0refillable0olymer3yringes · 2019. 12. 17. · #/#nahigh techpolymer delivery in nests for easy...

Advantages of our prefillable syringes:

SCHOTT forma vitrum ag

®

Folder_TopPac.indd 1-2 22.09.09 18:34

® syringes are ideally used for:

®

®

®

®

®COC polymer of the highest purity

Delivery in nests for easy handling and filling

Physical properties of COC polymer

Unit Test TOPAS®

Method 6013

Heat deflection temperature °C ISO 75 130HDT/B at 0.45 MPa part 1 and 2

Water vapor permeability g x mm DIN 53122 0.035(23°C; 85% r.h.) m² x d

Water absorption % ISO 62 <0.01(water immerson at 23°C)

Density g/cm³ ISO 1183 1.02

Tensile strength N/mm² ISO 527 66 part 1 and 2

Impact strength (Charpy) kJ/m² ISO 179/1eU 15

Light transmission % ASTM D 1003 92Water vapor permeability: comparison ofdifferent polymers measured at 40°C/90 % rh.

0,0 0,5 1,0 1,5 2,0 2,5 3,0 3,5 4,0

TOPAS® 0,1

PP 0.5

PVC 1.2

PC 4.0

®

®

SCHOTT TopPac® product portfolio*customer mould

Format inml

0.5*

1.0 long

1.0

2.25

3

5

10

50

Outsidediameterin mm

9.4

9.4

11.4

11.4

11.6

15.0

18.0

31.5

Insidediameter in mm

6.5

6.5

8.75

8.75

8.75

12.2

14.7

27.9

Total length in mm

45.9

64.5

45.9

64.4

82.4

76.9

97.7

128.8

SCHOTT TopPac® syringes have excellent barrier properties

® lid

Cut flange

1-3 ml

5-50 ml

Tyvek® lidNest

outer bag

tub

Tyvek® sealing foil

¹TOPAS® is a registered trademark of TOPAS Advanced Polymers GmbH.

g x mm

m² x d

The SCHOTT TopPac® production in class B clean room is a completely integrated process

Plunger

Plunger rod

Folder_TopPac.indd 3-5 22.09.09 18:35

® syringes are ideally used for:

®

®

®

®

®COC polymer of the highest purity

Delivery in nests for easy handling and filling

Physical properties of COC polymer

Unit Test TOPAS®

Method 6013

Heat deflection temperature °C ISO 75 130HDT/B at 0.45 MPa part 1 and 2

Water vapor permeability g x mm DIN 53122 0.035(23°C; 85% r.h.) m² x d

Water absorption % ISO 62 <0.01(water immerson at 23°C)

Density g/cm³ ISO 1183 1.02

Tensile strength N/mm² ISO 527 66 part 1 and 2

Impact strength (Charpy) kJ/m² ISO 179/1eU 15

Light transmission % ASTM D 1003 92Water vapor permeability: comparison ofdifferent polymers measured at 40°C/90 % rh.

0,0 0,5 1,0 1,5 2,0 2,5 3,0 3,5 4,0

TOPAS® 0,1

PP 0.5

PVC 1.2

PC 4.0

®

®

SCHOTT TopPac® product portfolio*customer mould

Format inml

0.5*

1.0 long

1.0

2.25

3

5

10

50

Outsidediameterin mm

9.4

9.4

11.4

11.4

11.6

15.0

18.0

31.5

Insidediameter in mm

6.5

6.5

8.75

8.75

8.75

12.2

14.7

27.9

Total length in mm

45.9

64.5

45.9

64.4

82.4

76.9

97.7

128.8

SCHOTT TopPac® syringes have excellent barrier properties

® lid

Cut flange

1-3 ml

5-50 ml

Tyvek® lidNest

outer bag

tub

Tyvek® sealing foil

¹TOPAS® is a registered trademark of TOPAS Advanced Polymers GmbH.

g x mm

m² x d

The SCHOTT TopPac® production in class B clean room is a completely integrated process

Plunger

Plunger rod

Folder_TopPac.indd 3-5 22.09.09 18:35

Advantages of our prefillable syringes:

SCHOTT forma vitrum ag

®

Folder_TopPac.indd 1-2 22.09.09 18:34