ACTAUNIVERSITATIS
UPSALIENSISUPPSALA
2019
Digital Comprehensive Summaries of Uppsala Dissertationsfrom the Faculty of Science and Technology 1824
Contacts and Interconnects forGermanium-based Monolithic 3DIntegrated Circuits
LUKAS JABLONKA
ISSN 1651-6214ISBN 978-91-513-0687-2urn:nbn:se:uu:diva-380573
Dissertation presented at Uppsala University to be publicly examined in Polhemsalen, Ångströmlaboratoriet, Lägerhyddsvägen 1, Uppsala, Friday, 20 September 2019 at 13:15 for the degree of Doctor of Philosophy. The examination will be conducted in English. Faculty examiner: PhD Fabrice Nemouchi (CEA-Leti, Grenoble, France).
AbstractJablonka, L. 2019. Contacts and Interconnects for Germanium-based Monolithic 3D Integrated Circuits. Digital Comprehensive Summaries of Uppsala Dissertations from the Faculty of Science and Technology 1824. 85 pp. Uppsala: Acta Universitatis Upsaliensis. ISBN 978-91-513-0687-2.
Three-dimensional integrated circuits have great potential for further increasing the number of transistors per area by stacking several device tiers on top of each other and without the need to continue the evermore complicated and expensive down-scaling of transistor dimensions. Among the different approaches towards the realization of such circuits, the monolithic approach, i.e. the tier-by-tier fabrication on a single substrate, is the most promising one in terms of integration density. Germanium is chosen as a substrate material instead of silicon in order to take advantage of its low fabrication temperatures as well as its high carrier mobilities. In this thesis, the work on two key components for the realization of such germanium-based three-dimensional integrated circuits is presented:the source/drain contacts to germanium the interconnects.
As a potential source/drain contact material, nickel germanide is investigated.In particular, the process temperature windows for the fabrication of morphologically stable nickel germanide layers formed from initial nickel layers below 10 nm are identified and the reaction between nickel and germanium is further studied by means of in-situ x-ray diffraction. The agglomeration temperature of nickel germanide is increased by 100 °C by the addition of tantalum and tungsten interlayers and capping layers. In an effort to more thoroughly characterize the contacts, a method to reliably extract the specific contact resistivity is implemented on germanium.
As a potential interconnect material cobalt is investigated. In a first step, highly conductive cobalt thin films are demonstrated by means of high-power impulse magnetron sputtering. The high conductivity of the cobalt films is owing to big grains, high density, high purity, and smooth interfaces. In a second step, the potential of high-power impulse magnetron sputtering for the metallization of nanostructures is further explored.
Lukas Jablonka, Department of Engineering Sciences, Solid State Electronics, Box 534, Uppsala University, SE-75121 Uppsala, Sweden.
© Lukas Jablonka 2019. Except where otherwise noted, this thesis is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License (https://creativecommons.org/licenses/by-sa/4.0/).
ISSN 1651-6214ISBN 978-91-513-0687-2urn:nbn:se:uu:diva-380573 (http://urn.kb.se/resolve?urn=urn:nbn:se:uu:diva-380573)
−40 −20 0 20 40
X [mm]
−40
−30
−20
−10
0
10
20
30
40
Y [
mm
]
(124.8 ±2.7) Ω/□
118
120
122
124
126
128
130
Sheet
Resi
stance [
Ω/□
]
50 100 150 200 250 300 3500.0
0.2
0.4
0.6
0.8
1.0
Equivalent hole diameter 𝑑eq [nm]
Yield
[1]
Figure 5.15. Yield in dependence of the equivalent hole diameter. Each datapoint isbased on measurements on 96 different devices.
HAAD
F
0
100
200
Al
0
50
100
Ti
0
50 Si
0
50
N
02040
O
02040
Ni
02040
Ge
0
50
100
Figure 5.16. HAADF-STEM micrograph and respective EDS maps of a contact holewith 𝑑nom = 250 nm.
51
0 10 20 30 40 50 60
Thickness [nm]
101
102
103R
esi
stiv
ity [
μΩ
cm
]DCMS -30 V
HiPIMS -30 V
DCMS -300 V
HiPIMS -300 V
Acta Universitatis UpsaliensisDigital Comprehensive Summaries of Uppsala Dissertationsfrom the Faculty of Science and Technology 1824
Editor: The Dean of the Faculty of Science and Technology
A doctoral dissertation from the Faculty of Science andTechnology, Uppsala University, is usually a summary of anumber of papers. A few copies of the complete dissertationare kept at major Swedish research libraries, while thesummary alone is distributed internationally throughthe series Digital Comprehensive Summaries of UppsalaDissertations from the Faculty of Science and Technology.(Prior to January, 2005, the series was published under thetitle “Comprehensive Summaries of Uppsala Dissertationsfrom the Faculty of Science and Technology”.)
Distribution: publications.uu.seurn:nbn:se:uu:diva-380573