FERROUS METALLURGY
ORE
Naturally Occurring substance from which a metal can be extracted at a profit
From a single ore more than one metal can be extracted.
ORE MINERALThe mineral containing ore from which a metal can be extracted at a profit
The naturally occurring materials containing iron are known as minerals of iron and mineral
deposits from which iron can be extracted at a profit (economically) are known as Iron-Ores.
GANGUEImpurities associated with the ores
METHODS OF REMOVAL OF GANGUE
1) Hand Picking(Sorting)
2) Crushing, Grinding and Dressing
3) Weathering (Removal of soluble impurities)
4) Calcinations (Heating @ high temp to remove volatile materials)
5) Roasting (Burning of ore in excess air)
6) Smelting (Fusing the ore by heating it in a suitable furnace)
EXTRACTIVE METALLURGY
It is a branch of Metallurgy which is a study of extraction of me tal, purification
and recycling
-
8/3/2019 demir cevheri-FerrousMetallurgy
3/46
Page 3 of46
Pyro metallurgical process Hydro metallurgical process Electro metallurgicalprocess
The process which is used toobtain metal from ore bythermal treatment.
In this process some salt orleaching agent or solution isused to obtain metal from ore
The process of winning andrefining of metal by the use of
electricity
LEACHANTChemical that dissolves a particular metal
EXTRACTION OF METAL FROM ORE
Separating the ore from gangue.
Driving away certain ingredients by heat short of fusion
Fusing the ore one or more times in the presence of certain reagents called Fluxeswhich combine with the non-metallic impurities and allow the metal to settle down in an
impure form. A metal thus obtained is further refined to be used.
RAW MATERIAL REQUIRED FOR MAKING IRONa) Iron Ore
b) Coking coal or Coke
c) Fluxes ( CaCO3, Dolomite: CaCO3.MgCO3 )
d) Air
APPROXIMATE QUANTITIES FOR MAKING 1 TONS OF IRONMaterial Quantity
Iron Ore 1.7-1.8
Coke 0.7-0.8
Fluxes 0.4-0.5
IRONSymbol: Fe
Atomic Number: 56
Commercial Forms %age of Carbon
Pig Iron 2.5-4.5
Wrought Iron 0.12-0.25
Steel 0.25-2.5
-
8/3/2019 demir cevheri-FerrousMetallurgy
4/46
Page 4 of46
ADVANTAGES AND DISADVANTAGES OF IRONAdvantages Disadvantages
Enormous deposits are present Poor Corrosion resistance
Easy to reduce than Non-Ferrous metals High density
Cheap metal Poor conductor of heat and electricity ascompared to Cu and Al
Forms series of alloys -
Magnetic in nature -
CLASSIFICATION OF IRON ORESa) Geological Classification
b) Mineralogical Classification
c) Impurities associated with Fe ore
d) Appearance/Texture
GEOLOGICAL CLASSIFICATION
Sedimentary Igneous Lateritic Replacement
These mainly includeSiO2 and iron ore inalternative bands. Iron is present
in the form ofstone
In the form ofpowder (Blue
Dust)
These are derivedfrom igneous materialof volcanic origin &occur mainly asmagnetite.
These are formed inconditions ofalternating dry & wetseasons resulting inleaching away ofSiO2 and alkalis fromthe mother-rockleaving behind mainly
Fe-ore.
The circulating waterremoves limestone(CaCO3) depositingiron carbonate in itsplace. Subsequentlythe surface weatheringoxidizes part of theiron carbonate to Fe-
oxide.
-
8/3/2019 demir cevheri-FerrousMetallurgy
5/46
Page 5 of46
MINERALOGICAL CLASSIFICATION OF IRON ORE
MinerologicalClassification
Magnetite Limonite
Liminite
Turgite
Geothite
Xanthosiderite
Limonite
Heamatite Chloropal Pyrite Siderite
-
8/3/2019 demir cevheri-FerrousMetallurgy
6/46
Page 6 of46
Properties Magnetite Limonite Heamatite Chloropal Pyrite Siderite
Formula Fe3O4 mFe2O3.nH2O Fe2O3 FeSiO3 FeS2 FeCO3
Commonname
Ferrosoferricoxide
Hydrousferric oxide
AnhydrousFerricoxide
IronSilicate
IronSulphide
IronCarbonate
%age of Fe 72.5% 52.13-66.31%
70% Decreasesdue toDolomite*
- Decreasesdue toDolomite*
Contribution 5% 40-60% - - -
SpecificGravity
5 - 5-6 - 4.95-5 -
Appearance Grey - Black Brown Red -Fool`sGold
-
EasyDetection
Magnetic innature
Mostly inall rocks,
Nonmagnetic
due to**d/c < 1.2
Highstrength
Insolublein water,
Fool`Gold,
Nonmagnet
Highstrength
Reduction Difficult Moderate EasyDifficut tobreak the
oreModerate
Difficut tobreak the
ore*Dolomite is self fluxing agent, Diabasic MgCO3.CaCO3 .
**orbital/shell ratio
LIMONITE ORE TYPES
Limonite Sub-Ore Formula
Liminite Fe2O3.3H2O
Turgite 2Fe2O3.H2O
Limonite 2Fe2O3.3H2O
Geothite Fe2O3.H2O
Xanthosiderite Fe2O3.2H2O
-
8/3/2019 demir cevheri-FerrousMetallurgy
7/46
Page 7 of46
CONCENTRATION OF IRON ORE
MECHANICAL CONCENTRATION OF IRON ORE
It involves mechanical concentration i.e. erosion of rocks containing iron ore by moving water.
More the speed of the water more will be the erosion. It also depends on the gradient of water.
So the corroded rock particles containing Fe ore moves with water, more dense the rock, earlier
will it settle down and dense rock will travel with water. Hence due to this mechanical factor the
concentration of Fe ore is different in different areas.
CHEMICAL CONCENTRATION OF IRON ORE
CRYSTALLIZATION
Magma inside the earth crust contains different iron ores along with other mineralcomposites. The solidification rate of magma is very slow hence the material having
similar composition will solidify or crystallize together. Hence due to this difference the
concentration of Fe ore is different in different areas.
PRECIPITATION
This involves water falling on rocks or water in the form of steam blowing the rock.
Chemical reactions take place on its surface and iron ores are separated from the rock
and are deposited there.
The chemical reaction or precipitation of iron ore depends on
Speed of moving water
Rate of the reaction
Chemical nature of gangue
Concentration of Iron
Ore
Mechanical
Chemical
Crystallization
Precipitation
-
8/3/2019 demir cevheri-FerrousMetallurgy
8/46
Page 8 of46
IRON ORE DEPOSITS IN PAKISTAN
Dilband
Nizampur
Chiniot
PachinkohRajoa
Langrial
Kalah Bagh
Chilgazi
Dommel Nisar
Name ofDeposit
Distancefrom
Karachi
Reserves % of Fe Ore Mineral Methods ofMining
km Million Ton
Kalabagh(Punjab)
1200 300 30-35 Silicates,Carbonates
Underground
Dilband(Balochistan)
800 200 35-45 Oxide,Heamatite
Open Cast
Nizampur(NWFP)
1600 100 30-35 Heamatite Underground
Pachinkoh(Balochistan)
1750 45 35-38 Heamatite,Magnetite
Underground
Langrial(NWFP)
1600 30 30-40 Silicates,Carbonates
Underground
Chilgazi(Balochistan)
1150 23 10-55 Magnetite Underground
Chiniot(Punjab)
1200 16 10-60 Silicates,Carbonates
Underground
Dommel Nizar
(NWFP)
1900 3 Upto 60 Magnetite Underground
Which is
better?
Have a
look
-
8/3/2019 demir cevheri-FerrousMetallurgy
9/46
Page 9 of46
Dilband resources are better than all deposits of Pakistan (Fe ore deposits) and thus have a fair
chance of development due to good accessibility, moderate grade (% of Fe), large reserves and
open cast minebility. These deposits consist of Hematite and are low in P2O5; hence are better
than many iron deposits of the world.
Dilband Ore Ores from USA & Europe
35-45% Fe 5-35% Fe
Low P2O5 High P2O5
Heamatite Heamatite & Limonite
VALUATION OF FE ORE1. Richness
2. Location
3. Composition of Gangue
4. Procedure required before smelting
Richness
% of Fe present in the ore, How much Fe is required, How much ore is required is dependent on% of Fee.g.India requires 2 ton ore (55-60% Fe) to produce 1 ton Fe whereas Australia requires 1.5 ton ofore (68% of Fe)
Location
Geological GeographicalHilly Area Deep Valleys Mode of Transportation
Composition of Gangue
Gangue material will affect the cost of the iron. If the amount of the gangue in the Fe ore is morethen we have to add fluxes to separate gangue which will as a result increase the cost ofproduction
Some compounds in gangueOxides, Carbonates, Sulphates, Na2O, K2O, P2O5,As2O3
They are reduced in Blast furnace
a. Totallyb. Partiallyc. Non-reducible
Totally Reduced in BFPhosphorous Arsenic
The entire amount of P in the ore isreduced and joins the pig iron. Thepresence of phosphorous affects theproperties of iron.
Usually not present in Fe ore but if it ispresent then following treatments are used
Prior Reduction
Calcination (Volatilization)
Dilband
-
8/3/2019 demir cevheri-FerrousMetallurgy
10/46
Page 10 of46
In general, the phosphorous content ofan ore reduces the value of the ore.Phosphorous in iron causes ColdShortness during rolling.
Roasting
Zn PbZinc in the iron ore does not pass into thepig iron but it volatilizes during reduction
These Zinc vapours penetrate into therefractory material (lining) and affect itsproperties.
Pb is reduced during Blast Furnaceoperation, it settles at the bottom ofthe furnace due to its high specificgravity (SG).
Partially Reduced in Blast FurnaceS, Mn, SiO2
Silica, compounds of manganese and sulphur are partially reduced in the blast furnace so Si,Mn and S join the pig iron. Amount of these depends on the nature of Fe ore and the operation
of burning fuel.Non-Reducible
It contains the oxides the oxides like Al2O3, MgO and Alkalis. These entirely stay with the slagduring smelting.
Al2O3 Alkali
Its presence in the slag producesMagnesium Aluminate and CalciumAluminates.
o It increase melting point of slag.o Decreases the viscosity of slag.
Al2O3 should be 5% in the slag.Because increasing it would increase thefluxes requirement.
MgO, CaO react with Al2O3.
Alkalis affect the refractory lining.
As a flux, they react with impuritiesand make slag.If present in the ore they prove to beprofitable (self fluxing).
Treatments & Procedure required before Smelting
Situation Treatment CommentsBig Lumps ComminutionSmall Lumps Agglomeration Because otherwise, the
oxygen/air blasts will blowaway the small lumps.
Carbonates Calcination Reducing toOxides
This will produce CO2
-
8/3/2019 demir cevheri-FerrousMetallurgy
11/46
Page 11 of46
SMELTING
Any metallurgical process in which metal in pure or crude form is separated by fusion from its
impurities with which it may be chemically combined or physically mixed is called smelting.
SLAG
The molten oxide product of melting is known as Slag. It is formed by both gangue and flux.
Raw Materials in Blast Furnace
Fe, Metallurgical Coal, FluxesMetallurgical coal Flux
The coal which can be converted intocoke is called Coking coal/Metallurgicalcoal.
In the absence of air (O2).Why not use coal? Because coke has:
o Strengtho Permeabilityo Higher calorific valueo Less volatile content (Higher
fixed-C content)o Less moistureo Less heating requirement
Coke should contain:o Volatile 2%o Ash 10%
o Fixed Carbon 85%o P = 0.018-0.04%o S = 0.6-1.5%o S by 0.1% Coke requirement
by 2%
They are added during smeltingFor bringing down the melting point,softening point of gangue.
To reduce viscosity of slagTo reduce the activity of some of itscomponents to make themstable/unstable.
-
8/3/2019 demir cevheri-FerrousMetallurgy
12/46
Page 12 of46
FORMULA FOR THE EVALUATION OF FLUX
It indicates that the quantity of SiO2 should be less than MgO + CaO. In general CaCO3 content
should not be less than 95%, SiO2 should be less than 5%. Nearly 0.5 ton of CaCO3 is needed
for producing 1 ton of Fe.
THE BLAST FURNACE FUEL-COKE
Why Coke?
Strong
Less Ash S, P
Quality control
Size
As the rank of coking coal decreases, its coking properties also diminish.
Ideally Coal =
7% ashLess than 1% S
About 5% P
COKE
It is a solid coherent residue achieved by heating coal in the absence of air.
FUNCTIONS OF COKE
Coke serves these major functions.
1. It is a fuel
2. Providing heat requirement for chemical reactants, melting of slag and metal.
3. It produces and regenerates reducing gases for the reduction of Fe oxide.
4. It provides an open permeable bed through which slag and metal passes down into the
hearth and hot reducing gases pass outward.
-
8/3/2019 demir cevheri-FerrousMetallurgy
13/46
Page 13 of46
QUALITY OF COKEIt is related to the quantity of coal, its processing and subsequent carbonization process.
In general the properties which determine the value of coke as a the blast furnace fuel are:
a) Chemical compositionb) Chemical reactivity
c) Thermal Stability
d) Size
e) Abrasion resistance and Strength
Quality of coke
Composition
Chemically the useful component of coke is fixed carbon which is the fuel as well as thereducing agent in the blast furnace. the balance is made up of ash contents, volatilematters, other impurities.
The inorganic residue left after burning it usually contains refractory oxides like silica,
alumina etc. It also contains Sulphur & Phosphorous.Reactivity
Defined as rate of reaction b/w coke and Oxygen and any other gases capable ofreacting with coke e.g.
C + O2 CO2The rate of burning of coke controls the rate of production of the blast furnace. In generalthe rate of burning of coke is directly proportional to:
i. Area of coke exposedii. Temperature and Pressureiii. Affinity of coke to oxygen (it depends on the blending material used and
the carbonization process adopted.)
Thermal StabilityDuring descent in the the blast furnace, the coke gets progressively heated; when thecoke gets heated beyond the temperature at which it was made in the coke oven, theprocess of carbonization restarts and the coke begins to contract.The temperature gradient results in the contraction and expansion of coke stresses andits consequent tendency to degradation. So in order to achieve thermal stability, highcarbonization temperature and uniform coke is used.
Size
Among all the qualities of good metallurgical coke the most important are its size andstrength.
The size range is known to affect the distribution of material inside the furnace andconsequently the gas flow which has a direct bearing on the production rate. It wasfound that:
a) If mean size of burden = 13mm then coke size 53mmb) This corresponds to an average coke to burden ratio:
Coke : Burden4 : 1
In general it has been suggested that the optimum coke size should be 3-5 times thanthat of burden.
-
8/3/2019 demir cevheri-FerrousMetallurgy
14/46
Page 14 of46
Abrasion resistance and strength
During the transportation of coke in the the blast furnace different abrasion actionsoccur.
In addition to this, coke has to withstand high temperature and nearly 20-25 meter tallburden lying over it, when it reaches the tuyere level.
A coke that breaks down under these additions will adversely affect furnace
permeability.It is an established practice to estimate the suitability of coke used in a the blast furnacein terms of its strength and abrasion resistance by measuring its shatter and abrasionindices.
SHATTER TEST (IMPACT RESISTANCE)It consists of carefully dropping of sample of certain fixed weight of coke from a standard height
on a standard quality floor. The shatter index is expressed as %age retained on various sieves
of certain fixed sizes.
TUMBLER TEST (ABRASION RESISTANCE)A standard weight of coke sample is part into a drum and rotating it for a fixed speed. The
abrasion index is expressed as the %age of the material retained on various sieves.
-
8/3/2019 demir cevheri-FerrousMetallurgy
15/46
Page 15 of46
ALTERNATIVE FUELS
Charcoal
It was used as alternative fuel to replace entirely the coke using small furnaces. Thecharcoal used should be strong and ferrous.
The Proportion of Fe made by charcoal is practically negligible.
Furnace height is to be lessened because it cannot bear the burden.
Wood is converted into charcoal on heating.Formed Coke
The solid fuel produced from non-coking lower rank coal is called formed coke.
Only that formed coke that has proper physical and chemical properties can be used inthe the blast furnace.
Formed Coke Conventional CokeCheaper CostlyLower manufacturing cost Higher manufacturing costContinuous operation of the plant unlikecoke ovens
Discontinuous manufacturing processes
Ferro Coke
Fe + C
A carbonized lump produced from a mixture of Fe bearing fines and non-metallurgicalcoal is known as ferro coke.
The %age of Fe bearing fines may vary from a few %ages to 15-20%. It has all thenecessary requirements for its use in the blast furnace.
Advantages:Non-metallurgical coal is used indirectly in the blast furnace.
The total fuel requirement reduces since certain proportion of pre-reduced Fe is already
inside the ferro coke.Coke consumption is reduced in the blast furnace and productivity is increased. Conclusion
The blast furnace cannot be run without a certain amount of coke in the charge.
The efficiency of the blast furnace mainly depends on quality of coke used as fuel. It istherefore necessary to understand certain properties of coke and devise means to obtainthese properties. Ferro coke and formed coke are being developed to substitute coke.
-
8/3/2019 demir cevheri-FerrousMetallurgy
16/46
Page 16 of46
MANUFACTURING OF FORMED COKE
The formed coal is charged to the carbonization furnace where the coal passes through
low temperature carbonizing zone and then it is heated @ 1000C.
The heating rate is controlled so as the coal not to be generated, collapse and break
caused by bulging and shrinking.
The carbonized coke is cooled to 1000C or lower temperature in the cooling zone before
it is discharged from the furnace.
Coking Coal
Dryer
Pulverization
Kneading
Forming
Carbonization
Formed Coke
Binder
Non-CokingCoal
-
8/3/2019 demir cevheri-FerrousMetallurgy
17/46
Page 17 of46
DISTRIBUTION OF BURDEN IN BLAST FURNACE
Burden contains Fe ore, coke and flux.
The blast furnace is essentially working on the counter current principle. The descending
solid charge meets the current of ascending gases and reduction of Fe ore along with its
progressive heating takes place during the passage.
Of all the reactions taking place inside the blast furnace, the reduction of the Fe ore is
the most important and the most difficult.
EFFICIENCY OF THE BLAST FURNACE (PRODUCTION RATE)
It is directly determined by 2 important factors
I. Rate of reduction of Fe-ore
II. Rate of heating of Burden
PERMEABILITY
The ability of the material to give way to the gases to pass is called permeability.
Higher the permeability, greater the gasses will pass through it. Otherwise choking takes place.
Permeability is necessary to reduce choking (resistance to flow of gases).
SHAPE AND SIZEIf the charge particles are of similar size then the burden would be automatically a uniformly
permeable burden irrespective of the way of charging in the furnace.
However, blast furnace charge consists of different sizes and shapes of coke and ore, therefore
it is very difficult to distribute them inside the furnace. In general finer the particles less will be
the permeability.
CHARGING MECHANISMIt consists of double bell charging mechanism. In this the materials are first charged in the small
bell which is then lowered to allow the material to drop into the lower big bell during which the
big bell remains closed. Then the small one is closed and the big bell is lowered to drop the
charge inside the furnace. Such an arrangement practically prevents the furnace exhaust gases
from escaping into the atmosphere while charging.
The above two factors depend on the time of contact and exposed volume
of charge to gas. The burden therefore inside the blast furnace should haveuniform and good bulk permeability.
-
8/3/2019 demir cevheri-FerrousMetallurgy
18/46
Page 18 of46
ELEMENTS OF DISTRIBUTION
A mass of material consisting of shapes, size and densities that falls inside the blast
furnace with various trajectories.
In general dense, small and irregular particles remain subsequently where they fall,
building ridges while light, large and smooth particles roll into troughs. As shown in the
figure.
This results in non-uniform permeability in the bed. The areas containing coarse particle
have less segregation while the areas containing fine particles have high segregation.
In general the coarse particles segregate in centre of the furnace shaft and the fine
particles segregate at or near the wall depending upon the clearance between the bell
and the furnace wall. As far as possible Fe ore should be present in area of maximum
gas flow for efficient reduction.
The size and system of charging are to be selected so as to have maximum utilization of
gas subject to ensure smooth performance of blast furnace.
FACTORS AFFECTING DISTRIBUTIONThe factors that affect the distribution of charge inside the blast furnace have been summarized
below
1. Design of the blast furnace and charging device
a) Angle and side of big bell
b) Speed of lowering of big bell
2. Inconsistency in physical properties of charging material
a) Size range of various charge materials
b) Angle of repose of raw material and other physical characteristics of charge
c) Density of charge
3. Level, system and sequence of charge program of revolving the distributora) Distribution of charge on big bell
b) Height of big bell from stock line i.e. the charge level in furnace throat
c) Order and proportions of charging of various raw materials
ANGLE AND SIZE OF THE BIG BELL
Angle = 50-530
Normal gap between the bell and the furnace wall is usually between 800-1000 mm.
Size of the bell depends upon the size of the throat of the blast furnace.
If the clearance between the bell and furnace wall is more, the crest is located furtheraway from wall.
If the gap is less between big bell and the furnace wall, the fines accumulate near the
wall and v-type contour is formed.
The V and M type contour formations at the stock-line, which are also called hoppers
depend upon the bell clearance from the wall
The more is the gap/clearance the crest is located further away from the wall and the
lesser is the gap the more fines accumulate nearer the wall.
-
8/3/2019 demir cevheri-FerrousMetallurgy
19/46
Page 19 of46
Too much or too narrow a gap between the bell corner and the throat wall tends to
segregate the sizes and prevents normal distribution from being achieved
Optimum ratio of throat to bell diameter results in optimum segregation of the burden
In the figure given below, a) is the V-type contour hopper and b) M- type contour hopper
1)STOCK LINE LEVELThe behavior of the particles immediately after their impact on the stock line controls the nature
of segregation i.e. uniformity and permeability in the burden. This behavior depends on
1. Height of fall of material from the bell on the stock line
2. Angle of Big Bell
The effect of height of the big bell above the stock line on the distribution of the charge is shown
in the figure. The lowering of the stock line to the point where the trajectory of fall of material
comes against the wall of the furnace results in the fine segregation near the wall.
This is shown at point h1 and as the level goes up the crest moves away from the wall (at higherlevel say h2 and h3). If the angle of inclination becomes steeper then the hopper will form in the
centre but if angle of inclination becomes deeper then the crust will move away from wall.
-
8/3/2019 demir cevheri-FerrousMetallurgy
20/46
Page 20 of46
2)SPEED OF LOWERING OF THE BIG BELL
1. The greater the speed of lowering of the big bell, the more the material will move toward
the wall and thereby alter the contour as well as distribution.
2. V type contour is formed if the speed is greater; on the other hand, the slower the speed,
more the material will move toward the centre and M type contour is formed. In short thespeed of lowering of the big bell should be maximum as far as possible because slower
speed tends to segregate the fines.
3)DENSITY OF CHARGED MATERIAL
Ore 5-6 g/cc
Flux 3-3.5 g/cc
Coke 1.5 g/cc
It means the rolling tendency of coke particles is more as compared to Fe ore. Since densities
cannot be altered the size may be so chosen that their differential rolling tendencies are offset tosome extent.
In general the size of the Fe ore is 3-5 times lower than that of coke.
4)ANGLE OF REPOSE
When a multi-particle material is allowed to gently fall on a horizontal plane, it tends to form a
conical heap. The base angle of this cone is called Angle of Repose.
Factors affecting Angle of Repose:
Particle size
Surface characteristics
Shape
PSD (Particle Size Distribution)
The smaller the Angle of Repose the more will be the homogeneity.
How to overcome Angle of Repose?
1. Eliminate the fines
2. Minimize the moisture
3. Remove the clay4. Dry the ore i.e. more dry ore (free from fines) more the angle of repose
-
8/3/2019 demir cevheri-FerrousMetallurgy
21/46
Page 21 of46
5)SIZE OF CHARGE PARTICLES
Increasing fines in the ore results in
1. Decrease in burden permeability
2. Increase in pressure drop
3. Decrease in reduction rate
The size ranges in order and practice;
More reducible 10-37 mm
Less reducible 10-25 mm
6)DISTRIBUTION OF CHARGE ON THE BIG BELL
Three systems are used for charging charge to furnace stock
1. Bucket Old one
2. Belt conveyer Modern
3. Double bell Present (>80%)
The distribution of charge on the big bell greatly affects the distribution in the furnace. For
distributing the charge on the the big bell different operations have been used. The Mckee
revolving distributor and its modifications are most widely used.
-
8/3/2019 demir cevheri-FerrousMetallurgy
22/46
Page 22 of46
MCKEE TOP OPERATION FOR CHARGING THE FURNACE
1) Both bells closed; skip discharging the charge in the small belt hopper.
2) The big bell closed. Small bell opened to allow the charge to fall in the big bell hopper.
3) Small bell closed, big bell opened to allow the charge to be dropped inside the furnace.
4) Both bells closed
MCKEE REVOLVING DISTRIBUTIONThe charging is carried out in the sequence of CCOO and the hopper is rotated through 60 after
every skip is dumped on the small bell which is lowered after every four (4) skips to dump the
charge on the big bell. After eight (8) such charges have been charged i.e. when 32 skips are
charged, the big bell is lowered to allow the whole charge to fall into the furnace.
Advantage;
Homogenous mixing of charge
4 skips
Small Bell (after
each skip 600)
THE BIG BELL
Furnace
After 8 times
Opened
Opened
-
8/3/2019 demir cevheri-FerrousMetallurgy
23/46
Page 23 of46
ORDER OF CHARGING
Mozumdar emphasizes the role of order of charging in the furnace distribution as change in the
system of the charging of raw material influences distribution and character of gas flow to an
extent considerably more than changes of level of charging and size of the charge, it is
therefore having all conditions similar on an average only 3.5% of the cases go to the credit of
control of distribution of gas flow by changing the size of the charge and 85% controls due to
change of system of charging.
The charging sequence in relation to the level of charging and the size of the charge has to be
adjusted so as to have maximum utilization of gas ensuring smooth performance of the furnace.
CHARGING SYSTEMS4 charging systems are commonly used.
1. Cn Om
2. Om Cn 3. Cn Om
4. OmCn
Cn Om Cn-1 (wide range of distribution of coke)
BURDEN PREPARATION-1
TREATMENT OF FE ORE
BURDEN QUALITY
In order to operate the blast furnace smoothly and for high production rate the burden shouldhave following properties.
Physical Chemical
1) A close size range with minimum of fines(PSD narrow)
2) Ability to withstand physical stresses3) Non-decrepitating nature4) Ability to withstand reducing conditions
without breaking5) Good bulk reducibility6) Low swelling index during reduction
7) A high softening temperature with anarrow temperature range of fusion
1) A high %age of Iron and low ganguecontents
2) A low %age of SiO2, Al2O3 etc3) Proper overall chemistry of the burden to
ensure clean slag and metal separationat minimum temperature.
-
8/3/2019 demir cevheri-FerrousMetallurgy
24/46
Page 24 of46
CRUSHING AND SIZEThe size of the Fe ore should not be too small or too large because;
If Fe ore contains too much fine particles
1) Permeability decreases2) Pressure drop inside the furnace increases (varying pressure of O2)
3) Reducibility decreases
If too large then
1) Material remains unreduced
2) Demand of heat increases
3) The maximum ore size is based on;
a) Ore chemistry
b) Bulk reducibility
c) Ore characteristics
In any crushing process we can reduce the size to 4-6 times
1st stage
150-250mm (reduced)
2nd stage
27-55mm (reduced)
BENEFICIATION TECHNIQUESConversion of low grade Fe ore to high grade Fe ore
1) Magnetic separation
2) Gravity separation
3) Froth floatation
4) Electrostatic separation5) Magnetic roasting
6) Low intensity magnetic separation
7) Washing
8) Calcination
Max. Size from run of mine = 100-
125mm
-
8/3/2019 demir cevheri-FerrousMetallurgy
25/46
Page 25 of46
MAGNETIC SEPARATION
Magnetite can be easily separated at low intensity magnetic field as it is strongly magnetic.
Weakly magnetic materials like hematite can be separated at high intensity magnetic field only.
Dry method is suitable in the particle size +6mm and wet method is suitable if the particle size is
-0.1mm. Magnetite can be separated at 1500 orested magnetic field intensity while hematite
can be separated at 12000 orested.
Usually ore is held on a rotating drum part of whose surface is magnetized. The non-magnetic
tailings fall from the drum. A series of magnetic separators are used in active beneficiation.
GRAVITY SEPARATION
HEAVY MEDIA
The method is used when the particle size is 6-40mm. An artificial heavy medium is prepared by
having ferro-silicon sand in a suspension in water such that the density lies in between that of
the Fe oxide and the gangue. The Fe oxide concentrate sinks and the gangue overflows as
tailing.
JIGGING
We use a perforated bottom on which ore particles are placed, the periodic impulses of water
flow are subjected through the perforation; as a result heavy particles move down and are
reduced as concentrate.
TABLING
It is suitable for sandy feeds. The feed moves over an inclined shaking table and is washed with
a cross stream of water. Its operation cost is high and output is very small i.e. 1-2 tons/hour.
SPIRAL
This method is suitable for materials having particle size 0.1-1.5mm. In it the ore is washed
down the spiral launder with a curved bottom. Fe mineral being heavier moves to the bottom of
the curved track while the lighter tailings sling toward the outer rim. The output of individual
spiral is very low. Therefore it is necessary to have no. of spirals.
FROTH FLOATATION
This method is based on the fact that surface property of some minerals can be temporarily
altered to make it either hydrophobic (abhorrence from water) or hydrophilic (water loving).
Hydrophobic minerals can be floated as froth if air is bubbled through a suspension of such
minerals in water. Various reagents are used according to the surface characteristics of metallic
minerals or gangue. Petroleum sulphonates, fatty acids and special oils etc are used to float iron
oxide. Starch tends to float silicon and depress iron oxide. Even though floatation reagents are
required in small amount but are costly so the overall cost of the process increases.
-
8/3/2019 demir cevheri-FerrousMetallurgy
26/46
Page 26 of46
ELECTROSTATIC SEPARATION
This involves the selective sorting of solid species by means of utilizing forces acting on the
charged bodies in an electric field. The difference in the electrical conductivities between iron
minerals and the gangue is made use of in separating the two with magnetic separation. The
use of electrostatic separation in the final stages improves the purity of the product and overall
concentration.
MAGNETIC ROASTING
Reduction
Hematite Magnetite
600-8000C, atm
It is better than high intensity magnetic separation
It is very easy to reduce hematite to magnetite under slightly reducing conditions at 600-800C
and the ore is then easily separated by using low intensity magnetic field.
WASHING
Washing means separation of particles based on their sizes by using such fluids in which finer
particles get suspended and hence washed away while the large particles completely fail to get
suspended and hence separated from the fines. Washing improves screening ability by
removing the fine particles.
DRYINGWet ores were initially being used by many operators from an economical point of view as the
hot gases of the blast furnace have the capacity to wet the charge. But the problem which was
faced was that the wet raw material cannot be screened efficiently so it is generally winded.
CALCININGFe is ultimately produced by reducing Fe oxide present in the ore. The use of OH, CO 3
2 or
sulphite type ores can be used for Fe making after calcining.
BLENDINGThis involves mixing two or more types of material from two or more sources to obtain a uniform
material of desired qualities over an extended period. The Fe ore blend may be made up of ore
from different sources or it may also include materials such as coke breeze and CaCO 3.
-
8/3/2019 demir cevheri-FerrousMetallurgy
27/46
Page 27 of46
AGGLOMERATION OF IRON OREThe fines in the iron ores need to be agglomerated into lumps of suitable physical
characteristics size/shape so it can be used in blast furnace. The techniques used are as:
1. Briqwetting
2. Nodulising
3. Extrusion
4. Sintering
5. Pelletising
BRIQWETTING
It essentially consists of pressing of ore fines with or without the binder into a block or briqwet of
some suitable size and shape and then subjected it to a hardening process. Cement briqwetting
is done with 1-5% cement as binder, press into blocks and harden in a tunnel kiln heated toabout 13500C. Production is 1000t/day from a single plant.
There are two types of briqwetting
Cold briqwetting
Hot briqwetting
COLD BRIQWETTING
It is produced by adding 10% cement and hardening them for several days like cement
concrete.
HOT BRIQWETTING
It is done by pressing ore fines at 800-10500C under normal or slightly reducing conditions.
NODULISING
Fine ore concentrate and some carbonesous material like tar are passed through a rotary kiln
which is slightly inclined to the horizontal. The temperature in the rotary kiln softens the ore, the
speed of rotary kiln is 1-2rpm, length is 30-60m, diameter is 2m and diameter of sinter zone is
4m. the charge takes 1-2 hour in the kiln. This technique is replaced by sintering and pelletising.
EXTRUSIONIt was used in 1950 on a small scale level. In this process moist ore with or without binder is fed
into a chamber and then extruded from that chamber. The product obtained is cylindrical and is
cut into a desired small size. The product is dried and fired before being used in blast furnace.
-
8/3/2019 demir cevheri-FerrousMetallurgy
28/46
Page 28 of46
SINTERING
It is a process of heating of mass of fine particles to the temperature little below the melting
point for the purpose of agglomeration of fines into lumps.
PELLLETISINGThe process consists of rolling of moist ore fines of less than 100 mesh size with or without a
binder into pellets usually 7-20mm in size. These green pellets are dried and fired before
charging to blast furnace.
SINTERING
It is a process of heating of mass of fine particles to the temperature little below the melting
point for the purpose of agglomeration of fines into lumps. In other words the sintering meansCasting without melting
PRINCIPLE OF SINTERINGIron ore sintering is carried out by putting a mixture of iron ore mixed
with solid fuel on a permeable grate. Coke breeze is normally used as
fuel. The top layer of this bed is heated to a sintering temperature by a
gas or an oil burner and air is drawn downward to the permeable grate
with the help of exhaust blowers. The narrow combustion zone
developed initially at the top layer that travels through the bed raising
the temperature of the bed. The cold blast drawn through the bed that
cools the already sintered layer and thereby gets itself heated. The
heat contained in blast is utilized in drawing and preheating the lower
layers in the bed. In the combustion zone the bonding takes place
between the grains and the strong and porous aggregate is formed.
The process is over when the combustion has reached the lowest layer
of the bed. The sintered coke is then removed from the grate in hot
condition or after partial cooling. It is broken, screen and cool to produce desired fraction. The undersized
is recycled and oversized is fully cooled and send to the Blast Furnace.
Permeable grate
Bed
Charge
hopper
Ignition
source
-
8/3/2019 demir cevheri-FerrousMetallurgy
29/46
Page 29 of46
QUALITY OF SINTERING
The main objective of sintering is to agglomerate of fines particles. The others are
1. Size of ore (specific size is required in order to do sintering)
2. Strong agglomeration with good bulk reduction that depends on nature of ore and
sintering process
3. To remove the volatile like CO2, H2O, SO2 etc
4. Flux incorporation in the burden
PROCESS VARIABLES OF SINTERING
There are certain variables that affect the process of sintering which are as
1. Bed permeability as decided by the particle size, shape of the mixture and thickness ofthe bed.
2. Thickness of the bed
3. Total volume of air blast drawn through the bed during sintering
4. Rate of blast drawn through the bed during sintering
5. Amount and quality of fuel added in the charge
6. Amount and quality of moisture added in the charge
7. Nature of ore fines
8. Any non-uniformity in the bed composition or in the process of sintering
During sintering heat exchange takes place between the solid charge and air blast that is drawn
through the bed. At any time during sintering the air blast initially gets heated that is it cools the
combustion zone and in turns heats the lower layer of the bed.
It is therefore essentially a phenomenon of gas solid heat exchange. In order to carry out both
the heating and cooling functions of gas phase affectively i.e to obtain a faster rate of heat
exchange the heat capacity of the blast drawn through the bed should be maximum, it means
that the volume of the air drawn through bed during sintering should be maximum. More
permeable the bed, the more will be air blast drawn through it. More permeable bed however
leads to loss of the strength in the resulting sinter. These two factors oppose each other and
hence should be adjusted at the optimum.
TYPES OF SINTER
There are three types of sinter
1. Acid sinter
2. Fluxed sinter
3. Super fluxed sinter
-
8/3/2019 demir cevheri-FerrousMetallurgy
30/46
Page 30 of46
ACID SINTER
In this process there is no addition of flux during agglomeration of fines of sintering. Fluxes are
added separately during reduction of iron ore in the blast furnace.
FLUXED SINTERIn this process the fluxes are added to make the basicity of the sinter equal to the basicity of
slag in the blast furnace.
Basicity of fluxed sinter= Basicity of slag in Blast Furnace
SUPER FLUXED SINTER
In this process the percentage of fluxes is added more than in fluxed sinter. The basicity of
super fluxed sinter should be greater than the basicity of slag in the blast furnace.
MECHANISM OF SINTERING
TYPES OF BOND IN PARTICLES OR FINES
The particles or fines during sintering form a bond between them. There are two types of
bonding exist between the particles which are
1. Solid state bonding
2. Slag or glass bonding
ORE BED
WET
DRY
CALCINING
COMBUSTION
-
8/3/2019 demir cevheri-FerrousMetallurgy
31/46
Page 31 of46
SOLID STATE BONDING
In solid state bonding the particles either diffuse or recrystallize. The physical change occurs in
the particles when they combined to form a bond. For example calcium carbonate heated at
high temperature and pressure is converted into marble.
SLAG OR GLASS BONDING
In this slag fuses and acts as binder between the fines and developed a bond. The chemical
composition changes during formation of bond. During chemical change iron ore fines convert
into ferrite, spinal, silicate. (Spinal) MgAl2O4 . Hercynite (FeAl2O4). Jacabsite (MnFe2O4)
Physical change occurs when time is large and temperature is low
Chemical change occurs when time is short and temperature is high
During bonding the probability may be
1. No chemical change no physical change
2. No chemical change but change physically
3. Both chemical and physical change
RAW MATERIALSThere raw materials specification should be proper in order to do better sintering process. There
are following raw materials specifications which are as
Charge size
Fuel content
Moisture
CHARGE SIZEIf the particle size of the charge is fine then the contact area will increase and on the other hand
permeability will decrease. So sintering process will be improper. In order to do better sintering
the particle size of the charge should be coarse, so that gasses can pass through the bed.
If we have less than 3mm fractions then above 6mm fractions along with are used.
FUEL CONTENT
Fuel content is used uniformly 6-8%. The percentage of fuel in the top layer of the bed should
be greater as compared to the lower layer because the heating is started from the bottom of the
bed and going upward.
-
8/3/2019 demir cevheri-FerrousMetallurgy
32/46
Page 32 of46
MOISTURE
Moisture controls the permeability of the bed. When moisture evaporates it produces porosity.
CONTROL OF SINTERING PROCESSSintering process is controlled by the following factors
Input heat
Ignition input source
Moisture content (permeability control)
Speed of grate/bed machine
Bed height
BLAST FURNACEIt is a steel tank lined with a refractory material (bricks).
PURPOSEThe purpose of blast furnace is to reduce iron oxide into molten iron called as hot metal.
RAW MATERIALSThe raw materials required for the production of iron are:
1. Iron ore
2. Limestone (fluxes)
3. Coke
4. Hot blast of air
DIAGRAM
-
8/3/2019 demir cevheri-FerrousMetallurgy
33/46
Page 33 of46
EQUIPMENTS/PARTS OF BLAST FURNACE
The blast furnace consists of the following parts
Foundation
Stack column
Hearth
Bosh
Charging facilities available
FOUNDATION
It is a massive steep reinforce concrete mass partially embedded below the ground level. It is
sufficiently strong to stand the loaded furnace weight.
SKIP CAR (CONVEYOR)
The skip cars and in some cases conveyors are used to deliver blast furnace charge to the top
of the furnace.
BOSH
The bosh is the inverted conical section. It has the maximum diameter.
RECEIVING HOPPER
The blast furnace charge is loaded into the receiving hoppers which in turn deliver the charge tothe rotating distributor. The rotating distributor helps in assuming the uniform distribution of
charge in furnace stack.
HEARTHIt is a crucible like vessel upon which the vertical shaft portion of the furnace sets. All the molten
metal and slag collect in the hearth before being drain.
BELLS (LARGE AND SMALL)
The large and small bells are conical shaped devices that form a gas tight lock hopper. Thehopper prevents the gas escaping from the furnace while it is being charge.
BUSTLE PIPESIt encircles the blast furnace and delivers the hot blast air from the blast line to furnace.
-
8/3/2019 demir cevheri-FerrousMetallurgy
34/46
Page 34 of46
TUYERES
The hot blast air is delivered to the furnace through water cooled opening called tuyeres. The
tuyeres are located at the top of hearth.
STACK COLUMNThe stack is the upper portion of furnace where the charge is preheated.
METAL AND SLAG NOTCHESThe molten metal is removed from the hearth through the metal notch. The metal is placed into
the transfer ladles, while the slag may be transferred through the slag pot.
PROCESSESThe production of iron in the blast furnace consists of the following steps which are as
INTRODUCTION OF THE CHARGEThe charge is introduced in the blast furnace through cup and cone arrangement.
INTRODUCTION OF HOT BLASTSimultaneously hot blast of air is introduced in the furnace through tuyeres.
COMBUSTION OF COKE
Coke present in the charge burns in the hot air producing CO2.
C + O2 CO2
PRODUCTION OF CO(REDUCING AGENT)The CO2 forms rise up reacts with C and produces CO.
CO2 + C 2CO
REDUCTION OF HEMATITE(Fe2O3)
CO formed is a powerful reducing agent. It reduces hematite to iron.
Fe2O3 + 3CO 2Fe + 3CO2
Fe2O3 + CO Fe3O4 + CO2
-
8/3/2019 demir cevheri-FerrousMetallurgy
35/46
Page 35 of46
Fe3O4 + CO FeO + CO2
FeO + CO Fe + CO2
DECOMPOSITION OF LIMESTONE
Due to high-temperature limestone decomposes into lime and carbon dioxide.
CaCO3 CaO + CO2
FORMATION OF SLAGCalcium oxide reacts with silica and formed calcium silicate which is called as slag.
The iron formed is collected at the bottom of the furnace and a slag formed a layer on it. The
iron obtained from this method is called pig iron. It contains carbon as major impurity.
REFRACTORY MATERIALSMaterials that retain their shape and chemical identity at a very high temperature are called
refractory materials. E.g. fire clay, Alumina, magnesia etc
These materials withstand at high temperature without fusing.
CLASSIFICATIONS OF REFRACTORY MATERIALSRefractory materials are classified on the basis of the following groups
Based on refractory material
Based on refractoriness
Based on method manufacturing
CLASSIFICATIONS ON THE BASIS OF REFRACTORY MATERIAL
REFRACTORY
MATERIALS
ACIDIC BASIC NEUTRAL
-
8/3/2019 demir cevheri-FerrousMetallurgy
36/46
Page 36 of46
Acidic refractries consist of acidic materials. They are not attacked by acidic materials but
easily attacked by basic materials E.g. Silica, quartz, fire clay
Basic refractries consist of basic materials. They are not attacked by basic materials but easily
attacked by acidic materials. E.g. Magnesite, dolomite refractroies.
Neutral refractories are made from weakly acidic and basic materials. They are not attacked
by both acidic and basic materials. E.g. Graphite, chromite, zirconia refractories.
CLASSIFICATIONS ON THE BASIS OF REFRACTORINESSAccording to the refractoriness, refractories are classified into four types.
CLASSIFICATIONS ON THE BASIS OF METHOD MANUFACTURING
DRY PROCESS: This process includes crushing the materials and presses it in a die and
produces the required shape. E.g. bricks refractory, tile refractory etc.
FUSED CAST: The refined raw materials are heated at 1900-2500C in a electric arc
furnace,until completely melted. The melted substance is poured into specific molds and left to
solidify gradually, resulting in a fused cast refractory. E.g. Alumina mullite, zirconia etc.
REFRACTORYMATERIALS
LOW HEATDUTY
(1520-16300C)
MODERATEHEAT DUTY
(1630-16700C)
HIGH HEAT DUTY
(1670-17300C)
SUPER HEAT DUTY
(Greater than 17360C)
REFRACTROY
MATERIALS
DRY
PROCESSFUSED CAST
HAND
MOULDING
-
8/3/2019 demir cevheri-FerrousMetallurgy
37/46
Page 37 of46
These refractroies have
Poor spalling resistance
Sudden expansion and contraction
High erosion and abrasion strength
HAND MOULDING: These refractroies are made from slurry materials. E.g. Gun type refractory,
Spray type refractory.
PROPERTIES OF REFRACTORY MATERIALS
1-REFRACTORINESSIt is the ability of a material to withstand very high temperature without softening or deformation
under particular service condition.
HOW TO MEASURE REFRACTORINESS
Since most of the refractories are mixtures of several metallic oxides, they dont have sharp
melting points. So the refractoriness of a refractory is generally measured as the softening
temperature and is expressed in terms of pyrometric cone equivalent (PCE).
PYROMETRIC CONE EQUIVALENT (PCE)
Pyrometric cone equivalent is the number which represents the softening temperature of a
refractory specimen of standard dimension and composition.
OBJECTIVE OF PCE TEST1. To determine the softening temperature of a test refractory material
2. To classify the refractoies
3. To determine the purity of refractories
4. To check whether the refractory can be used at a particular serving temperature
2-POROSITY
Porosity is defined as the ratio of its pore volume to bulk volume. Porosity is an important
property of refractory materials because it affects many other characteristics like chemical
stability, strength, abrasion resistance and thermal conductivity.
It reduces the strength
It reduces the resistance to abrasion
It reduces the resistance to corrosion
Highly porous refractory possess the thermal conductivity. This is due to presence of
more air voids, which act as insulators, and hence it is used in furnace lining.
High porous refractory reduces the thermal spalling. Gases and slag attack more easily
-
8/3/2019 demir cevheri-FerrousMetallurgy
38/46
Page 38 of46
3-THERMAL SPALLING
Thermal spalling is the property of cracking, breaking, peeling off a refractory material under
high temperature.
It is due to the following factors
1. Rapid change in temperature
2. Slag penetration
RAPID CHANGE IN TEMPERATURE
This causes uneven expansion and contraction within the mass of a refractory material and
leads to development of uneven stresses and strains.
SLAG PENETRATION
This causes the variation in the co-efficient of thermal expansion and leads to spalling. Thermal
spalling can be decreased by using high porosity, low co-efficient of expansion and good
thermal conductivity refractory.
4-SLAG RESISTANCE
Slag attacks the refractory at high temperature and alters its composition by forming of certain
compounds with the refractory material. A basic slag attacks acidic refractory and vice versa.
Rate of slag attacks is accelerated because of following reason
Defective joints and cracks in refractory material
Rough and extra porous surface
The movement of slag
The rate of slag attack is reduced if refractory is dense and smooth surface.
5-ABRASION RESISTANCEA refractory is subjected to wear when it comes in contact with the moving charge as in case of
blast furnace. Descending charge material result in abrasion or wearing off refractory lining
material
6-ERROSION RESISTANCEIt damages due to mechanical action occurs when metal or gas carrying dust and slag particles
hit against the refractory lining resulting in chipping off of particles from the refractory
-
8/3/2019 demir cevheri-FerrousMetallurgy
39/46
Page 39 of46
SELECTION OF REFRACTORIESThe refractories are selected on the basis of the following factors
1. Area of application
2. Working temperature
3. Extent of abrasion and impact
4. Structural load of furnace
5. Stress due to temperature gradient
6. Chemical composition/furnace environment
7. Heat transfer
8. Cost concentration
SOME IMPORTANT CLASS OF REFRACTORY
FIRE CLAY
It is hydrated alumina silicate Al2O3.2SiO2.2H2O containing about 25-45% Al2O3 and 50-80%
SiO2. The term fire bricks are referred to fire clay bricks. There crushing strength decreases with
increasing temperature. Porosity varies from 8-24% depending on the temperature on which it is
fired. Higher the porosity less will be the slag penetration and less will be the effect of sudden
changes in temperature. It is used in the upper part of Blast Furnace.
SILICA REFRACTORY
Raw material SiO2 refractory are the various forms of natural deposits of SiO2. For examplequartz, ganister, sandstone, sand. One of the great difficulties of SiO 2 refractory is that SiO2
occurs at different allotropic forms which are stable at different temperature. Sudden changes in
temperature causes fire crack in silica bricks and this causes disintegration or spalling.
HIGH ALUMINA REFRACTORY
They are not used extensively because they are very costly. As the general rule the
refractoriness increases with increasing alumina content of alumina silicate refractory compare
to fire clay refractory. It contains 45-95% alumina. High alumina refractory gives better service
under severe condition due to
High abrasion and erosion resistance
High spalling resistance/slag
Good volume stability
High refractoriness
-
8/3/2019 demir cevheri-FerrousMetallurgy
40/46
Page 40 of46
CARBON/GRAPHITE REFRACTORY
Carbon occurs in nature both in amorphous and crystalline form. Graphite is crystalline form of
carbon. In graphite carbon atoms are arranged in hexagonal structure. Graphite is infusible and
stable at about 36000C. It is not attack by slag and is resistant to thermal shock. Graphite is
less prone to oxidation compare to other amorphous form of carbon.
USES
1. Carbon bricks find more extensive use in lining bosh/hearth of Blast Furnace.
2. They are also used in furnaces where temperature is high and atomosphere is non
oxidize
3. Due to the presence of reducing atomoshpere in Blast Furnace the life of carbon
refractory is prolong
4. High thermal conductivity of carbon lining helps in easy temperature control in the lower
part of Blast Furnace
5. Iron and slag runner are also lined with carbon
CERAMIC GRAPHITE REFRACTORY
They are used in steel making process due to their high resistance of spalling and inactive
nature.
MgO graphite refractory is used in ladle lining
Alumina graphite refractory is used in nozzle, sliding gates
-
8/3/2019 demir cevheri-FerrousMetallurgy
41/46
Page 41 of46
MAJOR CAUSES OF FAILURE OF BLAST
FURNACE REFRACTORY
There are following factors that cause the failure of blast furnace refractory
Attacking of carbon mono oxide (CO) gas on the refractory
Action of alkali vapours
Action of other volatile matters
Action of acidic and basic slag
Abrasion of refractory by solid, liquid and gases
Action of molten metals
Condition of operation
Blowing in procedure
All these factors do not affect all the areas of blast furnace. One or more factors can affect atone area. For example in the stack, the lining has to stand with abrasion with solid burden and
CO attack, while in bosh region lining has to stand high temperature, erosion, attack of molten
acidic and basic slag. Similarly the hearth has to withstand the attack of molten metal and slag
without breaking.
BLOWING INThe process of starting a newly lined blast furnace is called blowing in.
In general the operation involves the following main steps
1. Drying
2. Filling
3. Lightening
DRYING
The new lining of the furnace contains significant portion of moisture which must be completely
removed before the temperature of the blast furnace raised. The operation is called drying in
which the furnace is slowly heated. The slowly temperature is about 200 0C which is slowly
increased to about 425
0
C. But furnace drying can be accomplished by
Hot blast from stove
Use of coke oven to generate and supply hot gasses
Use of coke fire in the hearth
In this process care must be taken to heat up and dry the furnace slowly to avoid cracks in the
newly built or required parts.
-
8/3/2019 demir cevheri-FerrousMetallurgy
42/46
Page 42 of46
FILLING
The blast furnace is then filled with the start of charge with generally consist of coke and fluxes
in the lower part and coke, flux and an increasing amount of ore in the upper part. So the fuel
ratio is much larger than the furnace operation.
It is so because we have to raise the temperature up to smelting temperature before the ore
reaches to the bottom of the furnace. Once the smelting temperature is reached, the burden or
proportion of ore is gradually increased as the furnace is operated until about two weeks it starts
carrying the normal burden.
LIGHTENING
The most common method to light the blast furnace is by using the low volume hot blast of
approximately 5500-6500C to ignite the coke in front of tuyers. The blast volume is increased
every few hours and after about 24hour 40-50% of full blast is achieved. It is increased until the
full blast is achieved that is 100%
OPERATION UNTIL REGULAR PRODUCTION
Soon after the furnace is lighted the slag begins to accumulate in the hearth and a little later the
iron as well. As soon as the slag reaches about the level tuyers it is drawn off at the sinter notch
and the operation continuous until sufficient iron has accumulated to tape. The first iron tape off
is not of proper grade as it is at this time impossible to have such temperature and composition
of slag as to produce iron of given grade. Within a few tapes however the furnace is usually
brought up to the production of desired grade.
BLOWING OUTThe process of shutting down the blast furnace i.e. for relining is called blowing out.
When a furnace is to be shut down or blown out the ore charge is gradually reduced and
stopped. Flux and fuel are continued until all metal and slag are tapped out and flux is then
discontinued. The fuel is gradually reduced and finally shut off and fired slowly burns out. The
furnace must be allow to cool gradually before being emptied
-
8/3/2019 demir cevheri-FerrousMetallurgy
43/46
Page 43 of46
BLAST FURNACE PRODUCTSThe blast furnace products contain
Pig iron
Slag
gasses
COMPOSITION OF PIG IRON
Pig iron is major product of blast furnace that contains the impurities carbon, silicon,
manganese, sulphur and phosphorus.
These impurities in the pig iron have the maximum range and depend on the burden chemistry
of the charge.
If the sulphur contents are very high in the pig iron then it will create hot shortness during
rolling, forging. This is because at high temperature sulphur reacts with iron and forms
iron sulphide (FeS) that produces cracks.
S, Si, P are not completely reduced in the blast furnace they should have the minimum
percentage in the pig iron in order to make steel.
Whatever is the phosphorus content in the burden; the whole of it is reduced and finally joins with molten metal. The presence of carbon in the pig iron is beneficial during its
conversion to steel. Whereas the presence of phosphorus in pig iron is detrimental, and
it adds to the cost of steel making. The contents of Si and S depends on the volume of
slag its basicity and operating temperature furnace and burden chemistry of charge.
These can therefore be varied within certain limits by adjusting the burden chemistry,
fuel rate and those conditions will affect the temperature of the blast furnace.of the
Elements Percentage impurities
Carbon 3.5-4.2%Silicon 0.5-2.5%Manganese 0.5-1.5%Phosphorus 0.04-2%Sulphur 0.04-0.15%
-
8/3/2019 demir cevheri-FerrousMetallurgy
44/46
Page 44 of46
SULPHUR PROBLEMIt is difficult for steel maker to control the sulphur specification and S content of steel. S
content of steel should not be more than 0.025-0.04. The process of steel making is capable of
reducing the S contents up to 40% in the hot metal charge. Its me an in order to achieve therequired percentage of S the hot metal should not contain more than maximum 0.06%. This
can be achieved by using coke having maximum 0.6% S. if the S in the ore is around 1% then
it is difficult to meet hot metal specification with respect to S contents. The sulphur problem is
more severe when the continuous casting of steel is adopted. The finished molten steel should
have no more than 0.025% S for continuous casting to operate smoothly. The coke use as a
fuel in the blast furnace should low in sulphur. The cost of fuel is in inverse proportion to its S
content.
For economical reason therefore every efforts must be made to eliminate S and produce
required quality of hot metal before putting it in the steel making furnace.
HOW TO CONTROL SULPHURDesulphurization inside the blast furnace can be affected in three different ways
By having higher basicity
By increasing the volume of slag
By increasing the hearth temperature
FeS + CaO + C CaS + FeO + CO
When the pig iron is tapped off from the blast furnace and is going to the steel making unit then
during its rout the following process are run to remove either silicon or sulphur
Basic burdening and desiliconization
Acidic burdening and desulphurization
-
8/3/2019 demir cevheri-FerrousMetallurgy
45/46
Page 45 of46
BASIC BURDENING OF BLAST FURNACEIf the alumina (Al2O3) content in the burden is high the furnace hearth temperature has to be on
the high side to keep the slag thick and free flowing. The basicity has also to be raised to obtain
proper slag in this case. These conditions are more favorable for disiliconisation of metal insidethe furnace. This can be fully used in obtaining pig iron containing less than 0.06% or preferably
0.04% sulphur. This often leads to high silicon contents of pig iron. Since silicon reduction is
favored at high temperature. The pig iron is treated externally to remove silicon and produce hot
metal of the specification required for steel making. This external treatment for elimination of
silicon from molten iron is known as external disiliconisartion
REMOVAL OF SILICON
Silicon is removed externally by lancing the oxygen in the hot metal before carrying it in the
steel unit. When oxygen is lanced then temperature of the hot metal increases due to the
exothermic reaction. The temperature is maintained around 1400-14500
C by adding iron oxide(Fe2O3) and calcium oxide (CaO) because at this temperature silicon reacts with oxygen and
forms silica (SiO2) and go to the slag. If the temperature is very high means above 1450 0C then
carbon has high tendency with oxygen. So decarburization takes place which we dont want. So
we use mill scale (iron oxide) and lime as reagent to maintain temperature of molten iron in
order to remove silicon.
For dephosphorisation and desiliconisation of molten pig iron we have to provide sufficient
amount of oxygen in order to oxidize all the amount of Si, P, Mn.
ACIDIC BURDENING OF BLAST FURNACEThe acidic burdening of blast furnace can be readily practiced if the total gangue in the ore and
coke are salacious in nature. The slag basicity is also reduced since high basicity is no longer
necessary. The furnace is often operated with basicity less than 1 that is the slag produced is
acidic and for which the burden chemistry is adjusted with more acidic and less basic oxides.
The net result is that the silicon content of the metal is low which is advantageous for
subsequent basic process of steel making.
REMOVAL OF SULPHURA lance of oxygen is lowered into molten iron ladle and several kilogram powder of magnesium
is added. Sulphur is reduced to magnesium sulphide in violent exothermic reaction
-
8/3/2019 demir cevheri-FerrousMetallurgy
46/46
DISPOSAL OF METAL
Major portion of molten iron is sent to steel making plant for its conversion to steel
DISPOSAL OF SLAG
Slag is carried in ladle to the slag dumping yard where it is tipped as waste material.
Alternatively the slag granules are produced in a granulation plant where molten slag is poured
in turbulent water. These granules are increasingly being used as construction material.
CONCLUSION
The main product of blast furnace is molten iron along with slag. The chemistry of metal is
important and is adjusted as per the overall economy of steel production from ore. The
chemistry of slag is adjusted to obtain efficiency operation of blast furnace. The waste product
that is slag is also being put to some use.
-------------------------------------------------------------------------------------------------------------------------------