cd101-105 for solvent based coating & printing

PRODUCT INFORMATION

2011-04-01

ASTROLL is the registered trademark for Kolon Industries' biaxially oriented PET film.

PI-1

CD101-105

For solvent based

Coating & Printing

Description

ASTROLL CD101-105 clear polyester films are chemically primed to provide enhanced adhesion

for solvent based coating and printing. CD-series possess optical clarity and low balanced

shrinkage for improved flatness after thermal processing.

ASTROLL CD101-105 are classified on side of chemically treated.

CODE Inside Outside

CD101 - Chemical

CD102 Corona Chemical

CD103 Chemical -

CD104 Chemical Corona

CD105 Chemical Chemical

Performance

ASTROLL CD101-105 are designed for excellent adhesion to numerous solvent-based coating

systems, so that it can be widely used in the field of food packaging, graphic arts, and other

industrial usages.

Application

☞ Gravure and flexographic printing

☞ Graphic arts

☞ Membrane switch

☞ Label

Schematic of ASTROLL○R CD101-105

Primer for adhesion

PET (12~300um, 48~1200G)

PRODUCT INFORMATION

2011-04-01


PI-2

Typical Properties of ASTROLL○R CD101-105

PRODUCT : ASTROLL○R

TYPE(CODE) : CD101

MAIN USAGE : Solvent based Coating & Printing

All the information given herein is the basic suggestion to the use of ASTROLL film. Even though the information is

accurate, users should carry out their own test regarding the fitness of ASTROLL film for their own particular usages.

Concerning this information, any liability, copyright, and freedom under patent are not assumed. The observance of all

legal regulations and patents is the user’s responsibility.

Properties Unit Value Test Method

Thickness um 50.0 75 (FB-1) 100 (FB-1)

Yield mm2/kg 울산 9.5 7.1

Tensile Strength MD

kg/mm2 25.0 19.0 19.0

ASTM D-882 TD 23.0 21.0 20.0

Elongation at break

MD %

170.0 210.0 210.0 ASTM D-882

TD 140.0 140.0 130.0

F-5 Value MD

kg/mm2 11.0 11.5 11.5

ASTM D-882 TD 10.5 11.0 11.5

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.2 0.7 1.0 ASTM D-2305

(150℃, 30min) TD 0.0 0.2 0.2

Friction Coefficient μs

- 0.30 0.70↓ 0.70↓

ASTM D-1894 μk 0.30 0.70↓ 0.70↓

Haze % 1.5 1.30 1.50 ASTM D-1003

Wetting Tension IN

dyne/cm -

ASTM D-2578 OUT 38±4 38 38

Test Condition Normal laboratory condition : 24℃, 45%RH

PRODUCT INFORMATION

2011-04-01


PI-3



TYPE(CODE) : CD101







Thickness um 125 (FB-1) 150 (FB-1) 175 (FB-1)

Yield mm2/kg 5.7 4.8 4.1

Tensile Strength MD

kg/mm2 18.0 17.0 18.0

ASTM D-882 TD 19.0 18.0 18.0

Elongation at break

MD %

230.0 240.0 240.0 ASTM D-882

TD 130.0 140.0 190.0

F-5 Value MD

kg/mm2 11.5 11.5 11.5

ASTM D-882 TD 11.5 11.5 11.5

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.0 1.0 1.0 ASTM D-2305

(150℃, 30min) TD 0.2 0.2 0.5


- 0.70↓ 0.70↓ 0.70↓

ASTM D-1894 μk 0.70↓ 0.70↓ 0.70↓

Haze % 1.80 2.00 2.50 ASTM D-1003

Wetting Tension IN

dyne/cm - - -

ASTM D-2578 OUT 38 38 38


PRODUCT INFORMATION

2011-04-01


PI-4



TYPE(CODE) : CD101







Thickness um 188 (FB-1)

Yield mm2/kg 3.8

Tensile Strength MD

kg/mm2 18.0

ASTM D-882 TD 18.0

Elongation at break

MD %

250.0 ASTM D-882

TD 200.0

F-5 Value MD

kg/mm2 11.0

ASTM D-882 TD 11.0

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.0 ASTM D-2305

(150℃, 30min) TD 0.5


- 0.70↓

ASTM D-1894 μk 0.70↓

Haze % 2.80 ASTM D-1003

Wetting Tension IN

dyne/cm -

ASTM D-2578 OUT 38


PRODUCT INFORMATION

2011-04-01


PI-5



TYPE(CODE) : CD102







Thickness um 11 12 15

Yield mm2/kg 김천 59.5 울산

Tensile Strength MD

kg/mm2 26.0 26.0 27.0

ASTM D-882 TD 27.0 27.0 26.0

Elongation at break

MD %

135.0 140.0 135.0 ASTM D-882

TD 140.0 140.0 140.0

F-5 Value MD

kg/mm2 11.0 11.0 11.0

ASTM D-882 TD 10.0 11.0 10.0

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.5 1.5 1.5 ASTM D-2305

(150℃, 30min) TD 0.0 0.0 0.0


- 0.30 0.35 0.35

ASTM D-1894 μk 0.35 0.35 0.35

Haze % 2.80 2.50 3.0 ASTM D-1003

Wetting Tension IN

dyne/cm 52 52 52

ASTM D-2578 OUT 38 38 38


PRODUCT INFORMATION

2011-04-01


PI-6



TYPE(CODE) : CD102








Yield mm2/kg 울산 김천 울산

Tensile Strength MD

kg/mm2 26.0 26.0 27.0

ASTM D-882 TD 25.0 27.0 26.0

Elongation at break

MD %

160.0 160.0 155.0 ASTM D-882

TD 140.0 140.0 150.0

F-5 Value MD

kg/mm2 11.0 11.0 11.0

ASTM D-882 TD 10.0 10.0 10.0

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.5 1.5 1.5 ASTM D-2305

(150℃, 30min) TD 0.0 0.0 0.0


- 0.30 0.30 0.30

ASTM D-1894 μk 0.35 0.35 0.35

Haze % 1.5 1.30 1.50 ASTM D-1003

Wetting Tension IN

dyne/cm 52 52 52

ASTM D-2578 OUT 38 38 38


PRODUCT INFORMATION

2011-04-01


PI-7



TYPE(CODE) : CD102









Tensile Strength MD

kg/mm2 27.0 25.0 26.0

ASTM D-882 TD 26.0 25.0 26.0

Elongation at break

MD %

155.0 165.0 165.0 ASTM D-882

TD 150.0 140.0 145.0

F-5 Value MD

kg/mm2 11.0 11.0 11.0

ASTM D-882 TD 10.0 11.0 10.0

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.5 1.0 1.2 ASTM D-2305

(150℃, 30min) TD 0.0 0.0 0.0


- 0.30 0.30 0.30

ASTM D-1894 μk 0.35 0.30 0.30

Haze % 3.5 1.5 1.5 ASTM D-1003

Wetting Tension IN

dyne/cm 52 52 52

ASTM D-2578 OUT 38 38 38


PRODUCT INFORMATION

2011-04-01


PI-8



TYPE(CODE) : CD102









Tensile Strength MD

kg/mm2 25.0 19.0 19.0

ASTM D-882 TD 23.0 21.0 20.0

Elongation at break

MD %

170.0 210.0 210.0 ASTM D-882

TD 140.0 140.0 130.0

F-5 Value MD

kg/mm2 11.0 11.5 11.5

ASTM D-882 TD 10.5 11.0 11.5

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.2 0.7 1.0 ASTM D-2305

(150℃, 30min) TD 0.0 0.2 0.2


- 0.30 0.70↓ 0.70↓

ASTM D-1894 μk 0.30 0.70↓ 0.70↓

Haze % 1.5 1.30 1.50 ASTM D-1003

Wetting Tension IN

dyne/cm 52 52 52

ASTM D-2578 OUT 38 38 38


PRODUCT INFORMATION

2011-04-01


PI-9



TYPE(CODE) : CD102








Yield mm2/kg 5.7 4.8 4.1

Tensile Strength MD

kg/mm2 18.0 17.0 18.0

ASTM D-882 TD 19.0 18.0 18.0

Elongation at break

MD %

230.0 240.0 240.0 ASTM D-882

TD 130.0 140.0 190.0

F-5 Value MD

kg/mm2 11.5 11.5 11.5

ASTM D-882 TD 11.5 11.5 11.5

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.0 1.0 1.0 ASTM D-2305

(150℃, 30min) TD 0.2 0.2 0.5


- 0.70↓ 0.70↓ 0.70↓

ASTM D-1894 μk 0.70↓ 0.70↓ 0.70↓

Haze % 1.80 2.00 2.50 ASTM D-1003

Wetting Tension IN

dyne/cm 52 52 52

ASTM D-2578 OUT 38 38 38


PRODUCT INFORMATION

2011-04-01


PI-10



TYPE(CODE) : CD102








Yield mm2/kg 3.8

Tensile Strength MD

kg/mm2 18.0

ASTM D-882 TD 18.0

Elongation at break

MD %

250.0 ASTM D-882

TD 200.0

F-5 Value MD

kg/mm2 11.0

ASTM D-882 TD 11.0

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.0 ASTM D-2305

(150℃, 30min) TD 0.5


- 0.70↓

ASTM D-1894 μk 0.70↓

Haze % 2.80 ASTM D-1003

Wetting Tension IN

dyne/cm 52

ASTM D-2578 OUT 38


PRODUCT INFORMATION

2011-04-01


PI-11



TYPE(CODE) : CD103








Yield mm2/kg 김천 59.5 울산

Tensile Strength MD

kg/mm2 26.0 26.0 27.0

ASTM D-882 TD 27.0 27.0 26.0

Elongation at break

MD %

135.0 140.0 135.0 ASTM D-882

TD 140.0 140.0 140.0

F-5 Value MD

kg/mm2 11.0 11.0 11.0

ASTM D-882 TD 10.0 11.0 10.0

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.5 1.5 1.5 ASTM D-2305

(150℃, 30min) TD 0.0 0.0 0.0


- 0.30 0.35 0.35

ASTM D-1894 μk 0.35 0.35 0.35

Haze % 2.80 2.50 3.0 ASTM D-1003

Wetting Tension IN

dyne/cm 38 38

ASTM D-2578 OUT


PRODUCT INFORMATION

2011-04-01


PI-12



TYPE(CODE) : CD103









Tensile Strength MD

kg/mm2 26.0 26.0 27.0

ASTM D-882 TD 25.0 27.0 26.0

Elongation at break

MD %

160.0 160.0 155.0 ASTM D-882

TD 140.0 140.0 150.0

F-5 Value MD

kg/mm2 11.0 11.0 11.0

ASTM D-882 TD 10.0 10.0 10.0

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.5 1.5 1.5 ASTM D-2305

(150℃, 30min) TD 0.0 0.0 0.0


- 0.30 0.30 0.30

ASTM D-1894 μk 0.35 0.35 0.35

Haze % 1.5 1.30 1.50 ASTM D-1003

Wetting Tension IN

dyne/cm 38 38

ASTM D-2578 OUT


PRODUCT INFORMATION

2011-04-01


PI-13



TYPE(CODE) : CD103









Tensile Strength MD

kg/mm2 27.0 25.0 26.0

ASTM D-882 TD 26.0 25.0 26.0

Elongation at break

MD %

155.0 165.0 165.0 ASTM D-882

TD 150.0 140.0 145.0

F-5 Value MD

kg/mm2 11.0 11.0 11.0

ASTM D-882 TD 10.0 11.0 10.0

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.5 1.0 1.2 ASTM D-2305

(150℃, 30min) TD 0.0 0.0 0.0


- 0.30 0.30 0.30

ASTM D-1894 μk 0.35 0.30 0.30

Haze % 3.5 1.5 1.5 ASTM D-1003

Wetting Tension IN

dyne/cm 38 38

ASTM D-2578 OUT


PRODUCT INFORMATION

2011-04-01


PI-14



TYPE(CODE) : CD103









Tensile Strength MD

kg/mm2 25.0 19.0 19.0

ASTM D-882 TD 23.0 21.0 20.0

Elongation at break

MD %

170.0 210.0 210.0 ASTM D-882

TD 140.0 140.0 130.0

F-5 Value MD

kg/mm2 11.0 11.5 11.5

ASTM D-882 TD 10.5 11.0 11.5

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.2 0.7 1.0 ASTM D-2305

(150℃, 30min) TD 0.0 0.2 0.2


- 0.30 0.70↓ 0.70↓

ASTM D-1894 μk 0.30 0.70↓ 0.70↓

Haze % 1.5 1.30 1.50 ASTM D-1003

Wetting Tension IN

dyne/cm 38 38 38

ASTM D-2578 OUT


PRODUCT INFORMATION

2011-04-01


PI-15



TYPE(CODE) : CD103








Yield mm2/kg 5.7 4.8 4.1

Tensile Strength MD

kg/mm2 18.0 17.0 18.0

ASTM D-882 TD 19.0 18.0 18.0

Elongation at break

MD %

230.0 240.0 240.0 ASTM D-882

TD 130.0 140.0 190.0

F-5 Value MD

kg/mm2 11.5 11.5 11.5

ASTM D-882 TD 11.5 11.5 11.5

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.0 1.0 1.0 ASTM D-2305

(150℃, 30min) TD 0.2 0.2 0.5


- 0.70↓ 0.70↓ 0.70↓

ASTM D-1894 μk 0.70↓ 0.70↓ 0.70↓

Haze % 1.80 2.00 2.50 ASTM D-1003

Wetting Tension IN

dyne/cm 38 38 38

ASTM D-2578 OUT


PRODUCT INFORMATION

2011-04-01


PI-16



TYPE(CODE) : CD103








Yield mm2/kg 3.8

Tensile Strength MD

kg/mm2 18.0

ASTM D-882 TD 18.0

Elongation at break

MD %

250.0 ASTM D-882

TD 200.0

F-5 Value MD

kg/mm2 11.0

ASTM D-882 TD 11.0

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.0 ASTM D-2305

(150℃, 30min) TD 0.5


- 0.70↓

ASTM D-1894 μk 0.70↓

Haze % 2.80 ASTM D-1003

Wetting Tension IN

dyne/cm 38

ASTM D-2578 OUT


PRODUCT INFORMATION

2011-04-01


PI-17



TYPE(CODE) : CD104









Tensile Strength MD

kg/mm2 25.0 19.0 19.0

ASTM D-882 TD 23.0 21.0 20.0

Elongation at break

MD %

170.0 210.0 210.0 ASTM D-882

TD 140.0 140.0 130.0

F-5 Value MD

kg/mm2 11.0 11.5 11.5

ASTM D-882 TD 10.5 11.0 11.5

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.2 0.7 1.0 ASTM D-2305

(150℃, 30min) TD 0.0 0.2 0.2


- 0.30 0.70↓ 0.70↓

ASTM D-1894 μk 0.30 0.70↓ 0.70↓

Haze % 1.5 1.30 1.50 ASTM D-1003

Wetting Tension IN

dyne/cm 38 38 38

ASTM D-2578 OUT 52 52 52


PRODUCT INFORMATION

2011-04-01


PI-18



TYPE(CODE) : CD104








Yield mm2/kg 5.7 4.8 4.1

Tensile Strength MD

kg/mm2 18.0 17.0 18.0

ASTM D-882 TD 19.0 18.0 18.0

Elongation at break

MD %

230.0 240.0 240.0 ASTM D-882

TD 130.0 140.0 190.0

F-5 Value MD

kg/mm2 11.5 11.5 11.5

ASTM D-882 TD 11.5 11.5 11.5

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.0 1.0 1.0 ASTM D-2305

(150℃, 30min) TD 0.2 0.2 0.5


- 0.70↓ 0.70↓ 0.70↓

ASTM D-1894 μk 0.70↓ 0.70↓ 0.70↓

Haze % 1.80 2.00 2.50 ASTM D-1003

Wetting Tension IN

dyne/cm 38 38 38

ASTM D-2578 OUT 52 52 52


PRODUCT INFORMATION

2011-04-01


PI-19



TYPE(CODE) : CD104








Yield mm2/kg 3.8

Tensile Strength MD

kg/mm2 18.0

ASTM D-882 TD 18.0

Elongation at break

MD %

250.0 ASTM D-882

TD 200.0

F-5 Value MD

kg/mm2 11.0

ASTM D-882 TD 11.0

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.0 ASTM D-2305

(150℃, 30min) TD 0.5


- 0.70↓

ASTM D-1894 μk 0.70↓

Haze % 2.80 ASTM D-1003

Wetting Tension IN

dyne/cm 38

ASTM D-2578 OUT 52


PRODUCT INFORMATION

2011-04-01


PI-20



TYPE(CODE) : CD105









Tensile Strength MD

kg/mm2 25.0 19.0 19.0

ASTM D-882 TD 23.0 21.0 20.0

Elongation at break

MD %

170.0 210.0 210.0 ASTM D-882

TD 140.0 140.0 130.0

F-5 Value MD

kg/mm2 11.0 11.5 11.5

ASTM D-882 TD 10.5 11.0 11.5

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.2 0.7 1.0 ASTM D-2305

(150℃, 30min) TD 0.0 0.2 0.2


- 0.30 0.70↓ 0.70↓

ASTM D-1894 μk 0.30 0.70↓ 0.70↓

Haze % 1.5 1.30 1.50 ASTM D-1003

Wetting Tension IN

dyne/cm 38 38 38

ASTM D-2578 OUT 38 38 38


PRODUCT INFORMATION

2011-04-01


PI-21



TYPE(CODE) : CD105








Yield mm2/kg 5.7 4.8 4.1

Tensile Strength MD

kg/mm2 18.0 17.0 18.0

ASTM D-882 TD 19.0 18.0 18.0

Elongation at break

MD %

230.0 240.0 240.0 ASTM D-882

TD 130.0 140.0 190.0

F-5 Value MD

kg/mm2 11.5 11.5 11.5

ASTM D-882 TD 11.5 11.5 11.5

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.0 1.0 1.0 ASTM D-2305

(150℃, 30min) TD 0.2 0.2 0.5


- 0.70↓ 0.70↓ 0.70↓

ASTM D-1894 μk 0.70↓ 0.70↓ 0.70↓

Haze % 1.80 2.00 2.50 ASTM D-1003

Wetting Tension IN

dyne/cm 38 38 38

ASTM D-2578 OUT 38 38 38


PRODUCT INFORMATION

2011-04-01


PI-22



TYPE(CODE) : CD105


All the information given herein is the basic suggestion to the use of ASTROLL film. Even though the information

is accurate, users should carry out their own test regarding the fitness of ASTROLL film for their own particular

usages. Concerning this information, any liability, copyright, and freedom under patent are not assumed. The

observance of all legal regulations and patents is the user’s responsibility.



Yield mm2/kg 3.8

Tensile Strength MD

kg/mm2 18.0

ASTM D-882 TD 18.0

Elongation at break

MD %

250.0 ASTM D-882

TD 200.0

F-5 Value MD

kg/mm2 11.0

ASTM D-882 TD 11.0

Modulus MD

kg/mm2

ASTM D-882 TD

Heat Shrinkage MD

% 1.0 ASTM D-2305

(150℃, 30min) TD 0.5


- 0.70↓

ASTM D-1894 μk 0.70↓

Haze % 2.80 ASTM D-1003

Wetting Tension IN

dyne/cm 38

ASTM D-2578 OUT 38


cd101-105 for solvent based coating & printing

Documents