collection - decolancollection 2012 compact. cutting edge laminates decolan proudly presents its...
TRANSCRIPT
-
Collectio
n
2 0 1 2
COMPACT
-
Cutting EdgeLaminatesDecolan proudly presents itsdecorative and distinct range ofhigh pressure Compact Laminates,available in spectacular coloursranging from solids, woodpatterns, abstracts & specialtextures.
PRODUCT COMPOSITIONDecorative surface papers impregnated with melamine resins are pressed overkraft paper core sheets, impregnated with thermosetting resins. These papers arethen cured at a pressure of 7 Mpa and temperature of 150 °C in which the resins
-
Outstanding characteristics ofGreenlam/decolan Compact Laminatesmake them ideal for both horizontal andvertical interior applications where thesurface should be functional, durable anddecorative.
Tissue overlay (for print decors)impregnated with melamine resins
Solid or print design paper layerimpregnated with melamine resins
Jet black colour kraft paper layersimpregnated with phenolic resins
Solid or print design paper layerimpregnated with melamine resins
Tissue overlay (for print decors)impregnated with melamine resins
Greenlam/decolan’s successful collection of CompactLaminates is available in various thickness* and size.They are engineered to meet special requirements such as:
• Exceptional self supporting properties
• Resistance to abrasion• Resistance to water
• Excellent hygiene properties• Resistance to harmful chemicals and organic solvents• Simple and quick assembly without the need for edging
and adhesive• In case of combustion, emits low amount of harmful gasses
and fumes
PRODUCT DESCRIPTION
Size & Thickness available
Thickness in mm4, 6, 9, 10, 12, 18, 25
10, 12, 18, 25
4 x 84.25 x 10
5 x 65 x 126 x 66 x 12
1220 x 2440300 x 3050
1550 x 18301550 x 36601830 x 18301830 x 3660
Size in Feet Size in mm
*Other thickness can also be made available on special request.
-
Adorn your décor with the best design, quality and performance worktoplaminates, manufactured to give a magnif icent look to your residentialand commercial space.
Purpose of Panels
Kitchen Tops Shelves
DesksCubicles
-
Greenlam/Decolan Compact Laminates are GREENGUARD
Explore Greenlam/Decolan’s rich array of compactlaminates available in elegant solids, versatile abstractsand genuine wood patterns. Add value and uniquenesswith décors that can blend well with contemporarylifestyles in various set-ups like
Restroom Cubicles
Partitions
Lockers
Worktops
Kid’s Furniture
Lab Furniture
School Furniture
Compact Application
Lockers
-
SpecialRaw SilkFinish
Compact GradeLaminates with
Greenlam/Decolan introduces
Compact Grade Laminates
with Special Raw Silk Finish to present you
something beyond luxury. Its pure silk pleasure.
Its fresh & soft aura can renew your decor & your life.
Touch it to feel it!
-
Antibacterial Compact Grade Laminates. These
compact laminates retards the growth of nearly
Freely found bacteria in environment whose
growth can be retarted includes:
• Staphylococcus aureus
• Streptococcus faecalis
• Escherichia coli
• Klebisella pneumoniae
Antibacterial CompactLaminates
To offer a safe living, Greenlam/Decolan introduces
-
Makes YourSurfacesHygienic
Antibacterial Compact Grade Laminatescan be used in the following areas:
• Restaurants
• Laboratories
• Hospitals andHealth Centres
• Lounges, Restrooms,Storage Rooms
• Restaurants
• Kindergarten
• Kitchens
ApplicationAreas
Not just beautiful, these compact laminates makes your surfaces germ-free andsecure. Produced by permanently incorporating a US-EPA approved, well-known andwidely used anti-microbial agent during the manufacturing, this range ensurescomplete health and hygiene for you and your family.
Wish you a happy and healthy life ahead!
-
ChemicalResistantCompactLaminates
Chemical Resistant compacts are meant for the
most challenging environments like clinics,
pathological labs, photographic darkrooms,
classrooms or stylish saloons where working
conditions are prone to use of chemicals.
This product is engineered by treating the decor
paper with special chemicals. The treatment given
to the Décor paper is an advanced formulation
which provides resistance from chemicals, abrasive
materials & other harsh substances.
-
Greenlam/Decolan Chemical Resistant Compact GradeLaminates can be used in the following areas:
Labs and pathologists’ work rooms
Counters and tabletops in hospitals
Photographers’ darkrooms
Beauty salons
Product testing facilities
Nurses’ stations, physician and dentist’s
examining and treatment rooms
Application Areas
-
929 Metaline Grey 923 Meta Silver 5853 Alu Taint
Quality Standards
SOLIDS
ABSTRACT
111 Designer White
134 Mud Ash
133 Moon Stone
166 Blush Pink 163 Bay
113 Frosty White
141 Beige 271 Light Grey 124 Mysore Ivory
121 Ivory 230 Cream Yellow 257 Olive 248 Leaf Green 217 Light Orange
284 Ozone 297 Blue Galaxy
275 Pearl Grey
268 Dust 291 Electric Blue 261 Dark Grey 401 Black
-
Thickness in mm4, 6, 9, 10, 12, 18, 25
10, 12, 18, 25
4 x 8* / 4.25 x 10*
5 x 6* / 5 x 12*6 x 6 / 6 x 12
1220 x 2440* / 1300 x 3050*
1550 x 1830* / 1550 x 3660*1830 x 1830 / 1830 x 3660
Size in Feet
DIMENSIONS OFFERING
Size in mm
WOODS
RAW SILK
682 Hiland Pine 770 Douglas Fur 719 Mangfall Beech
5003 Phillipine Teak
738 Oak
5525 Hickory Oak 5006 Thansau Maple 5018 Brooks Walnut 749 Sapele 5061 Fine Wenge
111 Designer White (RSL) 113 Frosty White (RSL)
284 Ozone (RSL) 738 Oak (RSL) 124 Mysore Ivory (RSL) 217 Light Orange (RSL) 5061 Fine Wenge (RSL)261 Dark Grey (RSL)
Refer the samples for the actual color of the designs shown. Note: All sample are in Suede Finish unless mentioned.
-
Chemical ResistanceCompact Laminate
9801 ARGENTWHITE 9802 CINEREAL 9803 BLACK
List of Chemicals ineffective against Chemical Resistant Compact LaminatesSize Available: 1550 mm x 3660 mm; Thicknesses Available: 12 mm, 13 mm, 16 mm & 18 mm
Chemicals
Acids
Nitric Acid (all concentrations)
Glacial Acetic Acid 99%(concentrated)
Sulfuric Acid (all concentrations)
Hydrochloric Acid (all concentrations)
Phosphoric Acid (all concentrations)
Formic Acid (all concentrations)
Acetic Acid (all concentrations)
Hydrofluoric Acid 48%(concentrated)
Aqua Regia
Chromic Trioxide (Chromic Acid Cleaning Solution)*
Picric Acid 1.2% (0.05M)
Tannic Acid (sat.)
Uric Acid (sat.)
Bases
Sodium Hydroxide (all concentrations)
Sodium Sulfide 15%
Ammonium Hydroxide (all concentrations)
Pottassium Hydroxide
Sodium Carbonate Saturated solution
Furfural
Solvents
Carbon Tetrachloride
Carbon Disulfide
Acetone
Benzene
Formaldehyde
Methanol
Ethyl Acetate
Toluene
n-Hexane
Ethyl Alcohol
Methyl Alcohol
Chloroform
Phenol (all concentrations)
EDTA
Xylene
Butyl Alcohol
Amyl Alcohol
Amyl Acetate
Cresol
Dioxane
Trichloroethane
Chlorobenzene
Dimethylformamide
Methylene Chloride
Methyl Ethyl Ketone
Methylated Spirits
Naphthalene
Tetrahydrofuran
Denatured Alcohol
Anilene Blue
General Reagents
Sodium Hypochlorite 5%
Calcium Hypochlorite (concentrated)
Hydrogen Peroxide 3%
Trisodium Phosphate 30%
Sodium aThiocyanate
Zinc Chloride
Lactated Ringers
Sucrose 50%
Gasoline
Kerosene
Nail polish remover
Mineral Oil
Vegetable Oils
Water
Sodium Chromate
Potassium Permanganate
Silver Nitrate
Formalin
Benedicts Solution
Phosphate Buffered Saline(PBS)
Copper Sulphate
Petroleum Jelly
Aluminon
Ethylene Glycol
Ethyle Acetate
Ethyl Ethor
Pine Oil
Methyl Methacrylate
Alconox (Lab. Detergent)
Karl Fisher Reagent
Urea
Naphtha
Cellosolve
Ammonium Phosphate
Iodine
Povidone Iodine
Tincture of Mercurochrome
Tincture of Iodine
Tincture of Merthiolate
Eucalyptol
Eucalyptol Ferric
Procaine
Zinc Oxide Ointment
Aromatic Ammonia
Thymol & Alcohol
Camphorated parachlorophenol
Quaternary Ammonia
Compounds
Monsel's Solution (Ferric Subsulfate)
Ferric Chloride
Sodium Azide
Bromothymol Blue
Phenolphthalein
Methyl Red
Methyl Orange
Gentian Violet 1%
Wright's Blood Stain
Methylene Blue
Nigrosine
Crystal Violet
Malachite Green
Cresol Red
Thymol Blue
Subsulphate purified
Isopropyl Alcohol
Citric acid
Ethanol (50%)
Fresh Coffee
Household Ammonia
#2 Pencil
Stamp pad ink
Shoe Polish
Tea Bag
Wax crayon
Yellow Mustard
-
Greenlam/DecolanCompact Laminates
TECHNICAL SPECIFICATIONS TYPE - COMPACT LAMINATE - CGS
Properties Specified ValuesNEMA LD 3-2005 Typical Value
Unit
Thickness 12.00 ± 0.60mm 12.00 ± 0.40Appearance � No ABC Defect No ABC DefectStraightness mm / meter (Max.) 1.5 1.2Diagonal difference mm (Max.) 6 3
� � �� a) Single side decorative surface� b) Double side decorative surface
Warpage120 4012 6Slight effect Slight effectRating (Min.)Light resistance
Cleanability Rating (Max.) 20 10Stain
a) Reagents 1 - 10b) Reagents 11 - 15
Rating (Min.) No effect Moderate effect
No effect Slight effect
Boilling water resistance No effect No effectRating (Min.)High temperature resistance Rating Slight effect No effectBall impact resistance mm (in) (Min.) 1900 (75") 2540 (100")
� � �a) Machine directionb) Cross direction
% (Max.) 0.3 0.15% (Max.) 0.7 0.30
Room temprature dimensional stabilitya) Machine directionb) Cross direction
% (Max.)% (Max.)
0.100.30.7 0.20
Wear resistance 400 400Cycles (Min.)Flexural strength �
a) Machine directionb) Cross direction
Mpa (Min.) (MD)Mpa (Min.) (CD)
124 13082.7 85
Flexural modulus �a) Machine directionb) Cross direction
Mpa (Min.) (MD)Mpa (Min.) (CD)
11000 115009650 10000
Tensile strength �a) Machine direction Mpa (Min.) (MD) 124 135
Dimensional change
mm (Max.)mm (Max.)
b) Cross direction Mpa (Min.) (CD) 82.7 90
S.No.
12345
67
8
910
11
12
13
1415
16
17
-
Greenlam/DecolanCompact Laminates
11000 - 12000
6 mm* 9 mm*
PropertiesS.No.
1 Thickness
Typical Value
2
3
4
5
6
7
8
9
10
11
12
13
14
15
16
17
TECHNICAL SPECIFIC ATIONS
.Resistance to surface waterResistance to immersion in boiling water
a) Mass increase
b) Thickness
Dimensional stability at deviated temperature
c) Appearance
a) Longitudinal
b) Transverse
Resistance to impact by large diameter ball
Dimensional stability at 20° C
a) Longitudinal
b) Transverse
a) Drop height
b) Diameter of indentation
Resistance to scratch
Resistance to staining
a) Group 1 & 2
b) Group 3 & 4
Resistance to colour change
Resistance to cigarette burns
a) In Xerox Arc light
b) In enclosed Carbon Arc light
Resistance to steam
Resistance to crazing
Resistance to moisture
Flexural modulus
Flexural strength
Resistance to dry heat at 180° C
Tensile strength
Unit
mm
Grade
Grade
Grade
Grade
Grade
Grade
Grade
Grade
Mpa
Mpa
Grade
Rev.
%%
Grade
%
%
%
%
cm
mm
N
Mpa
Specified Values As PerBS EN 438 &
IS 2046 : 1995
4.0 ± 0.30
Not worse than 5
Not worse than 4
Not worse than 6
Not worse than 5
Not worse than 3
Not worse than 4
Not worse than 4
Not worse than 4
10000 ( Min.)
100 ( Min. )
Not worse than 4
350 (Min.)
2.0 (Max.)
2.0 (Max.)
Not worse than 4
0.06 (Max.)
0.53 (Max.)
0.16 (Max.)
0.28 (Max.)
1800 mm
10 (Max.)
2.0 (Min.)
70 ( Min. )
6
5
6
5
4
5
5
5
100 - 120
80 - 90
5
400
0.48
0.70
5
0.03
0.14
0.10
0.14
2500 mm
4
2.5
Specified Values As PerBS EN 438 &
IS 2046 : 1995
9.0 ± 0.35
Not worse than 5
Not worse than 4
Not worse than 6
Not worse than 5
Not worse than 3
Not worse than 4
Not worse than 4
Not worse than 4
10000 ( Min.)
100 ( Min. )
Not worse than 4
350 (Min.)
2.0 (Max.)
2.0 (Max.)
Not worse than 4
0.06 (Max.)
0.53 (Max.)
0.16 (Max.)
0.28 (Max.)
1800 mm
10 (Max.)
2.0 (Min.)
70 ( Min. )
Typical Value
6
5
6
5
4
5
5
5
11000 - 12000
100 - 120
5
400
0.60
0.80
5
0.04
0.20
0.12
0.20
2500 mm
4
2.5
80 - 90
4.0 ± 0.20 9.0 ± 0.25
4 mm*
Typical Value
6
5
6
5
4
5
5
5
11000 - 12000
100 - 120
5
400
0.55
0.72
5
0.03
0.15
0.10
0.15
2500 mm
4
2.5
80 - 90
6.0 ± 0.20
Specified Values As PerBS EN 438 &
IS 2046 : 1995
6.0 ± 0.35
Not worse than 5
Not worse than 4
Not worse than 6
Not worse than 5
Not worse than 3
Not worse than 4
Not worse than 4
Not worse than 4
10000 ( Min.)
100 ( Min. )
Not worse than 4
350 (Min.)
2.0 (Max.)
2.0 (Max.)
Not worse than 4
0.06 (Max.)
0.53 (Max.)
0.16 (Max.)
0.28 (Max.)
1800 mm
10 (Max.)
2.0 (Min.)
70 ( Min. )
* Produced in 4’x8’ & 4.25’x10’ Sizes only
-
Greenlam/DecolanCompact Laminates
12 mm 18 mmSpecified Values As Per
BSEN 438 &IS 2046 : 1995
Specified Values As PerBSEN 438 &
IS 2046 : 1995UnitPropertiesS.No.
1 Thickness mm
Typical Value Typical Value
2
3
4
5
6
7
8
9
10
11
12
13
14
15
16
17
TECHNICAL SPECIFIC ATIONS
.
Resistance to dry heat at 180° C
Resistance to surface water
Resistance to immersion in boiling water
a) Mass increase
b) Thickness
Dimensional stability at deviated temperature
c) Appearance
a) Longitudinal
b) Transverse
Resistance to impact by large diameter ball
Dimensional stability at 20° C
a) Longitudinal
b) Transverse
a) Drop height
b) Diameter of indentation
Resistance to scratch
Resistance to staining
a) Group 1 & 2
b) Group 3 & 4
Resistance to colour change
Resistance to cigarette burns
a) In Xerox Arc light
b) In enclosed Carbon Arc light
Resistance to steam
Resistance to crazing
Resistance to moisture
Flexural modulus
Flexural strength
Tensile strength
Grade
Grade
Grade
Grade
Grade
Grade
Grade
Grade
Mpa
Mpa
Grade
Rev.
%
%
Grade
%
%
%
%
cm
mm
N
Mpa
Not worse than 5
Not worse than 4
Not worse than 6
Not worse than 5 Not worse than 5
Not worse than 3
Not worse than 4
Not worse than 4
Not worse than 4
10000 ( Min.)
100 ( Min. )
Not worse than 4
350 (Min.)
2.0 (Max.)
2.0 (Max.)
Not worse than 4
0.06 (Max.)
0.53 (Max.)
0.16 (Max.)
0.28 (Max.)
1800 mm
10 (Max.)
2.0 (Min.)
70 ( Min. )
Not worse than 5
Not worse than 4
Not worse than 6
Not worse than 3
Not worse than 4
Not worse than 4
Not worse than 4
10000 ( Min.)
100 ( Min. )
Not worse than 4
350 (Min.)
2.0 (Max.)
2.0 (Max.)
Not worse than 4
0.06 (Max.)
0.53 (Max.)
0.16 (Max.)
0.28 (Max.)
1800 mm
10 (Max.)
2.0 (Min.)
70 ( Min. )
6
5
6
5 5
4
5
5
5
11000
120
5
400
0.5
0.7
5
0.03
0.12
0.08
0.13
2500 mm
4
2.5
90
5
5
6
4
5
5
5
12000
120
90
5
400
0.20
0.40
5
0.03
0.10
0.08
0.10
2500 mm
4
2.5
12.0±0.40 18.0±0.5018.0±0.7012.0±0.5
-
Chemical ResistantCompact Laminates
ThicknessAppearanceStraightnessDiagonal DifferenceFlatness (allowable warp)Light ResistanceCleanabilityStain
a) Reagents 1-10b) Reagents 11-15
Boiling Water ResistanceHigh Temperature ResistanceBall Impact ResistanceDimensional Change
a) Machine Directionb) Cross Direction�
Room Temperature Dimensional Stabilitya) Machine Directionb) Cross Direction
Wear ResistanceScratch ResistanceFlexural Strength
a) Machine Directionb) Cross Direction
Flexural Modulusa) Machine Directionb) Cross Direction
Tensile Strengtha) Machine Directionb) Cross Direction
mm
mm/ meter (max.)mm (max.)mm (max.)Rating (min.)Rating (max.)
Rating (min.)Rating (min.)Rating (min.)Ratingmm (in) (min.)
% (max.)% (max.)
% (max.)% (max.)Cycles (min.)
N (min)
Mpa (min.) (MD)
Mpa (min.) (CD)
Mpa (min.) (MD)
Mpa (min.) (CD)
Mpa (min.) (MD)
Mpa (min.) (CD)
12.00 +/- 0.60No ABC defects1.5612Slight Effect20
No EffectModerate EffectNo EffectSlight Effect1900 (75")
0.30.7
0.30.74002.5
12482.7
110009650
124
82.7
12.00 +/- 0.40
No ABC defects1.23
6Slight Effect10
No EffectSlight Effect
No EffectNo Effect2540 (100")
0.150.3
0.10.2
6004.0
13085
1150010000
135
90
Conforms to SEFA 8.1-PL-2010; Chemical Spot Test*Chemical & Stain Resistance
UNITSpecified Values
NEMA LD-3;2005 Typical ValuePropertiesS.No.
TECHNICAL SPECIFICATIONS
1
2
3
4
5
6
7
8
9
10
11
12
13
14
15
16
17
18
19
-
mm 12.0 ± 0.40
5
600
0.20
5
0.70
0.07
0.14
2500
7
4.0
5
≥ 4
5
4
5
11000
120
90
1.45
Thickness
Resistance to Dry Heat at 180° C
Resistance to Surface Wear
Resistance to Immersion in Boiling Water (2 hours)a) Mass Increase
b) Thickness
c) Appearance
Dimensional Stability at Elevated Temperature
a) Longitudinal
b) Transverse
Resistance to Impact by Large Diameter Ball
a) Drop Height
b) Diameter of Indentation
Resistance to Scratching
Resistance to staining Group 1 & 2
Group 3
1
2
3
4
5
6
7
8
9
10
11
13
12
14
15
16
EN 438-4- 5
EN 438-2 -16
EN 438-2 -10
EN 438-2 - 12
EN 438-2 - 17
EN 438-2 - 21
EN 438-2 - 25
Chemical & Stain Resistance
Rating
Rev.
%
%
Rating
%
%
cm
mm
N
Rating
Resistance to Cigarette Burns
Resistance to Water Soak at 65°C for 48 hours
Resistance to Crazing
Flexural Modulus
Flexural Strength
Tensile Strength
Density
EN 438-2 - 26
EN 438-2 - 30
IS 2046:1995, Annexure Y
EN 438-2 - 24
EN ISO 178:2003
EN ISO 178:2003EN ISO 527-2:1996
EN ISO 1183 -1:2004
RatingRating
Rating
Rating
Mpa
MpaMpa
g/cm3
Conforms to SEFA 8.1-PL-2010; Chemical Spot Test*
UNITTEST METHOD AS PER
BS EN 438 Part 2 & 3:2005
12.0 ± 0.60
Not worse than 4
350 (min.)
2.0 (max.)
2.0 (max.)
Not worse than 4
0.30 (max)
0.60 (max)
180010 (max.)
2.0 (min.)
5
Not worse than 3
4
9000 (min.)
80 (min.)
60 (min.)
1.35
Not worse than 4
Not worse than 4
SpecifiedValues Typical ValuePropertiesS.No.
TECHNICAL SPECIFIC ATIONS
Chemical ResistantCompact Laminates
-
cre
ati
ve
stu
dio
mo
ren
o.i
t
HeadquartersCORSO SAN GOTTARDO 32CH-6830 CHIASSO (SWITZERLAND)ph. +4191 6821862fax +4191 6825610
UK Office39 CHAPMAN SQUARESW19 5QT LONDONfax +44 20 7900 2652
USA OfficeWOODLAWN OFFICE PARK601 WOODLAWN DRIVESUITE 320MARIETTA - GEORGIA 30067-3506COBB COUNTY - U.S.A.ph. (770) 3216595