Disediakan sebagai
Mereka disediakan sebagai
* Menyembuhkan kimia (pengaturan reaksi asam-basa dari bagian ionomer kaca)
* Ganda menyembuhkan (menggabungkan pengaturan reaksi ACIS-dasar GIC porsi dan cahaya menyembuhkan dari bagian resin)
* Tricure (gabungan reaksi pengaturan asam basa, bahan kimia dan cahaya sembuh polimerisasi bagian resin)
All of them are usually supplied as powder and liquid. The light cures type is supplied in dark shaded bottles (for light protection)
Composition
Since these are combination materials,they contain components of both resin and glass ionomer. However their proportions vary.
Semua dari mereka biasanya diberikan sebagai bubuk dan cair. Penyembuhan cahaya jenis diberikan dalam gelap berbayang botol (untuk perlindungan cahaya)
Komposisi
Karena ini adalah bahan kombinasi, mengandung komponen dari kedua resin dan kaca ionomer. Namun proporsi mereka bervariasi.
Powder : ion ieachable glasses (silica,alumina), photoinitiators or chemcical initiators or both, polymerizable resin
Liquid : polyacrylie acid , water, methacrylate monomer , hydroxyethyl methacrylate monomers
Powder: ion kaca leachable (silika, alumina), photoinitiators atau chemcical inisiator atau keduanya, resin polimerisasi
Liquid: asam poliakrilat, air, monomer metakrilat, monomer metakrilat hidroksietil
Setting reactionSetting includes both polymerization and axid-base reaction. The initial setting occurs by polymerization of the methacrylate groups giving it a high early strength. Polymerization may be
![Page 4: Dental Materials](https://reader036.vdocuments.us/reader036/viewer/2022082415/5695d2c41a28ab9b029ba72f/html5/thumbnails/4.jpg)
light cured or chemical cured depending on the type of cement. Subsequently the acid-base reaction sets it thereby completing the setting reaction and giving the cement its final strength.
Reaksi pengaturan
Pengaturan meliputi polimerisasi dan reaksi asam-basa. Pengaturan awal terjadi dengan polimerisasi kelompok metakrilat memberikan kekuatan awal yang tinggi. Polimerisasi dapat disembuhkan cahaya atau kimia disembuhkan tergantung pada jenis semen. Selanjutnya reaksi asam-basa set sana dengan menyelesaikan reaksi pengaturan dan memberikan semen kekuatan akhir.
Manipulation
RMGI is mixed and applied after conditioning the tooth with polycryle acid (10to 25%). The powder and liquid is mixed according to the manufacturer's instruction. Light cured RMGI is cured by exposure to blue light (whixh is used for curing composite)
Manipulasi
RMGI dicampur dan diterapkan setelah pengkondisian gigi dengan asam polycryle (10to 25%). Bubuk dan cair dicampur sesuai dengan instruksi produsen. Cahaya sembuh RMGI disembuhkan oleh paparan cahaya biru (whixh digunakan untuk menyembuhkan komposit)
PropertiesStrengthThe compressive strength is slightly lower (105 MPa) when compared to conventional GIC. The diametral tensile strength is however greater (20MPa). They have a greater fracture toughness because of the greater relilience of the resin component.
Properti
Kekuatan
Kuat tekan sedikit lebih rendah (105 MPa) bila dibandingkan dengan GIC konvensional. Kekuatan tarik diametral Namun lebih besar (20MPa). Mereka memiliki ketangguhan retak yang lebih besar karena relilience lebih besar dari komponen resin.
Zinc oxide / zinc sulphate cements
These are single component temporary filling materials.
Supplied asAs putty in small tubes, syringes or plastic containers. Representative products : cavit (ESPE) , Caviton (GC) , Coltosol (Coltene) . UseShort term restorations after caries excavation, root canal therapy, etc.
Seng oksida / seng sulfat semen
![Page 5: Dental Materials](https://reader036.vdocuments.us/reader036/viewer/2022082415/5695d2c41a28ab9b029ba72f/html5/thumbnails/5.jpg)
Ini adalah bahan mengisi sementara komponen tunggal.
Disediakan sebagai
Seperti takluk di tabung kecil, jarum suntik atau wadah plastik. Produk Perwakilan: Cavit (ESPE), Caviton (GC), Coltosol (Coltene).
Penggunaan
Restorasi jangka pendek setelah karies penggalian, terapi saluran akar, dll
CompositionZinc oxideZinc sulphate-1-hydrateCalcium sulphate -hemihydrateDibutyl phthalate (plastixizer)Diatomaceous earth
Komposisi
Seng oksida
Zinc-sulfat 1-hydrate
Kalsium sulfat -hemihydrate
Dibutil ftalat (plastixizer)
Tanah diatom